ISO 4661-2:2018

Rubber, vulcanized - Preparation of samples and test pieces - Part 2: Chemical tests

This document specifies a method of preparing samples from vulcanized rubber for use in chemical tests.

Caoutchouc vulcanisé — Préparation des échantillons et éprouvettes — Partie 2: Essais chimiques

Le présent document spécifie une méthode de préparation d'échantillons provenant de caoutchoucs vulcanisés pour utilisation dans des essais chimiques.

General Information

• Status: Published
• Publication Date: 25-Sep-2018
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 5 - Chemical tests
• Current Stage: 9093 - International Standard confirmed
• Start Date: 05-Jan-2024
• Completion Date: 13-Dec-2025

Relations

• Revises: ISO 4661-2:1987 - Rubber, vulcanized - Preparation of samples and test pieces - Part 2: Chemical tests
• Effective Date: 15-Dec-2017

Overview

ISO 4661-2:2018 - "Rubber, vulcanized - Preparation of samples and test pieces - Part 2: Chemical tests" specifies accepted methods for preparing samples of vulcanized rubber for chemical analysis. The standard ensures test portions are representative of the material under investigation and gives prescriptive preparation routes for different rubber forms (soft vulcanized rubber, ebonite and rubberized composites). It is part of the ISO 4661 series and is intended for laboratories, manufacturers and material analysts performing chemical tests on vulcanized rubber.

Key topics and requirements

• Representative sampling: Emphasizes that samples must reflect the desired property or constituent (e.g., include surface bloom when composition of original mix is required, or remove bloom for bulk composition).
• Avoid contamination and heat: Mechanical separation (blades, abrasive wheels, files) is preferred and heat generation should be avoided to prevent alteration of chemical composition.
• Soft vulcanized rubber: Comminute to pass a sieve of approximately 1.7 mm (scissors, rotating rasp, grinder, cryogenic crushing), or sheet to a thickness ≤ 0.5 mm on cold, tightly closed rolls. Type of grinder is immaterial provided no contamination/overheating.
• Ebonite: Rasp to powder passing an approximately 400 μm sieve; treat powder with a magnet to remove iron particles.
• Rubberized composites: Where mechanical separation is not possible, expose the rubber to solvent vapour only (for NR, SBR, BR: acetone or ETA - ethanol–toluene azeotrope). Keep exposure short to avoid extracting plasticizers. Remove solvent in air at room temperature and then treat as soft vulcanized rubber. If separation is impossible, cut material into small cubes to pass a 2 mm sieve and analyse the composite as a whole; determine rubber proportion by disintegration in a hot high‑boiling solvent and weighing, noting possible partial dissolution of other organic components.
• Reporting: Document and report the method of separation used; state when analysis is of a heterogeneous blend and caution about inhomogeneity errors.
• Safety/environment: The 2018 revision replaces chlorinated solvents with less hazardous solvents.

Applications and users

• Quality control and routine chemical analysis in rubber manufacturing and compound formulation.
• Third-party testing laboratories performing solvent-extract and compositional tests.
• Failure analysis and forensic material investigations of vulcanized rubber products.
• R&D and material characterization for automotive, industrial, seal and hose manufacturers.
• Regulatory and compliance testing where accurate chemical composition data is required.

Related standards

• ISO 1407:2011 - referenced for solvent selection and solvent-extract determination.
• Other parts of the ISO 4661 series for further test-piece preparation guidance.

Keywords: ISO 4661-2:2018, vulcanized rubber, sample preparation, chemical tests, rubber testing, ebonite, rubberized composites, solvent vapour, ISO 1407.

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 4661-2
Second edition
2018-09
Rubber, vulcanized — Preparation of
samples and test pieces —
Part 2:
Chemical tests
Caoutchouc vulcanisé — Préparation des échantillons et
éprouvettes —
Partie 2: Essais chimiques
Reference number
©
ISO 2018
© ISO 2018
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Fax: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii © ISO 2018 – All rights reserved

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Preparation of samples. 1
4.1 Soft vulcanized rubber . 1
4.2 Ebonite . 1
4.3 Rubberized composites . 1
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products,
Subcommittee SC 2, Testing and analysis.
This second edition cancels and replaces the first edition (ISO 4661-2:1987), which has been technically
revised.
The main changes compared to the previous edition are as follows:
— updating of the format of the document in regard to Clauses 2 and 3;
— replacement of chlorinated solvents with less hazardous solvents in 4.3.
A list of all parts in the ISO 4661 series can be found on the ISO website.
Any feedback or questions on this document should be directe
...

NORME ISO
INTERNATIONALE 4661-2
Deuxième édition
2018-09
Caoutchouc vulcanisé — Préparation
des échantillons et éprouvettes —
Partie 2:
Essais chimiques
Rubber, vulcanized — Preparation of samples and test pieces —
Part 2: Chemical tests
Numéro de référence
©
ISO 2018
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2018
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
Fax: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii © ISO 2018 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Préparation des échantillons . 1
4.1 Caoutchouc vulcanisé souple . 1
4.2 Ebonite . 1
4.3 Composites caoutchoutés . 1
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/iso/fr/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomères, sous-comité SC 2, Essais et analyses.
Cette deuxième édition annule et remplace la première (ISO 4661-2:1987), qui a fait l’objet d’une
révision technique.
Les principales modifications par rapport à la précédente édition sont les suivantes:
— mise à jour du format du document en ce qui concerne les Articles 2 et 3.
— remplacement des solvants chlorés par des solvants moins dangereux en 4.3.
Une liste de toutes les parties de la série ISO 4661 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve
...