CEN/TS 820-5:2004

Advanced technical ceramics - Methods of testing monolithic ceramics. Thermomechanical properties - Part 5: Determination of elastic moduli at elevated temperatures

This part of ENV 820 describes methods for determining the elastic moduli, specifically Young's modulus, shear modulus and Poisson's ratio, of advanced monolithic technical ceramics at temperatures above room temperature. The Technical Specification prescribes three alternative methods for determining some or all of these three parameters:
A   The determination of Young's modulus by static flexure of a thin beam in three- or four-point bending.
B   The determination of Young's modulus by forced longitudinal resonance, or Young's modulus, shear modulus and Poisson's ratio by forced flexural and torsional resonance, of a thin beam.
C   The determination of Young's modulus from the fundamental natural frequency of a struck bar (impulse excitation method).
This Technical Specification extends the above-defined room-temperature methods described in ENV 843-2 to elevated temperatures. All the test methods assume the use of homogeneous test pieces of linear elastic materials. The test assumes that the test piece has isotropic elastic properties. At high porosity levels all of the methods can become inappropriate. The maximum grain size (see EN 623-3), excluding deliberately added whiskers, should be less than 10% of the minimum dimension of the test piece.

Hochleistungskeramik - Monolithische Keramik - Thermomechanische Eigenschaften - Teil 5: Bestimmung der elastischen Moduln bei erhöhten Temperaturen

Céramiques techniques avancées - Méthodes d'essai des céramiques monolithiques - Propriétés thermomécaniques - Partie 5: Détermination des modules élastiques à températures élevées

La présente partie de EN 820 décrit des méthodes de détermination des modules élastiques, en particulier du module de Young, du module de cisaillement et du coefficient de Poisson des céramiques techniques avancées à des températures supérieures à la température ambiante Cette Spécification Technique décrit trois méthodes possibles permettant de déterminer un ou plusieurs de ces trois paramètres.
A   - Détermination du Module de Young par flexion statique d'une poutre mince en trois ou quatre points.
B   - Détermination du Module de Young par résonance longitudinale forcée ou détermination du module de Young, du module de cisaillement et du coefficient de Poisson par résonance forcée en flexion et en torsion d'une poutre mince.
C   - Détermination du module de Young à partir de la fréquence naturelle fondamentale d'une barre que l'on frappe( méthode d'excitation par impulsion);
La présente Spécification Technique étend les méthodes à température ambiante définies ci-dessus  et décrites dans ENV 843-2 aux températures élevées. Toutes les méthodes d'essai supposent l'utilisation d'éprouvettes homogènes faites en matériaux élastiques linéaires. L'essai est fait en considérant que l'éprouvette a des propriétés élastiques isotropes. Toutes ces méthodes peuvent se révéler inappropriées pour des niveaux de porosité élevés. Il convient que la granulométrie maximale (voir EN 623-3),qui ne tient pas compte de l'ajout de « whiskers », représente moins de 10% de la plus petite dimension de l'éprouvette.

Sodobna tehnična keramika – Metode za preskušanje monolitske keramike – Termomehanske lastnosti – 5. del: Ugotavljanje elastičnih modulov pri povišanih temperaturah

General Information

• Status: Withdrawn
• Publication Date: 10-Feb-2004
• ICS: 81.060.30 - Advanced ceramics
• Technical Committee: CEN/TC 184 - Advanced technical ceramics
• Drafting Committee: CEN/TC 184/WG 3 - Monolithic ceramics
• Current Stage: 9960 - Withdrawal effective - Withdrawal
• Start Date: 08-Jul-2009
• Completion Date: 08-Jul-2009
• Mandate: M/076 - Mandate to CEN/CENELEC for standardization in the field of advanced ceramics
• Ref Project: SIST-TS CEN/TS 820-5:2005 - Advanced technical ceramics - Methods of testing monolithic ceramics. Thermomechanical properties - Part 5: Determination of elastic moduli at elevated temperatures

Relations

• Replaced By: EN 820-5:2009 - Advanced technical ceramics - Thermomechanical properties of monolithic ceramics - Part 5: Determination of elastic moduli at elevated temperatures
• Effective Date: 11-Jul-2009

Standards Content (Sample)

SLOVENSKI STANDARD
SIST-TS CEN/TS 820-5:2005
01-januar-2005
6RGREQDWHKQLþQDNHUDPLND±0HWRGH]DSUHVNXãDQMHPRQROLWVNHNHUDPLNH±
7HUPRPHKDQVNHODVWQRVWL±GHO8JRWDYOMDQMHHODVWLþQLKPRGXORYSULSRYLãDQLK
WHPSHUDWXUDK
Advanced technical ceramics - Methods of testing monolithic ceramics.
Thermomechanical properties - Part 5: Determination of elastic moduli at elevated
temperatures
Hochleistungskeramik - Monolithische Keramik - Thermomechanische Eigenschaften -
Teil 5: Bestimmung der elastischen Moduln bei erhöhten Temperaturen
Céramiques techniques avancées - Méthodes d'essai des céramiques monolithiques -
Propriétés thermomécaniques - Partie 5: Détermination des modules élastiques a
températures élevées
Ta slovenski standard je istoveten z: CEN/TS 820-5:2004
ICS:
81.060.30 Sodobna keramika Advanced ceramics
SIST-TS CEN/TS 820-5:2005 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST-TS CEN/TS 820-5:2005

---------------------- Page: 2 ----------------------

SIST-TS CEN/TS 820-5:2005
TECHNICAL SPECIFICATION
CEN/TS 820-5
SPÉCIFICATION TECHNIQUE
TECHNISCHE SPEZIFIKATION
February 2004
ICS 81.060.30
English version
Advanced technical ceramics - Methods of testing monolithic
ceramics. Thermomechanical properties - Part 5: Determination
of elastic moduli at elevated temperatures
Céramiques techniques avancées - Céramiques Hochleistungskeramik - Monolithische Keramik -
monolithiques - Propriétés thermomécaniques - Partie 5: Thermomechanische Eigenschaften - Teil 5: Bestimmung
Détermination du module élastique à température élevée der elastischen Moduln bei erhöhten Temperaturen
This Technical Specification (CEN/TS) was approved by CEN on 19 October 2003 for provisional application.
The period of validity of this CEN/TS is limited initially to three years. After two years the members of CEN will be requested to submit their
comments, particularly on the question whether the CEN/TS can be converted into a European Standard.
CEN members are required to announce the existence of this CEN/TS in the same way as for an EN and to make the CEN/TS available
promptly at national level in an appropriate form. It is permissible to keep conflicting national standards in force (in parallel to the CEN/TS)
until the final decision about the possible conversion of the CEN/TS into an EN is reached.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,
Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36  B-1050 Brussels
© 2004 CEN All rights of exploitation in any form and by any means reserved Ref. No. CEN/TS 820-5:2004: E
worldwide for CEN national Members.

---------------------- Page: 3 ----------------------

SIST-TS CEN/TS 820-5:2005
CEN/TS 820-5:2004 (E)
Page
Contents
Foreword .3
1 Scope.4
2 Normative references.4
3 Terms and definitions.5
4 Method A: Static bending method.5
4.1 Principle .5
4.2 Apparatus.5
4.3 Test pieces.7
4.4 Procedure.7
4.5 Calculation of results.8
4.6 Accuracy and interferences.9
5 Method B: Resonance method .10
5.1 Principle .
...