Plastics hose — General-purpose collapsible water hose, textile-reinforced — Specification

ISO 8029:2014 specifies the requirements for four types of textile-reinforced thermoplastics collapsible water hoses for general applications for use in the temperature range of −10 °C to 55 °C. Such hoses are classified into four types, as follows: low pressure, designed for a maximum working pressure of up to 0,4 MPa (4,0 bar) at 23 °C and up to 0,2 MPa (2,0 bar) at 55 °C; medium pressure, for a maximum working pressure of up to 0,7 MPa (7,0 bar) at 23 °C and up to 0,36 MPa (3,6 bar) at 55 °C; high pressure, for a maximum working pressure of up to 1,0 MPa (10,0 bar) at 23 °C and up to 0,51 MPa (5,1 bar) at 55 °C; extra-high pressure, for a maximum working pressure of up to 1,55 MPa (15,5 bar) at 23 °C and up to 0,79 MPa (7,9 bar) at 55 °C.

Tuyaux plastiques — Tuyaux d'eau écrasables d'usage général renforcés textiles — Spécifications

L'ISO 8029:2014 spécifie les exigences pour quatre types de tuyaux d'eau écrasables thermoplastiques renforcés textiles destinés à des applications générales pour utilisation à des températures comprises entre -10 °C et 55 °C. Ces tuyaux sont classés selon les quatre types suivants: basse pression, conçus pour une pression maximale de service jusqu'à 0,4 MPa (4,0 bar) à 23 °C et jusqu'à 0,2 MPa (2,0 bar) à 55 °C; moyenne pression, pour une pression maximale de service jusqu'à 0,7 MPa (7,0 bar) à 23 °C et jusqu'à 0,36 MPa (3,6 bar) à 55 °C; haute pression, pour une pression maximale de service jusqu'à 1,0 MPa (10,0 bar) à 23 °C et de 0,51 MPa (5,1 bar) à 55 °C; très haute pression, pour une pression maximale de service jusqu'à 1,55 MPa (15,5 bar) à 23 °C et jusqu'à 0,79 MPa (7,9 bar) à 55 °C.

General Information

Status
Published
Publication Date
10-Aug-2014
Current Stage
9093 - International Standard confirmed
Due Date
10-Jan-2025
Completion Date
10-Jan-2025
Ref Project

Relations

Buy Standard

Standard
ISO 8029:2014 - Plastics hose — General-purpose collapsible water hose, textile-reinforced — Specification Released:8/11/2014
English language
16 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 8029:2014 - Plastics hose -- General-purpose collapsible water hose, textile-reinforced -- Specification
English language
16 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 8029:2014 - Tuyaux plastiques — Tuyaux d'eau écrasables d'usage général renforcés textiles — Spécifications Released:8/11/2014
French language
16 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 8029:2014 - Tuyaux plastiques -- Tuyaux d'eau écrasables d'usage général renforcés textiles -- Spécifications
French language
16 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


INTERNATIONAL ISO
STANDARD 8029
Third edition
2014-08-15
Plastics hose — General-purpose
collapsible water hose, textile-
reinforced — Specification
Tuyaux plastiques — Tuyaux d’eau écrasables d’usage général
renforcés textiles — Spécifications
Reference number
©
ISO 2014
© ISO 2014
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2014 – All rights reserved

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Classification . 2
5 Couplings and end fittings . 2
6 Materials and construction . 2
7 Dimensions and tolerances . 2
7.1 Inside diameter and tolerance . 2
7.2 Tolerance on length . 3
8 Physical properties . 4
8.1 Plastic compounds . 4
8.2 Performance requirements for finished hose . 4
9 Frequency of testing . 9
10 Test certificate/report . 9
11 Marking . 9
12 Recommendations for packaging and storage .10
Annex A (normative) Abrasion test .11
Annex B (normative) Type and routine testing .13
Annex C (informative) Production tests .14
Annex D (informative) Couplings and end fittings .15
Bibliography .16
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 45, Rubber and rubber products, Subcommittee
SC 1, Rubber and plastics hoses and hose assemblies.
This third edition cancels and replaces the second edition (ISO 8029:2007), which has been technically
revised. Fifteen sizes of inside diameter were added in order to conform to the couplings and end fittings
available in the market (see Table 1).
iv © ISO 2014 – All rights reserved

Introduction
This International Standard has been prepared to provide minimum requirements for the satisfactory
performance of textile-reinforced thermoplastic collapsible water hose, for discharge applications,
conveying water, aqueous sludge or slurries.
In view of such applications, requirements and the corresponding tests have been specified for exposure
to laboratory light sources (see 8.2.5) and for abrasion resistance (see 8.2.6).
INTERNATIONAL STANDARD ISO 8029:2014(E)
Plastics hose — General-purpose collapsible water hose,
textile-reinforced — Specification
1 Scope
This International Standard specifies the requirements for four types of textile-reinforced thermoplastics
collapsible water hoses for general applications for use in the temperature range of −10 °C to 55 °C. Such
hoses are classified into four types, as follows:
— low pressure, designed for a maximum working pressure of up to 0,4 MPa (4,0 bar) at 23 °C and up
to 0,2 MPa (2,0 bar) at 55 °C;
— medium pressure, for a maximum working pressure of up to 0,7 MPa (7,0 bar) at 23 °C and up to
0,36 MPa (3,6 bar) at 55 °C;
— high pressure, for a maximum working pressure of up to 1,0 MPa (10,0 bar) at 23 °C and up to
0,51 MPa (5,1 bar) at 55 °C;
— extra-high pressure, for a maximum working pressure of up to 1,55 MPa (15,5 bar) at 23 °C and up
to 0,79 MPa (7,9 bar) at 55 °C.
This International Standard does not apply to products used for fire-fighting or the conveyance of
drinking water.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 3, Preferred numbers — Series of preferred numbers
ISO 37, Rubber, vulcanized or thermoplastic — Determination of tensile stress-strain properties
ISO 188, Rubber, vulcanized or thermoplastic — Accelerated ageing and heat resistance tests
ISO 1307, Rubber and plastics hoses — Hose sizes, minimum and maximum inside diameters, and tolerances
on cut-to-length hoses
ISO 1402, Rubber and plastics hoses and hose assemblies — Hydrostatic testing
ISO 8033, Rubber and plastics hoses — Determination of adhesion between components
ISO 8330, Rubber and plastics hoses and hose assemblies — Vocabulary
ISO 9352, Plastics — Determination of resistance to wear by abrasive wheels
ISO 10619-1, Rubber and plastics hoses and tubing — Measurement of flexibility and stiffness — Part 1:
Bending tests at ambient temperature
ISO 10619-2, Rubber and plastics hoses and tubing — Measurement of flexibility and stiffness — Part 2:
Bending tests at sub-ambient temperatures
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
ISO 30013, Rubber and plastics hoses — Methods of exposure to laboratory light sources — Determination
of changes in colour, appearance and other physical properties
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 8330 apply.
4 Classification
Hoses are designated as one of the following four types depending on their pressure rating at the
specified temperatures:
— Type A: Low working pressure hose, designed for a maximum working pressure of up to 0,4 MPa
(4,0 bar) at 23 °C and up to 0,2 MPa (2,0 bar) at 55 °C;
— Type B: Medium working pressure hose, designed for a maximum working pressure of up to 0,7 MPa
(7,0 bar) at 23 °C and up to 0,36 MPa (3,6 bar) at 55 °C;
— Type C: High working pressure hose, designed for a maximum working pressure of up to 1,0 MPa
(10,0 bar) at 23 °C and up to 0,51 MPa (5,1 bar) at 55 °C;
— Type D: Extra high working pressure hose, designed for a maximum working pressure of up to
1,55 MPa (15,5 bar) at 23 °C and up to 0,79 MPa (7,9 bar) at 55 °C.
5 Couplings and end fittings
Hoses may be fitted with the appropriate coupling type and the end fitting to form hose assemblies.
Guidance on coupling type is given in Annex D and ISO/TR 17784:2003, Clause 7: Couplings.
6 Materials and construction
The hose shall consist of:
a) a flexible thermoplastic lining;
b) a reinforcement made of natural or synthetic textile material, applied by any suitable technique;
and
c) a flexible thermoplastic cover.
The lining and the cover shall be of uniform thickness, fully gelled and free from visible cracks, porosity,
foreign inclusions and other defects. The cover may have a smooth or fluted finish, and shall be abrasion-
resistant.
7 Dimensions and tolerances
7.1 Inside diameter and tolerance
The inside diameter of the hose and the tolerance on the inside diameter shall meet the requirements
of Table 1.
2 © ISO 2014 – All rights reserved

Table 1 — Inside diameter and tolerance
Inside diameter Tolerance on I.D.
(mm) (mm)
19 ±1,5
25 ±1,5
26,5 ±1,5
31,5 ±1,5
33 ±1,5
40 ±2,0
41 ±2,0
50 ±2,0
52,5 ±2,0
63 ±2,0
65 ±2,0
66 ±2,0
75 ±2,0
78 ±2,0
80 ±2,25
100 ±2,25
104 ±2,25
125 ±3,0
128 ±3,0
150 ±3,0
155 ±3,0
160 ±3,0
200 ±3,0
207 ±3,0
250 ±3,0
258 ±3,0
300 ±3,0
309 ±3,0
350 ±4,0
359 ±4,0
400 ±4,0
410 ±4,0
If special cases call for extra sizes:
— for smaller or larger dimensions, further numbers shall be chosen from the R10 series of
preferred numbers (see ISO 3), with tolerances as given in ISO 1307;
— for intermediate dimensions, numbers shall be chosen from the R20 series of preferred
numbers (see ISO 3), with the tolerances as given for the next-larger size in the table above.
7.2 Tolerance on length
If the cut length of the hose is less than or equal to 1 800 mm, the tolerance on length shall be as specified
in ISO 1307.
If the cut length of the hose is over 1 800 mm, the tolerance shall be ± 2 % of the length specified.
8 Physical properties
8.1 Plastic compounds
The physical properties of compounds used for the lining and the cover shall conform to the values in
Table 2, when determined by the methods listed in Table 2.
Tests shall be carried out either on test pieces taken from the hose or on test pieces taken from sheet
made, using a laboratory press, under the same conditions as used in the manufacture of the hose.
Table 2 — Physical properties of compounds
Requirements
Property Test method
Lining Cover
Tensile
...


INTERNATIONAL ISO
STANDARD 8029
Third edition
2014-08-15
Plastics hose — General-purpose
collapsible water hose, textile-
reinforced — Specification
Tuyaux plastiques — Tuyaux d’eau écrasables d’usage général
renforcés textiles — Spécifications
Reference number
©
ISO 2014
© ISO 2014
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2014 – All rights reserved

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Classification . 2
5 Couplings and end fittings . 2
6 Materials and construction . 2
7 Dimensions and tolerances . 2
7.1 Inside diameter and tolerance . 2
7.2 Tolerance on length . 3
8 Physical properties . 4
8.1 Plastic compounds . 4
8.2 Performance requirements for finished hose . 4
9 Frequency of testing . 9
10 Test certificate/report . 9
11 Marking . 9
12 Recommendations for packaging and storage .10
Annex A (normative) Abrasion test .11
Annex B (normative) Type and routine testing .13
Annex C (informative) Production tests .14
Annex D (informative) Couplings and end fittings .15
Bibliography .16
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 45, Rubber and rubber products, Subcommittee
SC 1, Rubber and plastics hoses and hose assemblies.
This third edition cancels and replaces the second edition (ISO 8029:2007), which has been technically
revised. Fifteen sizes of inside diameter were added in order to conform to the couplings and end fittings
available in the market (see Table 1).
iv © ISO 2014 – All rights reserved

Introduction
This International Standard has been prepared to provide minimum requirements for the satisfactory
performance of textile-reinforced thermoplastic collapsible water hose, for discharge applications,
conveying water, aqueous sludge or slurries.
In view of such applications, requirements and the corresponding tests have been specified for exposure
to laboratory light sources (see 8.2.5) and for abrasion resistance (see 8.2.6).
INTERNATIONAL STANDARD ISO 8029:2014(E)
Plastics hose — General-purpose collapsible water hose,
textile-reinforced — Specification
1 Scope
This International Standard specifies the requirements for four types of textile-reinforced thermoplastics
collapsible water hoses for general applications for use in the temperature range of −10 °C to 55 °C. Such
hoses are classified into four types, as follows:
— low pressure, designed for a maximum working pressure of up to 0,4 MPa (4,0 bar) at 23 °C and up
to 0,2 MPa (2,0 bar) at 55 °C;
— medium pressure, for a maximum working pressure of up to 0,7 MPa (7,0 bar) at 23 °C and up to
0,36 MPa (3,6 bar) at 55 °C;
— high pressure, for a maximum working pressure of up to 1,0 MPa (10,0 bar) at 23 °C and up to
0,51 MPa (5,1 bar) at 55 °C;
— extra-high pressure, for a maximum working pressure of up to 1,55 MPa (15,5 bar) at 23 °C and up
to 0,79 MPa (7,9 bar) at 55 °C.
This International Standard does not apply to products used for fire-fighting or the conveyance of
drinking water.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 3, Preferred numbers — Series of preferred numbers
ISO 37, Rubber, vulcanized or thermoplastic — Determination of tensile stress-strain properties
ISO 188, Rubber, vulcanized or thermoplastic — Accelerated ageing and heat resistance tests
ISO 1307, Rubber and plastics hoses — Hose sizes, minimum and maximum inside diameters, and tolerances
on cut-to-length hoses
ISO 1402, Rubber and plastics hoses and hose assemblies — Hydrostatic testing
ISO 8033, Rubber and plastics hoses — Determination of adhesion between components
ISO 8330, Rubber and plastics hoses and hose assemblies — Vocabulary
ISO 9352, Plastics — Determination of resistance to wear by abrasive wheels
ISO 10619-1, Rubber and plastics hoses and tubing — Measurement of flexibility and stiffness — Part 1:
Bending tests at ambient temperature
ISO 10619-2, Rubber and plastics hoses and tubing — Measurement of flexibility and stiffness — Part 2:
Bending tests at sub-ambient temperatures
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
ISO 30013, Rubber and plastics hoses — Methods of exposure to laboratory light sources — Determination
of changes in colour, appearance and other physical properties
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 8330 apply.
4 Classification
Hoses are designated as one of the following four types depending on their pressure rating at the
specified temperatures:
— Type A: Low working pressure hose, designed for a maximum working pressure of up to 0,4 MPa
(4,0 bar) at 23 °C and up to 0,2 MPa (2,0 bar) at 55 °C;
— Type B: Medium working pressure hose, designed for a maximum working pressure of up to 0,7 MPa
(7,0 bar) at 23 °C and up to 0,36 MPa (3,6 bar) at 55 °C;
— Type C: High working pressure hose, designed for a maximum working pressure of up to 1,0 MPa
(10,0 bar) at 23 °C and up to 0,51 MPa (5,1 bar) at 55 °C;
— Type D: Extra high working pressure hose, designed for a maximum working pressure of up to
1,55 MPa (15,5 bar) at 23 °C and up to 0,79 MPa (7,9 bar) at 55 °C.
5 Couplings and end fittings
Hoses may be fitted with the appropriate coupling type and the end fitting to form hose assemblies.
Guidance on coupling type is given in Annex D and ISO/TR 17784:2003, Clause 7: Couplings.
6 Materials and construction
The hose shall consist of:
a) a flexible thermoplastic lining;
b) a reinforcement made of natural or synthetic textile material, applied by any suitable technique;
and
c) a flexible thermoplastic cover.
The lining and the cover shall be of uniform thickness, fully gelled and free from visible cracks, porosity,
foreign inclusions and other defects. The cover may have a smooth or fluted finish, and shall be abrasion-
resistant.
7 Dimensions and tolerances
7.1 Inside diameter and tolerance
The inside diameter of the hose and the tolerance on the inside diameter shall meet the requirements
of Table 1.
2 © ISO 2014 – All rights reserved

Table 1 — Inside diameter and tolerance
Inside diameter Tolerance on I.D.
(mm) (mm)
19 ±1,5
25 ±1,5
26,5 ±1,5
31,5 ±1,5
33 ±1,5
40 ±2,0
41 ±2,0
50 ±2,0
52,5 ±2,0
63 ±2,0
65 ±2,0
66 ±2,0
75 ±2,0
78 ±2,0
80 ±2,25
100 ±2,25
104 ±2,25
125 ±3,0
128 ±3,0
150 ±3,0
155 ±3,0
160 ±3,0
200 ±3,0
207 ±3,0
250 ±3,0
258 ±3,0
300 ±3,0
309 ±3,0
350 ±4,0
359 ±4,0
400 ±4,0
410 ±4,0
If special cases call for extra sizes:
— for smaller or larger dimensions, further numbers shall be chosen from the R10 series of
preferred numbers (see ISO 3), with tolerances as given in ISO 1307;
— for intermediate dimensions, numbers shall be chosen from the R20 series of preferred
numbers (see ISO 3), with the tolerances as given for the next-larger size in the table above.
7.2 Tolerance on length
If the cut length of the hose is less than or equal to 1 800 mm, the tolerance on length shall be as specified
in ISO 1307.
If the cut length of the hose is over 1 800 mm, the tolerance shall be ± 2 % of the length specified.
8 Physical properties
8.1 Plastic compounds
The physical properties of compounds used for the lining and the cover shall conform to the values in
Table 2, when determined by the methods listed in Table 2.
Tests shall be carried out either on test pieces taken from the hose or on test pieces taken from sheet
made, using a laboratory press, under the same conditions as used in the manufacture of the hose.
Table 2 — Physical properties of compounds
Requirements
Property Test method
Lining Cover
Tensile
...


NORME ISO
INTERNATIONALE 8029
Troisième édition
2014-08-15
Tuyaux plastiques — Tuyaux d’eau
écrasables d’usage général renforcés
textiles — Spécifications
Plastics hose — General-purpose collapsible water hose, textile-
reinforced — Specification
Numéro de référence
©
ISO 2014
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2014
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2014 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Classification . 2
5 Raccords et extrémités de raccordement . 2
6 Matériaux et construction . 2
7 Dimensions et tolérances . 2
7.1 Diamètre intérieur et tolérance . 2
7.2 Tolérance sur la longueur . 4
8 Propriétés physiques . 4
8.1 Mélanges plastiques . 4
8.2 Exigences de performance d’un tuyau fini . 4
9 Fréquence d’essai . 9
10 Rapport/certificat d’essai . 9
11 Marquage . 9
12 Recommandations pour le conditionnement et le stockage .10
Annexe A (normative) Essai d’abrasion .11
Annexe B (normative) Essais d’homologation de type et de routine .13
Annexe C (informative) Essais de production .14
Annexe D (informative) Raccords et extrémités de raccordement .15
Bibliographie .16
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne
la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant les
références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de l’élaboration
du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par
l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à l’évaluation de
la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes de l’OMC concernant
les obstacles techniques au commerce (OTC), voir le lien suivant: Avant-propos — Informations
supplémentaires.
Le comité chargé de l’élaboration du présent document est l’ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 1, Tuyaux et flexibles en caoutchouc et en matière plastique.
Cette troisième édition annule et remplace la deuxième édition (ISO 8029:2007) dont elle constitue une
révision technique. Quinze dimensions de diamètre intérieur ont été ajoutées afin d’être conforme aux
raccordements et extrémités de raccordement disponibles sur le marché (voir Tableau 1).
iv © ISO 2014 – Tous droits réservés

Introduction
La présente Norme internationale a été préparée pour fournir les exigences minimales permettant
d’obtenir des performances satisfaisantes pour les tuyaux d’eau écrasables thermoplastiques renforcés
textiles destinés à des applications de refoulement, d’adduction d’eau, de boue ou de suspensions
aqueuses.
En regard de telles applications, les exigences, et les essais correspondants, ont été spécifiés pour
l’exposition aux sources lumineuses de laboratoires (voir 8.2.5) et pour la résistance à l’abrasion
(voir 8.2.6).
NORME INTERNATIONALE ISO 8029:2014(F)
Tuyaux plastiques — Tuyaux d’eau écrasables d’usage
général renforcés textiles — Spécifications
1 Domaine d’application
La présente Norme internationale spécifie les exigences pour quatre types de tuyaux d’eau écrasables
thermoplastiques renforcés textiles destinés à des applications générales pour utilisation à des
températures comprises entre -10 °C et 55 °C. Ces tuyaux sont classés selon les quatre types suivants:
— basse pression, conçus pour une pression maximale de service jusqu’à 0,4 MPa (4,0 bar) à 23 °C et
jusqu’à 0,2 MPa (2,0 bar) à 55 °C;
— moyenne pression, pour une pression maximale de service jusqu’à 0,7 MPa (7,0 bar) à 23 °C et jusqu’à
0,36 MPa (3,6 bar) à 55 °C;
— haute pression, pour une pression maximale de service jusqu’à 1,0 MPa (10,0 bar) à 23 °C et de
0,51 MPa (5,1 bar) à 55 °C;
— très haute pression, pour une pression maximale de service jusqu’à 1,55 MPa (15,5 bar) à 23 °C et
jusqu’à 0,79 MPa (7,9 bar) à 55 °C.
La présente Norme internationale ne s’applique pas aux produits utilisés pour la lutte contre les incendies
ou l’adduction d’eau potable.
2 Références normatives
Les documents suivants, en totalité ou en partie, sont référencés de manière normative dans le présent
document et sont indispensables pour son application. Pour les références datées, seule l’édition citée
s’applique. Pour les références non datées, la dernière édition du document de référence s’applique (y
compris les éventuels amendements).
ISO 3, Nombres normaux — Séries de nombres normaux
ISO 37, Caoutchouc vulcanisé ou thermoplastique — Détermination des caractéristiques de contrainte-
déformation en traction
ISO 188, Caoutchouc vulcanisé ou thermoplastique — Essais de résistance au vieillissement accéléré et à la
chaleur
ISO 1307, Tuyaux en caoutchouc et en plastique — Dimensions des tuyaux, diamètres intérieurs minimaux
et maximaux, et tolérances sur la longueur de coupe
ISO 1402, Tuyaux et flexibles en caoutchouc et en plastique — Essais hydrostatiques
ISO 8033, Tuyaux en caoutchouc et en plastique — Détermination de l’adhérence entre éléments
ISO 8330, Tuyaux et flexibles en caoutchouc et en plastique — Vocabulaire
ISO 9352, Plastiques — Détermination de la résistance à l’usure par galets abrasifs
ISO 10619-1, Tuyaux et tubes en caoutchouc et en plastique — Mesurage de la flexibilité et de la rigidité —
Partie 1: Essais de courbure à température ambiante
ISO 10619-2, Tuyaux et tubes en caoutchouc et en plastique — Mesurage de la flexibilité et de la rigidité —
Partie 2: Essais de courbure à des températures inférieures à l’ambiante
ISO 23529, Caoutchouc — Procédures générales pour la préparation et le conditionnement des éprouvettes
pour les méthodes d’essais physiques
ISO 30013, Tuyaux en caoutchouc et en plastique — Méthodes d’exposition à des sources lumineuses de
laboratoire — Détermination du changement de coloration, d’aspect et d’autres propriétés physiques
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 8330 s’appliquent.
4 Classification
Les tuyaux sont conçus selon l’un des quatre types suivants en fonction de leur pression nominale aux
températures spécifiées:
— Type A: Tuyau basse pression de service, conçu pour une pression maximale de service jusqu’à
0,4 MPa (4,0 bar) à 23 °C et jusqu’à 0,2 MPa (2,0 bar) à 55 °C;
— Type B: Tuyau moyenne pression de service, conçu pour une pression maximale de service jusqu’à
0,7 MPa (7,0 bar) à 23 °C et jusqu’à 0,36 MPa (3,6 bar) à 55 °C;
— Type C: Tuyau haute pression de service, conçu pour une pression maximale de service jusqu’à
1,0 MPa (10,0 bar) à 23 °C et jusqu’à 0,51 MPa (5,1 bar) à 55 °C;
— Type D: Tuyau très haute pression de service, conçu pour une pression maximale de service jusqu’à
1,55 MPa (15,5 bar) à 23 °C et jusqu’à 0,79 MPa (7,9 bar) à 55 °C.
5 Raccords et extrémités de raccordement
Les tuyaux peuvent être munis du type de raccord et d’extrémité de raccordement appropriés pour
former des assemblages flexibles. Des recommandations concernant les types de raccordement sont
données dans l’Annexe D et l’ISO/TR 17784:2003, Article 7: Raccords.
6 Matériaux et construction
Le tuyau doit se composer:
a) d’un tube intérieur thermoplastique souple;
b) d’un renfort constitué de matière textile synthétique ou naturelle, appliqué selon toute technique
adéquate; et
c) d’un revêtement thermoplastique souple.
Le tube intérieur et le revêtement doivent être d’une épaisseur homogène, totalement gélifiés et exempts
de craquelure, de porosité, d’inclusions d’impureté et autres défauts visibles. Le revêtement peut
présenter une finition lisse ou cannelée et doit être résistant à l’abrasion.
7 Dimensions et tolérances
7.1 Diamètre intérieur et tolérance
Le diamètre intérieur du tuyau et la tolérance sur le diamètre intérieur doivent se conformer aux
exigences du Tableau 1.
2 © ISO 2014 – Tous droits réservés

Tableau 1 — Diamètre intérieur et tolérance
Diamètre intérieur Tolérance sur diamètre intérieur
mm mm
19 ±1,5
25 ±1,5
26,5 ±1,5
31,5 ±1,5
33 ±1,5
40 ±2,0
41 ±2,0
50 ±2,0
52,5 ±2,0
63 ±2,0
65 ±2,0
66 ±2,0
75 ±2,0
78 ±2,0
80 ±2,25
100 ±2,25
104 ±2,25
125 ±3,0
128 ±3,0
150 ±3,0
155 ±3,0
160 ±3,0
200 ±3,0
207 ±3,0
250 ±3,0
258 ±3,0
300 ±3,0
309 ±3,0
350 ±4,0
359 ±4,0
400 ±4,0
410 ±4,0
Si des cas particuliers nécessitent d’autres dimensions:
—  pour des dimensions plus petites ou plus grandes, d’autres nombres doivent être choisis
dans la série R10 de nombres normaux (v
...


NORME ISO
INTERNATIONALE 8029
Troisième édition
2014-08-15
Tuyaux plastiques — Tuyaux d’eau
écrasables d’usage général renforcés
textiles — Spécifications
Plastics hose — General-purpose collapsible water hose, textile-
reinforced — Specification
Numéro de référence
©
ISO 2014
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2014
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2014 – Tous droits réservés

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Classification . 2
5 Raccords et extrémités de raccordement . 2
6 Matériaux et construction . 2
7 Dimensions et tolérances . 2
7.1 Diamètre intérieur et tolérance . 2
7.2 Tolérance sur la longueur . 4
8 Propriétés physiques . 4
8.1 Mélanges plastiques . 4
8.2 Exigences de performance d’un tuyau fini . 4
9 Fréquence d’essai . 9
10 Rapport/certificat d’essai . 9
11 Marquage . 9
12 Recommandations pour le conditionnement et le stockage .10
Annexe A (normative) Essai d’abrasion .11
Annexe B (normative) Essais d’homologation de type et de routine .13
Annexe C (informative) Essais de production .14
Annexe D (informative) Raccords et extrémités de raccordement .15
Bibliographie .16
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne
la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant les
références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de l’élaboration
du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par
l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à l’évaluation de
la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes de l’OMC concernant
les obstacles techniques au commerce (OTC), voir le lien suivant: Avant-propos — Informations
supplémentaires.
Le comité chargé de l’élaboration du présent document est l’ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 1, Tuyaux et flexibles en caoutchouc et en matière plastique.
Cette troisième édition annule et remplace la deuxième édition (ISO 8029:2007) dont elle constitue une
révision technique. Quinze dimensions de diamètre intérieur ont été ajoutées afin d’être conforme aux
raccordements et extrémités de raccordement disponibles sur le marché (voir Tableau 1).
iv © ISO 2014 – Tous droits réservés

Introduction
La présente Norme internationale a été préparée pour fournir les exigences minimales permettant
d’obtenir des performances satisfaisantes pour les tuyaux d’eau écrasables thermoplastiques renforcés
textiles destinés à des applications de refoulement, d’adduction d’eau, de boue ou de suspensions
aqueuses.
En regard de telles applications, les exigences, et les essais correspondants, ont été spécifiés pour
l’exposition aux sources lumineuses de laboratoires (voir 8.2.5) et pour la résistance à l’abrasion
(voir 8.2.6).
NORME INTERNATIONALE ISO 8029:2014(F)
Tuyaux plastiques — Tuyaux d’eau écrasables d’usage
général renforcés textiles — Spécifications
1 Domaine d’application
La présente Norme internationale spécifie les exigences pour quatre types de tuyaux d’eau écrasables
thermoplastiques renforcés textiles destinés à des applications générales pour utilisation à des
températures comprises entre -10 °C et 55 °C. Ces tuyaux sont classés selon les quatre types suivants:
— basse pression, conçus pour une pression maximale de service jusqu’à 0,4 MPa (4,0 bar) à 23 °C et
jusqu’à 0,2 MPa (2,0 bar) à 55 °C;
— moyenne pression, pour une pression maximale de service jusqu’à 0,7 MPa (7,0 bar) à 23 °C et jusqu’à
0,36 MPa (3,6 bar) à 55 °C;
— haute pression, pour une pression maximale de service jusqu’à 1,0 MPa (10,0 bar) à 23 °C et de
0,51 MPa (5,1 bar) à 55 °C;
— très haute pression, pour une pression maximale de service jusqu’à 1,55 MPa (15,5 bar) à 23 °C et
jusqu’à 0,79 MPa (7,9 bar) à 55 °C.
La présente Norme internationale ne s’applique pas aux produits utilisés pour la lutte contre les incendies
ou l’adduction d’eau potable.
2 Références normatives
Les documents suivants, en totalité ou en partie, sont référencés de manière normative dans le présent
document et sont indispensables pour son application. Pour les références datées, seule l’édition citée
s’applique. Pour les références non datées, la dernière édition du document de référence s’applique (y
compris les éventuels amendements).
ISO 3, Nombres normaux — Séries de nombres normaux
ISO 37, Caoutchouc vulcanisé ou thermoplastique — Détermination des caractéristiques de contrainte-
déformation en traction
ISO 188, Caoutchouc vulcanisé ou thermoplastique — Essais de résistance au vieillissement accéléré et à la
chaleur
ISO 1307, Tuyaux en caoutchouc et en plastique — Dimensions des tuyaux, diamètres intérieurs minimaux
et maximaux, et tolérances sur la longueur de coupe
ISO 1402, Tuyaux et flexibles en caoutchouc et en plastique — Essais hydrostatiques
ISO 8033, Tuyaux en caoutchouc et en plastique — Détermination de l’adhérence entre éléments
ISO 8330, Tuyaux et flexibles en caoutchouc et en plastique — Vocabulaire
ISO 9352, Plastiques — Détermination de la résistance à l’usure par galets abrasifs
ISO 10619-1, Tuyaux et tubes en caoutchouc et en plastique — Mesurage de la flexibilité et de la rigidité —
Partie 1: Essais de courbure à température ambiante
ISO 10619-2, Tuyaux et tubes en caoutchouc et en plastique — Mesurage de la flexibilité et de la rigidité —
Partie 2: Essais de courbure à des températures inférieures à l’ambiante
ISO 23529, Caoutchouc — Procédures générales pour la préparation et le conditionnement des éprouvettes
pour les méthodes d’essais physiques
ISO 30013, Tuyaux en caoutchouc et en plastique — Méthodes d’exposition à des sources lumineuses de
laboratoire — Détermination du changement de coloration, d’aspect et d’autres propriétés physiques
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 8330 s’appliquent.
4 Classification
Les tuyaux sont conçus selon l’un des quatre types suivants en fonction de leur pression nominale aux
températures spécifiées:
— Type A: Tuyau basse pression de service, conçu pour une pression maximale de service jusqu’à
0,4 MPa (4,0 bar) à 23 °C et jusqu’à 0,2 MPa (2,0 bar) à 55 °C;
— Type B: Tuyau moyenne pression de service, conçu pour une pression maximale de service jusqu’à
0,7 MPa (7,0 bar) à 23 °C et jusqu’à 0,36 MPa (3,6 bar) à 55 °C;
— Type C: Tuyau haute pression de service, conçu pour une pression maximale de service jusqu’à
1,0 MPa (10,0 bar) à 23 °C et jusqu’à 0,51 MPa (5,1 bar) à 55 °C;
— Type D: Tuyau très haute pression de service, conçu pour une pression maximale de service jusqu’à
1,55 MPa (15,5 bar) à 23 °C et jusqu’à 0,79 MPa (7,9 bar) à 55 °C.
5 Raccords et extrémités de raccordement
Les tuyaux peuvent être munis du type de raccord et d’extrémité de raccordement appropriés pour
former des assemblages flexibles. Des recommandations concernant les types de raccordement sont
données dans l’Annexe D et l’ISO/TR 17784:2003, Article 7: Raccords.
6 Matériaux et construction
Le tuyau doit se composer:
a) d’un tube intérieur thermoplastique souple;
b) d’un renfort constitué de matière textile synthétique ou naturelle, appliqué selon toute technique
adéquate; et
c) d’un revêtement thermoplastique souple.
Le tube intérieur et le revêtement doivent être d’une épaisseur homogène, totalement gélifiés et exempts
de craquelure, de porosité, d’inclusions d’impureté et autres défauts visibles. Le revêtement peut
présenter une finition lisse ou cannelée et doit être résistant à l’abrasion.
7 Dimensions et tolérances
7.1 Diamètre intérieur et tolérance
Le diamètre intérieur du tuyau et la tolérance sur le diamètre intérieur doivent se conformer aux
exigences du Tableau 1.
2 © ISO 2014 – Tous droits réservés

Tableau 1 — Diamètre intérieur et tolérance
Diamètre intérieur Tolérance sur diamètre intérieur
mm mm
19 ±1,5
25 ±1,5
26,5 ±1,5
31,5 ±1,5
33 ±1,5
40 ±2,0
41 ±2,0
50 ±2,0
52,5 ±2,0
63 ±2,0
65 ±2,0
66 ±2,0
75 ±2,0
78 ±2,0
80 ±2,25
100 ±2,25
104 ±2,25
125 ±3,0
128 ±3,0
150 ±3,0
155 ±3,0
160 ±3,0
200 ±3,0
207 ±3,0
250 ±3,0
258 ±3,0
300 ±3,0
309 ±3,0
350 ±4,0
359 ±4,0
400 ±4,0
410 ±4,0
Si des cas particuliers nécessitent d’autres dimensions:
—  pour des dimensions plus petites ou plus grandes, d’autres nombres doivent être choisis
dans la série R10 de nombres normaux (v
...

Questions, Comments and Discussion