(Main)Thermoplastics pipes and fittings — Vicat softening temperature: General test method and test conditions for vinyl chloride-based (PVC-U, PVC-C, PVC-Hi) and acryl nitrile-based (ABS, ASA) pipes and fittings
Thermoplastics pipes and fittings — Vicat softening temperature: General test method and test conditions for vinyl chloride-based (PVC-U, PVC-C, PVC-Hi) and acryl nitrile-based (ABS, ASA) pipes and fittings
The method specified is based on determining the temperature at which a standard indenter, under a force of 50 N ± 1 N, penetrates 1 mm into the surface of a test piece cut from the wall of a pipe or fitting while the temperature is raised at a constant rate. Is applicable only to thermoplastics materials for which it is possible to measure the temperature at which the rate of softening becomes rapid. Is based on ISO 306:1994 which, however, applies to materials in the form of sheets.
Tubes et raccords en matières thermoplastiques — Température de ramollissement Vicat : Méthode d'essai générale et conditions d’essai pour les tubes et raccords à base de chlorure de vinyle (PVC-U, PVC-C, PVC-Hi) et à base d'acrylonitrile (ABS, ASA)
General Information
Relations
Standards Content (Sample)
FINAL DRAFT
International
Standard
ISO/FDIS 2507
ISO/TC 138/SC 5
Thermoplastics pipes and fittings —
Secretariat: NEN
Vicat softening temperature:
Voting begins on:
General test method and test
2025-10-15
conditions for vinyl chloride-based
Voting terminates on:
(PVC-U, PVC-C, PVC-Hi) and acryl
2025-12-10
nitrile-based (ABS, ASA) pipes and
fittings
Tubes et raccords en matières thermoplastiques — Température
de ramollissement Vicat : Méthode d'essai générale et conditions
d’essai pour les tubes et raccords à base de chlorure de vinyle
(PVC-U, PVC-C, PVC-Hi) et à base d'acrylonitrile (ABS, ASA)
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/CEN PARALLEL PROCESSING LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
ISO/FDIS 2507:2025(en) © ISO 2025
FINAL DRAFT
ISO/FDIS 2507:2025(en)
International
Standard
ISO/FDIS 2507
ISO/TC 138/SC 5
Thermoplastics pipes and fittings —
Secretariat: NEN
Vicat softening temperature:
Voting begins on:
General test method and test
conditions for vinyl chloride-based
Voting terminates on:
(PVC-U, PVC-C, PVC-Hi) and acryl
nitrile-based (ABS, ASA) pipes and
fittings
Tubes et raccords en matières thermoplastiques — Température
de ramollissement Vicat : Méthode d'essai générale et conditions
d’essai pour les tubes et raccords à base de chlorure de vinyle
(PVC-U, PVC-C, PVC-Hi) et à base d'acrylonitrile (ABS, ASA)
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
© ISO 2025
IN ADDITION TO THEIR EVALUATION AS
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/CEN PARALLEL PROCESSING
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
or ISO’s member body in the country of the requester.
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland Reference number
ISO/FDIS 2507:2025(en) © ISO 2025
ii
ISO/FDIS 2507:2025(en)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Apparatus . 2
6 Test specimens . 5
6.1 Specimen preparation from pipes .5
6.2 Specimen preparation from fittings .6
6.3 Number of test specimen .7
7 Conditioning . 7
8 Procedure . 7
9 Test report . 8
Bibliography . 9
iii
ISO/FDIS 2507:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 138, Plastics pipes, fittings and valves for the
transport of fluids, Subcommittee SC 5, General properties of pipes, fittings and valves of plastic materials and
their accessories — Test methods and basic specifications, in collaboration with the European Committee for
Standardization (CEN) Technical Committee CEN/TC 155, Plastics piping systems and ducting systems, in
accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This third edition of ISO 2507 cancels and replaces ISO 2507-1:1995, ISO 2507-2:1995 and ISO 2507-3:1995,
which have been technically revised.
The main changes are as follows:
— the document was modified following edition 6 of ISO 306:2022;
— the procedure for test piece preparation from pipes and fittings was described in more detail;
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
ISO/FDIS 2507:2025(en)
Introduction
This document is based on ISO 306.
For convenience of use, it has been considered preferable to draw up a complete document for use in
determining the Vicat softening temperature of thermoplastics pipes and fittings. For further details,
reference to ISO 306 is recommended.
However, that ISO 306 is applicable to materials in the form of sheets, whereas this document is applicable to
products in the form of pipes and fittings.
This document gives the general conditions under which the Vicat softening temperature of pipes and
fittings is determined and provides the particular requirements for conducting tests on pipes and fittings of
various materials.
v
FINAL DRAFT International Standard ISO/FDIS 2507:2025(en)
Thermoplastics pipes and fittings — Vicat softening
temperature: General test method and test conditions for
vinyl chloride-based (PVC-U, PVC-C, PVC-Hi) and acryl nitrile-
based (ABS, ASA) pipes and fittings
1 Scope
This document specifies a specific method for determining the Vicat softening temperature (VST) of
thermoplastics pipes and fittings. It includes the adaption of method B 50 of ISO 306:2022 using a force of
50 N and a heating rate of 50 °C/h and the procedure for specimen preparation.
It includes the particular test conditions for determining the Vicat softening temperature (VST) of
unplasticized poly(vinylchloride) (PVC-U) or chlorinated poly(vinylchloride) (PVC-C) pipes and fittings, for
high impact resistance poly(vinylchloride) (PVC-HI) pipes and for acrylonitrile/butadiene/styrene (ABS)
and acrylonitrile/styrene/acrylic ester (ASA) pipes and fittings.
This document can also be used for pipes and fittings from other materials (e.g. PE-UHMW).
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 472, Plastics — Vocabulary
ISO 16012, Plastics — Determination of linear dimensions of test specimens
IEC 60584-1, Thermocouples — Part 1: EMF specifications and tolerances
IEC 60584-3, Thermocouples — Part 3: Extension and compensating cables — Tolerances and identification system
IEC 60751, Industrial platinum resistance thermometers and platinum temperature sensors
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 472 and the following apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
penetration
distance over which the indenting tip shall penetrate into the specimen under test
Note 1 to entry: It is expressed in millimetres (mm).
ISO/FDIS 2507:2025(en)
3.2
load
force applied to test specimen by means of the indenting tip
Note 1 to entry: It is expressed in Newtons (N).
3.3
vicat softening temperature
VST
temperature at which a flat-ended indenter will penetrate the specimen to a depth of 1 mm under a specified
load (3.2) using a selected uniform rate of temperature rise
Note 1 to entry: It is expressed in degrees Celsius (°C)
4 Principle
The temperature at which a standard indenting tip with a flat point, under a standardised load penetrates
(1,00 ± 0,01) mm into the surface of a test specimen, cut from the wall of a plastics pipe or a fitting, is
determined. The intending tip exerts a specified force of (50 ± 1) N perpendicular to the test specimen, while
the specimen is heated at a uniform rate of (50 ± 5) °C/h.
The temperature, in degree Celsius (°C), of the specimen, measured as close as possible to the indented area
at 1 mm penetration, is quoted as the VST.
5 Apparatus
5.1 Means of producing penetration
The apparatus shall be constructed essentially as shown in Figure 1. It consists of a rigid metal frame in
which a rod moves freely in the vertical direction. One end of the rod
...
ISO/DISFDIS 2507:2025(en)
ISO/TC 138/SC 5
Secretariat: NEN
Date: 2025-05-02
Thermoplastics pipes and fittings - — Vicat softening temperature:
General test method and test conditions for vinyl chloride - -based
(PVC-U, PVC-C, PVC-HIHi) and acrylonitrile - acryl nitrile-based (ABS,
ASA) pipes and fittings
Tubes et raccords en matières thermoplastiques — Température de ramollissement Vicat : Méthode d'essai
générale et conditions d’essai pour les tubes et raccords à base de chlorure de vinyle (PVC-U, PVC-C, PVC-Hi) et à
base d'acrylonitrile (ABS, ASA)
FDIS stage
ISO/FDIS 2507:2025(en)
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication
may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying,
or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO
at the address below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: + 41 22 749 01 11
EmailE-mail: copyright@iso.org
Website: www.iso.orgwww.iso.org
Published in Switzerland
ii
ISO/FDIS 2507:2025(en)
Contents
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Apparatus . 2
6 Test specimens . 6
7 Conditioning . 11
8 Procedure . 11
9 Test report . 12
Bibliography . 13
Foreword . 3
Introduction . 4
1 Scope . 4
2 Normative references . 4
3 Terms, definitions and abbreviated terms . 5
4 Principle . 5
5 Apparatus . 5
5.1 Means of producing penetration . 5
5.2 Indenter . 6
5.3 Heating equipment . 6
5.4 Weights . 6
5.5 Temperature-measuring device . 6
5.6 Penetration-measuring device. 7
5.7 Micrometers and gauges . 7
5.8 Oven with air circulation for drying materials . 7
6 Test specimens . 8
6.1 Specimen preparation from pipes . 8
6.2 Specimen preparation from fittings . 11
6.3 Number of test specimen . 11
7 Conditioning . 11
7.1 General . 11
8 Procedure . 12
9 Test report . 12
iii
ISO/FDIS 2507:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of
ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights
in respect thereof. As of the date of publication of this document, ISO had not received notice of (a) patent(s)
which may be required to implement this document. However, implementers are cautioned that this may not
represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents.www.iso.org/patents. ISO shall not be held responsible for identifying any or all such
patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.htmlwww.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 138, Plastics pipes, fittings and valves for the
transport of fluids, Subcommittee SC 5, General properties of pipes, fittings and valves of plastic materials and
their accessories — Test methods and basic specifications, in collaboration with the European Committee for
Standardization (CEN) Technical Committee CEN/TC 155, Plastics piping systems and ducting systems, in
accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This third edition of ISO 2507 cancels and replaces ISO 2507-1:1995, ISO 2507-2:1995 and ISO 2507-3:1995,
which have been technically revised.
The main changes are as follows:
— — the document was modified following edition 6 of ISO 306:2022;
— — the procedure for test piece preparation from pipes and fittings was described in more detail;
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.htmlwww.iso.org/members.html.
iv
ISO/FDIS 2507:2025(en)
Introduction
This document is based on ISO 306.
For convenience of use, it has been considered preferable to draw up a complete document for use in
determining the Vicat softening temperature of thermoplastics pipes and fittings. For further details, reference
to ISO 306 is recommended.
Please note, howeverHowever, that ISO 306 is applicable to materials in the form of sheets, whereas this
document is applicable to products in the form of pipes and fittings.
This document gives the general conditions under which the Vicat softening temperature of pipes and fittings
is determined and provides the particular requirements for conducting tests on pipes and fittings of various
materials.
v
DRAFT International Standard ISO/DIS 2507:2025(en)
Thermoplastics pipes and fittings — Vicat softening temperature:
General test method and test conditions for vinyl chloride-based (PVC-
U, PVC-C, PVC-HIHi) and acrylonitrileacryl nitrile-based (ABS,
ASA) pipes and fittings
1 Scope
This document specifies a specific method for determining the Vicat softening temperature (VST) of
thermoplastics pipes and fittings. It includes the adaption of method B 50 of ISO 306:2022 using a force of
50 N and a heating rate of 50 °C/h and the procedure for specimen preparation.
It includes the particular test conditions for determining the Vicat softening temperature (VST) of
unplasticized poly(vinylchloride) (PVC-U) or chlorinated poly(vinylchloride) (PVC-C) pipes and fittings, for
high impact resistance poly(vinylchloride) (PVC-HI) pipes and for acrylonitrile/butadiene/styrene (ABS) and
acrylonitrile/styrene/acrylic ester (ASA) pipes and fittings.
Note: This document can also be used for pipes and fittings from other materials (e.g. PE-UHMW).
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 306:2022, Plastics — Thermoplastic materials — Determination of Vicat softening temperature (VST)
ISO 472, Plastics — Vocabulary
ISO 16012, Plastics — Determination of linear dimensions of test specimens
IEC 60584--1, Thermocouples — Part 1: EMF specifications and tolerances
IEC 60584--3, Thermocouples — Part 3: Extension and compensating cables -— Tolerances and identification
system
IEC 60751, Industrial platinum resistance thermometers and platinum temperature sensors
3 Terms, and definitions and abbreviated terms
For the purposes of this document, the terms and definitions given in ISO 472 and the following apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— — ISO Online browsing platform: available at https://www.iso.org/obphttps://www.iso.org/obp
ISO/FDIS 2507:2025(en)
— — IEC Electropedia: available at https://www.electropedia.org/https://www.electropedia.org/
3.1 3.1
penetration
distance over which the indenting tip shall penetrate into the specimen under test
Note 1 to entry: It is expressed in millimetres (mm).
3.2 3.2
load
force applied to test specimen by means of the indenting tip
Note 1 to entry: It is expressed in Newtons (N).
3.3 3.3
vicat softening temperature
VST
temperature at which a flat-ended indenter will penetrate the specimen to a depth of 1 mm under a specified
load (3.2)(3.2) using a selected uniform rate of temperature rise.
Note 1 to entry: It is expressed in degrees Celsius (°C)
4 Principle
The temperature at which a standard indenting tip with a flat point, under a standardised load penetrates
(1,00 ± 0,01) mm into the surface of a test specimen, cut from the wall of a plastics pipe or a fitting, is
determined. The intending tip exerts a specified force of (50 ± 1) N perpendicular to the test specimen, while
the specimen is heated at a uniform rate of (50 ± 5) °C/h.
The temperature, in degree Celsius (°C), of the specimen, measured as close as possible to the indented area
at 1 mm penetration, is quoted as the VST.
5 Apparatus
5.1 Means of producing penetration
The apparatus shall be constructed essentially as shown in Figure 1.Figure 1. It consists of a rigid metal frame
in which a rod moves freely in the vertical direction. One end of the rod is fitted with a weight-carrying plate
and the ot
...
PROJET FINAL
Norme
internationale
ISO/FDIS 2507
ISO/TC 138/SC 5
Tubes et raccords en matières
Secrétariat: NEN
thermoplastiques — Température
Début de vote:
de ramollissement Vicat : Méthode
2025-10-15
d'essai générale et conditions
Vote clos le:
d’essai pour les tubes et raccords
2025-12-10
à base de chlorure de vinyle
(PVC-U, PVC-C, PVC-Hi) et à base
d'acrylonitrile (ABS, ASA)
Thermoplastics pipes and fittings — Vicat softening temperature:
General test method and test conditions for vinyl chloride-based
(PVC-U, PVC-C, PVC-Hi) and acryl nitrile-based (ABS, ASA) pipes
and fittings
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
Numéro de référence
ISO/FDIS 2507:2025(fr) © ISO 2025
PROJET FINAL
ISO/FDIS 2507:2025(fr)
Norme
internationale
ISO/FDIS 2507
ISO/TC 138/SC 5
Tubes et raccords en matières
Secrétariat: NEN
thermoplastiques — Température
Début de vote:
de ramollissement Vicat : Méthode
2025-10-15
d'essai générale et conditions
Vote clos le:
d’essai pour les tubes et raccords
2025-12-10
à base de chlorure de vinyle
(PVC-U, PVC-C, PVC-Hi) et à base
d'acrylonitrile (ABS, ASA)
Thermoplastics pipes and fittings — Vicat softening temperature:
General test method and test conditions for vinyl chloride-based
(PVC-U, PVC-C, PVC-Hi) and acryl nitrile-based (ABS, ASA) pipes
and fittings
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
© ISO 2025 INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
NORMES POUVANT
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse Numéro de référence
ISO/FDIS 2507:2025(fr) © ISO 2025
ii
ISO/FDIS 2507:2025(fr)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 2
5 Appareillage . 2
5.1 Moyens de produire une pénétration .2
5.2 Pénétrateur .3
5.3 Dispositif de chauffage .3
5.4 Poids .3
5.5 Dispositif de mesure de la température .3
5.6 Dispositif de mesure de la pénétration .4
5.7 Micromètres et comparateurs .4
5.8 Étuve avec circulation d’air pour le séchage des matériaux .4
6 Éprouvettes. 5
6.1 Préparation de l’éprouvette à partir de tubes .5
6.2 Préparation de l’éprouvette à partir de raccords .7
6.3 Nombre d’éprouvettes .8
7 Conditionnement . 8
8 Mode opératoire . 8
9 Rapport d’essai . 9
Bibliographie . 10
iii
ISO/FDIS 2507:2025(fr)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 138, Tubes, raccords et robinetterie en
matières plastiques pour le transport des fluides, sous-comité SC 5, Propriétés générales des tubes, raccords
et robinetteries en matières plastiques et leurs accessoires – Méthodes d’essais et spécifications de base, en
collaboration avec le comité technique CEN/TC 155, Systèmes de canalisations et de gaines en plastiques, du
Comité européen de normalisation (CEN) conformément à l’Accord de coopération technique entre l’ISO et le
CEN (Accord de Vienne).
Cette troisième édition de l’ISO 2507 annule et remplace l’ISO 2507-1:1995, l’ISO 2507-2:1995 et
l’ISO 2507-3:1995 qui ont fait l’objet d’une révision technique.
Les principales modifications sont les suivantes:
— le document a été modifié en fonction de l’édition 6 de l’ISO 306:2022.
— le mode opératoire de préparation des éprouvettes à partir de tubes et raccords a été décrit de manière
plus détaillée.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.
iv
ISO/FDIS 2507:2025(fr)
Introduction
Le présent document est basé sur l’ISO 306.
Pour des questions de facilité d’emploi, il a été jugé préférable de rédiger un document complet utilisable
pour la détermination de la température de ramollissement Vicat des tubes et des raccords en matières
thermoplastiques. Pour plus de précisions, il est recommandé de se reporter à l’ISO 306.
Cependant, l’ISO 306 s’applique à des matières sous forme de plaques, tandis que le présent document
s’applique à des produits sous forme de tubes et de raccords.
Le présent document indique les conditions générales dans lesquelles la température de ramollissement
Vicat des tubes et des raccords est déterminée et fournit les exigences particulières pour la réalisation
d’essais sur des tubes et des raccords à base de différentes matières.
v
PROJET FINAL Norme internationale ISO/FDIS 2507:2025(fr)
Tubes et raccords en matières thermoplastiques —
Température de ramollissement Vicat : Méthode d'essai
générale et conditions d’essai pour les tubes et raccords à
base de chlorure de vinyle (PVC-U, PVC-C, PVC-Hi) et à base
d'acrylonitrile (ABS, ASA)
1 Domaine d’application
Le présent document spécifie une méthode spécifique pour déterminer la température de ramollissement
Vicat (VST) des tubes et des raccords en matières thermoplastiques. Elle inclut l’adaptation de la méthode
B 50 de l’ISO 306:2022 en utilisant une force de 50 N et une vitesse d’élévation de la température de 50 °C/h
ainsi que le mode opératoire pour la préparation des éprouvettes.
Elle comprend les conditions d’essai particulières permettant de déterminer la température de
ramollissement Vicat (VST) des tubes et des raccords en poly(chlorure de vinyle) non plastifié (PVC-U) ou
en poly(chlorure de vinyle) chloré (PVC-C), des tubes en poly(chlorure de vinyle) à résistance aux chocs
améliorée (PVC-HI) et des tubes et des raccords en acrylonitrile/butadiène/styrène (ABS) et en acrylonitrile/
styrène/ester acrylique (ASA).
Le présent document peut également être utilisé pour les tubes et raccords fabriqués à partir d'autres
matériaux (par exemple, PE-UHMW).
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 291, Plastiques — Atmosphères normales de conditionnement et d'essai
ISO 472, Plastiques — Vocabulaire
ISO 16012, Plastiques — Détermination des dimensions linéaires des éprouvettes
IEC 60584-1, Couples thermoélectriques — Partie 1: Spécifications et tolérances en matière de FEM
IEC 60584-3, Couples thermoélectriques — Partie 3: Câbles d’extension et de compensation — Tolérances et
système d’identification
IEC 60751, Thermomètres à résistance de platine et capteurs thermométriques de platine industriels
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 472 ainsi que les suivants,
s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en normalisation,
consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
ISO/FDIS 2507:2025(fr)
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
3.1
pénétration
distance sur laquelle la pointe du pénétrateur doit s’enfoncer dans l’éprouvette soumise à essai
Note 1 à l'article: Elle est exprimée en millimètres (mm).
3.2
charge
force exercée sur l’éprouvette par la pointe du pénétrateur
Note 1 à l'article: Elle est exprimée en newtons (N).
3.3
température de ramollissement Vicat
VST
température à laquelle un pénétrateur à bout plat va s’enfoncer de 1 mm dans une éprouvette sous une
charge (3.2) spécifiée en utilisant une vitesse d’élévation de la température uniforme et sélectionnée
Note 1 à l'article: Elle est exprimée en degrés Celsius (°C).
4 Principe
Détermination de la température à laquelle la pointe d’un pénétrateur normalisé avec une pointe plate, sous
une charge normalisée, s’enfonce de (1,00 ± 0,01) mm dans la surface d’une éprouvette découpée dans la
paroi d’un tube ou d’un raccord en plastique. La pointe du pénétrateur exerce une force spécifiée de (50 ± 1) N
perpendiculaire à l’éprouvette, tandis que celle-ci est chauffée à une vitesse uniforme de (50 ± 5) °C/h.
La température de l’éprouvette, exprimée en degrés Celsius (°C) et mesurée le plus près possible de la
surface où agit le pénétrat
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.
Loading comments...