ASTM F1864-05(2010)

Standard Test Method for Dust Erosion Resistance of Optical and Infrared Transparent Materials and Coatings

SIGNIFICANCE AND USE
All materials on exterior aircraft surfaces are subject to abrasion from airborne particles of various sizes and shapes. Transparent materials are particularly vulnerable to abrasion, since their performance is based on their ability to transmit light with a minimal amount of scatter. Scratches, pitting, and coating removal and delamination as a result of abrasion may increase scatter, reduce transmission, and degrade the performance of transparent materials. Visually transparent materials are required for pilot and air crew enclosures, such as canopies, windshields, and viewpoints. Materials transparent in the IR region (8 to 12 μm) are required for tracking, targeting, and navigational instrumentation.
This test method is intended to provide a calibrated and repeatable means of determining the relative abrasion resistance of materials and coatings for optical and IR transparent materials and coatings. The test parameters for this test method can be directly related to dust cloud densities and velocities to which transparent materials are exposed in the field.
SCOPE
1.1 This test method covers the resistance of transparent plastics and coatings used in aerospace windscreens, canopies, and viewports to surface erosion as a result of dust impingement. This test method simulates flight through a defined particle cloud environment by means of independent control of particle size, velocity, impact angle, mass loading, and test duration.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

• Status: Historical
• Publication Date: 30-Apr-2010
• ICS: 49.040 - Coatings and related processes used in aerospace industry
• Technical Committee: F07 - Aerospace and Aircraft
• Drafting Committee: F07.08 - Transparent Enclosures and Materials

Relations

• Replaces: ASTM F1864-05 - Standard Test Method for Dust Erosion Resistance of Optical and Infrared Transparent Materials and Coatings
• Effective Date: 01-May-2010
• Referred By: ASTM F790-23 - Standard Guide for Testing Materials for Aerospace Plastic Transparent Enclosures
• Effective Date: 01-May-2010

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: F1864 − 05(Reapproved 2010)
Standard Test Method for
Dust Erosion Resistance of Optical and Infrared Transparent
1
Materials and Coatings
This standard is issued under the fixed designation F1864; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3.1.2 mean IR transmission, n—for the purposes of this
standard, the average percentage of light transmitted by a
1.1 This test method covers the resistance of transparent
material in the 8- to 12-µm bandwidth.
plastics and coatings used in aerospace windscreens, canopies,
3.1.3 sweep time, n—the time required for one translation
and viewports to surface erosion as a result of dust impinge-
pass.
ment. This test method simulates flight through a defined
particlecloudenvironmentbymeansofindependentcontrolof
3.1.4 translation pass, n—the translation of the specimen
particle size, velocity, impact angle, mass loading, and test
platformfromtheverticalorhorizontallimittothecorrespond-
duration.
ing vertical or horizontal limit.
1.2 This standard does not purport to address all of the
3.1.5 translation cycle, n—the translation of the specimen
safety concerns, if any, associated with its use. It is the
platformfromtheverticalorhorizontallimittothecorrespond-
responsibility of the user of this standard to establish appro-
ingverticalorhorizontallimitandbacktotheinitialverticalor
priate safety and health practices and determine the applica-
horizontal limit. Two translation passes are equivalent to one
bility of regulatory limitations prior to use.
translation cycle.
3.2 Symbols:
2. Referenced Documents
2
2.1 ASTM Standards:
2
A = reference surface area of specimen platform (cm ),
D618Practice for Conditioning Plastics for Testing
s
3
C = simulated cloud concentration (g/m ),
D1003Test Method for Haze and Luminous Transmittance
c
h = percent haze before exposure,
of Transparent Plastics o
h = percent haze after exposure,
D1193Specification for Reagent Water e
m˙ = rate of particle mass impacting the reference surface
p
E11Specification forWovenWireTest Sieve Cloth andTest
area (g/min),
Sieves
2
m˙ = incremental mass loading (g/cm ),
i
E168Practices for General Techniques of Infrared Quanti-
2
m = total mass loading (g/cm ),
3
T
tative Analysis (Withdrawn 2015)
N = number of increments,
V = particle impact velocity (m/s),
p
3. Terminology
t = sweep time(s),
s
3.1 Definitions of Terms Specific to This Standard: T = optical or mean infrared (IR) transmission after expo-
e
sure (%),
3.1.1 mass loading, n—the mass of dust per unit of total
T = optical or mean IR transmission before exposure (%),
exposed surface area (including the sample holder) that im-
o
α = impact angle (normal incidence=90°),
pinges on the specimens.
∆t = exposure time (min) for loading increment i,
i
2
φ = incremental dust load (g/cm ) for loading increment i,
i
1
This test method is under the jurisdiction of ASTM Committee F07 on
2
Φ = total dust load (g/cm ),
Aerospace andAircraft and is the direct responsibility of Subcommittee F07.08 on
∆h = change in percent haze, and
Transparent Enclosures and Materials.
Current edition approved May 1, 2010. Published June 2010. Originally
∆T = change in optical or IR transmission.
approved in 1998. Last previous edition approved in 2005 as F1864–05. DOI:
10.1520/F1864-05R10.
4. Summary of Test Method
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
4.1 This test method consists of: (1) measuring and record-
Standards volume information, refer to the standard’s Document Summary page on
ing the light transmission properties, at visual or infrared
the ASTM website.
3
wavelengths, of test coupons; (2) mounting the coupons in a
The last approved version of this historical standard is referenced on
www.astm.org. test fixture; (3) exposing the coupons to a dust particle stream;
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
F1864 − 05 (2010)
and (4) remeasuring the light transmission properties to deter- 5.2 This test method is intended to provide a calibrated and
mine changes in these properties. repeatable means of determining the relative abrasion resis-
tance of materials and coatings for optical and IR transparent
4.2 The dust particle stream simulates flight at a specified
materialsandcoatings.Thetestparametersforthistestmethod
velocitythroughadustcloudofspecifieddensity.Simulationis
can be directly related to dust cloud densit
...