Standard Specification for High-Strength Zinc–5 % Aluminum-Mischmetal Alloy-Coated Steel Core Wire for Use in Overhead Electrical Conductors

ABSTRACT
This specification covers round, high-strength, zinc-aluminum-mischmetal (Zn-5Al-MM) alloy-coated, steel core wire with Class A Zn-5Al-MM alloy coating used for mechanical reinforcement in the manufacture of special aluminum and aluminum-alloy conductors, steel reinforced. The base metal shall be steel produced by the open-hearth, electric furnace, or basic oxygen process. The wire shall be cold drawn and coated with Zn-5Al-MM alloy to produce the desired properties. Chemical requirements of the steel, such as carbon, manganese, phosphorus, sulfur, and silicon shall meet the requirements prescribed in this specification. The Zn-5Al-MM-coated steel core wire shall conform to the tensile and elongation requirements. Test methods for tensile, wrap, coating and adherence shall be also be performed.
SCOPE
1.1 This specification covers round, high strength, zinc–5 % aluminum-mischmetal (Zn–5Al–MM) alloy-coated, steel core wire with one class of Zn–5Al–MM coating (MA3) for use in overhead electrical conductors.  
1.2 This specification covers wire of diameter from 0.0500 to 0.1900 in. inclusive or 1.27 to 4.82 mm inclusive.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

• Status: Historical
• Publication Date: 28-Feb-2019
• ICS: 77.140.65 - Steel wire, wire ropes and link chains
• Technical Committee: B01 - Electrical Conductors
• Drafting Committee: B01.05 - Conductors of Ferrous Metals

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:B803/B803M −19
Standard Specification for
High-Strength Zinc–5% Aluminum-Mischmetal Alloy-Coated
1
Steel Core Wire for Use in Overhead Electrical Conductors
This standard is issued under the fixed designation B803/B803M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope B193 Test Method for Resistivity of Electrical Conductor
Materials
1.1 This specification covers round, high strength, zinc–5 %
B750 Specification for GALFAN
aluminum-mischmetal (Zn–5Al–MM) alloy-coated, steel core
E47 Test Methods for Chemical Analysis of Zinc Die-
wire with one class of Zn–5Al–MM coating (MA3) for use in
3
Casting Alloys (Withdrawn 1997)
overhead electrical conductors.
E1277 Test Method for Analysis of Zinc-5 % Aluminum-
1.2 This specification covers wire of diameter from 0.0500
Mischmetal Alloys by ICP Emission Spectrometry
to 0.1900 in. inclusive or 1.27 to 4.82 mm inclusive.
E29 Practice for Using Significant Digits in Test Data to
1.3 The values stated in either SI units or inch-pound units Determine Conformance with Specifications
are to be regarded separately as standard. The values stated in 2.3 Other Standard:
each system may not be exact equivalents; therefore, each GF-1 Standard Practice for Determination of Cerium and
system shall be used independently of the other. Combining Lanthanum Compositions in GalfanAlloy (5 %Al-0.04 %
4
values from the two systems may result in non-conformance La-0.04 % Ce-Bal SHG Zn)
with the standard.
3. Terminology
1.4 This international standard was developed in accor-
3.1 Abbreviations:
dance with internationally recognized principles on standard-
3.1.1 MM—mischmetal
ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom-
3.1.2 Zn–5Al–MM—zinc–5 % aluminum mischmetal alloy
mendations issued by the World Trade Organization Technical
3.2 Definitions:
Barriers to Trade (TBT) Committee.
3.2.1 lot—unless otherwise specified in the contract or
order, a lot shall consist of all coils of wire of the same
2. Referenced Documents
diameter and unit lengths submitted for inspection at the same
2.1 The following documents of the issue in effect on date
time.
of material purchase form a part of this specification to the
3.2.2 product code—Defines product coating type, coating
extent referenced herein.
class and strength grade. This specification covers only High
2
2.2 ASTM Standards:
StrengthClassA Zn–5Al–MMcoatedproductsandidentifiedas
A90/A90M Test Method for Weight [Mass] of Coating on
product code MA3.
Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
4. Ordering Information
A370 Test Methods and Definitions for Mechanical Testing
of Steel Products
4.1 Orders for material under this specification shall include
A751 Test Methods, Practices, and Terminology for Chemi-
the following information:
cal Analysis of Steel Products
4.1.1 Quantity of each size,
4.1.2 Wire diameter in inches or millimeters (Section 13),
4.1.3 Certification, if required (Section 18),
1
This specification is under the jurisdiction of ASTM Committee B01 on
4.1.4 Test report, if required (Section 18), and
Electrical Conductors and is the direct responsibility of Subcommittee B01.05 on
4.1.5 Package Size (Section 19).
Conductors of Ferrous Metals.
4.1.6 Product Code (Paragraph 3.2.2).
Current edition approved March 1, 2019. Published April 2019. Originally
approved in 1989. Last previous edition approved in 2016 as B803/B803M – 08
(2016). DOI: 10.1520/B0803_B0803M-19.
2 3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or The last approved version of this historical standard is referenced on
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM www.astm.org.
4
Standards volume information, refer to the standard’s Document Summary page on Available from International Lead Zinc Research Organization (ILZRO), 1822
the ASTM website. NC Highway 54 East, Suite 120, Durham, NC 27713, http://www.ilzro.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
B803/B803M−19
TABLE 2 Tensile Requirements
4.1.7 Order Example: five multiple lengths of 12 000 ft.
each, 0.1327 in. MA3 wire, packaged onto wooden non- Stress at 1 % Ultimate Tensile Elongation in 10
Specified Diameter
Extension, min Strength, min in., min %
returnable reels, with certified test report.
in. ksi ksi
5. Materials and Manufacture 0.0500 to 0.0899, incl 210 235 3.0
0.0900 to 0.1199, incl 205 230 3.0
5.1 The base metal shall be s
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: B803/B803M − 08 (Reapproved 2016) B803/B803M − 19
Standard Specification for
High-Strength Zinc–5 % Aluminum-Mischmetal Alloy-Coated
1
Steel Core Wire for Use in Overhead Electrical Conductors
This standard is issued under the fixed designation B803/B803M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This specification covers round, high strength, zinc–5 % aluminum-mischmetal (Zn–5Al–MM) alloy-coated, steel core wire
with one class of Zn–5Al–MM coating (MA3) for use in overhead electrical conductors.
1.2 This specification covers wire of diameter from 0.0500 to 0.1900 in. inclusive or 1.27 to 4.82 mm inclusive.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2.1 The following documents of the issue in effect on date of material purchase form a part of this specification to the extent
referenced herein.
2
2.2 ASTM Standards:
A90/A90M Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
B193 Test Method for Resistivity of Electrical Conductor Materials
B750 Specification for GALFAN
3
E47 Test Methods for Chemical Analysis of Zinc Die-Casting Alloys (Withdrawn 1997)
E1277 Test Method for Analysis of Zinc-5 % Aluminum-Mischmetal Alloys by ICP Emission Spectrometry
E29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
2.3 Other Standard:
GF-1 Standard Practice for Determination of Cerium and Lanthanum Compositions in Galfan Alloy (5 % Al-0.04 % La-0.04 %
4
Ce-Bal SHG Zn)
3. Terminology
3.1 Abbreviations:
3.1.1 MM—mischmetal
3.1.2 Zn–5Al–MM—zinc–5 % aluminum mischmetal alloy
3.2 Definitions:
1
This specification is under the jurisdiction of ASTM Committee B01 on Electrical Conductors and is the direct responsibility of Subcommittee B01.05 on Conductors
of Ferrous Metals.
Current edition approved Oct. 1, 2016March 1, 2019. Published October 2016April 2019. Originally approved in 1989. Last previous edition approved in 20082016 as
ɛ1
B803/B803M – 08 (2016). . DOI: 10.1520/B0803_B0803M-08R16.10.1520/B0803_B0803M-19.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
3
The last approved version of this historical standard is referenced on www.astm.org.
4
Available from International Lead Zinc Research Organization (ILZRO), 1822 NC Highway 54 East, Suite 120, Durham, NC 27713, http://www.ilzro.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
B803/B803M − 19
3.2.1 lot—unless otherwise specified in the contract or order, a lot shall consist of all coils of wire of the same diameter and
unit lengths submitted for inspection at the same time.
3.2.2 product code—Defines product coating type, coating class and strength grade. This specification covers only High
Strength Class A Zn–5Al–MM coated products and identified as product code MA3.
4. Ordering Information
4.1 Orders for material under this specification shall include the following information:
4.1.1 Quantity of each size,
4.1.2 Wire diameter in inches or millimeters (Section 13),
4.1.3 Certification, if required (Section 18),
4.1.4 Test report, if required (Section 18), and
4.1.5 Package Size (Section 19).
4.1.6 Product Code (Paragraph 3.2.2).
4.1.7 Order Example: five multiple lengths of 12 000
...