SIST EN ISO 6506-4:2006

Metallic materials - Brinell hardness test - Part 4: Table of hardness values (ISO 6506-4:2005)

This part of ISO 6506 gives a table of the Brinell hardness values for use in tests on flat surfaces.

Metallische Werkstoffe - Härteprüfung nach Brinell - Teil 4: Tabelle zur Bestimmung der Härte (ISO 6506-4:2005)

In diesem Teil von ISO 6506 ist eine Tabelle zur Bestimmung der Brinellhärte für die Prüfung auf ebenen Oberflächen enthalten.

Matériaux métalliques - Essai de dureté Brinell - Partie 4: Tableaux des valeurs de dureté (ISO 6506-4:2005)

L'ISO 6506-4:2005 donne un tableau de valeurs de dureté Brinell pour utilisation sur des surfaces planes.

Kovinski materiali – Preskus trdote po Brinellu – 4. del: Tabela za določanje trdote (ISO 6506-4:2005)

General Information

• Status: Withdrawn
• Publication Date: 28-Feb-2006
• Withdrawal Date: 14-Oct-2014
• ICS: 77.040.10 - Mechanical testing of metals
• Technical Committee: PKG - Testing of metallic materials
• Current Stage: 9900 - Withdrawal (Adopted Project)
• Start Date: 13-Oct-2014
• Due Date: 05-Nov-2014
• Completion Date: 15-Oct-2014
• Ref Project: EN ISO 6506-4:2005 - Metallic materials - Brinell hardness test - Part 4: Table of hardness values (ISO 6506-4:2005)

Relations

• Replaced By: SIST EN ISO 6506-4:2014 - Metallic materials - Brinell hardness test - Part 4: Table of hardness values (ISO 6506-4:2014)
• Effective Date: 01-Dec-2014

Standards Content (Sample)

SLOVENSKI STANDARD
SIST EN ISO 6506-4:2006
01-marec-2006
.RYLQVNLPDWHULDOL±3UHVNXVWUGRWHSR%ULQHOOX±GHO7DEHOD]DGRORþDQMHWUGRWH
,62
Metallic materials - Brinell hardness test - Part 4: Table of hardness values (ISO 6506-
4:2005)
Metallische Werkstoffe - Härteprüfung nach Brinell - Teil 4: Tabelle zur Bestimmung der
Härte (ISO 6506-4:2005)
Matériaux métalliques - Essai de dureté Brinell - Partie 4: Tableaux des valeurs de
dureté (ISO 6506-4:2005)
Ta slovenski standard je istoveten z: EN ISO 6506-4:2005
ICS:
77.040.10 Mehansko preskušanje kovin Mechanical testing of metals
SIST EN ISO 6506-4:2006 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

EUROPEAN STANDARD
EN ISO 6506-4
NORME EUROPÉENNE
EUROPÄISCHE NORM
December 2005
ICS 77.040.10

English Version
Metallic materials - Brinell hardness test - Part 4: Table of
hardness values (ISO 6506-4:2005)
Matériaux métalliques - Essai de dureté Brinell - Partie 4: Metallische Werkstoffe - Härteprüfung nach Brinell - Teil 4:
Tableaux des valeurs de dureté (ISO 6506-4:2005) Tabelle zur Bestimmung der Härte (ISO 6506-4:2005)
This European Standard was approved by CEN on 14 December 2005.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the Central Secretariat or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official
versions.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,
Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36  B-1050 Brussels
© 2005 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 6506-4:2005: E
worldwide for CEN national Members.

---------------------- Page: 2 ----------------------

EN ISO 6506-4:2005 (E)





Foreword


This document (EN ISO 6506-4:2005) has been prepared by Technical Committee ISO/TC 164
"Mechanical testing of metals" in collaboration with Technical Committee ECISS/TC 1 "Steel -
Mechanical testing", the secretariat of which is held by AFNOR.

This European Standard shall be given the status of a national standard, either by publication of
an identical text or by endorsement, at the latest by June 2006, and conflicting national
standards shall be withdrawn at the latest by June 2006.

According to the CEN/CENELEC Internal Regulations, the national standards organizations of
the following countries are bound to implement this European Standard: Austria, Belgium,
Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary,
Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,
Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.


Endorsement notice

The text of ISO 6506-4:2005 has been approved by CEN as EN ISO 6506-4:2005 without any
modifications.

2

---------------------- Page: 3 ----------------------

INTERNATIONAL ISO
STANDARD 6506-4
First edition
2005-12-15


Metallic materials — Brinell hardness
test —
Part 4:
Table of hardness values
Matériaux métalliques — Essai de dureté Brinell —
Partie 4: Tableaux pour les essais de dureté




Reference number
ISO 6506-4:2005(E)
©
ISO 2005

---------------------- Page: 4 ----------------------

ISO 6506-4:2005(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.


©  ISO 2005
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland

ii © ISO 2005 – All rights reserved

---------------------- Page: 5 ----------------------

ISO 6506-4:2005(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
Draft International Standards adopted by the technical committees are circulated to the member bodies for
voting. Publication as an International Standard requires approval by at least 75 % of the member bodies
casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 6506-4 was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals, Subcommittee
SC 3, Hardness testing.
This first edition of ISO 6506-4 cancels and replaces Annex C of ISO 6506-1:1999.
ISO 6506 consists of the following parts, under the general title Metallic materials — Brinell hardness test:
— Part 1: Test method
— Part 2: Verification and calibration of testing machines
— Part 3: Calibration of reference blocks
— Part 4: Table of hardness values
© ISO 2005 – All rights reserved iii

---------------------- Page: 6 ----------------------

ISO 6506-4:2005(E)
Introduction
Attention is drawn to the fact that in this part of ISO 6506, only the use of the hardmetal ball indenter is
specified.
The designation of the Brinell hardness is HBW and should not be confused with the former designation HB,
or HBS when a steel ball indenter was used.

iv © ISO 2005 – All rights reserved

---------------------- Page: 7 ----------------------

INTERNATIONAL STANDARD ISO 6506-4:2005(E)

Metallic materials — Brinell hardness test —
Part 4:
Table of hardness values
1 Scope
This part of ISO 6506 gives a table of the Brinell hardness values for use in tests on flat surfaces.
2 Determination of the Brinell hardness for testing on flat surfaces
See Table 1.
Table 1
2
Ball indenter, D
Force-diameter ratio, 0,102 × F/D
mm
30 15 10 5 2,5 1
Test force, F
10  29,42 kN 14,71 kN 9,807 kN 4,903 kN 2,452 kN 980,7 N
5  7,355 kN — 2,452 kN 1,226 kN 612,9 N 245,2 N
 2,5 1,839 kN — 612,9 N 306,5 N 153,2 N 61,29 N
  1 294,2 N — 98,07 N 49,03 N 24,52 N 9,807 N
Mean diameter of the indentation, d Brinell hardness, HBW
mm
2,40 1,200 0,600 0 0,240 653 327 218 109 54,5 21,8
2,41 1,205 0,602 4 0,241 648 324 216 108 54,0 21,6
2,42 1,210 0,605 0 0,242 643 321 214 107 53,5 21,4
2,43 1,215 0,607 5 0,243 637 319 212 106 53,1 21,2
2,44 1,220 0,610 0 0,244 632 316 211 105 52,7 21,1
2,45 1,225 0,612 5 0,245 627 313 209 104 52,2 20,9
2,46 1,230 0,615 0 0,246 621 311 207 104 51,8 20,7
2,47 1,235 0,617 5 0,247 616 308 205 103 51,4 20,5
2,48 1,240 0,620 0 0,248 611 306 204 102 50,9 20,4
2,49 1,245 0,622 5 0,249 606 303 202 101 50,5 20,2
2,50 1,250 0,625 0 0,250 601 301 200 100 50,1 20,0
2,51 1,255 0,627 5 0,251 597 298 199 99,4 49,7 19,9

© ISO 2005 – All rights reserved 1

---------------------- Page: 8 ----------------------

ISO 6506-4:2005(E)
Table 1 (continued)
2
Ball indenter, D
Force-diameter ratio, 0,102 × F/D
mm
10 5 2,5 1 30 15 10 5 2,5 1
Mean diameter of the indentation, d Brinell hardness, HBW
mm
2,52 1,260 0,630 0 0,252 592 296 197 98,6 49,3 19,7
2,53 1,265 0,632 5 0,253 587 294 196 97,8 48,9 19,6
2,54 1,270 0,635 0 0,254 582 291 194 97,1 48,5 19,4
2,55 1,275 0,637 5 0,255 578 289 193 96,3 48,1 19,3
2,56 1,280 0,640 0 0,256 573 287 191 95,5 47,8 19,1
2,57 1,285 0,642 5 0,257 569 284 190 94,8 47,4 19,0
2,58 1,290 0,645 0 0,258 564 282 188 94,0 47,0 18,8
2,59 1,295 0,647 5 0,259 560 280 187 93,3 46,6 18,7
2,60 1,300 0,650 0 0,260 555 278 185 92,6 46,3 18,5
2,61 1,305 0,652 5 0,261 551 276 184 91,8 45,9 18,4
2,62 1,310 0,655 0 0,262 547 273 182 91,1 45,6 18,2
2,63 1,315 0,657 5 0,263 543 271 181 90,4 45,2 18,1
2,64 1,320 0,660 0 0,264 538 269 179 89,7 44,9 17,9
2,65 1,325 0,662 5 0,265 534 267 178 89,0 44,5 17,8
2,66 1,330 0,665 0 0,266 530 265 177 88,4 44,2 17,7
2,67 1,335 0,667 5 0,267 526 263 175 87,7 43,8 17,5
2,68 1,340 0,670 0 0,268 522 261 174 87,0 43,5 17,4
2,69 1,345 0,672 5 0,269 518 259 173 86,4 43,2 17,3
2,70 1,350 0,675 0 0,270 514 257 171 85,7 42,9 17,1
2,71 1,355 0,677 5 0,271 510 255 170 85,1 42,5 17,0
2,72 1,360 0,680 0 0,272 507 253 169 84,4 42,2 16,9
2,73 1,365 0,682 5 0,273 503 251 168 83,8 41,9 16,8
2,74 1,370 0,685 0 0,274 499 250 166 83,2 41,6 16,6
2,75 1,375 0,687 5 0,275 495 248 165 82,6 41,3 16,5
2,76 1,380 0,690 0 0,276 492 246 164 81,9 41,0 16,4
2,77 1,385 0,692 5 0,277 488 244 163 81,3 40,7 16,3
2,78 1,390 0,695 0 0,278 485 242 162 80,8 40,4 16,2
2,79 1,395 0,697 5 0,279 481 240 160 80,2 40,1 16,0
2,80 1,400 0,700 0 0,280 477 239 159 79,6 39,8 15,9
2,81 1,405 0,702 5 0,281 474 237 158 79,0 39,5 15,8
2,82 1,410 0,705 0 0,282 471 235 157 78,4 39,2 15,7
2,83 1,415 0,707 5 0,283 467 234 156 77,9 38,9 15,6
2,84 1,420 0,710 0 0,284 464 232 155 77,3 38,7 15,5
2,85 1,425 0,712 5 0,285 461 230 154 76,8 38,4 15,4

2 © ISO 2005 – All rights reserved

---------------------- Page: 9 ----------------------

ISO 6506-4:2005(E)
Table 1 (continued)
2
Ball indenter, D
Force-diameter ratio, 0,102 × F/D
mm
10 5 2,5 1 30 15 10 5 2,5 1
Mean diameter of the indentation, d Brinell hardness, HBW
mm
2,86 1,430 0,715 0 0,286 457 229 152 76,2 38,1 15,2
2,87 1,435 0,717 5 0,287 454 227 151 75,7 37,8 15,1
2,88 1,440 0,720 0 0,288 451 225 150 75,1 37,6 15,0
2,89 1,445 0,722 5 0,289 448 224 149 74,6 37,3 14,9
2,90 1,450 0,725 0 0,290 444 222 148 74,1 37,0 14,8
2,91 1,455 0,727 5 0,291 441 221 147 73,6 36,8 14,7
2,92 1,460 0,730 0 0,292 438 219 146 73,0 36,5 14,6
2,93 1,465 0,732 5 0,293 435 218 145 72,5 36,3 14,5
2,94 1,470 0,735 0 0,294 432 216 144 72,0 36,0 14,4
2,95 1,475 0,737 5 0,295 429 215 143 71,5 35,8 14,3
2,96 1,480 0,740 0 0,296 426 213 142 71,0 35,5 14,2
2,97 1,485 0,742 5 0,297 423 212 141 70,5 35,3 14,1
2,98 1,490 0,745 0 0,298 420 210 140 70,1 35,0 14,0
2,99 1,495 0,747 5 0,299 417 209 139 69,6 34,8 13,9
3,00 1,500 0,750 0 0,300 415 207 138 69,1 34,6 13,8
3,01 1,505 0,752 5 0,301 412 206 137 68,6 34,3 13,7
3,02 1,510 0,755 0 0,302 409 205 136 68,2 34,1 13,6
3,03 1,515 0,757 5 0,303 406 203 135 67,7 33,9 13,5
3,04 1,520 0,760 0 0,304 404 202 135 67,3 33,6 13,5
3,05 1,525 0,762 5 0,305 401 200 134 66,8 33,4 13,4
3,06 1,530 0,765 0 0,306 398 199 133 66,4 33,2 13,3
3,07 1,535 0,767 5 0,307 395 198 132 65,9 33,0 13,2
3,08 1,540 0,770 0 0,308 393 196 131 65,5 32,7 13,1
3,09 1,545 0,772 5 0,309 390 195 130 65,0 32,5 13,0
3,10 1,550 0,775 0 0,310 388 194 129 64,6 32,3 12,9
3,11 1,555 0,777 5 0,311 385 193 128 64,2 32,1 12,8
3,12 1,560 0,780 0 0,312 383 191 128 63,8 31,9 12,8
3,13 1,565 0,782 5 0,313 380 190 127 63,3 31,7 12,7
3,14 1,570 0,787 0 0,314 378 189 126 62,9 31,5 12,6
3,15 1,575 0,787 5 0,315 375 188 125 62,5 31,3 12,5
3,16 1,580 0,790 0 0,316 373 186 124 62,1 31,1 12,4
3,17 1,585 0,792 5 0,317 370 185 123 61,7 30,9 12,3
3,18 1,590 0,795 0 0,318 368 184 123 61,3 30,7 12,3
3,19 1,595 0,797 5 0,319 366 183 122 60,9 30,5 12,2
© ISO 2005 – All rights reserved 3

---------------------- Page: 10 ----------------------

ISO 6506-4:2005(E)
Table 1 (continued)
2
Ball indenter, D
Force-diameter ratio, 0,102 × F/D
mm
10 5 2,5 1 30 15 10 5 2,5 1
Mean diameter of the indentation, d Brinell hardness, HBW
mm
3,20 1,600 0,800 0 0,320 363 182 121 60,5 30,3 12,1
3,21 1,605 0,802 5 0,321 361 180 120 60,1 30,1 12,0
3,22 1,610 0,805 0 0,322 359 179 120 59,8 29,9 12,0
3,23 1,615 0,807 5 0,323 356 178 119 59,4 29,7 11,9
3,24 1,620 0,810 0 0,324 354 177 118 59,0 29,5 11,8
3,25 1,625 0,812 5 0,325 352 176 117 58,6 29,3 11,7
3,26 1,630 0,815 0 0,326 350 175 117 58,3 29,1 11,7
3,27 1,635 0,817 5 0,327 347 174 116 57,9 29,0 11,6
3,28 1,640 0,820 0 0,328 345 173 115 57,5 28,8 11,5
3,29 1,645 0,822 5 0,329 343 172 114 57,2 28,6 11,4
3,30 1,650 0,825 0 0,330 341 170 114 56,8 28,4 11,4
3,31 1,655 0,827 5 0,331 339 169 113 56,5 28,2 11,3
3,32 1,660 0,830 0 0,332 337 168 112 56,1 28,1 11,2
3,33 1,665 0,832 5 0,333 335 167 112 55,8 27,9 11,2
3,34 1,670 0,835 0 0,334 333 166 111 55,4 27,7 11,1
3,35 1,675 0,837 5 0,335 331 165 110 55,1 27,5 11,0
3,36 1,680 0,840 0 0,336 329 164 110 54,8 27,4 11,0
3,37 1,685 0,842 5 0,337 326 163 109 54,4 27,2 10,9
3,38 1,690 0,845 0 0,338 325 162 108 54,1 27,0 10,8
3,39 1,695 0,847 5 0,339 323 161 108 53,8 26,9 10,8
3,40 1,700 0,850 0 0,340 321 160 107 53,4 26,7 10,7
3,41 1,705 0,852 5 0,341 319 159 106 53,1 26,6 10,6
3,42 1,710 0,855 0 0,342 317 158 106 52,8 26,4 10,6
3,43 1,715 0,857 5 0,343 315 157 105 52,5 26,2 10,5
3,44 1,720 0,860 0 0,344 313 156 104 52,2 26,1 10,4
3,45 1,725 0,862 5 0,345 311 156 104 51,8 25,9 10,4
3,46 1,730 0,865 0 0,346 309 155 103 51,5 25,8 10,3
3,47 1,735 0,867 5 0,347 307 154 102 51,2 25,6 10,2
3,48 1,740 0,870 0 0,348 306 153 102 50,9 25,5 10,2
3,49 1,745 0,872 5 0,349 304 152 101 50,6 25,3 10,1
3,50 1,750 0,875 0 0,350 302 151 101 50,3 25,2 10,1
3,51 1,755 0,877 5 0,351 300 150 100 50,0 25,0 10,0
3,52 1,760 0 880 0 0,352 298 149 99,5 49,7 24,9 9,95
3,53 1,765 0,882 5 0,353 297 148 98,9 49,4 24,7 9,89
4 © ISO 2005 – All rights reserved

---------------------- Page: 11 ----------------------

ISO 6506-4:2005(E)
Table 1 (continued)
2
Ball indenter, D
Force-diameter ratio, 0,102 × F/D
mm
10 5 2,5 1 30 15 10 5 2,5 1
Mean diameter of the indentation, d Brinell hardness, HBW
mm
3,54 1,
...