IEC 60317-3:2004

Specifications for particular types of winding wires - Part 3: Polyester enamelled round copper wire, class 155

Specifies the requirements of enamelled round copper winding wire of class 155 with a sole coating based on polyester resin, which may be modified provided it retains the chemical identity of the original resin and meets all specified wire requirements. Class 155 is a thermal class that requires a minimum temperature index of 155 and a heat shock temperature of at least 175 °C. The temperature in degrees Celsius corresponding to the temperature index is not necessarily that at which it is recommended that the wire be operated and this will depend on many factors, including the type of equipment involved. The range of nominal conductor diameters covered by this standard is as follows: - grade 1: 0,020 mm up to and including 3,150 mm; - grade 2: 0,020 mm up to and including 5,000 mm. The nominal conductor diameters are specified in Clause 4 of IEC 60317-0-1. The main changes with respect to the previous edition are listed below: - new requirements for appearance, Subclause 3.2, added; - the constant K, applied in calculating the number of revolutions for the peel test, Clause 8, increased from 130 mm to 150 mm; - the test temperature for the cut-through test, Clause 10, increased from 240 °C to 270 °C; - new pin hole test, Clause 23, added.
This publication is to be read in conjunction with IEC 60317-0-1:2008.

Spécifications pour types particuliers de fils de bobinage - Partie 3: Fil de section circulaire en cuivre émaillé avec polyester, classe 155

Spécifie les exigences concernant les fils de bobinage de section circulaire en cuivre émaillé de classe 155 avec un revêtement unique à base de résine polyester qui peut être modifiée pour autant que cette résine conserve l'identité chimique de la résine initiale et réponde à toutes les exigences du fil. La classe 155 est une classe thermique qui exige un indice de température minimal de 155 et une température de choc thermique d'au moins 175 °C. La température en degrés Celsius correspondant à l'indice de température n'est pas nécessairement celle à laquelle il est recommandé d'utiliser le fil; cela dépendra de beaucoup de facteurs, y compris du type d'équipement considéré. La gamme des diamètres nominaux des conducteurs couverte par la présente norme est la suivante: - grade 1: 0,020 mm jusque et y compris 3,150 mm; - grade 2: 0,020 mm jusque et y compris 5,000 mm. Les diamètres nominaux des conducteurs sont spécifiés dans l'Article 4 de la CEI 60317-0-1. Les modifications principales par rapport à l'édition précédente sont les suivantes: - ajout de nouvelles exigences pour les aspects, voir paragraphe 3.2; - la constante K, appliquée en calculant le nombre de tours pour l'essai de décollement (Article 8), augmentée de 130 mm à 150 mm; - la température d'essai pour l'essai de thermoplasticité (Article 10), augmentée de 240 °C 270 °C; - nouvel essai de détection des micro-fissures en immersion, Article 23, ajouté.
Cette publication doit être lue conjointement avec la CEI 60317-0-1:2008.

General Information

• Status: Published
• Publication Date: 03-Jan-2022
• ICS: 01 - GENERALITIES. TERMINOLOGY. STANDARDIZATION. DOCUMENTATION
• ICS: 29.060.10 - Wires
• Technical Committee: TC 55 - Winding wires
• Current Stage: WPUB - Publication withdrawn
• Completion Date: 04-Jan-2022

Standards Content (Sample)

NORME CEI
INTERNATIONALE IEC
60317-3
INTERNATIONAL
Troisième édition
STANDARD
Third edition
2004-08
Spécifications pour types particuliers
de fils de bobinage –
Partie 3:
Fil de section circulaire en cuivre émaillé
avec polyester, classe 155
Specifications for particular types
of winding wires –
Part 3:
Polyester enamelled round copper wire,
class 155
Numéro de référence
Reference number
CEI/IEC 60317-3:2004
---------------------- Page: 1 ----------------------
Numérotation des publications Publication numbering

Depuis le 1er janvier 1997, les publications de la CEI As from 1 January 1997 all IEC publications are

sont numérotées à partir de 60000. Ainsi, la CEI 34-1 issued with a designation in the 60000 series. For

devient la CEI 60034-1. example, IEC 34-1 is now referred to as IEC 60034-1.
Editions consolidées Consolidated editions

Les versions consolidées de certaines publications de la The IEC is now publishing consolidated versions of its

CEI incorporant les amendements sont disponibles. Par publications. For example, edition numbers 1.0, 1.1

exemple, les numéros d’édition 1.0, 1.1 et 1.2 indiquent and 1.2 refer, respectively, to the base publication,

respectivement la publication de base, la publication de the base publication incorporating amendment 1 and

base incorporant l’amendement 1, et la publication de the base publication incorporating amendments 1

base incorporant les amendements 1 et 2. and 2.
Informations supplémentaires Further information on IEC publications
sur les publications de la CEI

Le contenu technique des publications de la CEI est The technical content of IEC publications is kept

constamment revu par la CEI afin qu'il reflète l'état under constant review by the IEC, thus ensuring that

actuel de la technique. Des renseignements relatifs à the content reflects current technology. Information

cette publication, y compris sa validité, sont dispo- relating to this publication, including its validity, is

nibles dans le Catalogue des publications de la CEI available in the IEC Catalogue of publications

(voir ci-dessous) en plus des nouvelles éditions, (see below) in addition to new editions, amendments

amendements et corrigenda. Des informations sur les and corrigenda. Information on the subjects under

sujets à l’étude et l’avancement des travaux entrepris consideration and work in progress undertaken by the

par le comité d’études qui a élaboré cette publication, technical committee which has prepared this

ainsi que la liste des publications parues, sont publication, as well as the list of publications issued,

également disponibles par l’intermédiaire de: is also available from the following:

• Site web de la CEI (www.iec.ch) • IEC Web Site (www.iec.ch)
• Catalogue des publications de la CEI • Catalogue of IEC publications

Le catalogue en ligne sur le site web de la CEI The on-line catalogue on the IEC web site

(www.iec.ch/searchpub) vous permet de faire des (www.iec.ch/searchpub) enables you to search by a

recherches en utilisant de nombreux critères, variety of criteria including text searches,

comprenant des recherches textuelles, par comité technical committees and date of publication. On-

d’études ou date de publication. Des informations en line information is also available on recently

ligne sont également disponibles sur les nouvelles issued publications, withdrawn and replaced

publications, les publications remplacées ou retirées, publications, as well as corrigenda.

ainsi que sur les corrigenda.
• IEC Just Published • IEC Just Published

Ce résumé des dernières publications parues This summary of recently issued publications

(www.iec.ch/online_news/justpub) est aussi dispo- (www.iec.ch/online_news/justpub) is also available

nible par courrier électronique. Veuillez prendre by email. Please contact the Customer Service

contact avec le Service client (voir ci-dessous) Centre (see below) for further information.

pour plus d’informations.
• Service clients • Customer Service Centre

Si vous avez des questions au sujet de cette If you have any questions regarding this

publication ou avez besoin de renseignements publication or need further assistance, please

supplémentaires, prenez contact avec le Service contact the Customer Service Centre:

clients:
Email: [e-mail] Email: [e-mail]
Tél: [phone] Tel: [phone]
Fax: [phone] Fax: [phone]
---------------------- Page: 2 ----------------------
NORME CEI
INTERNATIONALE IEC
60317-3
INTERNATIONAL
Troisième édition
STANDARD
Third edition
2004-08
Spécifications pour types particuliers
de fils de bobinage –
Partie 3:
Fil de section circulaire en cuivre émaillé
avec polyester, classe 155
Specifications for particular types
of winding wires –
Part 3:
Polyester enamelled round copper wire,
class 155
” IEC 2004 Droits de reproduction réservés  Copyright - all rights reserved

Aucune partie de cette publication ne peut être reproduite ni No part of this publication may be reproduced or utilized in any

utilisée sous quelque forme que ce soit et par aucun procédé, form or by any means, electronic or mechanical, including

électronique ou mécanique, y compris la photocopie et les photocopying and microfilm, without permission in writing from

microfilms, sans l'accord écrit de l'éditeur. the publisher.

International Electrotechnical Commission, 3, rue de Varembé, PO Box 131, CH-1211 Geneva 20, Switzerland

Telephone: [phone] Telefax: [phone] E-mail: [e-mail] Web: www.iec.ch

CODE PRIX
Commission Electrotechnique Internationale PRICE CODE J
International Electrotechnical Commission
ɆɟɠɞɭɧɚɪɨɞɧɚɹɗɥɟɤɬɪɨɬɟɯɧɢɱɟɫɤɚɹɄɨɦɢɫɫɢɹ
Pour prix, voir catalogue en vigueur
For price, see current catalogue
---------------------- Page: 3 ----------------------
– 2 – 60317-3 ” CEI:2004
SOMMAIRE

AVANT-PROPOS..................................................................................................................4

INTRODUCTION...................................................................................................................8

1 Domaine d'application...................................................................................................10

2 Références normatives .................................................................................................10

3 Définitions et notes générales concernant les méthodes d'essai et aspects....................10

3.1 Définitions et notes générales concernant les méthodes d'essai ...........................10

3.2 Aspects ...............................................................................................................12

4 Dimensions ..................................................................................................................12

5 Résistance électrique ...................................................................................................12

6 Allongement .................................................................................................................12

7 Effet de ressort.............................................................................................................12

8 Souplesse et adhérence ...............................................................................................12

9 Choc thermique ............................................................................................................12

10 Thermoplasticité ...........................................................................................................12

11 Résistance à l'abrasion (diamètres nominaux des conducteurs au moins égaux à

0,250 mm et inférieurs ou égaux à 2,500 mm) ...............................................................12

12 Résistance aux solvants ...............................................................................................14

13 Tension de claquage ....................................................................................................14

14 Continuité de l'isolant ...................................................................................................14

15 Indice de température...................................................................................................14

16 Résistance aux réfrigérants ..........................................................................................16

17 Brasabilité ....................................................................................................................16

18 Adhérence par chaleur ou par solvant ..........................................................................16

19 Facteur de dissipation diélectrique................................................................................16

20 Résistance à l'huile de transformateur...........................................................................16

23 Détection des micro-fissures en immersion ...................................................................16

30 Conditionnement ..........................................................................................................16

Tableau 1 – Résistance à l'abrasion ....................................................................................14

---------------------- Page: 4 ----------------------
60317-3 ” IEC:2004 – 3 –
CONTENTS

FOREWORD.........................................................................................................................5

INTRODUCTION...................................................................................................................9

1 Scope ..........................................................................................................................11

2 Normative references ...................................................................................................11

3 Definitions and general notes on methods of test and appearance .................................11

3.1 Definitions and general notes on methods of test..................................................11

3.2 Appearance.........................................................................................................13

4 Dimensions ..................................................................................................................13

5 Electrical resistance .....................................................................................................13

6 Elongation....................................................................................................................13

7 Springiness ..................................................................................................................13

8 Flexibility and adherence ..............................................................................................13

9 Heat shock ...................................................................................................................13

10 Cut-through ..................................................................................................................13

11 Resistance to abrasion (nominal conductor diameters from 0,250 mm up to and

including 2,500 mm) .....................................................................................................13

12 Resistance to solvents..................................................................................................15

13 Breakdown voltage .......................................................................................................15

14 Continuity of insulation .................................................................................................15

15 Temperature index .......................................................................................................15

16 Resistance to refrigerants .............................................................................................17

17 Solderability .................................................................................................................17

18 Heat or solvent bonding ................................................................................................17

19 Dielectric dissipation factor ...........................................................................................17

20 Resistance to transformer oil ........................................................................................17

23 Pin hole test .................................................................................................................17

30 Packaging ....................................................................................................................17

Table 1 – Resistance to abrasion ........................................................................................15

---------------------- Page: 5 ----------------------
– 4 – 60317-3 ” CEI:2004
COMMISSION ÉLECTROTECHNIQUE INTERNATIONALE
____________
SPÉCIFICATIONS POUR TYPES PARTICULIERS
DE FILS DE BOBINAGE –
Partie 3: Fil de section circulaire en cuivre émaillé
avec polyester, classe 155
AVANT-PROPOS

1) La Commission Electrotechnique Internationale (CEI) est une organisation mondiale de normalisation

composée de l'ensemble des comités électrotechniques nationaux (Comités nationaux de la CEI). La CEI a

pour objet de favoriser la coopération internationale pour toutes les questions de normalisation dans les

domaines de l'électricité et de l'électronique. A cet effet, la CEI – entre autres activités – publie des Normes

internationales, des Spécifications techniques, des Rapports techniques, des Spécifications accessibles au

public (PAS) et des Guides (ci-après dénommés "Publication(s) de la CEI"). Leur élaboration est confiée à des

comités d'études, aux travaux desquels tout Comité national intéressé par le sujet traité peut participer. Les

organisations internationales, gouvernementales et non gouvernementales, en liaison avec la CEI, participent

également aux travaux. La CEI collabore étroitement avec l'Organisation Internationale de Normalisation (ISO),

selon des conditions fixées par accord entre les deux organisations.

2) Les décisions ou accords officiels de la CEI concernant les questions techniques représentent, dans la mesure

du possible, un accord international sur les sujets étudiés, étant donné que les Comités nationaux de la CEI

intéressés sont représentés dans chaque comité d’études.

3) Les Publications de la CEI se présentent sous la forme de recommandations internationales et sont agréées

comme telles par les Comités nationaux de la CEI. Tous les efforts raisonnables sont entrepris afin que la CEI

s'assure de l'exactitude du contenu technique de ses publications; la CEI ne peut pas être tenue responsable

de l'éventuelle mauvaise utilisation ou interprétation qui en est faite par un quelconque utilisateur final.

4) Dans le but d'encourager l'uniformité internationale, les Comités nationaux de la CEI s'engagent, dans toute la

mesure possible, à appliquer de façon transparente les Publications de la CEI dans leurs publications

nationales et régionales. Toutes divergences entre toutes Publications de la CEI et toutes publications

nationales ou régionales correspondantes doivent être indiquées en termes clairs dans ces dernières.

5) La CEI n’a prévu aucune procédure de marquage valant indication d’approbation et n'engage pas sa

responsabilité pour les équipements déclarés conformes à une de ses Publications.

6) Tous les utilisateurs doivent s'assurer qu'ils sont en possession de la dernière édition de cette publication.

7) Aucune responsabilité ne doit être imputée à la CEI, à ses administrateurs, employés, auxiliaires ou

mandataires, y compris ses experts particuliers et les membres de ses comités d'études et des Comités

nationaux de la CEI, pour tout préjudice causé en cas de dommages corporels et matériels, ou de tout autre

dommage de quelque nature que ce soit, directe ou indirecte, ou pour supporter les coûts (y compris les frais

de justice) et les dépenses découlant de la publication ou de l'utilisation de cette Publication de la CEI ou de

toute autre Publication de la CEI, ou au crédit qui lui est accordé.

8) L'attention est attirée sur les références normatives citées dans cette publication. L'utilisation de publications

référencées est obligatoire pour une application correcte de la présente publication.

9) L’attention est attirée sur le fait que certains des éléments de la présente Publication de la CEI peuvent faire

l’objet de droits de propriété intellectuelle ou de droits analogues. La CEI ne saurait être tenue pour

responsable de ne pas avoir identifié de tels droits de propriété et de ne pas avoir signalé leur existence.

La Norme internationale CEI 60317-3 a été établie par le comité d'études 55 de la CEI: Fils

de bobinage.

Cette troisième édition de la CEI 60317-3 annule et remplace la deuxième édition, parue en

1990, et son amendement 1 (1997). Cette édition constitue une révision technique.

Les modifications principales par rappo
...