ISO 7530-9:1993

Nickel alloys — Flame atomic absorption spectrometric analysis — Part 9: Determination of vanadium content

The principle of the method specified is dissolving a test portion in acid, aspiring the test solution into a nitrous oxide-acetylene flame of an atomic absorption spectrometer, measuring the absorbance of the resonance line energy from the spectrum of vanadium and comparison with that of calibration solutions at a wavelength of 318,4 nm. The method may be used to determine vanadium contents in the range of 0,05 % (m/m) to 1 % (m/m).

Alliages de nickel — Analyse par spectrométrie d'absorption atomique dans la flamme — Partie 9: Dosage du vanadium

Nikljeve zlitine - Plamenska atomska absorpcijska spektrometrična analiza - 9. del: Ugotavljanje deleža vanadija

General Information

• Status: Published
• Publication Date: 18-Aug-1993
• ICS: 77.120.40 - Nickel, chromium and their alloys
• Technical Committee: ISO/TC 155 - Nickel and nickel alloys
• Drafting Committee: ISO/TC 155 - Nickel and nickel alloys
• Current Stage: 9093 - International Standard confirmed
• Start Date: 08-Sep-2025
• Completion Date: 14-Feb-2026
• Ref Project: SIST ISO 7530-9:1996 - Nickel alloys -- Flame atomic absorption spectrometric analysis -- Part 9: Determination of vanadium content

Overview

ISO 7530-9:1993 is an international standard developed by the International Organization for Standardization (ISO) that specifies a flame atomic absorption spectrometric method for determining vanadium content in nickel alloys. The procedure outlined in this document allows for accurate analysis of vanadium within the range of 0.05% (m/m) to 1% (m/m). The standard is part of the ISO 7530 series, which addresses the flame atomic absorption spectrometric analysis of various elements in nickel alloys, ensuring consistency and reliability in chemical analysis across industries.

Key Topics

• Nickel Alloys Analysis: This part focuses on determining vanadium, an element that significantly affects the properties of nickel-based materials.
• Flame Atomic Absorption Spectrometry (FAAS): The method involves dissolving a sample in acid, introducing it into a nitrous oxide-acetylene flame, and measuring the absorbance specific to vanadium at a wavelength of 318.4 nm.
• Calibration and Accuracy: The standard describes the preparation of calibration solutions and reagent blanks to ensure result accuracy, referencing the use of vanadium standard solutions and strontium chloride as a matrix modifier.
• Applicability Range: The method is suitable for vanadium concentrations from 0.05% to 1% (mass fraction), supporting applications in a wide range of nickel alloy compositions.
• Quality and Reproducibility: Guidance is provided on ensuring repeatability and reproducibility, referencing ISO 5725 for statistical treatment of laboratory results.

Applications

ISO 7530-9:1993 is essential for:

• Metallurgical Quality Control: Used extensively in laboratories for the precise measurement of vanadium during the production of nickel alloys, helping manufacturers maintain desired material characteristics.
• Aerospace and Power Generation: Nickel alloys with controlled vanadium content are critical in environments demanding high strength and resistance to heat and corrosion, such as turbine engines and power plants.
• Accredited Analytical Testing: Laboratories performing compliance testing and certification of nickel alloys use this standard to provide trusted analytical results.
• Research and Development: Facilitates the development of new nickel alloys by allowing accurate monitoring and adjustment of vanadium levels during alloy formulation.
• Material Certification: Supports producers and users in providing documentation and certification of vanadium content per international requirements.

Related Standards

• ISO 7530-1:1990 - General requirements and sample dissolution procedures for nickel alloy analysis.
• ISO 7530-2 to ISO 7530-8 - Methods for determining cobalt, chromium, copper, iron, manganese, aluminium, and silicon contents in nickel alloys using flame atomic absorption spectrometry.
• ISO 5725:1986 - Guidance on the precision and accuracy of test methods, used for validating analytical results in inter-laboratory settings.

Practical Value

By following ISO 7530-9:1993, laboratories and manufacturers ensure consistent and internationally accepted methods for vanadium determination in nickel alloys. This enhances the quality and reliability of materials used in critical industrial sectors, supports regulatory compliance, and fosters international trade by using standardized analytical procedures. The flame atomic absorption spectrometric approach outlined in this standard delivers reliable results, crucial for the demanding specifications of modern engineering applications.

Keywords: ISO 7530-9:1993, nickel alloys, vanadium determination, flame atomic absorption spectrometric analysis, chemical analysis, material quality control, metallurgical testing, standard methods.

Standards Content (Sample)

SLOVENSKI STANDARD
01-avgust-1996
1LNOMHYH]OLWLQH3ODPHQVNDDWRPVNDDEVRUSFLMVNDVSHNWURPHWULþQDDQDOL]DGHO
8JRWDYOMDQMHGHOHåDYDQDGLMD
Nickel alloys -- Flame atomic absorption spectrometric analysis -- Part 9: Determination
of vanadium content
Alliages de nickel -- Analyse par spectrométrie d'absorption atomique dans la flamme --
Partie 9: Dosage du vanadium
Ta slovenski standard je istoveten z: ISO 7530-9:1993
ICS:
77.120.40 Nikelj, krom in njune zlitine Nickel, chromium and their
alloys
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

INTERNATIONAL
IS0
STANDARD
7530-g
First edition
1993-08-I 5
Nickel alloys - Flame atomic absorption
spectrometric analysis -
Part 9:
Determination of vanadium content
Alliages de nickel - Analyse par spectromhrie d’absorption a tomique
dans la flamme -
Partie 9: Dosage du vanadium
Reference number
IS0 7530-g: 1993(E)
IS0 7530-g: 1993(E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide
federation of national standards bodies (IS0 member bodies). The work
of preparing International Standards is normally carried out through IS0
technical committees. Each member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard IS0 7530-9 was prepared by Technical Committee
ISO/TC 155, Nickel and nickel alloys, Sub-Committee SC 4, Analysis of
nickel alloys.
IS0 7530 consists of the following parts, under the general title Nickel al-
loys - Flame atomic absorption spectrome tric analysis:
- Part I: General requirements and sample dissolution
- Part 2: Determination of cobalt content
- Part 3: Determination of chromium content
- Part 4: Determination of copper content
- Part 5: De termination of iron con tent
- Part 6: Determination of manganese content
- Part 7: De termination of aluminium content
- Part 8: De termination of silicon content
- Part 9: Determination of vanadium content
0 IS0 1993
All rights reserved. No part of this publication may be reproduced or utilized in any form or
by any means, electronic or mechanical, including photocopying and microfilm, without per-
mission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-1211 Geneve 20 l Switzerland
Printed in Switzerland
ii
IS0 7530=9:1993(E)
INTERNATIONAL STANDARD
Nickel alloys - Flame atomic absorption
spectrometric analysis -
Part 9:
Determination of vanadium content
Measurement of the absorbance of the resonance
1 Scope
line energy from the spectrum of vanadium and com-
parison with that of calibration solutions at a wave-
This part of IS0 7530 specifies a flame atomic ab-
length of 318,4 nm.
sorption spectrometric method for the determination
of vanadium in the range of 0,05 % (m/m) to
1 % (m/m) in nickel alloys. Typical compositions of
nickel alloys are given in annex B of IS0 7530-I :1990.
4 Reagents
The general requirements concerning the apparatus,
In addition to the reagents listed in clause 4 of
sampling, dissolution of the test sample, atomic ab-
IS0 7530-I :I 990, the following special reagents are
sorption measurements, calculations and test report
required.
are given in IS0 7530-l.
4.1 Ammonium metavanadate (NHJO,), an alter-
2 Normative references
native to pure vanadium metal.
The following standards contain provisions which,
through reference in this text, constitute provisions
4.2 Strontium chloride, solution.
of this part of IS0 7530. At the time of publication, the
editions indicated were valid. All standards are subject
Transfer 113,5 g of strontium chloride hexahydrate
to revision, and parties to agreements based on this
(SrCI,.GH,O) to a 600 ml beaker, dissolve in 400 ml
part of IS0 7530 are encouraged to investigate the
of hot water (50 “C to 60 “C), cool and transfer to a
possibility of applying the most recent editions of the
1 000 ml one-mark volumetric flask. Make up to the
standards indicated below. Members of IEC and IS0
mark with water and mix. The strontium chloride
maintain registers of currently valid International
should be free of heavy metals
Standards.
IS0 5725:1986, Precision of test methods - De
...

INTERNATIONAL
IS0
STANDARD
7530-g
First edition
1993-08-I 5
Nickel alloys - Flame atomic absorption
spectrometric analysis -
Part 9:
Determination of vanadium content
Alliages de nickel - Analyse par spectromhrie d’absorption a tomique
dans la flamme -
Partie 9: Dosage du vanadium
Reference number
IS0 7530-g: 1993(E)
IS0 7530-g: 1993(E)
Foreword
IS0 (the International Organization for Standardization) is a worldwide
federation of national standards bodies (IS0 member bodies). The work
of preparing International Standards is normally carried out through IS0
technical committees. Each member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. IS0
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard IS0 7530-9 was prepared by Technical Committee
ISO/TC 155, Nickel and nickel alloys, Sub-Committee SC 4, Analysis of
nickel alloys.
IS0 7530 consists of the following parts, under the general title Nickel al-
loys - Flame atomic absorption spectrome tric analysis:
- Part I: General requirements and sample dissolution
- Part 2: Determination of cobalt content
- Part 3: Determination of chromium content
- Part 4: Determination of copper content
- Part 5: De termination of iron con tent
- Part 6: Determination of manganese content
- Part 7: De termination of aluminium content
- Part 8: De termination of silicon content
- Part 9: Determination of vanadium content
0 IS0 1993
All rights reserved. No part of this publication may be reproduced or utilized in any form or
by any means, electronic or mechanical, including photocopying and microfilm, without per-
mission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-1211 Geneve 20 l Switzerland
Printed in Switzerland
ii
IS0 7530=9:1993(E)
INTERNATIONAL STANDARD
Nickel alloys - Flame atomic absorption
spectrometric analysis -
Part 9:
Determination of vanadium content
Measurement of the absorbance of the resonance
1 Scope
line energy from the spectrum of vanadium and com-
parison with that of calibration solutions at a wave-
This part of IS0 7530 specifies a flame atomic ab-
length of 318,4 nm.
sorption spectrometric method for the determination
of vanadium in the range of 0,05 % (m/m) to
1 % (m/m) in nickel alloys. Typical compositions of
nickel alloys are given in annex B of IS0 7530-I :1990.
4 Reagents
The general requirements concerning the apparatus,
In addition to the reagents listed in clause 4 of
sampling, dissolution of the test sample, atomic ab-
IS0 7530-I :I 990, the following special reagents are
sorption measurements, calculations and test report
required.
are given in IS0 7530-l.
4.1 Ammonium metavanadate (NHJO,), an alter-
2 Normative references
native to pure vanadium metal.
The following standards contain provisions which,
through reference in this text, constitute provisions
4.2 Strontium chloride, solution.
of this part of IS0 7530. At the time of publication, the
editions indicated were valid. All standards are subject
Transfer 113,5 g of strontium chloride hexahydrate
to revision, and parties to agreements based on this
(SrCI,.GH,O) to a 600 ml beaker, dissolve in 400 ml
part of IS0 7530 are encouraged to investigate the
of hot water (50 “C to 60 “C), cool and transfer to a
possibility of applying the most recent editions of the
1 000 ml one-mark volumetric flask. Make up to the
standards indicated below. Members of IEC and IS0
mark with water and mix. The strontium chloride
maintain registers of currently valid International
should be free of heavy metals
Standards.
IS0 5725:1986, Precision of test methods - Deter- standard reference solution
4.3 Vanadium,
mination of repeatability and reproducibility for a
(1,000 g/l)-
standard test method by inter-laboratory tests.
4.3.1 Preparation from vanadium metal
IS0 7530-l :1990, Nickel alloys - Flame atomic ab-
sorption spectrometric analysis - Part 1: General re-
Weigh, to the nearest 0,001 g, 1,000 g of vanadium
quirements and sample dissolution.
metal of 99,9 % (m/m) minimum purity and transfer to
a 400 ml beaker. Add 60 ml of hydrochloric acid
20 ml of
and nitric acid
3 Principle (P20 = 1 I1 8 g/ml)
(p20 = I,41 g/ml) and heat to complete dissolution.
Cool and transfer
...

NORME ISO
7530-g
INTERNATIONALE
Première édition
1993-08-I 5
Alliages de nickel - Analyse par
spectrométrie d’absorption atomique dans
la flamme -
Partie 9:
Dosage du vanadium
Nickel alloys - Flame atomic absorption spectrometric analysis -
Part 9: Determination of vanadium content
Numéro de référence
ISO 7530=9:1993(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une féderation
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comite membre interessé par une
étude a le droit de faire partie du comite technique creé à cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mités membres votants.
La Norme internationale ISO 7530-9 a été élaboree par le comite techni-
que lSO/TC 155, Nickel et alliages de nickel, sous-comité SC 4, Analyse
des alliages de nickel.
L’ISO 7530 comprend les parties suivantes, présentées sous le titre gé-
néral Alliages de nickel - Analyse par spectrométrie d’absorption atomi-
que dans la flamme:
- Partie 1: Caractéristiques générales et mise en solution de
I’échan tillon
- Partie 2: Dosage du cobalt
- Partie 3: Dosage du chrome
- Partie 4: Dosage du cuivre
- Partie 5: Dosage du fer
- Partie 6: Dosage du manganèse
- Partie 7: Dosage de l’aluminium
- Partie 8: Dosage du silicium
- Partie 9: Dosage du vanadium
43 60 1993
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite
ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l’accord écrit de l’éditeur.
Organisation internationale de normalisation
Case Postale 56 l CH-l 211 Geneve 20 l Suisse
Imprimé en Suisse
ii
ISO 7530-g: 1993( F)
NORME INTERNATIONALE
Alliages de nickel - Analyse par spectrométrie
d’absorption atomique dans la flamme -
Partie 9:
Dosage du vanadium
ISO 7530-l : 1990, Alliages de nickel - Analyse par
1 Domaine d’application
spectromé trie d’absorption atomique dans la flamme
- Partie 1: Caractéristiques générales et mise en
La présente partie de I’ISO 7530 prescrit une mé-
solution de Mchan tillon.
thode de dosage par spectrométrie d’absorption ato-
mique dans la flamme du vanadium à des teneurs
comprises entre 0,05 % (dm) et 1 % (dm) dans les
alliages de nickel. Les compositions types de certains
3 Principe
alliages de nickel sont données dans l’annexe B de
I’ISO 7530-I :1990.
Mise en solution d’une prise d’essai dans l’acide et
aspiration de la solution dans la flamme monoxyde de
Les prescriptions générales concernant l’appareillage,
diazote/acétylène d’un spectrometre d’absorption
l’échantillonnage, la mise en solution de l’échantillon
atomique.
pour essai, les mesurages d’absorption atomique, les
calculs et le rapport d’essai sont données dans
Mesurage de I’absorbance de l’énergie de la raie de
I’ISO 7530-l.
résonance du spectre de vanadium et comparaison
de celle-ci avec les solutions d’étalonnage à une lon-
gueur d’onde de 318,4 nm.
4 Réactifs
2 Références normatives
Outre les réactifs énumérés à l’article 4 de
Les normes suivantes contiennent des dispositions
I’ISO 7530-I :1990, les réactifs spéciaux suivants sont
qui, par suite de la référence qui en est faite, consti-
nécessaires.
tuent des dispositions valables pour la présente partie
de I’ISO 7530. Au moment de la publication, les édi-
tions indiquées étaient en vigueur. Toute norme est
4.1 Métavanadate d’ammonium
(WJQ),
sujette à révision et les parties prenantes des accords
comme solution alternative au métal pur de vanadium.
fondes sur la présente partie de I’ISO 7530 sont invi-
tées à rechercher la possibilité d’appliquer les éditions
les plus récentes des normes indiquées ci-après. Les
4.2 Chlorure de strontium, solution.
membres de la CEI et de I’ISO possèdent le registre
des Normes internationales en vigueur à un moment Transférer 113,5 g de chlorure de strontium
donné. hexahydraté (SrCI,,GH,O) dans un bécher de 600 ml,
dissoudre dans 400 ml d’eau chaude (50 “C à 60 OC),
ISO 5725: 1986, Fidélité des methodes d’essai - De- refroidir et transférer dans une fiole jaugée de
termina tion de la repetabilite et de la reproductibilite 1 000 ml. Compléter au volume avec de l’eau et
d’une méthode d’essai normalisee par essais interla- homogénéiser. Le chlorure de strontium doit être
bora toires. exempt de métaux lourds.

ISO 7530-S: 1993(F)
7.1.1 Dilution initiale pour des teneurs en
4.3 Vanadium, solution etalon de réference
vanadium comprises entre 0,05 % (m/m) et
(1,000 gli>*
0,35 %(dm)
4.3.1 Préparation
...

NORME ISO
7530-g
INTERNATIONALE
Première édition
1993-08-I 5
Alliages de nickel - Analyse par
spectrométrie d’absorption atomique dans
la flamme -
Partie 9:
Dosage du vanadium
Nickel alloys - Flame atomic absorption spectrometric analysis -
Part 9: Determination of vanadium content
Numéro de référence
ISO 7530=9:1993(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une féderation
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comite membre interessé par une
étude a le droit de faire partie du comite technique creé à cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mités membres votants.
La Norme internationale ISO 7530-9 a été élaboree par le comite techni-
que lSO/TC 155, Nickel et alliages de nickel, sous-comité SC 4, Analyse
des alliages de nickel.
L’ISO 7530 comprend les parties suivantes, présentées sous le titre gé-
néral Alliages de nickel - Analyse par spectrométrie d’absorption atomi-
que dans la flamme:
- Partie 1: Caractéristiques générales et mise en solution de
I’échan tillon
- Partie 2: Dosage du cobalt
- Partie 3: Dosage du chrome
- Partie 4: Dosage du cuivre
- Partie 5: Dosage du fer
- Partie 6: Dosage du manganèse
- Partie 7: Dosage de l’aluminium
- Partie 8: Dosage du silicium
- Partie 9: Dosage du vanadium
43 60 1993
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite
ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l’accord écrit de l’éditeur.
Organisation internationale de normalisation
Case Postale 56 l CH-l 211 Geneve 20 l Suisse
Imprimé en Suisse
ii
ISO 7530-g: 1993( F)
NORME INTERNATIONALE
Alliages de nickel - Analyse par spectrométrie
d’absorption atomique dans la flamme -
Partie 9:
Dosage du vanadium
ISO 7530-l : 1990, Alliages de nickel - Analyse par
1 Domaine d’application
spectromé trie d’absorption atomique dans la flamme
- Partie 1: Caractéristiques générales et mise en
La présente partie de I’ISO 7530 prescrit une mé-
solution de Mchan tillon.
thode de dosage par spectrométrie d’absorption ato-
mique dans la flamme du vanadium à des teneurs
comprises entre 0,05 % (dm) et 1 % (dm) dans les
alliages de nickel. Les compositions types de certains
3 Principe
alliages de nickel sont données dans l’annexe B de
I’ISO 7530-I :1990.
Mise en solution d’une prise d’essai dans l’acide et
aspiration de la solution dans la flamme monoxyde de
Les prescriptions générales concernant l’appareillage,
diazote/acétylène d’un spectrometre d’absorption
l’échantillonnage, la mise en solution de l’échantillon
atomique.
pour essai, les mesurages d’absorption atomique, les
calculs et le rapport d’essai sont données dans
Mesurage de I’absorbance de l’énergie de la raie de
I’ISO 7530-l.
résonance du spectre de vanadium et comparaison
de celle-ci avec les solutions d’étalonnage à une lon-
gueur d’onde de 318,4 nm.
4 Réactifs
2 Références normatives
Outre les réactifs énumérés à l’article 4 de
Les normes suivantes contiennent des dispositions
I’ISO 7530-I :1990, les réactifs spéciaux suivants sont
qui, par suite de la référence qui en est faite, consti-
nécessaires.
tuent des dispositions valables pour la présente partie
de I’ISO 7530. Au moment de la publication, les édi-
tions indiquées étaient en vigueur. Toute norme est
4.1 Métavanadate d’ammonium
(WJQ),
sujette à révision et les parties prenantes des accords
comme solution alternative au métal pur de vanadium.
fondes sur la présente partie de I’ISO 7530 sont invi-
tées à rechercher la possibilité d’appliquer les éditions
les plus récentes des normes indiquées ci-après. Les
4.2 Chlorure de strontium, solution.
membres de la CEI et de I’ISO possèdent le registre
des Normes internationales en vigueur à un moment Transférer 113,5 g de chlorure de strontium
donné. hexahydraté (SrCI,,GH,O) dans un bécher de 600 ml,
dissoudre dans 400 ml d’eau chaude (50 “C à 60 OC),
ISO 5725: 1986, Fidélité des methodes d’essai - De- refroidir et transférer dans une fiole jaugée de
termina tion de la repetabilite et de la reproductibilite 1 000 ml. Compléter au volume avec de l’eau et
d’une méthode d’essai normalisee par essais interla- homogénéiser. Le chlorure de strontium doit être
bora toires. exempt de métaux lourds.

ISO 7530-S: 1993(F)
7.1.1 Dilution initiale pour des teneurs en
4.3 Vanadium, solution etalon de réference
vanadium comprises entre 0,05 % (m/m) et
(1,000 gli>*
0,35 %(dm)
4.3.1 Préparation
...