ASTM A336/A336M-10
(Specification)Standard Specification for Alloy Steel Forgings for Pressure and High-Temperature Parts
Standard Specification for Alloy Steel Forgings for Pressure and High-Temperature Parts
ABSTRACT
This specification deals with ferritic alloy steel forgings for high-pressure and high-temperature parts, such as boilers, pressure vessels, and associated equipment. The steel grades covered here include the following: Grade F1; Grade F11, Classes 1, 2, and 3; Grade F12; Grade F5; Grade F5A; Grade F9; Grade F6; Grades F21 and F22, Classes 1 and 3; Grade F91, Grade F3V; and Grade F22V. Other steel grades may also be treated under this specification. Alloy steels shall be melted, forged, and rough machined at stipulated conditions. Except as permitted for Grade F22V, steel forgings shall be annealed or normalized and tempered, but may alternatively be liquid quenched and tempered as well. Impact and Charpy V-notch tests shall be performed wherein specimens shall conform to specified mechanical requirements such as notch toughness, tensile strength, yield strength, elongation, and reduction of area. Materials shall also undergo heat and product analyses and conform to specified chemical requirements.
SCOPE
1.1 This specification covers ferritic steel forgings for boilers, pressure vessels, high-temperature parts, and associated equipment.
1.2 Forgings made of steel grades listed in Specification A335/A335M, may also be ordered under this specification. The chemical, tensile, heat treatment, and marking requirements of Specification A335/A335M shall apply, except the forging shall conform to the chemical requirements of Tables 1 and 2 of Specification A335/A335M only with respect to heat analysis. On product analysis they may deviate from these limits to the extent permitted in Table 1 of this specification.
1.3 Supplementary Requirements S1 to S9 are provided for use when additional testing or inspection is desired. These shall apply only when specified individually by the purchaser in the order.
1.4 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.
1.5 Specification A336/A336M formerly included austenitic steel forgings, which are now found in Specification A965/A965M.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: A336/A336M – 10
Standard Specification for
Alloy Steel Forgings for Pressure and High-Temperature
1
Parts
This standard is issued under the fixed designationA336/A336M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* 2. Referenced Documents
2 3
1.1 This specification covers ferritic steel forgings for 2.1 ASTM Standards:
boilers, pressure vessels, high-temperature parts, and associ- A275/A275M Practice for Magnetic Particle Examination
ated equipment. of Steel Forgings
1.2 Forgings made of steel grades listed in Specification A335/A335M Specification for Seamless Ferritic Alloy-
A335/A335M, may also be ordered under this specification. Steel Pipe for High-Temperature Service
The chemical, tensile, heat treatment, and marking require- A370 Test Methods and Definitions for Mechanical Testing
ments of Specification A335/A335M shall apply, except the of Steel Products
forging shall conform to the chemical requirements ofTables 1 A788/A788M Specification for Steel Forgings, General Re-
and 2 of Specification A335/A335M only with respect to heat quirements
analysis. On product analysis they may deviate from these A965/A965M Specification for Steel Forgings, Austenitic,
limits to the extent permitted in Table 1 of this specification. for Pressure and High Temperature Parts
1.3 Supplementary Requirements S1 to S9 are provided for E165 PracticeforLiquidPenetrantExaminationforGeneral
usewhenadditionaltestingorinspectionisdesired.Theseshall Industry
apply only when specified individually by the purchaser in the 2.2 Other Standard:
order. ASMEBoilerandPressureVesselCode SectionIII,Nuclear
1.4 Unless the order specifies the applicable “M” specifica- Facility Components and Section IX, Welding Qualifica-
4
tion designation, the material shall be furnished to the inch- tions
pound units.
3. Ordering Information and General Requirements
1.5 SpecificationA336/A336M formerly included austenitic
steel forgings, which are now found in Specification A965/ 3.1 In addition to the ordering information required by
SpecificationA788/A788M, the purchaser should include with
A965M.
1.6 The values stated in either SI units or inch-pound units the inquiry and order the following information:
3.1.1 Adrawingorsketchthatshowstestlocationswhenthe
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each testing is in accordance with 8.1.1.3.
3.1.2 The intended use of forgings if 5.1 is applicable.
system shall be used independently of the other. Combining
values from the two systems may result in non-conformance 3.2 Material supplied to this specification shall conform to
the requirements of Specification A788/A788M, which out-
with the standard.
lines additional ordering information, manufacturing require-
ments, testing and retesting methods and procedures, marking,
certification,productanalysisvariations,andadditionalsupple-
mentary requirements.
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
3
A01.06 on Steel Forgings and Billets. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved May 1, 2010. Published June 2010. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1955. Last previous edition approved in 2009 as A336/A336M – 09. Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/A0336_A0336M-10. the ASTM website.
2 4
For ASME Boiler and Pressure Vessel Code applications, see related Specifi- Available from American Society of Mechanical Engineers (ASME), ASME
cation SA-336/SA-336M in Section II of that Code. International Headquarters, Three Park Ave., New York, NY 10016-5990.
*ASummary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
A336/A336M – 10
2
TABLE 1 Tensile Requirements
Ferritic Steels
Grade
F11, F11, F11, F21, F21, F22, F22,
F1 F12 F5 F5A F9 F6 F6NM F91 F911 F92 F3V F3VCb F22V
Class 2 Class 3 Class 1 Class 3 Class 1 Class 3 Class 1
70- 70- 75- 60- 70- 60- 80- 85- 85- 115- 75- 60- 75- 60- 90- 90- 90- 85- 85- 85-
Tensile
95 95 100 85 95 85 105 110 110 140 100 85 100 85 110 120 120 110 110 110
strength,
[485- [485- [515- [415- [485- [415- [550- [585-
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A336/A336M–09 Designation: A336/A336M – 10
Standard Specification for
Alloy Steel Forgings for Pressure and High-Temperature
1
Parts
This standard is issued under the fixed designationA336/A336M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
2
1.1 This specification covers ferritic steel forgings for boilers, pressure vessels, high-temperature parts, and associated
equipment.
1.2 Forgings made of steel grades listed in Specification A335/A335M, may also be ordered under this specification. The
chemical, tensile, heat treatment, and marking requirements of Specification A335/A335M shall apply, except the forging shall
conform to the chemical requirements of Tables 1 and 2 of Specification A335/A335M only with respect to heat analysis. On
product analysis they may deviate from these limits to the extent permitted in Table 1 of this specification.
1.3 Supplementary Requirements S1 to S9 are provided for use when additional testing or inspection is desired. These shall
apply only when specified individually by the purchaser in the order.
1.4 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound
units.
1.5 SpecificationA336/A336Mformerlyincludedausteniticsteelforgings,whicharenowfoundinSpecificationA965/A965M.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
2. Referenced Documents
3
2.1 ASTM Standards:
A275/A275M Practice for Magnetic Particle Examination of Steel Forgings
A335/A335M Specification for Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A788/A788M Specification for Steel Forgings, General Requirements
A965/A965M Specification for Steel Forgings, Austenitic, for Pressure and High Temperature Parts
E165 Practice for Liquid Penetrant Examination for General Industry
2.2 Other Standard:
4
ASME Boiler and Pressure Vessel Code Section III, Nuclear Facility Components and Section IX, Welding Qualifications
3. Ordering Information and General Requirements
3.1 In addition to the ordering information required by Specification A788/A788M, the purchaser should include with the
inquiry and order the following information:
3.1.1 A drawing or sketch that shows test locations when the testing is in accordance with 8.1.1.3.
3.1.2 The intended use of forgings if 5.1 is applicable.
3.2 Material supplied to this specification shall conform to the requirements of Specification A788/A788M, which outlines
additional ordering information, manufacturing requirements, testing and retesting methods and procedures, marking, certification,
1
This specification is under the jurisdiction ofASTM CommitteeA01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of SubcommitteeA01.06
on Steel Forgings and Billets.
Current edition approved Feb. 15, 2009. Published March 2009. Originally approved in 1955. Last previous edition approved in 2008 as A336/A336M–08. DOI:
10.1520/A0336_A0336M-09.
Current edition approved May 1, 2010. Published June 2010. Originally approved in 1955. Last previous edition approved in 2009 as A336/A336M – 09. DOI:
10.1520/A0336_A0336M-10.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-336/SA-336M in Section II of that Code.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. ForAnnualBookofASTMStandards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Three Park Ave., New York, NY 10016-5990.
*ASummary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
A336/A336M – 10
2
TABLE 1 Te
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A336/A336M–09 Designation: A336/A336M – 10
Standard Specification for
Alloy Steel Forgings for Pressure and High-Temperature
1
Parts
This standard is issued under the fixed designationA336/A336M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
2
1.1 This specification covers ferritic steel forgings for boilers, pressure vessels, high-temperature parts, and associated
equipment.
1.2 Forgings made of steel grades listed in Specification A335/A335M, may also be ordered under this specification. The
chemical, tensile, heat treatment, and marking requirements of Specification A335/A335M shall apply, except the forging shall
conform to the chemical requirements of Tables 1 and 2 of Specification A335/A335M only with respect to heat analysis. On
product analysis they may deviate from these limits to the extent permitted in Table 1 of this specification.
1.3 Supplementary Requirements S1 to S9 are provided for use when additional testing or inspection is desired. These shall
apply only when specified individually by the purchaser in the order.
1.4 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound
units.
1.5 SpecificationA336/A336Mformerlyincludedausteniticsteelforgings,whicharenowfoundinSpecificationA965/A965M.
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
2. Referenced Documents
3
2.1 ASTM Standards:
A275/A275M Practice for Magnetic Particle Examination of Steel Forgings
A335/A335M Specification for Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A788/A788M Specification for Steel Forgings, General Requirements
A965/A965M Specification for Steel Forgings, Austenitic, for Pressure and High Temperature Parts
E165 Practice for Liquid Penetrant Examination for General Industry
2.2 Other Standard:
4
ASME Boiler and Pressure Vessel Code Section III, Nuclear Facility Components and Section IX, Welding Qualifications
3. Ordering Information and General Requirements
3.1 In addition to the ordering information required by Specification A788/A788M, the purchaser should include with the
inquiry and order the following information:
3.1.1 A drawing or sketch that shows test locations when the testing is in accordance with 8.1.1.3.
3.1.2 The intended use of forgings if 5.1 is applicable.
3.2 Material supplied to this specification shall conform to the requirements of Specification A788/A788M, which outlines
additional ordering information, manufacturing requirements, testing and retesting methods and procedures, marking, certification,
1
This specification is under the jurisdiction ofASTM CommitteeA01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of SubcommitteeA01.06
on Steel Forgings and Billets.
Current edition approved Feb. 15, 2009. Published March 2009. Originally approved in 1955. Last previous edition approved in 2008 as A336/A336M–08. DOI:
10.1520/A0336_A0336M-09.
Current edition approved May 1, 2010. Published June 2010. Originally approved in 1955. Last previous edition approved in 2009 as A336/A336M – 09. DOI:
10.1520/A0336_A0336M-10.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-336/SA-336M in Section II of that Code.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. ForAnnualBookofASTMStandards
volume information, refer to the standard’s Document Summary page on the ASTM website.
4
Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Three Park Ave., New York, NY 10016-5990.
*ASummary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
A336/A336M – 10
2
TABLE 1 Te
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.