ISO 3738:1976

Hardmetals — Rockwell hardness test (Scale A)

Métaux-durs — Essai de dureté Rockwell (échelle A)

General Information

• Status: Withdrawn
• Publication Date: 30-Jun-1976
• Withdrawal Date: 30-Jun-1976
• ICS: 77.040.10 - Mechanical testing of metals
• ICS: 77.160 - Powder metallurgy
• Technical Committee: ISO/TC 119/SC 4 - Sampling and testing methods for hardmetals
• Drafting Committee: ISO/TC 119/SC 4 - Sampling and testing methods for hardmetals
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 01-Oct-1982

Relations

• Revised: ISO 3738-1:1982 - Hardmetals — Rockwell hardness test (scale A) — Part 1: Test method
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL STANDARD @ ‘!E& 3738
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .MEX,!IYHAPOnHAR OPiAHMlAUMR no CTAHLlAPTM3AUAH *ORGANISATION INTERNATIONALE DE NORMALISATION
.
Hardmetals - Rockwell hardness test (scale A)
*
Métaux durs - Essai de dureté Rockwell (échelle A)
First edition - 1976-07-01
Ref. No. IS0 3738-1976 (E)
UDC 621.762.1 : 661.665.2 : 620.178.152.42
Descriptors : powder metallurgy, hardmetals, mechanical tests, hardness tests, Rockwell hardness.
Price based on 2 pages

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 Member Bodies). The work of developing
International Standards is carried out through IS0 Technical Committees. Every
Member Body interested in a subject for which a Technical Committee has been set
up has the right to be represented on that Committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the Technical Committees are circulated
to the Member Bodies for approval before their acceptance as International
Standards by the IS0 Council.
IS0 3738 was drawn up by Technical Committee
International Standard
ISO/TC 119, Powder metallurgical materials and products, and was circulated to
the Member Bodies in April 1975.
It has been approved by the Member Bodies of the following countries
Austria Ireland Sweden
Brazil Italy Turkey
Bulgaria Korea, Rep. of United Kingdom
Canada Mexico U.S.S. R.
Czechoslovakia Portugal Yugoslavia
Egypt, Arab Rep. of Romania
France
South Africa, Rep. of
Germany Spain
The Member Body of the following country expressed disapproval of the document
on technical grounds :
U.S.A.
O International Organization for Standardization, 1976
Printed in Switzerland

---------------------- Page: 2 ----------------------
INTERNATIONAL STANDARD IS0 3738-1976 (E)
Hardmetals - Rockwell hardness test (scale A)
4 SYMBOLS AND DESIGNATIONS
1 SCOPE AND FIELD OF APPLICATION
See table 1 and the figure.
This international Standard specifies a method of Rockwell
hardness test (scale A) for hardmetals.
TABLE 1
NOTE - Attention is drawn to an agreement between the Secre-
Designation
Symbol
tariats of IS0 Technical Committees for metals (iSO/TC 17, 26,
79, 119 and 155) to establish an integration of the existing IS0
publications for Rockwell hardness testing into one single Inter- ff Angle at the tip of the diamond cone (120" 1
national Standard which should apply to all metallic materials.
R Radius of curvature at the tip of the cone
Depending on the results of this co-ordination work, the present
(0,2 mm)
International Standard may be revised or withdrawn within a few
years.
Preliminary load = 98 ? 2 N (10 ? 0,2 kgf)
FO
Additional load = 491 N (50 kgf)
FI
2 REFERENCE
F Total load = FO + FI = 98 + 491
ISOIR 80, Rockwell hardness test (B and C scales) for steel. = 589 f 4 N (60 ? 0,45 kgf)
Depth of indentation under preliminary load
h0
3 PRINCIPLE
before application of additional load
Increase in depth of indentation under
hl
The test consists in forcing a conical diamond indenter into
additional load
a test piece in two operations and measuring the permanent
e Permanent increase of depth of indentation
increase e of the depth of indentation by means of a depth
under preliminary load after removal
gauge under defined conditions.
of additional load, expressed in units
The unit of measurement for e is 0,002 mm; from the
of 0,002 mm
measurement of e, a number known as the Rockwell A
HRA Rockwell hardness A = 100 -e
hardness is deduced.
I
I
t
Surface of test piece
Datum line
E
E
2
1

---------------------- Page: 3 ----------------------
IS0 3738-1976 (E)
5 APPARATUS 7.1.3 The time of applying the additional load after the
movement of the pointer has stopped shall not exceed 2 s.
5.1 Testing equipment with a reading accuracy of 0,2 unit
While maintaining the preli
...

,aim,
NORME INTERNATIONALE @ 3738
'*E&
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .MFXZlYH4POaHAR OPiAHM3AIIMR Il0 CTAHnAPTM3AUMM .ORGANISATION INTERNATIONALE DE NORMALISATION
Métaux durs - Essai de dureté Rockwell (échelle A)
Q,
Hardmetals - Rockwell hardness test (scale A)
Première édition - 1976-07-01
-
- LL CDU 621.762.1 : 661.665.2 : 620.178.152.42 Réf. no : IS0 3738-1976 (F)
(D I-
Q,
.i
Descripteurs : métallurgie des poudres, métal dur, essai mécanique, essai de dureté. dureté Rockwell.
Co
2
eY
z
Prix base sur 2 pages

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation Internationale de Normalisation) est une fédération mondiale'
d'organismes nationaux de normalisation (Comités Membres ISO). L'élaboration des
Normes Internationales est confiée aux Comités Techniques ISO. Chaque Comité
Membre intéressé par une étude a le droit de faire partie du Comité Technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I'ISO, participent également aux travaux.
Les Projets de Normes Internationales adoptés par les Comités Techniques sont
soumis aux Comités Membres pour approbation, avant leur acceptation comme
Normes Internationales par le Conseil de I'ISO.
La Norme Internationale IS0 3738 a été établie par le Comité Technique
ISO/TC 119, Matières premières et produits de la métallurgie des poudres, et sou-
mise aux Comités Membres en avril 1975.
Elle a été approuvée par les Comités Membres des pays suivants :
Afrique du Sud, Rép. d' Espagne Suède
Allemagne France Tchécoslovaquie
Irlande Turquie
Autriche
Brésil Italie U.R.S.S.
Bulgarie Mexique Yougoslavie
Portugal
Canada
Corée, Rép. de Roumanie
Royaume-Uni
Égypte, Rép. arabe d'
Le Comité Membre du pays suivant a désapprouvé le document pour des raisons
techniques :
U.S.A.
O Organisation Internationale de Normalisation, 1976 e
Imprimé en Suisse

---------------------- Page: 2 ----------------------
IS0 3738-1976 (FI
NORME INTERNATIONALE
Rockwell (échelle A)
Métaux durs - Essai de dureté
1 OBJET ET DOMAINE D'APPLICATION 4 SYMBOLES ET DESIGNATIONS
Voir tableau 1 et figure.
La présente Norme Internationale spécifie une méthode
d'essai de dureté Rockwell (échelle A) pour les métaux
durs.
NOTE - L'attention est attirée sur le fait qu'un accord est intervenu
TABLEAU 1
entre les Secrétariats des Comités Techniques IS0 traitant des mé-
taux (ISO/'TC 17,26, 79, 119 et 155) en vue de réunir toutes les pu-
blications IS0 sur l'essai Rockwell en une seule Norme Inter-
Désignation
Symbole
qationale qui s'appliquerait à tous les matériaux métalliques. Selon
les résultats de ces travaux de coordination, la présente Norme Inter-
Angle au sommet du cône en diamant (120")
(Y
nationale pourra, dans quelques années, être révisée ou annulée.
R Rayon de courbure au sommet du cône (0,2 mm)
= 98 t 2 N (10 f 0.2 kgf)
Charge initiale
2 RÉFÉRENCE
FO
Charge additionnelle = 491 N (50 kgf)
F1
ISO/R 80, Essai de dureté Rockwell (échelles B et C) pour
Charge totale = F 0 + FI = 98 + 491
F
I 'acier.
= 589 f 4 N (60 f 0.45 kgf)
Profondeur de pénétration sous la charge
3 PRINCIPE h0
initiale avant application de la surcharge
L'essai consiste à enfoncer, en deux temps, dans une éprou-
Accroissement de la profondeur de pénétration
hl
vette, un pénétrateur conique en diamant et à mesurer I'ac-
sous l'effet de la surcharge additionnelle
croissement rémanent de la profondeur de pénétration e
Accroissement rémanent de la profondeur de
e
à l'aide d'une jauge de profondeur dans des conditions
pénétration sous la charge initiale
définies.
après enlèvement de la charge additionnelle
L'unité de mesure e vaut 0,002 mm; du résultat de ce mesu-
HRA Dureté Rockwell A = 100 -e
rage, on déduit un nombre appelé dureté Rockwell A.
I-
F l'&'
II
liol
Surface de l'éprouvette
f
O Origine de la mesure
-r
1 O0
I al
1

---------------------- Page: 3 ----------------------
IS0 3738-1976 (F)
7.1.2 La vitesse d'application de la charge additionnelle
5 APPAREILLAGE
doit être réglée de façon que le mouvement du pé
...