ASTM B574-05

Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod

SCOPE
1.1 This specification covers rod of low-carbon nickel-chromium-molybdenum alloys (UNS N10276, N06022, N06035, N06455, N06058, and N06059)*, low-carbon nickel-molybdenum-chromium-tantalum (UNS N06210), low-carbon nickel-chromium-molybdenum-copper alloy (UNS N06200), and low-carbon nickel-chromium-molybdenum-tungsten (UNS N06686) as shown in , for use in general corrosive service.
1.2 The following products are covered under this specification:
1.2.1 Rods 5/16to 3/4 in. (7.94 to 19.05 mm), exclusive, in diameter, hot or cold finished, solution annealed and pickled, or mechanically descaled.
1.2.2 Rods 3/4to 31/2 in. (19.05 to 88.9 mm), inclusive, in diameter, hot or cold finished, solution annealed, ground or turned.
1.2.3 Rods 1/4 to 3 1/2 in. (6.35 to 88.9 mm), inclusive, in diameter, solution annealed, cold finished, as cold finished, ground or turned (N06059 and N06686 only, see and ).
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

• Status: Historical
• Publication Date: 31-Jan-2005
• ICS: 77.150.40 - Nickel and chromium products
• Technical Committee: B02 - Nonferrous Metals and Alloys
• Drafting Committee: B02.07 - Refined Nickel and Cobalt and Their Alloys

Relations

• Replaces: ASTM B574-04 - Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod
• Effective Date: 01-Feb-2005
• Replaced By: ASTM B574-06 - Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod
• Effective Date: 01-Jun-2006
• Referred By: ASTM F467-13(2018) - Standard Specification for Nonferrous Nuts for General Use
• Effective Date: 01-Feb-2005
• Referred By: ASTM B462-18e1 - Standard Specification for Forged or Rolled Nickel Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service
• Effective Date: 01-Feb-2005
• Referred By: ASTM F467M-06a(2018) - Standard Specification for Nonferrous Nuts for General Use (Metric)
• Effective Date: 01-Feb-2005
• Referred By: ASTM B366/B366M-23 - Standard Specification for Factory-Made Wrought Nickel and Nickel Alloy Fittings
• Effective Date: 01-Feb-2005
• Referred By: ASTM F468M-06(2018) - Standard Specification for Nonferrous Bolts, Hex Cap Screws, and Studs for General Use (Metric)
• Effective Date: 01-Feb-2005
• Referred By: ASTM F468-23 - Standard Specification for Nonferrous Bolts, Hex Cap Screws, Socket Head Cap Screws, and Studs for General Use
• Effective Date: 01-Feb-2005

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B 574 – 05
Standard Specification for
Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon
Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon
Nickel-Chromium-Molybdenum-Copper, and Low-Carbon
1
Nickel-Chromium-Molybdenum-Tungsten Alloy Rod
This standard is issued under the fixed designation B 574; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 2. Referenced Documents
2 3
1.1 This specification covers rod of low-carbon nickel- 2.1 ASTM Standards:
chromium-molybdenum alloys (UNS N10276, N06022, B 880 Specification for General Requirements for Chemical
N06035, N06455, N06058, and N06059)*, low-carbon nickel- Check Analysis Limits for Nickel, Nickel Alloys and
molybdenum-chromium-tantalum (UNS N06210), low-carbon Cobalt Alloys
nickel-chromium-molybdenum-copper alloy (UNS N06200), E8 Test Methods for Tension Testing of Metallic Materials
and low-carbon nickel-chromium-molybdenum-tungsten E29 Practice for Using Significant Digits in Test Data to
(UNS N06686) as shown in Table 1, for use in general Determine Conformance with Specifications
corrosive service. E55 PracticeforSamplingWroughtNonferrousMetalsand
1.2 The following products are covered under this specifi- Alloys for Determination of Chemical Composition
cation: E 1473 Test Methods for Chemical Analysis of Nickel,
5 3
1.2.1 Rods ⁄16 to ⁄4 in. (7.94 to 19.05 mm), exclusive, in Cobalt, and High-Temperature Alloys
diameter,hotorcoldfinished,solutionannealedandpickled,or
3. Terminology
mechanically descaled.
3 1
3.1 Definitions of Terms Specific to This Standard:
1.2.2 Rods ⁄4 to 3 ⁄2 in. (19.05 to 88.9 mm), inclusive, in
diameter, hot or cold finished, solution annealed, ground or 3.1.1 rod, n—a product of round solid section furnished in
straight lengths.
turned.
1 1
1.2.3 Rods ⁄4 to 3 ⁄2 in. (6.35 to 88.9 mm), inclusive, in
4. Ordering Information
diameter, solution annealed, cold finished, as cold finished,
4.1 It is the responsibility of the purchaser to specify all
ground or turned (N06059 and N06686 only, see Table 2 and
requirements that are necessary for material ordered under this
Table 3).
specification. Examples of such requirements include, but are
1.3 The values stated in inch-pound units are to be regarded
not limited to the following:
as the standard. The values given in parentheses are for
4.1.1 Alloy—Table 1.
information only.
4.1.2 Dimensions—Nominal diameter and length. The
1.4 This standard does not purport to address all of the
shortest useable multiple length should be specified (Table 4).
safety concerns, if any, associated with its use. It is the
4.1.3 Certification— State if certification or a report of test
responsibility of the user of this standard to become familiar
results is required (Section 15).
with all hazards including those identified in the appropriate
4.1.4 Purchaser Inspection—State which tests or inspec-
Material Safety Data Sheet for this product/material as pro-
tions are to be witnessed (Section 13).
vided by the manufacturer, to establish appropriate safety and
4.1.5 Samples for Product (Check) Analysis—State whether
health practices, and determine the applicability of regulatory
samples should be furnished (9.2.2).
limitations prior to use.
5. Chemical Composition
1
This specification is under the jurisdiction of ASTM Committee B02 on
5.1 The material shall conform to the composition limits
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
specified in Table 1.
B02.07 on Refined Nickel and Cobalt and Their Alloys.
Current edition approved Feb. 1, 2005. Published February 2005. Originally
approved in 1972. Last previous edition approved in 2004 as B 574 – 04.
2 3
For ASME Boiler and Pressure Vessel Code applications see related Specifi- For referenced ASTM standards, visit the ASTM website, www.astm.org, or
cation SB-574 in Section II of that Code. contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
* New designation established in accordance withASTM E 527 and SAE J1086, Standards volume information, refer to the standard’s Document Summary page on
Practice for Numbering Metals and Alloys (UNS). the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
B574–05
TABLE 1 Chemical Requirements
Composition Limits, %
Element
Alloy Alloy Alloy Alloy Alloy Alloy Alloy Alloy Alloy
N06035 N10276 N06022 N06455 N06059 N06058 N06200 N06210 N06686
Molybdenum 7.60–9.00 15.0–17.0 12.5–14.5 14.0–17.0 15.0–16.5 19.0 - 21.0 15.0–17.0 18.0–20.
...