ISO 1183-2:2019

Plastics — Methods for determining the density of non-cellular plastics — Part 2: Density gradient column method

This document specifies a gradient column method for the determination of the density of non-cellular moulded or extruded plastics or pellets in void-free form. Density gradient columns are columns containing a mixture of two liquids, the density in the column increasing uniformly from top to bottom. NOTE Density is frequently used to follow variations in physical structure or composition of plastic materials. Density can also be useful in assessing the uniformity of samples or specimens. The density of plastic materials can depend upon the choice of specimen preparation method. When this is the case, precise details of the specimen preparation method are intended to be included in the appropriate material specification.

Plastiques — Méthodes de détermination de la masse volumique des plastiques non alvéolaires — Partie 2: Méthode de la colonne à gradient de masse volumique

Le présent document spécifie une méthode qui utilise une colonne à gradient pour déterminer la masse volumique des plastiques non alvéolaires, moulés ou extrudés, ou de granulés exempts de cavités fermées. Les colonnes à gradient de masse volumique contiennent un mélange de deux liquides, dont la masse volumique augmente uniformément du haut de la colonne vers le bas. NOTE La masse volumique est fréquemment utilisée pour suivre les variations de la structure physique ou de la composition des matériaux plastiques. La masse volumique peut également se révéler utile pour évaluer l'uniformité des échantillons ou des éprouvettes. La masse volumique des matériaux plastiques peut dépendre du choix de la méthode de préparation de l'échantillon. Lorsque cela est applicable, des détails précis de la méthode de préparation de l'échantillon doivent être donnés dans les spécifications appropriées relatives à la matière.

General Information

• Status: Published
• Publication Date: 27-Feb-2019
• ICS: 83.080.01 - Plastics in general
• Technical Committee: ISO/TC 61/SC 5 - Physical-chemical properties
• Drafting Committee: ISO/TC 61/SC 5/WG 11 - Analytical methods
• Current Stage: 9092 - International Standard to be revised
• Due Date: 20-Nov-2024
• Completion Date: 20-Nov-2024

Relations

• Consolidated By: ISO 5157:2023 - Textiles — Environmental aspects — Vocabulary
• Effective Date: 06-Jun-2022
• Revises: ISO 1183-2:2004 - Plastics — Methods for determining the density of non-cellular plastics — Part 2: Density gradient column method
• Effective Date: 15-Dec-2017

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 1183-2
Second edition
2019-03
Plastics — Methods for determining
the density of non-cellular plastics —
Part 2:
Density gradient column method
Plastiques — Méthodes de détermination de la masse volumique des
plastiques non alvéolaires —
Partie 2: Méthode de la colonne à gradient de masse volumique
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Fax: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Conditioning . 2
5 Method . 2
5.1 Apparatus . 2
5.2 Immersion liquids . 2
5.3 Specimens . 3
5.4 Procedure . 3
5.4.1 Preparation and calibration of glass floats . 3
5.4.2 Preparation of density gradient column . 3
5.4.3 Measurement of density . 3
5.4.4 Calculations . 4
6 Test report . 4
Annex A (informative) Liquid systems suitable for density determinations .6
Annex B (informative) Preparation of density gradient column . 7
Bibliography .11
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 5, Physical-
chemical properties.
This second edition cancels and replaces the first edition (ISO 1183-2:2004), which has been technically
revised. The main changes compared to the previous edition are as follows:
— normative references have been changed to undated;
— text has been revised editorially.
A list of all parts in the ISO 1183 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved

INTERNATIONAL STANDARD ISO 1183-2:2019(E)
Plastics — Methods for determining the density of non-
cellular plastics —
Part 2:
Density gradient column method
WARNING — The use of this document may involve hazardous materials, operations or equipment.
This document does not purport to address all of the safety problems, if any, associated with
its use. It is the responsibility of the user of this document to establish appropriate health and
safety practices.
1 Scope
This document specifies a gradient column method for the determination of the density of non-cellular
moulded or extruded plastics or pellets in void-free form. Density gradient columns are columns
containing a mixture of two liquids, the density in the column increasing uniformly from top to bottom.
NOTE Density is frequently used to follow variations in physical structure or composition of plastic
materials. Density can also be useful in assessing the uniformity of samples or specimens. The density of plastic
materials can depend upon the choice of specimen preparation method. When this is the case, precise details of
the specimen preparation method are intended to be included in the appropriate material specification.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 1183-1, Plastics — Methods for determining the density of non-cellular plastics — Part 1: Immersion
method, liquid pycnometer method and titration method
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
3.1
density
ρ
3 3
ratio of the mass m of a sample to its volume V (at the temperature T) expressed in kg/m , kg/dm (g/
cm ), or kg/l (g/ml)
[1]
Note 1 to entry: The following terms, based upon ISO 80000-4 , are given in Table 1 for clarification.
Table 1 — Density terms
Term Symbol Formulation Units
kg/m
3 3
Density ρ m/V kg/dm (g/cm )
kg/l (g/ml)
m /kg
3 3
Specific volume ν V/m (= 1/ρ) dm /kg (cm /g)
l/kg (ml/g)
4 Conditioning
Conditioning and testing shall be in accordance with ISO 291 or the appropriate material standard. In
general, conditioning specimens to constant temperature is not required, because the determination
itself brings the specimen to the constant temperature of the test.
Specimens which change in density during the test to such an extent that the change is greater than the
required accuracy of the density determination shall be conditioned prior to measurement in accordance
with the applicable material specification. When changes in density with time or atmospheric conditions
are the primary purpose of the measurements, the specimens shall be conditioned as described in the
material specification and, if no material specification exists, then as agreed upon by the interested
parties.
5 Method
5.1 Apparatus
5.1.1 Density gradient column, consisting of a suitable graduated column, not less than 40 mm
in diameter, with a cover. The height of the column shall be compatible with the accuracy required. A
graduation interval of 1 mm for the scale on the column is normal.
5.1.2 Liquid bath, capable of being thermostatically controlled to within ±0,1 °C or ±0,5 °C, depending
on the sensitivity required (see Annex B).
5.1.3 Calibrated glass floats, covering the density range in which measurements are to be made and
approximately evenly distributed throughout this range.
These may be purchased from an accredited source or prepared as described in 5.4.1.
5.1.4 Balance, accurate to ±0,1 mg.
5.1.5 Siphon or pipette assembly, for filling the gradient column (5.1.1), as shown in Figure B.1 or B.2,
or any other suitable device.
5.2 Immersion liquids
Required are two miscible liquids of different densities, freshly distilled in the case of pure liquids. The
densities of various liquids are given in Annex A as a guide.
The liquid with which the specimen comes into contact during the measurement shall have no effect on
the specimen.
Prepare the mixture of liquids as specified in 5.4.1.2.
2 © ISO 2019 – All rights reserved

5.3 Specimens
Specimens shall consist of pieces of the material cut to any convenient shape for ease of identification.
The dimensions of each piece shall be chosen to permit accurate measurement of the position of the
centre of the piece.
When cutting specimens from larger samples, care shall be taken to ensure that the characteristics
of the material are not changed due to excessive heat generation. The surface of the specimen shall be
smooth and free from cavities to minimize the entrapment of air bubbles upon immersion in the liquid,
otherwise errors will be introduced.
NOTE Specimens of less than 5 mm in diameter are normally suitable.
5.4 Procedure
5.4.1 Preparation and calibration of glass floats
5.4.1.1 The glass floats (5.1.3) may be produced by any convenient method. They shall be approximately
spherical, of diameter not greater than 5 mm and fully annealed.
5.4.1.2 To prepare the glass floats for use, prepare a series of mixtures of about 500 ml of the two
immersion liquids (5.2) covering the density range to be used in the density gradient column (5.1.1).
With the floats and column at ambient temperature, place the floats carefully into these mixtures.
Adjust selected floats to match approximately the densities of the mixtures:
a) either by rubbing the float on a glass plate covered with a thin slurry of silicon carbide of particle
size less than 38 µm (400 mesh) or another suitable abrasive;
b) or by etching the float with hydrofluoric acid.
5.4.1.3 Determine the exact density of each glass float calibrated as above by placing it in a mixture of
two suitable liquids (5.2) in the bath (5.1.2) maintained at (t ± 0,1) °C, where t is 23 °C or 27 °C (whichever
will be used for the density gradient column). If the float sinks, add the denser of the two liquids (if
the float rises, add the less dense) and stir gently to homogenize. Allow the mixture to stabilize. If the
float still moves, adjust the density of the mixture again. Repeat this procedure until the float remains
stationary for at least 30 min.
5.4.1.4 For each float, determine, to the nearest 0,000 1 g/ml, the density of the solution in which the
float remained in equilibrium, using the pycnometer method (method B) described in ISO 1183-1 or any
other suitable method. Apply the buoyancy correction described in ISO 1183-1, if necessary. Record this
density as the density of the float.
Calibrated glass floats may also be purchased from accredited manufacturers.
5.4.2 Preparation of density gradient column
Methods for preparing the density gradient column ar
...

INTERNATIONAL ISO
STANDARD 1183-2
Second edition
2019-03
Plastics — Methods for determining
the density of non-cellular plastics —
Part 2:
Density gradient column method
Plastiques — Méthodes de détermination de la masse volumique des
plastiques non alvéolaires —
Partie 2: Méthode de la colonne à gradient de masse volumique
Reference number
©
ISO 2019
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Fax: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Conditioning . 2
5 Method . 2
5.1 Apparatus . 2
5.2 Immersion liquids . 2
5.3 Specimens . 3
5.4 Procedure . 3
5.4.1 Preparation and calibration of glass floats . 3
5.4.2 Preparation of density gradient column . 3
5.4.3 Measurement of density . 3
5.4.4 Calculations . 4
6 Test report . 4
Annex A (informative) Liquid systems suitable for density determinations .6
Annex B (informative) Preparation of density gradient column . 7
Bibliography .11
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: www .iso .org/iso/foreword .html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 5, Physical-
chemical properties.
This second edition cancels and replaces the first edition (ISO 1183-2:2004), which has been technically
revised. The main changes compared to the previous edition are as follows:
— normative references have been changed to undated;
— text has been revised editorially.
A list of all parts in the ISO 1183 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www .iso .org/members .html.
iv © ISO 2019 – All rights reserved

INTERNATIONAL STANDARD ISO 1183-2:2019(E)
Plastics — Methods for determining the density of non-
cellular plastics —
Part 2:
Density gradient column method
WARNING — The use of this document may involve hazardous materials, operations or equipment.
This document does not purport to address all of the safety problems, if any, associated with
its use. It is the responsibility of the user of this document to establish appropriate health and
safety practices.
1 Scope
This document specifies a gradient column method for the determination of the density of non-cellular
moulded or extruded plastics or pellets in void-free form. Density gradient columns are columns
containing a mixture of two liquids, the density in the column increasing uniformly from top to bottom.
NOTE Density is frequently used to follow variations in physical structure or composition of plastic
materials. Density can also be useful in assessing the uniformity of samples or specimens. The density of plastic
materials can depend upon the choice of specimen preparation method. When this is the case, precise details of
the specimen preparation method are intended to be included in the appropriate material specification.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 1183-1, Plastics — Methods for determining the density of non-cellular plastics — Part 1: Immersion
method, liquid pycnometer method and titration method
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https: //www .iso .org/obp
— IEC Electropedia: available at http: //www .electropedia .org/
3.1
density
ρ
3 3
ratio of the mass m of a sample to its volume V (at the temperature T) expressed in kg/m , kg/dm (g/
cm ), or kg/l (g/ml)
[1]
Note 1 to entry: The following terms, based upon ISO 80000-4 , are given in Table 1 for clarification.
Table 1 — Density terms
Term Symbol Formulation Units
kg/m
3 3
Density ρ m/V kg/dm (g/cm )
kg/l (g/ml)
m /kg
3 3
Specific volume ν V/m (= 1/ρ) dm /kg (cm /g)
l/kg (ml/g)
4 Conditioning
Conditioning and testing shall be in accordance with ISO 291 or the appropriate material standard. In
general, conditioning specimens to constant temperature is not required, because the determination
itself brings the specimen to the constant temperature of the test.
Specimens which change in density during the test to such an extent that the change is greater than the
required accuracy of the density determination shall be conditioned prior to measurement in accordance
with the applicable material specification. When changes in density with time or atmospheric conditions
are the primary purpose of the measurements, the specimens shall be conditioned as described in the
material specification and, if no material specification exists, then as agreed upon by the interested
parties.
5 Method
5.1 Apparatus
5.1.1 Density gradient column, consisting of a suitable graduated column, not less than 40 mm
in diameter, with a cover. The height of the column shall be compatible with the accuracy required. A
graduation interval of 1 mm for the scale on the column is normal.
5.1.2 Liquid bath, capable of being thermostatically controlled to within ±0,1 °C or ±0,5 °C, depending
on the sensitivity required (see Annex B).
5.1.3 Calibrated glass floats, covering the density range in which measurements are to be made and
approximately evenly distributed throughout this range.
These may be purchased from an accredited source or prepared as described in 5.4.1.
5.1.4 Balance, accurate to ±0,1 mg.
5.1.5 Siphon or pipette assembly, for filling the gradient column (5.1.1), as shown in Figure B.1 or B.2,
or any other suitable device.
5.2 Immersion liquids
Required are two miscible liquids of different densities, freshly distilled in the case of pure liquids. The
densities of various liquids are given in Annex A as a guide.
The liquid with which the specimen comes into contact during the measurement shall have no effect on
the specimen.
Prepare the mixture of liquids as specified in 5.4.1.2.
2 © ISO 2019 – All rights reserved

5.3 Specimens
Specimens shall consist of pieces of the material cut to any convenient shape for ease of identification.
The dimensions of each piece shall be chosen to permit accurate measurement of the position of the
centre of the piece.
When cutting specimens from larger samples, care shall be taken to ensure that the characteristics
of the material are not changed due to excessive heat generation. The surface of the specimen shall be
smooth and free from cavities to minimize the entrapment of air bubbles upon immersion in the liquid,
otherwise errors will be introduced.
NOTE Specimens of less than 5 mm in diameter are normally suitable.
5.4 Procedure
5.4.1 Preparation and calibration of glass floats
5.4.1.1 The glass floats (5.1.3) may be produced by any convenient method. They shall be approximately
spherical, of diameter not greater than 5 mm and fully annealed.
5.4.1.2 To prepare the glass floats for use, prepare a series of mixtures of about 500 ml of the two
immersion liquids (5.2) covering the density range to be used in the density gradient column (5.1.1).
With the floats and column at ambient temperature, place the floats carefully into these mixtures.
Adjust selected floats to match approximately the densities of the mixtures:
a) either by rubbing the float on a glass plate covered with a thin slurry of silicon carbide of particle
size less than 38 µm (400 mesh) or another suitable abrasive;
b) or by etching the float with hydrofluoric acid.
5.4.1.3 Determine the exact density of each glass float calibrated as above by placing it in a mixture of
two suitable liquids (5.2) in the bath (5.1.2) maintained at (t ± 0,1) °C, where t is 23 °C or 27 °C (whichever
will be used for the density gradient column). If the float sinks, add the denser of the two liquids (if
the float rises, add the less dense) and stir gently to homogenize. Allow the mixture to stabilize. If the
float still moves, adjust the density of the mixture again. Repeat this procedure until the float remains
stationary for at least 30 min.
5.4.1.4 For each float, determine, to the nearest 0,000 1 g/ml, the density of the solution in which the
float remained in equilibrium, using the pycnometer method (method B) described in ISO 1183-1 or any
other suitable method. Apply the buoyancy correction described in ISO 1183-1, if necessary. Record this
density as the density of the float.
Calibrated glass floats may also be purchased from accredited manufacturers.
5.4.2 Preparation of density gradient column
Methods for preparing the density gradient column ar
...

NORME ISO
INTERNATIONALE 1183-2
Deuxième édition
2019-03
Plastiques — Méthodes de
détermination de la masse volumique
des plastiques non alvéolaires —
Partie 2:
Méthode de la colonne à gradient de
masse volumique
Plastics — Methods for determining the density of non-cellular
plastics —
Part 2: Density gradient column method
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
Fax: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Conditionnement . 2
5 Méthode . 2
5.1 Appareillage. 2
5.2 Liquides d’immersion . 3
5.3 Échantillons . 3
5.4 Mode opératoire . 3
5.4.1 Préparation et étalonnage des flotteurs en verre . 3
5.4.2 Préparation de la colonne à gradient de masse volumique . 4
5.4.3 Mesurage de la masse volumique. 4
5.4.4 Calculs . 4
6 Rapport d’essai . 5
Annexe A (informative) Systèmes liquides appropriés pour déterminer la masse volumique .6
Annexe B (informative) Préparation de la colonne à gradient de masse volumique .7
Bibliographie .11
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/iso/fr/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 5,
Propriétés physicochimiques.
Cette deuxième édition annule et remplace la première édition (ISO 1183-2:2004), qui a fait l’objet d’une
révision technique. Les principales modifications par rapport à l’édition précédente sont les suivantes:
— Les références normatives ont été changées en références non-datées;
— Le texte a fait l’objet d’une révision éditoriale.
Une liste de toutes les parties de la série ISO 1183 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/fr/members .html.
iv © ISO 2019 – Tous droits réservés

NORME INTERNATIONALE ISO 1183-2:2019(F)
Plastiques — Méthodes de détermination de la masse
volumique des plastiques non alvéolaires —
Partie 2:
Méthode de la colonne à gradient de masse volumique
AVERTISSEMENT — L’utilisation du présent document peut impliquer l’exécution d’opérations
et l’utilisation de matières et d’équipements dangereux. Ce document n’a pas pour but de traiter
tous les problèmes de sécurité éventuels qui sont liés à son utilisation. Il incombe à l’utilisateur
du présent document de mettre en place des pratiques appropriées en matière d’hygiène et de
sécurité.
1 Domaine d’application
Le présent document spécifie une méthode qui utilise une colonne à gradient pour déterminer la masse
volumique des plastiques non alvéolaires, moulés ou extrudés, ou de granulés exempts de cavités
fermées. Les colonnes à gradient de masse volumique contiennent un mélange de deux liquides, dont la
masse volumique augmente uniformément du haut de la colonne vers le bas.
NOTE La masse volumique est fréquemment utilisée pour suivre les variations de la structure physique ou
de la composition des matériaux plastiques. La masse volumique peut également se révéler utile pour évaluer
l’uniformité des échantillons ou des éprouvettes. La masse volumique des matériaux plastiques peut dépendre du
choix de la méthode de préparation de l’échantillon. Lorsque cela est applicable, des détails précis de la méthode
de préparation de l’échantillon doivent être donnés dans les spécifications appropriées relatives à la matière.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les
références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 291, Plastiques — Atmosphères normales de conditionnement et d'essai
ISO 1183-1, Plastiques — Méthodes de détermination de la masse volumique des plastiques non alvéolaires —
Partie 1: Méthode par immersion, méthode du pycnomètre en milieu liquide et méthode par titrage
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https: //www .iso .org/obp
— IEC Electropedia: disponible à l’adresse http: //www .electropedia .org/
3.1
masse volumique
ρ
rapport de la masse m d’un échantillon à son volume V (à la température T), exprimé en kg/m , en kg/
3 3
dm (g/cm ) ou en kg/l (g/ml)
[1]
Note 1 à l'article: Les termes suivants, tirés de l’ISO 80000-4 , sont indiqués dans le Tableau 1 pour clarification.
Tableau 1 — Termes relatifs à la masse volumique
Terme Symbole Formule Unités
kg/m
3 3
Masse volumique ρ m/V kg/dm (g/cm )
kg/l (g/ml)
m /kg
3 3
Volume massique ν V/m (= 1/ρ) dm /kg (cm /g)
l/kg (ml/g)
4 Conditionnement
Le conditionnement et les essais doivent être en conformité avec l’ISO 291 ou avec la norme relative
à la matière considérée. En général, il n’est pas exigé de conditionner les échantillons à température
constante, car ils sont amenés à la température constante de l’essai au cours de l’évaluation elle-même.
Les échantillons, dont la masse volumique varie pendant l’essai à tel point que cette variation peut
dépasser l’exactitude requise pour cette détermination, doivent être conditionnés avant le mesurage,
selon les spécifications applicables à la matière considérée. Lorsque les variations de la masse volumique
avec le temps ou les conditions atmosphériques sont le principal objet des mesurages, les échantillons
doivent être conditionnés conformément à la description donnée dans les spécifications relatives au
matériau et, en l’absence de toute spécification relative au matériau, conformément à un accord conclu
entre les parties intéressées.
5 Méthode
5.1 Appareillage
5.1.1 Colonne à gradient de masse volumique, constituée d’une colonne graduée appropriée,
d’au moins 40 mm de diamètre, avec un bouchon. La hauteur de la colonne doit être compatible avec
l’exactitude requise. Un intervalle de graduation de 1 mm sur l’échelle de la colonne est normal.
5.1.2 Bain liquide, pouvant être thermorégulé à ± 0,1 °C ou à ± 0,5 °C près, en fonction de la sensibilité
requise (voir l’Annexe B).
5.1.3 Flotteurs en verre étalonnés, couvrant la plage des masses volumiques dans laquelle les
mesurages doivent être effectués et répartis à peu près régulièrement sur toute cette plage.
On peut les acheter auprès d’une source accréditée ou les préparer conformément à la description
donnée en 5.4.1.
5.1.4 Balance, d’une exactitude de ± 0,1 mg.
5.1.5 Siphon ou montage de pipettes, pour le remplissage de la colonne à gradient (5.1.1), comme
représenté sur la Figure B.1 ou B.2, ou tout autre dispositif approprié.
2 © ISO 2019 – Tous droits réservés

5.2 Liquides d’immersion
Deux liquides miscibles ayant des masses volumiques différentes et fraîchement distillés dans le cas de
liquides purs sont nécessaires. Les masses volumiques de différents liquides sont données en Annexe A
à titre indicatif.
Le liquide dans lequel l’échantillon est immergé pendant le mesurage ne doit avoir aucune action sur
celui-ci.
Préparer le mélange de liquides tel que spécifié en 5.4.1.2.
5.3 Échantillons
Les échantillons doivent être constitués de fragments de matière découpés selon une forme permettant
d’en faciliter l’identification. Les dimensions de chaque fragment doivent être choisies de façon qu’il soit
possible d’en localiser exactement le centre.
Lorsque les échantillons sont découpés à partir de grandes pièces, il faut veiller à ce que les
caractéristiques du matériau ne soient pas modifiées en raison d’une production de chaleur excessive.
La surface de l’échantillon doit être lisse et exempte de cavités de façon à réduire au minimum toute
rétention de bulles d’air pendant l’immersion dans le liquide, sinon des erreurs seront introduites.
NOTE Des échantillons d’un diamètre inférieur à 5 mm conviennent en principe.
5.4 Mode opératoire
5.4.1 Préparation et étalonnage des flotteurs en verre
5.4.1.1 Les flotteurs en verre (5.1.3) peuvent être produits selon toute méthode convenable. Ils doivent
être à peu près sphériques, d’un diamètre inférieur ou égal à 5 mm et complètement recuits.
5.4.1.2 Pour préparer les flotteurs en verre en vue de leur utilisation, préparer une série de mélanges
d’environ 500 ml des deux liquides d’immersion (5.2) couvrant la plage des masses volumiques à
utiliser dans la colonne à gradient de masse volumique (5.1.1)
...

NORME ISO
INTERNATIONALE 1183-2
Deuxième édition
2019-03
Plastiques — Méthodes de
détermination de la masse volumique
des plastiques non alvéolaires —
Partie 2:
Méthode de la colonne à gradient de
masse volumique
Plastics — Methods for determining the density of non-cellular
plastics —
Part 2: Density gradient column method
Numéro de référence
©
ISO 2019
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
Fax: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Conditionnement . 2
5 Méthode . 2
5.1 Appareillage. 2
5.2 Liquides d’immersion . 3
5.3 Échantillons . 3
5.4 Mode opératoire . 3
5.4.1 Préparation et étalonnage des flotteurs en verre . 3
5.4.2 Préparation de la colonne à gradient de masse volumique . 4
5.4.3 Mesurage de la masse volumique. 4
5.4.4 Calculs . 4
6 Rapport d’essai . 5
Annexe A (informative) Systèmes liquides appropriés pour déterminer la masse volumique .6
Annexe B (informative) Préparation de la colonne à gradient de masse volumique .7
Bibliographie .11
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www .iso .org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: www .iso .org/iso/fr/avant -propos.
Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 5,
Propriétés physicochimiques.
Cette deuxième édition annule et remplace la première édition (ISO 1183-2:2004), qui a fait l’objet d’une
révision technique. Les principales modifications par rapport à l’édition précédente sont les suivantes:
— Les références normatives ont été changées en références non-datées;
— Le texte a fait l’objet d’une révision éditoriale.
Une liste de toutes les parties de la série ISO 1183 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www .iso .org/fr/members .html.
iv © ISO 2019 – Tous droits réservés

NORME INTERNATIONALE ISO 1183-2:2019(F)
Plastiques — Méthodes de détermination de la masse
volumique des plastiques non alvéolaires —
Partie 2:
Méthode de la colonne à gradient de masse volumique
AVERTISSEMENT — L’utilisation du présent document peut impliquer l’exécution d’opérations
et l’utilisation de matières et d’équipements dangereux. Ce document n’a pas pour but de traiter
tous les problèmes de sécurité éventuels qui sont liés à son utilisation. Il incombe à l’utilisateur
du présent document de mettre en place des pratiques appropriées en matière d’hygiène et de
sécurité.
1 Domaine d’application
Le présent document spécifie une méthode qui utilise une colonne à gradient pour déterminer la masse
volumique des plastiques non alvéolaires, moulés ou extrudés, ou de granulés exempts de cavités
fermées. Les colonnes à gradient de masse volumique contiennent un mélange de deux liquides, dont la
masse volumique augmente uniformément du haut de la colonne vers le bas.
NOTE La masse volumique est fréquemment utilisée pour suivre les variations de la structure physique ou
de la composition des matériaux plastiques. La masse volumique peut également se révéler utile pour évaluer
l’uniformité des échantillons ou des éprouvettes. La masse volumique des matériaux plastiques peut dépendre du
choix de la méthode de préparation de l’échantillon. Lorsque cela est applicable, des détails précis de la méthode
de préparation de l’échantillon doivent être donnés dans les spécifications appropriées relatives à la matière.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les
références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 291, Plastiques — Atmosphères normales de conditionnement et d'essai
ISO 1183-1, Plastiques — Méthodes de détermination de la masse volumique des plastiques non alvéolaires —
Partie 1: Méthode par immersion, méthode du pycnomètre en milieu liquide et méthode par titrage
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https: //www .iso .org/obp
— IEC Electropedia: disponible à l’adresse http: //www .electropedia .org/
3.1
masse volumique
ρ
rapport de la masse m d’un échantillon à son volume V (à la température T), exprimé en kg/m , en kg/
3 3
dm (g/cm ) ou en kg/l (g/ml)
[1]
Note 1 à l'article: Les termes suivants, tirés de l’ISO 80000-4 , sont indiqués dans le Tableau 1 pour clarification.
Tableau 1 — Termes relatifs à la masse volumique
Terme Symbole Formule Unités
kg/m
3 3
Masse volumique ρ m/V kg/dm (g/cm )
kg/l (g/ml)
m /kg
3 3
Volume massique ν V/m (= 1/ρ) dm /kg (cm /g)
l/kg (ml/g)
4 Conditionnement
Le conditionnement et les essais doivent être en conformité avec l’ISO 291 ou avec la norme relative
à la matière considérée. En général, il n’est pas exigé de conditionner les échantillons à température
constante, car ils sont amenés à la température constante de l’essai au cours de l’évaluation elle-même.
Les échantillons, dont la masse volumique varie pendant l’essai à tel point que cette variation peut
dépasser l’exactitude requise pour cette détermination, doivent être conditionnés avant le mesurage,
selon les spécifications applicables à la matière considérée. Lorsque les variations de la masse volumique
avec le temps ou les conditions atmosphériques sont le principal objet des mesurages, les échantillons
doivent être conditionnés conformément à la description donnée dans les spécifications relatives au
matériau et, en l’absence de toute spécification relative au matériau, conformément à un accord conclu
entre les parties intéressées.
5 Méthode
5.1 Appareillage
5.1.1 Colonne à gradient de masse volumique, constituée d’une colonne graduée appropriée,
d’au moins 40 mm de diamètre, avec un bouchon. La hauteur de la colonne doit être compatible avec
l’exactitude requise. Un intervalle de graduation de 1 mm sur l’échelle de la colonne est normal.
5.1.2 Bain liquide, pouvant être thermorégulé à ± 0,1 °C ou à ± 0,5 °C près, en fonction de la sensibilité
requise (voir l’Annexe B).
5.1.3 Flotteurs en verre étalonnés, couvrant la plage des masses volumiques dans laquelle les
mesurages doivent être effectués et répartis à peu près régulièrement sur toute cette plage.
On peut les acheter auprès d’une source accréditée ou les préparer conformément à la description
donnée en 5.4.1.
5.1.4 Balance, d’une exactitude de ± 0,1 mg.
5.1.5 Siphon ou montage de pipettes, pour le remplissage de la colonne à gradient (5.1.1), comme
représenté sur la Figure B.1 ou B.2, ou tout autre dispositif approprié.
2 © ISO 2019 – Tous droits réservés

5.2 Liquides d’immersion
Deux liquides miscibles ayant des masses volumiques différentes et fraîchement distillés dans le cas de
liquides purs sont nécessaires. Les masses volumiques de différents liquides sont données en Annexe A
à titre indicatif.
Le liquide dans lequel l’échantillon est immergé pendant le mesurage ne doit avoir aucune action sur
celui-ci.
Préparer le mélange de liquides tel que spécifié en 5.4.1.2.
5.3 Échantillons
Les échantillons doivent être constitués de fragments de matière découpés selon une forme permettant
d’en faciliter l’identification. Les dimensions de chaque fragment doivent être choisies de façon qu’il soit
possible d’en localiser exactement le centre.
Lorsque les échantillons sont découpés à partir de grandes pièces, il faut veiller à ce que les
caractéristiques du matériau ne soient pas modifiées en raison d’une production de chaleur excessive.
La surface de l’échantillon doit être lisse et exempte de cavités de façon à réduire au minimum toute
rétention de bulles d’air pendant l’immersion dans le liquide, sinon des erreurs seront introduites.
NOTE Des échantillons d’un diamètre inférieur à 5 mm conviennent en principe.
5.4 Mode opératoire
5.4.1 Préparation et étalonnage des flotteurs en verre
5.4.1.1 Les flotteurs en verre (5.1.3) peuvent être produits selon toute méthode convenable. Ils doivent
être à peu près sphériques, d’un diamètre inférieur ou égal à 5 mm et complètement recuits.
5.4.1.2 Pour préparer les flotteurs en verre en vue de leur utilisation, préparer une série de mélanges
d’environ 500 ml des deux liquides d’immersion (5.2) couvrant la plage des masses volumiques à
utiliser dans la colonne à gradient de masse volumique (5.1.1)
...