ISO 2740:2009
(Main)Sintered metal materials, excluding hardmetals — Tensile test pieces
Sintered metal materials, excluding hardmetals — Tensile test pieces
ISO 2740:2009 is applicable to all sintered metals and alloys, excluding hardmetals. ISO 2740:2009 specifies: 1) the die cavity dimensions used for making tensile test pieces by pressing and sintering, and by Metal Injection Moulding (MIM) and sintering; and 2) the dimensions of tensile test pieces machined from sintered and powder forged materials.
Matériaux en métal fritté, à l'exclusion des métaux-durs — Éprouvettes pour essai de traction
L'ISO 2740:2009 s'applique à tous les métaux et alliages frittés, à l'exclusion des métaux-durs. Elle spécifie: 1) les dimensions internes de la matrice utilisées pour la réalisation d'éprouvettes d'essai de traction, par compression et frittage ou par injection-moulage de métal et frittage; 2) les dimensions des éprouvettes de traction usinées dans des matériaux frittés ou frittés-forgés.
General Information
Relations
Buy Standard
Standards Content (Sample)
МЕЖДУНАРОДНЫЙ ISO
СТАНДАРТ 2740
Пятое издание
2009-05-15
Материалы металлические
спеченные, кроме твердых сплавов.
Образцы для испытаний на
растяжение
Sintered metal materials, excluding hardmetals – Tensile test pieces
Ответственность за подготовку русской версии несёт GOST
R (Российская Федерация) в соответствии со статьёй 18.1 Устава
Ссылочный номер
ISO 2740:2009(R)
©
ISO 2009
---------------------- Page: 1 ----------------------
ISO 2740:2009(R)
Отказ от ответственности при работе в PDF
Настоящий файл PDF может содержать интегрированные шрифты. В соответствии с условиями лицензирования, принятыми
фирмой Adobe, этот файл можно распечатать или смотреть на экране, но его нельзя изменить, пока не будет получена
лицензия на установку интегрированных шрифтов в компьютере, на котором ведется редактирование. В случае загрузки
настоящего файла заинтересованные стороны принимают на себя ответственность за соблюдение лицензионных условий
фирмы Adobe. Центральный секретариат ISO не несет никакой ответственности в этом отношении.
Adobe - торговый знак фирмы Adobe Systems Incorporated.
Подробности, относящиеся к программным продуктам, использованным для создания настоящего файла PDF, можно найти в
рубрике General Info файла; параметры создания PDF были оптимизированы для печати. Были приняты во внимание все
меры предосторожности с тем, чтобы обеспечить пригодность настоящего файла для использования комитетами-членами
ISO. В редких случаях возникновения проблемы, связанной со сказанным выше, просьба проинформировать Центральный
секретариат по адресу, приведенному ниже.
ДОКУМЕНТ ЗАЩИЩЕН АВТОРСКИМ ПРАВОМ
© ISO 2009
Все права сохраняются. Если не указано иное, никакую часть настоящей публикации нельзя копировать или использовать в
какой-либо форме или каким-либо электронным или механическим способом, включая фотокопии и микрофильмы, без
предварительного письменного согласия ISO, которое должно быть получено после запроса о разрешении, направленного по
адресу, приведенному ниже, или в комитет-член ISO в стране запрашивающей стороны.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Опубликовано в Швейцарии
ii © ISO 2009 - Все права сохраняются
---------------------- Page: 2 ----------------------
ISO 2740:2009(R)
Содержание Страница
Предисловие .iv
1 Область применения .1
2 Нормативные ссылки .1
3 Метод испытания.1
4 Изготовление испытательных образцов.1
5 Испытательные образцы, полученные инжекционным формованием металла (MIM) .2
6 Механически обработанные испытательные образцы.3
7 Идентификация испытательных образцов.3
© ISO 2009 - Все права сохраняются iii
---------------------- Page: 3 ----------------------
ISO 2740:2009(R)
Предисловие
Международная организация по стандартизации (ISO) является всемирной федерацией национальных
организаций по стандартизации (комитетов-членов ISO). Разработка международных стандартов
обычно осуществляется техническими комитетами ISO. Каждый комитет-член, заинтересованный в
деятельности, для которой был создан технический комитет, имеет право быть представленным в
этом комитете. Международные правительственные и неправительственные организации, имеющие
связи с ISO, также принимают участие в работах. ISO работает в тесном сотрудничестве с
Международной электротехнической комиссией (IEC) по всем вопросам стандартизации в области
электротехники.
Международные стандарты разрабатываются в соответствии с правилами, установленными в
Директивах ISO/IEC, Часть 2.
Основная задача технических комитетов состоит в подготовке международных стандартов. Проекты
международных стандартов, одобренные техническими комитетами, рассылаются комитетам-членам
на голосование. Их опубликование в качестве международных стандартов требует одобрения, по
меньшей мере, 75 % комитетов-членов, принимающих участие в голосовании.
Следует иметь в виду, что некоторые элементы этого документа могут быть объектом патентных прав.
Организация ISO не должна нести ответственность за идентификацию какого-либо одного или всех
патентных прав.
ISO 2740 подготовлен Техническим комитетом ISO/TC 119, Порошковая металлургия, Подкомитетом
SC 3, Методы отбора проб и испытаний для спеченных металлических материалов (кроме
твердых сплавов).
Данное пятое издание отменяет и заменяет четвертое издание (ISO 2740:2007), которое было
незначительно пересмотрено.
iv © ISO 2009 - Все права сохраняются
---------------------- Page: 4 ----------------------
МЕЖДУНАРОДНЫЙ СТАНДАРТ ISO 2740:2009(R)
Материалы металлические спеченные, кроме твердых
сплавов. Образцы для испытаний на растяжение
1 Область применения
Настоящий международный стандарт распространяется на все спеченные металлы и сплавы, кроме
твердых сплавов.
Настоящий международный стандарт устанавливает:
⎯ размеры полости пресс-формы, используемой для изготовления образцов для испытания на
растяжение путем прессования и спекания, и инжекционным формованием металла (MIM) и
спеканием;
⎯ размеры испытательных образцов, обработанных из спеченных и штампованных в горячем
состоянии порошковых материалов.
2 Нормативные ссылки
Следующие ссылочные нормативные документы являются обязательными для применения
настоящего документа. Для жестких ссылок применяется только цитируемое издание документа. Для
плавающих ссылок необходимо использовать самое последнее издание нормативного ссылочного
документа (включая любые изменения).
ISO 6892, Материалы металлические. Испытание на растяжение при температуре окружающей
среды
ISO 7500-1, Материалы металлические. Проверка испытательных машин для приложения
статической одноосной нагрузки. Часть 1. Машины для испытания на растяжение/сжатие.
Проверка и калибрование системы измерения нагрузки
3 Метод испытания
3.1 Образцы должны испытываться в соответствии с ISO 6892, а машина для испытания на
растяжение должна калиброваться по Классу 1, в соответствии с ISO 7500-1.
3.2 Данные должны регистрироваться для двух или нескольких испытательных образов.
4 Изготовление испытательных образцов
4.1 Спрессованные и спеченные испытательные образцы
Образцы для испытания на растяжение должны иметь толщины от 5 мм до 6,5 мм. Допуск на толщину
1,5 мм позволяет менять насыпную плотность в металлических порошках. В процессе испытания
более тонкие образцы имеют меньшое проскальзывание захвата и более вероятно их разрушение
около центра расчетной (базовой) длины.
© ISO 2009 - Все права сохраняются 1
---------------------- Page: 5 ----------------------
ISO 2740:2009(R)
При необходимости измерения удлинения, могут быть слегка прочерчены риски на расстоянии 25 мм
друг от друга и симметрично относительно центральной линии [см. Рисунки 1 a) и 2 a)]. Толщина
между прочерченными рисками не должна меняться более чем на 0,04 мм. Расчетная длина должна
быть размечена так, чтобы не влиять на свойства растяжения.
По причине возможности создания микроскопических расслоений в углах испытательных образцов,
спрессованных в лабораторных условиях, необходимо провести металлографический анализ на
представительных спеченных образцах, чтобы показать отсутствие микроскопических расслоений
длиной более 0,25 мм.
4.2 Требования к пресс-форме
Размеры двух допускаемых полостей пресс-форм показаны на Рисунках 1 b) и 2 b). Желательно, чтобы
пресс-формы были из твердого сплава и имели чистоту пове
...
INTERNATIONAL ISO
STANDARD 2740
Fifth edition
2009-05-15
Sintered metal materials, excluding
hardmetals — Tensile test pieces
Matériaux en métal fritté, à l'exclusion des métaux-durs — Éprouvettes
pour essai de traction
Reference number
ISO 2740:2009(E)
©
ISO 2009
---------------------- Page: 1 ----------------------
ISO 2740:2009(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
COPYRIGHT PROTECTED DOCUMENT
© ISO 2009
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2009 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 2740:2009(E)
Contents Page
Foreword. iv
1 Scope .1
2 Normative references .1
3 Method of testing.1
4 Manufacture of test pieces .1
5 Metal injection-moulded test pieces.2
6 Machined test pieces.2
7 Identification of test pieces .3
© ISO 2009 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 2740:2009(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 2740 was prepared by Technical Committee ISO/TC 119, Powder metallurgy, Subcommittee SC 3,
Sampling and testing methods for sintered metal materials (excluding hardmetals).
This fifth edition cancels and replaces the fourth edition (ISO 2740:2007), of which it constitutes a minor
revision.
iv © ISO 2009 – All rights reserved
---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 2740:2009(E)
Sintered metal materials, excluding hardmetals — Tensile test
pieces
1 Scope
This International Standard is applicable to all sintered metals and alloys, excluding hardmetals.
This International Standard specifies:
⎯ the die cavity dimensions used for making tensile test pieces by pressing and sintering, and by Metal
Injection Moulding (MIM) and sintering;
⎯ the dimensions of tensile test pieces machined from sintered and powder forged materials.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 6892, Metallic materials — Tensile testing at ambient temperature
ISO 7500-1, Metallic materials — Verification of static uniaxial testing machines — Part 1: Tension/com-
pression testing machines — Verification and calibration of the force-measuring system
3 Method of testing
3.1 Test pieces shall be tested in accordance with ISO 6892, and the tensile test machine shall be
calibrated to Class 1, in accordance with ISO 7500-1.
3.2 Data are to be reported for three or more test pieces.
4 Manufacture of test pieces
4.1 Pressed and sintered test pieces
The tensile test pieces shall have thicknesses from 5 mm to 6,5 mm. A thickness tolerance of 1,5 mm
accommodates varying apparent densities in metal powders. During testing, the thinner pieces have less grip
slippage and are more likely to break near the centre of the gauge length.
If necessary for measuring elongation, marks may be lightly scribed 25 mm apart and symmetrically about the
centre line [see Figures 1 a) and 2 a)]. Between the scribed marks, the thickness shall not vary by more than
0,04 mm. The gauge length shall be scribed in such a way that the tensile properties are not affected.
© ISO 2009 – All rights reserved 1
---------------------- Page: 5 ----------------------
ISO 2740:2009(E)
Because of the possibility of creating microlaminations in the corners of test pieces compacted under
laboratory conditions, representative sintered test pieces shall be examined metallographically to show that
there are no microlaminations longer than 0,25 mm.
...
NORME ISO
INTERNATIONALE 2740
Cinquième édition
2009-05-15
Matériaux en métal fritté, à l'exclusion
des métaux-durs — Éprouvettes pour
essai de traction
Sintered metal materials, excluding hardmetals — Tensile test pieces
Numéro de référence
ISO 2740:2009(F)
©
ISO 2009
---------------------- Page: 1 ----------------------
ISO 2740:2009(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2009
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2009 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 2740:2009(F)
Sommaire Page
Avant-propos. iv
1 Domaine d'application.1
2 Références normatives .1
3 Méthode d'essai .1
4 Confection des éprouvettes d'essai .1
5 Éprouvettes d'essai en métal injecté-moulé.2
6 Éprouvettes usinées.3
7 Identification des éprouvettes d'essai.3
© ISO 2009 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO 2740:2009(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 2740 a été élaborée par le comité technique ISO/TC 119, Métallurgie des poudres, sous-comité SC 3,
Échantillonnage et méthodes d’essais des matériaux métalliques frittés (à l’exclusion des métaux-durs).
Cette cinquième édition annule et remplace la quatrième édition (ISO 2740:2007), dont elle constitue une
révision mineure.
iv © ISO 2009 – Tous droits réservés
---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 2740:2009(F)
Matériaux en métal fritté, à l'exclusion des métaux-durs —
Éprouvettes pour essai de traction
1 Domaine d'application
La présente Norme internationale s'applique à tous les métaux et alliages frittés, à l'exclusion des métaux-
durs.
La présente Norme internationale spécifie:
⎯ les dimensions internes de la matrice utilisées pour la réalisation d'éprouvettes d'essai de traction, par
compression et frittage ou par injection-moulage de métal et frittage;
⎯ les dimensions des éprouvettes de traction usinées dans des matériaux frittés ou frittés-forgés.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 6892:1998, Matériaux métalliques — Essai de traction à température ambiante
ISO 7500-1:2004, Matériaux métalliques — Vérification des machines pour essais statiques uniaxiaux —
Partie 1: Machines d'essai de traction/compression — Vérification et étalonnage du système de mesure de
force
3 Méthode d'essai
3.1 Les éprouvettes d'essai doivent être soumises à l'essai conformément à l'ISO 6892, et la machine
d'essai de traction doit être étalonnée en classe 1, selon l'ISO 7500-1.
3.2 Dans le rapport d'essai, il faut consigner les données pour trois éprouvettes ou davantage.
4 Confection des éprouvettes d'essai
4.1 Éprouvettes obtenues par compression et frittage
L'épaisseur des éprouvettes d'essai de traction doit être comprise entre 5 mm et 6,5 mm. Une tolérance de
1,5 mm sur l'épaisseur permet de tenir compte de la variété des masses volumiques apparentes des poudres
métalliques. Lors de l'essai, une éprouvette plus mince a moins de chance de glisser dans les mors qui
l'agrippent et est davantage susceptible de se casser près du centre de la longueur entre repères.
Si nécessaire, pour mesurer l'allongement, des traits repères peuvent être tracés symétriquement à 25 mm
l'un de l'autre, de part et d'autre de la ligne médiane [voir Figures 1 a) et 2 a)]. Entre ces traits repères,
l'épaisseur ne doit pas varier de plus de 0,04 mm. La longueur entre repères doit être tracée de manière à ne
pas affecter les caractéristiques de traction.
© ISO 2009 – Tous droits réservés 1
---------------------- Page: 5 ----------------------
ISO 2740:2009(F)
Comme il est toujours possible que des microfissures apparaissent sur les arêtes des éprouvettes fabriquées
par compression dans les conditions du laboratoire, il est nécessaire de procéder à un examen
métallographique d'éprouvettes frittées représentatives afin de démontrer l'absence de microfissures dont la
longueur est supérieure à 0,25 mm.
4.2 Spécification des matrices
Les dimensions internes des deux types de matrice autorisés sont représentées aux Figures 1 b) et 2 b). Il est
recommandé que les matrices soient, de préférence, en métal-dur et leur finition de surface doit permettre la
compression des éprouvettes dans des conditions normales. Les matrices peuvent comporter une petite
dépouille de façon à faciliter l'éjection et pour éviter aux éprouvettes de présenter des fissur
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.