ASTM E2102-11
(Test Method)Standard Test Method for Measurement of Mass Loss and Ignitability for Screening Purposes Using a Conical Radiant Heater
Standard Test Method for Measurement of Mass Loss and Ignitability for Screening Purposes Using a Conical Radiant Heater
SIGNIFICANCE AND USE
This test method provides a means for screening materials, products, or assemblies, for the mass loss, and ignitability they exhibit under specified heat flux exposure conditions. As an option, the test method is also suitable for screening for the heat released, by using a thermopile method (See Annex A2).
Terminology E176, on fire standards, states that fire-test-response characteristics include ease of ignition and mass loss (both measured in this test method), as well as flame spread, smoke generation, fire endurance, and toxic potency of smoke.
The mass loss rate of a material, product, or assembly is a fire-test-response characteristic that gives an indication of its burning rate. Thus, a lower mass loss rate is often associated with slower burning. Note, however, that mass loss is not always a result of combustion, and that this method does not assess release of smoke or combustion products.
The time to ignition of a material, product, or assembly is a fire-test-response characteristic that gives an indication of its propensity to ignite at the applied heat flux level and subsequently to release heat and spread flame over its surface. Thus, a longer time to ignition is an indication of a lower propensity for the material, product, or assembly to become involved and contribute to fire spread or growth; however this method does not assess the smoke or combustion products released.
The apparatus used for this test method is suitable to assess the critical heat flux for ignition of the materials, products, or assemblies tested, by assessing ignitability at various heat fluxes (see Appendix X3 for guidance).
Values determined by this test are specific to the specimen in the form and thickness tested and are not inherent fundamental properties of the material, product, or assembly tested. Thus, closely repeatable or reproducible experimental results are not to be expected from this test method when tests are conducted for a given material, product, or as...
SCOPE
1.1 This fire-test-response standard provides a means of measuring mass loss and ignitability, for screening purposes, from essentially planar materials, products, or assemblies (including surface finishes), exposed to controlled levels of radiant heating, with or without an external ignitor. This test method is intended for screening purposes only.
1.2 The principal fire-test-response characteristics obtained from this test method are those associated with mass loss from the specimens tested, as a function of time. Time to sustained flaming is also determined. Heat release is, optionally, determined using thermopile measurements detailed in Annex A2.
1.2.1 The fire-test-response characteristics obtained from this test are best used for comparisons between materials with some similarities in composition or structure.
1.3 The relationship between mass loss and heat release depends on the material, product, or assembly tested, and no universal formula exists for calculation of heat release using mass loss measurements (see also additional limitations in 5.7).
1.4 The fire-test-response characteristics obtained from this test method are also obtainable with the apparatus used in Test Method E1354 (the cone calorimeter) or in an applications standards of that equipment (see also 5.4). The referenced test methods permit measurements of added fire-test-response characteristics.
1.5 The fire-test-response characteristics obtained by this test method are specific to the specimen tested, in the form and thickness tested, and are not an inherent property of the material, product, or assembly.
1.6 This fire-test-response method does not provide information on the fire performance of the test specimens under fire conditions other than those conditions specified in this test method. For additional limitations of this test method, see 5.7.
1.7 Use the SI system of units in referee decisions; see . The units given in par...
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
An American National Standard
Designation:E2102–11
Standard Test Method for
Measurement of Mass Loss and Ignitability for Screening
1
Purposes Using a Conical Radiant Heater
This standard is issued under the fixed designation E2102; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
INTRODUCTION
The screening fire-test-response method described in this standard uses a radiant energy source
similar to that used in the cone calorimeter, Test Method E1354. However, the test method apparatus
is much simpler, because it excludes measurements of oxygen consumption or of smoke obscuration,
which are incorporated into the cone calorimeter to measure heat and smoke release. A fire-test-
response standard describes a test method from which one or more fire-test-response characteristics
can be measured, as a result of exposure to a prescribed source of heat or flame, under controlled
conditions. There are many occasions, typically for initial research and development, when there is a
need for screening samples of materials, products, or assemblies, using a simple test. This allows the
user to verify whether certain fire-test-response characteristics of the sample fall within the expected
margins. Screening tests, as related to fire, are described in fire terminology as fire-response tests
performed to determine whether a material, product, or assembly (a) exhibits any unusual fire-related
characteristics, (b) has certain expected fire-related characteristics, or (c) is capable of being
preliminarily categorized according to the fire characteristic in question. Screening tests addressing
fire properties should be chosen so that the energy input (as heat or flame) is representative of that in
the fire test method for which screening is desired.
1. Scope 1.3 The relationship between mass loss and heat release
depends on the material, product, or assembly tested, and no
1.1 This fire-test-response standard provides a means of
universal formula exists for calculation of heat release using
measuring mass loss and ignitability, for screening purposes,
masslossmeasurements(seealsoadditionallimitationsin5.7).
from essentially planar materials, products, or assemblies
1.4 The fire-test-response characteristics obtained from this
(including surface finishes), exposed to controlled levels of
test method are also obtainable with the apparatus used in Test
radiant heating, with or without an external ignitor. This test
Method E1354 (the cone calorimeter) or in an applications
method is intended for screening purposes only.
standards of that equipment (see also 5.4). The referenced test
1.2 The principal fire-test-response characteristics obtained
methodspermitmeasurementsofaddedfire-test-responsechar-
from this test method are those associated with mass loss from
acteristics.
the specimens tested, as a function of time. Time to sustained
1.5 The fire-test-response characteristics obtained by this
flaming is also determined. Heat release is, optionally, deter-
test method are specific to the specimen tested, in the form and
mined using thermopile measurements detailed in Annex A2.
thickness tested, and are not an inherent property of the
1.2.1 The fire-test-response characteristics obtained from
material, product, or assembly.
this test are best used for comparisons between materials with
1.6 This fire-test-response method does not provide infor-
some similarities in composition or structure.
mation on the fire performance of the test specimens under fire
conditions other than those conditions specified in this test
1
This test method is under the jurisdiction of ASTM Committee E05 on Fire
method. For additional limitations of this test method, see 5.7.
Standards and is the direct responsibility of Subcommittee E05.21 on Smoke and
Combustion Products. 1.7 Use the SI system of units in referee decisions; see
Current edition approved May 1, 2011. Published June 2011. Originally
IEEE/ASTM SI-10. The units given in parentheses are for
approved in 2000. Last previous edition approved in 2009 as E2102 - 09. DOI:
information only.
10.1520/E2102-11.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
E2102–11
1.8 This standard is used to measure and describe the E1740 Test Method for Determining the Heat Release Rate
responseofmaterials,products,orassembliestoheatandflame and Other Fire-Test-Response Characteristics ofWall Cov-
under controlled conditions, but does not by itself incorporate ering or Ceiling Covering Composites Using a Cone
...
This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
An American National Standard
Designation:E2102–09 Designation:E2102–11
Standard Test Method for
Measurement of Mass Loss and Ignitability for Screening
1
Purposes Using a Conical Radiant Heater
This standard is issued under the fixed designation E2102; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
INTRODUCTION
The screening fire-test-response method described in this standard uses a radiant energy source
similar to that used in the cone calorimeter, Test Method E1354. However, the test method apparatus
is much simpler, because it excludes measurements of oxygen consumption or of smoke obscuration,
which are incorporated into the cone calorimeter to measure heat and smoke release. A fire-test-
response standard describes a test method from which one or more fire-test-response characteristics
can be measured, as a result of exposure to a prescribed source of heat or flame, under controlled
conditions. There are many occasions, typically for initial research and development, when there is a
need for screening samples of materials, products, or assemblies, using a simple test. This allows the
user to verify whether certain fire-test-response characteristics of the sample fall within the expected
margins. Screening tests, as related to fire, are described in fire terminology as fire-response tests
performed to determine whether a material, product, or assembly (a) exhibits any unusual fire-related
characteristics, (b) has certain expected fire-related characteristics, or (c) is capable of being
preliminarily categorized according to the fire characteristic in question. Screening tests addressing
fire properties should be chosen so that the energy input (as heat or flame) is representative of that in
the fire test method for which screening is desired.
1. Scope
1.1 This fire-test-response standard provides a means of measuring mass loss and ignitability, for screening purposes, from
essentially planar materials, products, or assemblies (including surface finishes), exposed to controlled levels of radiant heating,
with or without an external ignitor. This test method is intended for screening purposes only.
1.2 The principal fire-test-response characteristics obtained from this test method are those associated with mass loss from the
specimens tested, as a function of time.Time to sustained flaming is also determined. Heat release is, optionally, determined using
thermopile measurements detailed in Annex A2.
1.2.1 The fire-test-response characteristics obtained from this test are best used for comparisons between materials with some
similarities in composition or structure.
1.3 The relationship between mass loss and heat release depends on the material, product, or assembly tested, and no universal
formula exists for calculation of heat release using mass loss measurements (see also additional limitations in 5.7).
1.4 The fire-test-response characteristics obtained from this test method are also obtainable with the apparatus used in Test
Method E1354 (the cone calorimeter) or in an applications standards of that equipment (see also 5.4).The referenced test methods
permit measurements of added fire-test-response characteristics.
1.5 The fire-test-response characteristics obtained by this test method are specific to the specimen tested, in the form and
thickness tested, and are not an inherent property of the material, product, or assembly.
1.6 This fire-test-response method does not provide information on the fire performance of the test specimens under fire
conditions other than those conditions specified in this test method. For additional limitations of this test method, see 5.7.
1.7 Use the SI system of units in referee decisions; see IEEE/ASTM SI-10. The units given in parentheses are for information
only.
1.8 This standard is used to measure and describe the response of materials, products, or assemblies to heat and flame under
controlled conditions, but does not by itself incorporate all factors required for fire hazard or fire risk assessment of the materials,
1
ThistestmethodisunderthejurisdictionofASTMCommitteeE05onFireStandardsandisthedirectresponsibilityofSubcommitteeE05.21onSmokeandCombustion
Products.
Current edition approved Oct.May 1, 2009.2011. Published October 2009.June 2011. Originally approved in 2000. Last previous edition approved in 2008
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.