Plastics -- Melamine-formaldehyde powder moulding compounds (MF-PMCs)

This part of ISO 14528 specifies the methods of preparation of test specimens and the test methods to be used in determining the properties of powder moulding compounds (PMCs). Requirements for handling test material and for conditioning both the test material before moulding and the specimens before testing are given here. Procedures and conditions for the preparation of test specimens and procedures for measuring properties of the materials from which these specimens are made are given. Properties and test methods which are suitable and necessary to characterize PMCs are listed. The properties have been selected from the general test methods in ISO 10350-1. Other test methods in wide use for, or of particular significance to, PMCs are also included in this part of ISO 14528, as are the designatory properties found in ISO 14528-1. In order to obtain reproducible and comparable test results, it is necessary to use the methods of preparation and conditioning, the specimen dimensions and the test procedures specified herein. Values determined will not necessarily be identical to those obtained using specimens of different dimensions or prepared using different procedures.

Plastiques -- Poudres à mouler à base de mélamine-formaldéhyde (MF-PMC)

La présente partie de l'ISO 14528 spécifie les méthodes de préparation des éprouvettes et les méthodes d'essai ŕ appliquer pour déterminer les propriétés des poudres ŕ mouler (PMC). Elle fixe les exigences concernant, d'une part, le traitement du matériau pour essai, et d'autre part, le conditionnement du matériau pour essai avant moulage et des éprouvettes avant les essais. Elle précise les modes opératoires et les conditions ŕ appliquer pour la préparation des éprouvettes et pour le mesurage des propriétés des matériaux ŕ partir desquels sont fabriquées les éprouvettes. Elle fournit une liste des propriétés et des méthodes d'essai appropriées et nécessaires ŕ la caractérisation des PMC. Ces propriétés ont été choisies parmi les méthodes d'essai générales de l'ISO 10350-1. D'autres méthodes d'essai largement utilisées avec les PMC, ou présentant une importance particuličre, sont également incluses dans la présente partie de l'ISO 14528, tout comme les propriétés de désignation données dans l'ISO 14528-1. Pour obtenir des résultats reproductibles et comparables, il est nécessaire d'utiliser les méthodes de préparation et de conditionnement, les dimensions d'éprouvettes et les modes opératoires d'essai spécifiés dans le présent document. Les valeurs déterminées ne seront pas nécessairement identiques ŕ celles obtenues en utilisant des éprouvettes de dimensions différentes ou préparées selon d'autres modes opératoires.

General Information

Status
Published
Publication Date
17-Nov-1999
Current Stage
6060 - International Standard published
Start Date
31-Aug-1999
Completion Date
18-Nov-1999
Ref Project

RELATIONS

Buy Standard

Standard
ISO 14528-2:1999 - Plastics -- Melamine-formaldehyde powder moulding compounds (MF-PMCs)
English language
11 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 14528-2:1999 - Plastiques -- Poudres a mouler a base de mélamine-formaldéhyde (MF-PMC)
French language
11 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (sample)

INTERNATIONAL ISO
STANDARD 14528-2
First edition
1999-11-15
Plastics — Melamine-formaldehyde powder
moulding compounds (MF-PMCs) —
Part 2:
Preparation of test specimens and
determination of properties
Plastiques — Poudres à mouler à base de mélamine-formaldéhyde
(MF-PMC) —
Partie 2: Préparation des éprouvettes et détermination des propriétés
Reference number
ISO 14528-2:1999(E)
ISO 1999
---------------------- Page: 1 ----------------------
ISO 14528-2:1999(E)
PDF disclaimer

This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not

be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this

file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this

area.
Adobe is a trademark of Adobe Systems Incorporated.

Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters

were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event

that a problem relating to it is found, please inform the Central Secretariat at the address given below.

© ISO 1999

All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic

or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's member body

in the country of the requester.
ISO copyright office
Case postale 56 � CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 734 10 79
E-mail copyright@iso.ch
Web www.iso.ch
Printed in Switzerland
ii © ISO 1999 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 14528-2:1999(E)
Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO

member bodies). The work of preparing International Standards is normally carried out through ISO technical

committees. Each member body interested in a subject for which a technical committee has been established has

the right to be represented on that committee. International organizations, governmental and non-governmental, in

liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical

Commission (IEC) on all matters of electrotechnical standardization.

International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.

Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.

Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.

Attention is drawn to the possibility that some of the elements of this part of ISO 14528 may be the subject of

patent rights. ISO shall not be held responsible for identifying any or all such patent rights.

International Standard ISO 14528-2 was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee

SC 12, Thermosetting materials.

After a transition period of, at the most, four years, the three parts of ISO 14528 (see below), together with the

three parts of ISO 14527, will replace ISO 2112:1990, of which they constitute a technical revision.

ISO 14528 consists of the following parts, under the general title Plastics — Melamine-formaldehyde powder

moulding compounds (MF-PMCs):
� Part 1: Designation system and basis for specifications
� Part 2: Preparation of test specimens and determination of properties
� Part 3: Requirements for selected moulding compounds
© ISO 1999 – All rights reserved iii
---------------------- Page: 3 ----------------------
INTERNATIONAL STANDARD ISO 14528-2:1999(E)
Plastics — Melamine-formaldehyde powder moulding compounds
(MF-PMCs) —
Part 2:
Preparation of test specimens and determination of properties
1 Scope

This part of ISO 14528 specifies the methods of preparation of test specimens and the test methods to be used in

determining the properties of powder moulding compounds (PMCs). Requirements for handling test material and

for conditioning both the test material before moulding and the specimens before testing are given here.

Procedures and conditions for the preparation of test specimens and procedures for measuring properties of the

materials from which these specimens are made are given. Properties and test methods which are suitable and

necessary to characterize PMCs are listed.

The properties have been selected from the general test methods in ISO 10350-1. Other test methods in wide use

for, or of particular significance to, PMCs are also included in this part of ISO 14528, as are the designatory

properties found in ISO 14528-1.

In order to obtain reproducible and comparable test results, it is necessary to use the methods of preparation and

conditioning, the specimen dimensions and the test procedures specified herein. Values determined will not

necessarily be identical to those obtained using specimens of different dimensions or prepared using different

procedures.
2 Normative references

The following normative documents contain provisions which, through reference in this text, constitute provisions of

this part of ISO 14528. For dated references, subsequent amendments to, or revisions of, any of these publications

do not apply. However, parties to agreements based on this part of ISO 14528 are encouraged to investigate the

possibility of applying the most recent editions of the normative documents indicated below. For undated

references, the latest edition of the normative document referred to applies. Members of ISO and IEC maintain

registers of currently valid International Standards.

ISO 60:1977, Plastics — Determination of apparent density of material that can be poured from a specified funnel.

ISO 62:1999, Plastics — Determination of water absorption.

ISO 75-2:1993, Plastics — Determination of temperature of deflection under load — Part 2: Plastics and ebonite.

ISO 120:1977, Plastics — Phenol-formaldehyde mouldings — Determination of free ammonia and ammonium

compounds — Colorimetric comparison method.
ISO 171:1980, Plastics — Determination of bulk factor of moulding materials.
ISO 178:1993, Plastics — Determination of flexural properties.
© ISO 1999 – All rights reserved 1
---------------------- Page: 4 ----------------------
ISO 14528-2:1999(E)

ISO 179-1:— , Plastics — Determination of Charpy impact properties — Part 1: Non-instrumented impact test.

ISO 291:1997, Plastics — Standard atmospheres for conditioning and testing.

ISO 295:— , Plastics — Compression moulding of test specimens of thermosetting materials.

ISO 472:1999, Plastics — Vocabulary.

ISO 527-1:1993, Plastics — Determination of tensile properties — Part 1: General principles.

ISO 527-2:1993, Plastics — Determination of tensile properties — Part 2: Test conditions for moulding and

extrusion plastics.

ISO 899-1:1993, Plastics — Determination of creep behaviour — Part 1: Tensile creep.

ISO 1183:1987, Plastics — Methods for determining the density and relative density of non-cellular plastics.

ISO 2039-1:1993, Plastics — Determination of hardness — Part 1: Ball indentation method.

ISO 2112:1990, Plastics — Aminoplastic moulding materials — Specification.

ISO 2577:1984, Plastics — Thermosetting moulding materials — Determination of shrinkage.

ISO 2818:1994, Plastics — Preparation of test specimens by machining.
ISO 3167:1993, Plastics — Multipurpose test specimens.

ISO 3671:1976, Plastics — Aminoplastic moulding materials — Determination of volatile matter.

ISO 4589-2:1996, Plastics — Determination of burning behaviour by oxygen index — Part 2: Ambient-temperature

test.

ISO 4614:1977, Plastics — Melamine-formaldehyde mouldings — Determination of extractable formaldehyde.

ISO 6603-2:— , Plastics — Determination of puncture impact behaviour of rigid plastics — Part 2: Instrumented

impact testing.

ISO 7808:1992, Plastics — Thermosetting moulding materials — Determination of transfer flow.

ISO 8256:1990, Plastics — Determination of tensile-impact strength.

ISO 10350-1:1998, Plastics — Acquisition and presentation of comparable single-point data — Part 1: Moulding

materials.

ISO 10724-1:1998, Plastics — Injection moulding of test specimens of thermosetting powder moulding compounds

(PMCs) — Part 1: General principles and moulding of multipurpose test specimens.

ISO 10724-2:1998, Plastics — Injection moulding of test specimens of thermosetting powder moulding compounds

(PMCs) — Part 2: Small plates.

ISO 11359-2:1999, Plastics — Thermomechanical analysis (TMA) — Part 2: Determination of coefficient of linear

thermal expansion and glass transition temperature.
1) To be published. (Revision of ISO 179:1993)
2) To be published. (Revision of ISO 295:1991)
3) To be published. (Revision of ISO 6603-2:1989)
2 © ISO 1999 – All rights reserved
---------------------- Page: 5 ----------------------
ISO 14528-2:1999(E)

ISO 14528-1:1999, Plastics — Phenolic powder moulding compounds (PF-PMCs) — Part 1: Designation system

and basis for specifications.

ISO 14528-3:1999, Plastics — Phenolic powder moulding compounds (PF-PMCs) — Part 3: Requirements for

selected moulding compounds.

ISO 15062:— , Plastics — Determination of the thermal-flow and cure behaviour of thermosetting materials by

torque rheometry.

IEC 60093:1980, Methods of test for volume resistivity and surface resistivity of solid electrical insulating materials.

IEC 60112:1979, Method for determining the comparative and the proof tracking indices of solid insulating

materials under moist conditions.

IEC 60167:1964, Methods of test for the determination of the insulation resistance of solid insulating materials.

IEC 60243-1:1998, Electrical strength of insulating materials — Test methods — Part 1: Tests at power

frequencies.

IEC 60250:1969, Recommended methods for the determination of the permittivity and dielectric dissipation factor

of electrical insulating materials at power, audio and radio frequencies including metre wavelengths.

IEC 60296:1982, Specification for unused mineral insulating oils for transformers and switchgear.

IEC 60695-11-10:1999, Fire hazard testing — Part 11-10: Test flames — 50 W horizontal and vertical flame test

methods.

IEC 60695-11-20:1999, Fire hazard testing — Part 11-20: Test flames — 500 W flame test methods.

IEC 60707:1999, Flammability of solid non-metallic materials when exposed to flame sources — List of test

methods.
3 Terms and definitions

For the purposes of this part of ISO 14528, the terms and definitions given in ISO 472 and ISO 14528-1 apply, plus

the following:
3.1
thermal flow

parameter which characterizes the flow behaviour of plasticized thermosetting moulding compounds, e.g. when

filling a mould cavity, and for which the minimum torque M measured in accordance with ISO 15062 may be taken

as a measure
4 Preparation of test specimens
4.1 General

It is essential that specimens are always prepared by the same procedure (either injection moulding or

compression moulding), using the same processing conditions.

The procedure to be used for each test method is indicated in Tables 3 and 4 (M = injection moulding,

Q = compression moulding).
4) To be published.
© ISO 1999 – All rights reserved 3
---------------------- Page: 6 ----------------------
ISO 14528-2:1999(E)

The material shall be kept in moisture-proof containers until it is required for use.

The moisture content of filled or reinforced materials shall be expressed as a percentage of the total mass of the

compound.
4.2 Pretreatment of t
...

NORME ISO
INTERNATIONALE 14528-2
Première édition
1999-11-15
Plastiques — Poudres à mouler à base
de mélamine-formaldéhyde (MF-PMC) —
Partie 2:
Préparation des éprouvettes et
détermination des propriétés
Plastics — Melamine-formaldehyde powder moulding compounds
(MF-PMCs) —
Part 2: Preparation of test specimens and determination of properties
Numéro de référence
ISO 14528-2:1999(F)
ISO 1999
---------------------- Page: 1 ----------------------
ISO 14528-2:1999(F)
PDF – Exonération de responsabilité

Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier peut

être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence autorisant

l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées acceptent de fait la

responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute responsabilité en la

matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.

Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du

fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation de

ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer le

Secrétariat central à l'adresse donnée ci-dessous.
© ISO 1999

Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque

forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l’ISO à

l’adresse ci-après ou du comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 � CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 734 10 79
E-mail copyright@iso.ch
Web www.iso.ch
ImpriméenSuisse
ii © ISO 1999 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 14528-2:1999(F)
Avant-propos

L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de

normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux

comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité

technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en

liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission

électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.

Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,

Partie 3.

Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour

vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités

membres votants.

L’attention est appelée sur le fait que certains des éléments de la présente partie de l’ISO 14528 peuvent faire

l’objet de droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable de

ne pas avoir identifié de tels droits de propriété et averti de leur existence.

La Norme internationale ISO 14528-2 a été élaborée par le comité technique ISO/TC 61, Plastiques, sous-comité

SC 12, Matériaux thermodurcissables.

Après une période de transition d’au plus quatre ans, les trois parties de l’ISO 14528 (voir ci-dessous),

conjointement aux trois parties de l'ISO 14527, remplaceront l’ISO 2112:1990, dont elles constitueront une révision

technique.

L'ISO 14528 comprend les parties suivantes, présentées sous le titre général Plastiques — Poudres à mouler à

base de mélamine-formaldéhyde (MF-PMC):
� Partie 1: Système de désignation et base de spécification
� Partie 2: Préparation des éprouvettes et détermination des propriétés
� Partie 3: Exigences relatives à certaines poudres à mouler
© ISO 1999 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
NORME INTERNATIONALE ISO 14528-2:1999(F)
Plastiques — Poudres à mouler à base de mélamine-formaldéhyde
(MF-PMC) —
Partie 2:
Préparation des éprouvettes et détermination des propriétés
1 Domaine d'application

La présente partie de l’ISO 14528 spécifie les méthodes de préparation des éprouvettes et les méthodes d’essai à

appliquer pour déterminer les propriétés des poudres à mouler (PMC). Elle fixe les exigences concernant, d’une

part, le traitement du matériau pour essai, et d’autre part, le conditionnement du matériau pour essai avant

moulage et des éprouvettes avant les essais.

Elle précise les modes opératoires et les conditions à appliquer pour la préparation des éprouvettes et pour le

mesurage des propriétés des matériaux à partir desquels sont fabriquées les éprouvettes. Elle fournit une liste des

propriétés et des méthodes d’essai appropriées et nécessaires à la caractérisation des PMC.

Ces propriétés ont été choisies parmi les méthodes d’essai générales de l’ISO 10350-1. D’autres méthodes d’essai

largement utilisées avec les PMC, ou présentant une importance particulière, sont également incluses dans la

présente partie de l’ISO 14528, tout comme les propriétés de désignation données dans l’ISO 14528-1.

Pour obtenir des résultats reproductibles et comparables, il est nécessaire d’utiliser les méthodes de préparation et

de conditionnement, les dimensions d’éprouvettes et les modes opératoires d’essai spécifiés dans le présent

document. Les valeurs déterminées ne seront pas nécessairement identiques à celles obtenues en utilisant des

éprouvettes de dimensions différentes ou préparées selon d’autres modes opératoires.

2 Références normatives

Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,

constituent des dispositions valables pour la présente partie de l'ISO 14528. Pour les références datées, les

amendements ultérieurs ou les révisions de ces publications ne s’appliquent pas. Toutefois, les parties prenantes

aux accords fondés sur la présente partie de l'ISO 14528 sont invitées à rechercher la possibilité d'appliquer les

éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière

édition du document normatif en référence s’applique. Les membres de l'ISO et de la CEI possèdent le registre des

Normes internationales en vigueur.

ISO 60:1977, Plastiques — Détermination de la masse volumique apparente des matières susceptibles de

s’écouler à travers un entonnoir donné.
ISO 62:1999, Plastiques — Détermination de l’absorption d’eau.

ISO 75-2:1993, Plastiques — Détermination de la température de fléchissement sous charge — Partie 2:

Plastiques et ébonite.

ISO 120:1977, Plastiques — Pièces moulées à base de phénoplastes — Dosage de l’ammoniac libre et des

composés ammoniacaux — Méthode par comparaison colorimétrique.

ISO 171:1980, Plastiques — Détermination du facteur de contraction des matières à mouler.

© ISO 1999 – Tous droits réservés 1
---------------------- Page: 4 ----------------------
ISO 14528-2:1999(F)
ISO 178:1993, Plastiques — Détermination des propriétés en flexion.

ISO 179-1:— , Plastiques — Détermination des caractéristiques au choc Charpy — Partie 1: Essai de choc non

instrumenté.
ISO 291:1997, Plastiques — Atmosphères normales de conditionnement et d’essai.

ISO 295:— , Plastiques — Moulage par compression des éprouvettes en matières thermodurcissables.

ISO 472:1999, Plastiques — Vocabulaire.

ISO 527-1:1993, Plastiques — Détermination des propriétés en traction — Partie 1: Principes généraux.

ISO 527-2:1993, Plastiques — Détermination des propriétés en traction — Partie 2: Conditions d’essai des

plastiques pour moulage et extrusion.

ISO 899-1:1993, Plastiques — Détermination du comportement au fluage — Partie 1: Fluage en traction.

ISO 1183:1987, Plastiques — Méthodes pour déterminer la masse volumique et la densité relative des plastiques

non alvéolaires.

ISO 2039-1:1993, Plastiques — Détermination de la dureté — Partie 1: Méthode de pénétration à la bille.

ISO 2577:1984, Plastiques — Matières à mouler thermodurcissables — Détermination du retrait.

ISO 2818:1994, Plastiques — Préparation des éprouvettes par usinage.
ISO 3167:1993, Plastiques — Éprouvettes à usages multiples.

ISO 3671:1976, Matières plastiques — Matières à mouler aminoplastes — Détermination des matières volatiles.

ISO 4589-2:1996, Plastiques — Détermination du comportement au feu au moyen de l’indice d’oxygène —

Partie 2: Essai à la température ambiante.

ISO 4614:1977, Plastiques — Pièces moulées à base de résine mélamine-formaldéhyde — Détermination du

formaldéhyde extractible.

ISO 6603-2:— , Plastiques — Détermination du comportement des plastiques rigides perforés sous l'effet d'un

choc — Partie 2: Essai de choc instrumenté.

ISO 7808:1992, Plastiques — Matières à mouler thermodurcissables — Détermination de la fluidité par transfert.

ISO 8256:1990, Plastiques — Détermination de la résistance au choc-traction.

ISO 10350-1:1998, Plastiques — Acquisition et présentation de caractéristiques intrinsèques comparables —

Partie 1: Matériaux pour moulage.

ISO 10724-1:1998, Plastiques — Moulage par injection d’éprouvettes en compositions de poudre à mouler (PMC)

thermodurcissables — Partie 1: Principes généraux et moulage d’éprouvettes à usages multiples.

ISO 10724-2:1998, Plastiques — Moulage par injection d’éprouvettes en compositions de poudre à mouler (PMC)

thermodurcissables — Partie 2: Petites plaques.
1) À publier. (Révision de l’ISO 179:1993)
2) À publier. (Révision de l’ISO 295:1991)
3) À publier. (Révision de l’ISO 6603-2:1989)
2 © ISO 1999 – Tous droits réservés
---------------------- Page: 5 ----------------------
ISO 14528-2:1999(F)

ISO 11359-2:1999, Plastiques — Analyse thermomécanique (TMA) — Partie 2: Détermination du coefficient de

dilatation thermique linéique et de la température de transition vitreuse.

ISO 14528-1:1999, Plastiques — Poudres à mouler à base de mélamine-formaldéhyde (MF-PMC) — Partie 1:

Système de désignation et base de spécification.

ISO 14528-3:1999, Plastiques — Poudres à mouler à base de mélamine-formaldéhyde (MF-PMC) — Partie 3:

Exigences relatives à certaines poudres à mouler.

ISO 15062:— , Plastiques — Détermination de la fluidité à chaud et du comportement à la cuisson des matériaux

thermodurcissables au moyen d’un rhéomètre à couple.

CEI 60093:1980, Méthodes pour la mesure de la résistivité transversale et de la résistivité superficielle des

matériaux isolants électriques solides.

CEI 60112:1979, Méthode pour déterminer les indices de résistance et de tenue au cheminement des matériaux

isolants solides dans des conditions humides.

CEI 60167:1964, Méthodes d’essai pour la détermination de la résistance d’isolement des isolants solides.

CEI 60243-1:1998, Rigidité diélectrique des matériaux isolants — Méthodes d’essai — Partie 1: Essais aux

fréquences industrielles.

CEI 60250:1969, Méthodes recommandées pour la détermination de la permittivité et du facteur de dissipation des

isolants électriques aux fréquences industrielles, audibles et radioélectriques (ondes métriques comprises).

CEI 60296:1982, Spécification des huiles minérales isolantes neuves pour transformateurs et appareillage de

connexion.

CEI 60695-11-10 :1999, Essais relatifs aux risques du feu — Partie 11-10: Flammes d’essai — Méthodes d’essai

horizontale et verticale à la flamme de 50 W.

CEI 60695-11-20 :1999, Essais relatifs aux risques du feu — Partie 11-20: Flammes d’essai — Méthodes d’essai à

la flamme de 500 W.

CEI 60707:1999, Inflammabilité des matériaux solides non métalliques soumis à des sources d'allumage à flamme —

Liste des méthodes d'essai.
3 Termes et définitions

Pour les besoins de la présente partie de l'ISO 14528, les termes et définitions donnés dans l'ISO 472 et dans

l'ISO 14528-1 s'appliquent, conjointement avec la suivante:
3.1
fluidité à chaud

paramètre qui caractérise le comportement à l’écoulement des poudres à mouler thermodurcissables plastifiées,

par exemple lors du remplissage de la cavité du moule, et pour lequel le couple minimal, M , mesuré

conformément à l’ISO 15062, peut être utilisé comme valeur de mesure
4 ) À publier.
© ISO 1999 – Tous droits réservés 3
---------------------- Page: 6 ----------------------
ISO 14528-2:1999(F)
4 Préparation des éprouvettes
4.1 Généralités

Il est essentiel que les éprouvettes soient toujours préparées suivant le même mode opératoire (moulage par

compression ou injection), en utilisant les mêmes conditions de mise en œuvre.

Le mode opératoire devant être utilisé pour chaque méthode d’essai est indiqué dans les Tableaux 3 et 4

(M = moulage par injection, Q = moulage par compression).

Le matériau doit être conservé dans des conteneurs étanches à l’humidité jusqu’à son utilisation.

La teneur en humidité des matériaux chargés ou renforcés doit être exprimée en pourcentage de la masse totale

de matière.
4.2 Traitement préalable du matériau
Avant la mise en œuvre par moulage par injection, aucun traitement
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.