ASTM A562/A562M-10(2021)
(Specification)Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Titanium for Glass or Diffused Metallic Coatings
Standard Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Titanium for Glass or Diffused Metallic Coatings
ABSTRACT
This specification covers standard requirements for titanium-bearing carbon steel plates intended for welded glass lined pressure vessels or other applications where the presence of free-iron carbide would be deleterious to the coating. The steel shall be killed and thermally treated to produce the required grain refinement specification. Heat and product analyses shall be performed wherein the material shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, copper, and titanium. The steel plate shall conform to tensile requirements such as tensile strength, yield strength, and elongation.
SCOPE
1.1 This specification2 covers titanium-bearing carbon steel plates intended for welded glass lined pressure vessels or other applications where the presence of free-iron carbide would be deleterious to the coating. A minimum specific ratio of titanium to carbon is specified.
1.2 The maximum thickness of plates is limited to 2 in. [50 mm].
1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: A562/A562M −10 (Reapproved 2021)
Standard Specification for
Pressure Vessel Plates, Carbon Steel, Manganese-Titanium
for Glass or Diffused Metallic Coatings
This standard is issued under the fixed designationA562/A562M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope A577/A577M Specification for Ultrasonic Angle-Beam Ex-
2 amination of Steel Plates
1.1 This specification covers titanium-bearing carbon steel
A578/A578M Specification for Straight-Beam Ultrasonic
plates intended for welded glass lined pressure vessels or other
Examination of Rolled Steel Plates for Special Applica-
applications where the presence of free-iron carbide would be
tions
deleterioustothecoating.Aminimumspecificratiooftitanium
to carbon is specified.
3. General Requirements and Ordering Information
1.2 The maximum thickness of plates is limited to 2 in. [50
3.1 Material supplied to this material specification shall
mm].
conform to Specification A20/A20M. These requirements out-
line the testing and retesting methods and procedures, permit-
1.3 The values stated in either inch-pound units or SI units
are to be regarded separately as standard. Within the text, the ted variations in dimensions, and mass, quality and repair of
defects, marking, loading, and ordering information.
SI units are shown in brackets. The values stated in each
system are not exact equivalents; therefore, each system must
3.2 In addition to the basic requirements of this
be used independently of the other. Combining values from the
specification, certain supplementary requirements are available
two systems may result in nonconformance with the specifi-
when additional control, testing, or examination is required to
cation.
meet end use requirements.
1.4 This international standard was developed in accor-
3.3 If the requirements of this specification are in conflict
dance with internationally recognized principles on standard-
with the requirements of Specification A20/A20M, the require-
ization established in the Decision on Principles for the
ments of this specification shall prevail.
Development of International Standards, Guides and Recom-
mendations issued by the World Trade Organization Technical 4. Manufacture
Barriers to Trade (TBT) Committee.
4.1 Steelmaking Practice—The steel shall be killed.
2. Referenced Documents
5. Heat Treatment
2.1 ASTM Standards:
5.1 Plates shall be thermally treated to produce grain
A20/A20M SpecificationforGeneralRequirementsforSteel
refinement, either by normalizing or heating uniformly for hot
Plates for Pressure Vessels
forming at a minimum temperature of 1600°F [870°C] or some
A435/A435M Specification for Straight-Beam Ultrasonic
higher agreed temperature, and held at this temperature for a
Examination of Steel Plates
minimum of 1 h/in. [2.4 min/mm] of thickness.
6. Chemical Requirements
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
6.1 The steel shall conform to the chemical requirements
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
A01.11 on Steel Plates for Boilers and Pressure Vessels. shown in Table 1 unless otherwise modified in accordance with
Current edition approved March 1, 2021. Published March 2021. Originally
Supplementary Requirement S17, Vacuum Carbo
...