ASTM C230/C230M-20

Standard Specification for Flow Table for Use in Tests of Hydraulic Cement

ABSTRACT
This specification covers requirements for the flow table and accessory apparatus used in making flow tests for consistency or mortars in tests of hydraulic cement. The flow table shall consist of an integrally cast rigid iron frame and a circular rigid table top. Other details of the flow table, its mounting and lubrication are described in the specification. The conical mold for casting the flow specimen and the caliper for measuring the diameter of the mortar after it has been spread by the operation of the table are also discussed.
SCOPE
1.1 This specification covers requirements for the flow table and accessory apparatus (Note 1) used in making flow tests for consistency of mortars in tests of hydraulic cement, such as but not limited to Test Method C1437.
Note 1: To help clarify the design of the flow table and accessory apparatus see the drawing in Fig. 1 [Fig. 2]. This drawing is for informational purposes only.
FIG. 1 Flow Table and Accessory Apparatus (Partial) (IP)  
FIG. 1 Flow Table and Accessory Apparatus (Partial) (IP) (continued)  
FIG. 2 Flow Table and Accessory Apparatus (Partial) [SI]  
FIG. 2 Flow Table and Accessory Apparatus (Partial) [SI] (continued)  
FIG. 2 Flow Table and Accessory Apparatus (Partial) [SI] (continued)
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. It is permissible to use an inch-pound caliper and mold with a SI flow table or a SI caliper and mold with an inch-pound flow table. It is not permissible to mix a SI mold with an inch-pound caliper or an inch-pound mold with a SI caliper.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

• Status: Historical
• Publication Date: 31-May-2020
• ICS: 91.100.10 - Cement. Gypsum. Lime. Mortar
• Technical Committee: C01 - Cement
• Drafting Committee: C01.22 - Workability

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: C230/C230M −20
Standard Specification for
1
Flow Table for Use in Tests of Hydraulic Cement
This standard is issued under the fixed designation C230/C230M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* C219 Terminology Relating to Hydraulic and Other Inor-
ganic Cements
1.1 This specification covers requirements for the flow table
C1437 Test Method for Flow of Hydraulic Cement Mortar
and accessory apparatus (Note 1) used in making flow tests for
consistency of mortars in tests of hydraulic cement, such as but
3. Terminology
not limited to Test Method C1437.
3.1 Definitions:
NOTE 1—To help clarify the design of the flow table and accessory
3.1.1 The terms in this standard specification are defined in
apparatus see the drawing in Fig. 1 [Fig. 2]. This drawing is for
Terminology C125 and Terminology C219.
informational purposes only.
4. Flow Table and Frame
1.2 The values stated in either SI units or inch-pound units
are to be regarded separately as standard. The values stated in
4.1 The flow table apparatus shall consist of an integrally
each system may not be exact equivalents; therefore, each
cast rigid iron frame and a circular rigid table top 10 6 0.1 in.
system shall be used independently of the other. Combining
[255 6 2.5 mm] in diameter, with a shaft attached perpendicu-
values from the two systems may result in non-conformance
lar to the table top by means of a screw thread. The table top
with the standard. It is permissible to use an inch-pound caliper
and shaft with contact shoulder shall be mounted on a frame in
and mold with a SI flow table or a SI caliper and mold with an
such a manner that it can be raised and dropped vertically
inch-pound flow table. It is not permissible to mix a SI mold
through the specified height of 0.500 6 0.005 in. [12.7 6
with an inch-pound caliper or an inch-pound mold with a SI
0.13 mm] for new tables and of 0.500 6 0.015 in. [12.7 6
caliper.
0.38 mm] for tables in use, by means of a rotated cam. The
table top shall have a fine machined plane surface, free of
1.3 This standard does not purport to address all of the
blowholes and surface defects. The top shall be scribed with
safety concerns, if any, associated with its use. It is the
5
eight equidistant lines 2 ⁄8 in. [68 mm] long, extending from
responsibility of the user of this standard to establish appro-
the outside circumference toward the center of the table. Each
priate safety and health practices and determine the applica-
1
bility of regulatory limitations prior to use. line shall end with a scribed arc, ⁄4 in. [6 mm] long, whose
3
center point is the center of the table top with a radiusof2 ⁄8 in.
1.4 This international standard was developed in accor-
[59.5 mm]. The scribe lines shall be made with a 60° tool to a
dance with internationally recognized principles on standard-
depth of 0.01 in. [0.25 mm].The table top shall be of cast brass
ization established in the Decision on Principles for the
or bronze having a Rockwell hardness number not less than
Development of International Standards, Guides and Recom-
25 HRB with an edge thickness of 0.3 in. [7.5 mm], and shall
mendations issued by the World Trade Organization Technical
have six integral radial stiffening ribs. The table top and
Barriers to Trade (TBT) Committee.
attached shaft shall weigh 9 6 0.1 lb [4.08 6 0.05 kg] and the
weight shall be symmetrical around the center of the shaft.
2. Referenced Documents
2
4.2 The cam and vertical shaft shall be of medium carbon
2.1 ASTM Standards:
machinery steel, hardened on the end of the shaft contacting
C125 Terminology Relating to Concrete and Concrete Ag-
the cam and the tip of the cam contacting the shaft. The shaft
gregates
shall be straight and the difference between the diameter of the
shaft and the diameter of the bore of the frame shall be not less
1
This specification is under the jurisdiction of ASTM Committee C01 on
than 0.002 in. [0.05 mm] and not more than 0.003 in.
Cement and is the direct responsibility of Subcommittee C01.22 on Workability.
[0.08 mm] for new tables and shall be maintained at 0.002 to
CurrenteditionapprovedJune1,2020.PublishedJuly2020.Originallyapproved
0.010 in. [0.05 to 0.25 mm] for tables in use. The end of the
in 1949. Last previous edition approved in 2014 as C230/C230M – 14. DOI:
10.1520/C0230_C0230M-20.
shaft shall not fall upon the camat the end of the drop,butshall
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
make contact with the cam not less than 120° from the point of
contact ASTM Customer Service at [e-mail].
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: C230/C230M − 14 C230/C230M − 20
Standard Specification for
1
Flow Table for Use in Tests of Hydraulic Cement
This standard is issued under the fixed designation C230/C230M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This specification covers requirements for the flow table and accessory apparatus (Note 1) used in making flow tests for
consistency of mortars in tests of hydraulic cement, such as but not limited to Test Method C1437.
NOTE 1—To help clarify the design of the flow table and accessory apparatus see the drawing in Fig. 1 [Fig. 2]. This drawing is for informational
purposes only.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard. It is permissible to use an inch-pound caliper and mold with a SI
flow table or a SI caliper and mold with an inch-pound flow table. It is not permissible to mix a SI mold with an inch-pound caliper
or an inch-pound mold with a SI caliper.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
C1437 Test Method for Flow of Hydraulic Cement Mortar
2
2.1 ASTM Standards:
C125 Terminology Relating to Concrete and Concrete Aggregates
C219 Terminology Relating to Hydraulic and Other Inorganic Cements
C1437 Test Method for Flow of Hydraulic Cement Mortar
3. Terminology
3.1 Definitions:
3.1.1 The terms in this standard specification are defined in Terminology C125 and Terminology C219.
4. Flow Table and Frame
4.1 The flow table apparatus shall consist of an integrally cast rigid iron frame and a circular rigid table top 10 6 0.1 in. [255
6 2.5 mm] in diameter, with a shaft attached perpendicular to the table top by means of a screw thread. The table top and shaft
with contact shoulder shall be mounted on a frame in such a manner that it can be raised and dropped vertically through the
specified height of 0.500 6 0.005 in. [12.7 6 0.13 mm] for new tables and of 0.500 6 0.015 in. [12.7 6 0.38 mm] for tables in
use, by means of a rotated cam. The table top shall have a fine machined plane surface, free of blowholes and surface defects. The
5
top shall be scribed with eight equidistant lines 2 ⁄8 in. [68 mm] long, extending from the outside circumference toward the center
1
of the table. Each line shall end with a scribed arc, ⁄4 in. [6 mm] long, whose center point is the center of the table top with a radius
3
of 2 ⁄8 in. [59.5 mm]. The scribe lines shall be made with a 60° tool to a depth of 0.01 in. [0.25 mm]. The table top shall be of cast
1
This specification is under the jurisdiction of ASTM Committee C01 on Cement and is the direct responsibility of Subcommittee C01.22 on Workability.
Current edition approved Oct. 1, 2014June 1, 2020. Published October 2014July 2020. Originally approved in 1949. Last previous edition approved in 20132014 as
C230/C230M – 13.C230/C230M – 14. DOI: 10.1520/C0230_C0230M-14.10.1520/C0230_C0230M-20.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
C230/C230M − 20
FIG. 1 Flow Table and Accessory Apparatus (Partial) (in./lb)(IP)
brass or bronze having a Rockwell hardness
...