EN ISO 2507-1:2017
(Main)Thermoplastics pipes and fittings - Vicat softening temperature - Part 1: General test method (ISO 2507-1:1995)
Thermoplastics pipes and fittings - Vicat softening temperature - Part 1: General test method (ISO 2507-1:1995)
The method specified is based on determining the temperature at which a standard indenter, under a force of 50 N ± 1 N, penetrates 1 mm into the surface of a test piece cut from the wall of a pipe or fitting while the temperature is raised at a constant rate. Is applicable only to thermoplastics materials for which it is possible to measure the temperature at which the rate of softening becomes rapid. Is based on ISO 306:1994 which, however, applies to materials in the form of sheets.
Rohre und Formstücke aus Thermoplasten - Vicat-Erweichungstemperatur - Teil 1: Allgemeines Prüfverfahren (ISO 2507-1:1995)
Tubes et raccords en matières thermoplastiques - Température de ramollissement Vicat - Partie 1: Méthode générale d'essai (ISO 2507-1:1995)
Plastomerne cevi in fitingi - Temperatura zmehčišča po Vicatu - 1. del: Splošna preskusna metoda (ISO 2507-1:1995)
Določena metoda temelji na določevanju temperature, pri kateri preskusna konica pod silo 50 N ± 1 N prodre 1 mm v površino preskusnega dela, izrezanega iz stene cevi ali fitinga, pri čemer se temperatura viša z enakomerno hitrostjo. Uporablja se samo za plastomerne materiale, za katere je mogoče izmeriti temperaturo, pri kateri se začne material hitro mehčati. Temelji na standardu ISO 306:1994, ki se uporablja za materiale v obliki plošč.
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
01-januar-2018
1DGRPHãþD
SIST EN 727:1997
3ODVWRPHUQHFHYLLQILWLQJL7HPSHUDWXUD]PHKþLãþDSR9LFDWXGHO 6SORãQD
SUHVNXVQDPHWRGD ,62
Thermoplastics pipes and fittings - Vicat softening temperature - Part 1: General test
method (ISO 2507-1:1995)
Rohre und Formstücke aus Thermoplasten - Vicat-Erweichungstemperatur - Teil 1:
Allgemeines Prüfverfahren (ISO 2507-1:1995)
Tubes et raccords en matières thermoplastiques - Température de ramollissement Vicat
- Partie 1: Méthode générale d'essai (ISO 2507-1:1995)
Ta slovenski standard je istoveten z: EN ISO 2507-1:2017
ICS:
23.040.20 Cevi iz polimernih materialov Plastics pipes
23.040.45 Fitingi iz polimernih Plastics fittings
materialov
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
EN ISO 2507-1
EUROPEAN STANDARD
NORME EUROPÉENNE
October 2017
EUROPÄISCHE NORM
ICS 23.040.20; 23.040.45 Supersedes EN 727:1994
English Version
Thermoplastics pipes and fittings - Vicat softening
temperature - Part 1: General test method (ISO 2507-
1:1995)
Tubes et raccords en matières thermoplastiques - Rohre und Formstücke aus Thermoplasten - Vicat-
Température de ramollissement Vicat - Partie 1: Erweichungstemperatur - Teil 1: Allgemeines
Méthode générale d'essai (ISO 2507-1:1995) Prüfverfahren (ISO 2507-1:1995)
This European Standard was approved by CEN on 19 September 2017.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this
European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references
concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN
member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by
translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management
Centre has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland,
Turkey and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2017 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 2507-1:2017 E
worldwide for CEN national Members.
Contents Page
European Foreword . 3
European Foreword
The text of ISO 2507-1:1995 has been prepared by Technical Committee ISO/TC 138 “Plastics pipes,
fittings and valves for the transport of fluids” of the International Organization for Standardization
(ISO) and has been taken over as EN ISO 2507-1:2017 by Technical Committee CEN/TC 155 “Plastics
piping systems and ducting systems” the secretariat of which is held by NEN.
This European Standard shall be given the status of a national standard, either by publication of an
identical text or by endorsement, at the latest by April 2018 and conflicting national standards shall be
withdrawn at the latest by October 2020.
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. CEN shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN 727:1994.
According to the CEN-CENELEC Internal Regulations, the national standards organizations of the
following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia,
Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands,
Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and
the United Kingdom.
Endorsement notice
The text of ISO 2507-1:1995 has been approved by CEN as a EN ISO 2507-1:2017 without any
modification.
INTERNATIONAL ISO
STANDARD 2507-1
First edition
1995-02-15
Thermoplastics pipes and fittings -
Vicat softening temperature -
Part 1:
General test method
Tubes et raccords en matieres thermoplastiques - Tempkature de
ramollissemen t Vita t -
Partie 1: Methode g&&ale d ’essai
Reference number
ISO 2507-1:1995(E)
ISO 2507=1:1995(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide
federation of national Standards bodies (ISO member bodies). The work
of preparing International Standards is normally carried out through ISO
technical committees. Esch member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard ISO 2507-1 was prepared by Technical Committee
lSO/TC 138, Plastics pipes, fittings and valves for the transport of fluids,
Subcommittee SC 5, General properties of pipes, fittings and valves of
plastic materials and their accessories - Test methods and basic specifi-
ca tions.
This first edition of ISO 2507-1, and ISO 2507-2, cancels and replaces the
second edition of ISO 2507 (ISO 25073 982) of which it constitutes a
technical revision.
ISO 2507 consists of the following Parts, under the general title Thermo-
plastics pipes and fittings - Vita t softening tempera tut-e:
- Part 7: General test method
- Part 2: Test conditions for unplasticized poly(vinyl chloride) (PVC-U)
or chlorinated poly(vinyl chloride) (PVC-C) pipes and fittings and for
high impact resistance poly(vin yl chloride) (PVC-Hl) pipes
- Part 3: Test conditions for acryionitrile/butadiene/styrene (ABS) and
acrylonitrile/styrene/acrylic ester (ASA) pipes and fittings
0 ISO 1995
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronie or mechanical, including photocopying and
microfilm, without Permission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-1 211 Geneve 20 l Switzerland
Printed in Switzerland
ii
0 ISO
ISO 2507=1:1995(E)
Introduction
This International Standard is based on ISO 306.
For convenience of use, it has been considered preferable to draw up a
complete document for use in determining the Vicat softening tempera-
ture of thermoplastics pipes and fittings. For further details, reference to
ISO 306 is recommended.
Please note, however, that ISO 306 is applicable to materials in the form
of sheets, whereas this International Standard is applicable to materials in
the form of pipes and fittings.
ISO 2507 comprises three Parts: the first gives the general conditions
under which the Vicat softening temperature of a pipe or fitting is deter-
mined, the other two Parts provide the particular requirements for con-
ducting tests on pipes and fittings of different materials (see the
Foreword).
The basic specifications for various materials are given in the informative
annexes of the appropriate Parts.
. . .
Ill
This page intentionally left blank
INTERNATIONAL STANDARD 0 ISO ISO 2507-1: 1995( E)
Thermoplastics pipes and fittings - Vicat softening
temperature -
Part 1:
General test method
1 Scope 3 Principle
Determination of the temperature at which a Standard
This part of ISO 2507 specifies a general method for
indenter, under a forte of 50 N + 1 N, penetrates
determining the Vicat softening temperature of
1 mm into the surface of a test piece tut from the
thermoplastics pipes and fittings. lt includes the ad-
wall of a pipe or fitting while the temperature is raised
aptation of method B of ISO 306:1994, using a forte
at a constant rate.
of 50 N.
The temperature at which the Penetration is 1 mm is
This method is applicable only to thermoplastics ma-
called the Vicat softening temperature (VST), in de-
terials for which it is possible to measure the
grees Celsius.
temperature at which their rate of softening becomes
rapid.
lt is not applicable to crystalline or semi-crystalline
4 Apparatus
polymers.
4.1 Rod, provided with a load-carrying plate (4.4),
held in a rigid metal frame so that it tan move freely
in the ver
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.