Standard Test Methods for Concrete Pipe, Manhole Sections, or Tile (Metric)

ABSTRACT
These test methods cover production and acceptance tests for concrete pipes, manhole sections, and tiles. Tests include procedures for evaluating external load crushing strength, flat slab top, core strength, absorption, hydrostatic, permeability, manhole step, cylinder, gasket lubricant, joint shear, alkalinity, and gasket measurements. Aside from the procedures, this standard also details the significance and use of and the required test apparatus for each test.
SCOPE
1.1 These test methods cover testing of concrete pipe, manhole sections, and tile. The test methods described are used in production testing and acceptance testing to evaluate the properties provided for in the specifications.  
1.2 The test methods appear in the following order:    
Section  
External Load Crushing Strength  
4  
Flat Slab Top  
5  
Core Strength  
6  
Absorption  
7  
Hydrostatic  
8  
Permeability  
9  
Manhole Step  
10  
Cylinder  
11  
Gasket Lubricant  
12  
Joint Shear  
13  
Alkalinity  
14  
Gasket Measurements  
15
1.3 The test specimens shall not have been exposed to a temperature below 4°C for the 24 h immediately preceding the test.  
1.4 If any test specimen fails because of mechanical reasons such as failure of testing equipment or improper specimen preparation, it shall be discarded and another specimen taken.  
1.5 Specimens shall be selected in accordance with the specifications for the type of pipe or tile being tested.  
1.6 These methods are the metric companion of Test Methods C497.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to consult and establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Sep-2013
Technical Committee
Drafting Committee
Current Stage
Ref Project

Relations

Buy Standard

Standard
ASTM C497M-13ae1 - Standard Test Methods for Concrete Pipe, Manhole Sections, or Tile (Metric)
English language
14 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
´1
Designation: C497M − 13a
StandardTest Methods for
1
Concrete Pipe, Manhole Sections, or Tile (Metric)
This standard is issued under the fixed designation C497M; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1
ε NOTE—Editorially corrected figure reference in 16.4.1 in April 2014.
1. Scope 2. Referenced Documents
2
2.1 ASTM Standards:
1.1 These test methods cover testing of concrete pipe,
C31/C31M Practice for Making and Curing Concrete Test
manhole sections, and tile.The test methods described are used
Specimens in the Field
in production testing and acceptance testing to evaluate the
C39/C39M Test Method for Compressive Strength of Cylin-
properties provided for in the specifications.
drical Concrete Specimens
1.2 The test methods appear in the following order:
C42/C42M Test Method for Obtaining and Testing Drilled
Section
Cores and Sawed Beams of Concrete
External Load Crushing Strength 4
C617 Practice for Capping Cylindrical Concrete Specimens
Flat Slab Top 5
Core Strength 6 C670 Practice for Preparing Precision and Bias Statements
Absorption 7
for Test Methods for Construction Materials
Hydrostatic 8
C822 Terminology Relating to Concrete Pipe and Related
Permeability 9
Manhole Step 10
Products
Cylinder 11
C1231/C1231M Practice for Use of Unbonded Caps in
Gasket Lubricant 12
DeterminationofCompressiveStrengthofHardenedCon-
Joint Shear 13
Alkalinity 14
crete Cylinders
Gasket Measurements 15
D2240 Test Method for Rubber Property—Durometer Hard-
1.3 The test specimens shall not have been exposed to a
ness
temperature below 4°C for the 24 h immediately preceding the
E4 Practices for Force Verification of Testing Machines
test.
3. Terminology
1.4 If any test specimen fails because of mechanical reasons
3.1 Definitions—Fordefinitionsoftermsrelatingtoconcrete
such as failure of testing equipment or improper specimen
pipe, see Terminology C822.
preparation, it shall be discarded and another specimen taken.
1.5 Specimens shall be selected in accordance with the
4. External Load Crushing Strength Test by the Three-
specifications for the type of pipe or tile being tested.
Edge Bearing Test Method
1.6 These methods are the metric companion of Test Meth-
4.1 Summary of Test Method—The test specimen is tested in
ods C497.
a machine designed to apply a crushing force upon the
specimen in a plane through the vertical axis extending along
1.7 This standard does not purport to address all of the
the length of the specimen.
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to consult and
4.2 Significance and Use—The crushing test method shall
establish appropriate safety and health practices and deter-
be either a quality control test performed to establish that the
mine the applicability of regulatory limitations prior to use.
finished, shippable pipe has sufficient strength to withstand the
crushing loads stated in the specifications or a proof of design
test performed to prove the adequacy of design.
1
These test methods are under the jurisdiction of ASTM Committee C13 on
Concrete Pipe and are the direct responsibility of Subcommittee C13.09 on Methods
2
of Test. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Oct. 1, 2013. Published October 2013. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1980. Last previous edition approved in 2013 as C497M – 13. DOI: Standards volume information, refer to the standard’s Document Summary page on
10.1520/C0497M-13AE01. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
´1
C497M − 13a
4.3 Apparatus: manufacturer, the center of the load shall be applied at any
4.3.1 The testing machine shall be of any type of sufficient point of the overall length (L ) of the specimen. The load shall
1
be applied either at a single point or at multiple points
capacity and shall be capable of providing the rate of loading
prescribed in 4.5.3. dependent on the length of the specimen being tested and the
rigidity of the test frame.
4.3.2 The testing machine shall be substantial and rigid
throughout, so that the distribution of the load will not be
NOTE 1—The user of these test methods is advised that multiple points
affectedappreciablybythedeformationoryieldingofanypart.
of load applications to the upper bearing will perm
...