SIST EN ISO 6507-2:2006
(Main)Metallic materials - Vickers hardness test - Part 2: Verification and calibration of testing machines (ISO 6507-2:2005)
Metallic materials - Vickers hardness test - Part 2: Verification and calibration of testing machines (ISO 6507-2:2005)
This part of ISO 6507 specifies a method of verification of testing machines for determining Vickers hardness in accordance with ISO 6507-1. It specifies a direct verification method for checking the main functions of the machine operation, and an indirect method suitable for the overall checking of the machine. The indirect method may be used on its own for periodic routine checking of the machine in service. If a testing machine is also to be used for other methods of hardness testing, it shall be verified independently for each method. This part of ISO 6507 is also applicable to portable hardness testing machines.
Metallische Werkstoffe - Härteprüfung nach Vickers - Teil 2: Prüfung und Kalibrierung der Prüfmaschinen (ISO 6507-2:2005)
In diesem Teil von ISO 6507 ist das Verfahren für die Prüfung von Härteprüfmaschinen zur Bestimmung der Vickershärte nach ISO 6507-1 festgelegt.
Es ist ein direktes Prüfverfahren zur Prüfung von Hauptfunktionen der Prüfmaschine und ein indirektes Prüfverfahren, das für die Ermittlung der Funktionsfähigkeit der Prüfmaschine geeignet ist, festgelegt. Das indirekte Prüfverfahren kann für die regelmäßige Routineüberprüfung beim Anwender eingesetzt werden.
Wird eine Prüfmaschine auch für andere Härteprüfverfahren verwendet, muss sie unabhängig für jedes Verfahren geprüft werden.
Dieser Teil von ISO 6507 ist auch auf tragbare Härteprüfgeräte anwendbar.
Matériaux métalliques - Essai de dureté Vickers - Partie 2: Vérification et étalonnage des machines d'essai (ISO 6507-2:2005)
L'ISO 6507-2:2005 spécifie une méthode de vérification des machines d'essai utilisées pour la détermination de la dureté Vickers conformément à l'ISO 6507-1.
Kovinski materiali – Preskus trdote po Vickersu – 2. del: Preverjanje in umerjanje naprav za preskušanje (ISO 6507-2:2005)
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
SIST EN ISO 6507-2:2006
01-marec-2006
1DGRPHãþD
SIST EN ISO 6507-2:1998
Kovinski materiali – Preskus trdote po Vickersu – 2. del: Preverjanje in umerjanje
naprav za preskušanje (ISO 6507-2:2005)
Metallic materials - Vickers hardness test - Part 2: Verification and calibration of testing
machines (ISO 6507-2:2005)
Metallische Werkstoffe - Härteprüfung nach Vickers - Teil 2: Prüfung und Kalibrierung
der Prüfmaschinen (ISO 6507-2:2005)
Matériaux métalliques - Essai de dureté Vickers - Partie 2: Vérification et étalonnage des
machines d'essai (ISO 6507-2:2005)
Ta slovenski standard je istoveten z: EN ISO 6507-2:2005
ICS:
77.040.10 Mehansko preskušanje kovin Mechanical testing of metals
SIST EN ISO 6507-2:2006 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
EUROPEAN STANDARD
EN ISO 6507-2
NORME EUROPÉENNE
EUROPÄISCHE NORM
December 2005
ICS 77.040.10 Supersedes EN ISO 6507-2:1997
English Version
Metallic materials - Vickers hardness test - Part 2: Verification
and calibration of testing machines (ISO 6507-2:2005)
Matériaux métalliques - Essai de dureté Vickers - Partie 2: Metallische Werkstoffe - Härteprüfung nach Vickers - Teil
Vérification et étalonnage des machines d'essai (ISO 6507- 2: Prüfung und Kalibrierung der Prüfmaschinen (ISO 6507-
2:2005) 2:2005)
This European Standard was approved by CEN on 14 December 2005.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the Central Secretariat or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official
versions.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,
Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36 B-1050 Brussels
© 2005 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 6507-2:2005: E
worldwide for CEN national Members.
---------------------- Page: 2 ----------------------
EN ISO 6507-2:2005 (E)
Foreword
This document (EN ISO 6507-2:2005) has been prepared by Technical Committee ISO/TC 164
"Mechanical testing of metals" in collaboration with Technical Committee ECISS/TC 1 "Steel -
Mechanical testing", the secretariat of which is held by AFNOR.
This European Standard shall be given the status of a national standard, either by publication of
an identical text or by endorsement, at the latest by June 2006, and conflicting national
standards shall be withdrawn at the latest by June 2006.
This document supersedes EN ISO 6507-2:1997.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of
the following countries are bound to implement this European Standard: Austria, Belgium,
Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary,
Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,
Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
Endorsement notice
The text of ISO 6507-2:2005 has been approved by CEN as EN ISO 6507-2:2005 without any
modifications.
2
---------------------- Page: 3 ----------------------
INTERNATIONAL ISO
STANDARD 6507-2
Third edition
2005-12-15
Metallic materials — Vickers hardness
test —
Part 2:
Verification and calibration of testing
machines
Matériaux métalliques — Essai de dureté Vickers —
Partie 2: Vérification et étalonnage des machines d'essai
Reference number
ISO 6507-2:2005(E)
©
ISO 2005
---------------------- Page: 4 ----------------------
ISO 6507-2:2005(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
© ISO 2005
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2005 – All rights reserved
---------------------- Page: 5 ----------------------
ISO 6507-2:2005(E)
Contents Page
Foreword. iv
1 Scope . 1
2 Normative references . 1
3 General conditions . 1
4 Direct verification. 2
5 Indirect verification. 4
6 Intervals between verifications . 7
7 Verification report/calibration certificate . 8
Annex A (informative) Notes on diamond indenters . 9
Annex B (informative) Uncertainty of measurement of the calibration results of the hardness
testing machine. 10
Bibliography . 16
© ISO 2005 – All rights reserved iii
---------------------- Page: 6 ----------------------
ISO 6507-2:2005(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 6507-2 was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals, Subcommittee
SC 3, Hardness testing.
This third edition cancels and replaces the second edition (ISO 6507-2:1997), which has been technically
revised.
ISO 6507 consists of the following parts, under the general title Metallic materials — Vickers hardness test:
⎯ Part 1: Test method
⎯ Part 2: Verification and calibration of testing machines
⎯ Part 3: Calibration of reference blocks
⎯ Part 4: Tables of hardness values
iv © ISO 2005 – All rights reserved
---------------------- Page: 7 ----------------------
INTERNATIONAL STANDARD ISO 6507-2:2005(E)
Metallic materials — Vickers hardness test —
Part 2:
Verification and calibration of testing machines
1 Scope
This part of ISO 6507 specifies a method of verification of testing machines for determining Vickers hardness
in accordance with ISO 6507-1.
It specifies a direct verification method for checking the main functions of the machine operation, and an
indirect method suitable for the overall checking of the machine. The indirect method may be used on its own
for periodic routine checking of the machine in service.
If a testing machine is also to be used for other methods of hardness testing, it shall be verified independently
for each method.
This part of ISO 6507 is also applicable to portable hardness testing machines.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 376, Metallic materials — Calibration of force-proving instruments used for the verification of uniaxial
testing machines
ISO 3878, Hardmetals — Vickers hardness test
ISO 6507-1:2005, Metallic materials — Vickers hardness test — Part 1: Test method
ISO 6507-3, Metallic materials — Vickers hardness test — Part 3: Calibration of reference blocks
3 General conditions
Before a Vickers hardness testing machine is verified, the machine shall be checked to ensure that it is
properly set up in accordance with the manufacturer's instructions:
Especially, it should be checked that:
a) the plunger holding the indenter is capable of sliding in its guide;
b) the indenter-holder is firmly mounted in the plunger;
c) the test force can be applied and removed without shock or vibration and in such a manner that the
readings are not influenced;
© ISO 2005 – All rights reserved 1
---------------------- Page: 8 ----------------------
ISO 6507-2:2005(E)
d) if the measuring system is integral with the machine
⎯ the change from removing the test force to measuring mode does not influence the readings,
⎯ illumination does not affect the readings,
⎯ the centre of the indentation is in the centre of the field of view, if necessary.
The illumination device of the measuring microscope shall produce uniform lighting of the whole observed field
and maximum contrast between the indentation and the surrounding surface.
4 Direct verification
4.1 General
4.1.1 Direct verification should be carried out at a temperature of (23 ± 5) °C. If the verification is made
outside this temperature range, this shall be reported in the verification report.
4.1.2 The instruments used for verification and calibration shall be traceable to national standards.
4.1.3 Direct verification involves:
a) calibration of the test force;
b) verification of the indenter;
c) calibration of the measuring system;
d) verification of the testing cycle.
4.2 Calibration of the test force
4.2.1 Each test force used within the working range of the testing machine shall be measured. Whenever
applicable, this shall be done at not less than three positions of the plunger uniformly spaced throughout its
range of movement during testing.
4.2.2 Three readings shall be taken for each test force at each position of the plunger. Immediately before
each reading is taken, the plunger shall have been moved in the same direction as during testing.
4.2.3 The test force shall be measured by one of the following two methods:
⎯ by means of an elastic proving device in accordance with ISO 376:2004, class 1, or
⎯ by balancing against a force, accurate to ± 0,2 %, applied by means of calibrated masses or another
method with the same accuracy.
4.2.4 Each measurement of the force shall be within the tolerances of the nominal value of the test force, as
given in Table 1.
2 © ISO 2005 – All rights reserved
---------------------- Page: 9 ----------------------
ISO 6507-2:2005(E)
Table 1
Ranges of the test force, F Tolerances
N %
F W 1,961 ± 1,0
0,098 07 u F < 1,961 ± 1,5
4.3 Verification of the indenter
4.3.1 The four faces of the square-based diamond pyramid shall be polished and free from surface defects.
4.3.2 The verification of the shape of the indenter can be made by direct measurement or by measurement
of its projection on a screen.
4.3.3 The angle between the opposite faces at the vertex of the diamond pyramid shall be 136° ± 0,5° (see
Figure 1).
NOTE The angle between the opposite faces may also be determined by the angle between the opposite edges; this
value is 148,11° ± 0,76°.
4.3.4 The angle between the axis of the diamond pyramid and the axis of the indenter-holder (normal to the
seating surface) shall be less than 0,50°. The four faces shall meet at a point; the maximum permissible
length of the line of conjunction between opposite faces is given in Table 2 (see also Figure 2).
Figure 1 — Angle of the diamond pyramid
Key
a = length of line of conjunction
Figure 2 — Line of conjunction on the top of the indenter (schematic)
© ISO 2005 – All rights reserved 3
---------------------- Page: 10 ----------------------
ISO 6507-2:2005(E)
Table 2
Maximum permissible length of the line of conjunction,
Ranges of test force, F
a
N mm
F W 49,03
0,002
1,961 u F < 49,03
0,001
0,098 07 u F < 1,961
0,000 5
4.4 Calibration of the measuring system
4.4.1 The resolution required of the measuring system depends on the size of the smallest indentation to be
measured.
The scale of the measuring system shall be graduated to permit estimation of the diagonals of the indentation
in accordance with Table 3.
Table 3
Diagonal length, d
Resolution of the measuring system Maximum permissible error
mm
d u 0,040
0,000 2 mm 0,000 4 mm
0,040 < d u 0,200 0,5 % of d 1,0 % of d
d > 0,200 0,001 mm 0,002 mm
NOTE The diagonal length of the indentation determines the necessary magnification V of the measuring system according to the
following condition:
V × d W 14 mm
For indentation diagonals d < 0,035 mm this condition may not be fulfilled, but the magnification should be at least × 400.
The resolution of the measuring system for Vickers hardness testing of hardmetals is specified in ISO 3878.
4.4.2 The measuring system shall be verified by measurements made on an object micrometer at a
minimum of five intervals over each working range.
The maximum permissible error shall not exceed the values given in Table 3.
4.5 Verification of the testing cycle
The testing cycle shall be timed with an uncertainty of ± 1,0 s and shall conform to the testing cycle of
ISO 6507-1.
5 Indirect verification
5.1 Indirect verification should be carried out at a temperature of (23 ± 5) °C by means of reference blocks
calibrated in accordance with ISO 6507-3. If the verification is made outside this temperature range, this shall
be reported in the verification report.
4 © ISO 2005 – All rights reserved
---------------------- Page: 11 ----------------------
ISO 6507-2:2005(E)
5.2 On each reference block, the reference indentation shall be measured. For each block, the difference
between the mean measured value and the certified mean diagonal shall not exceed the maximum
permissible errors given in Table 3.
5.3 The machine shall be verified at each test force which is used. For each test force, two reference blocks
shall be selected from the hardness ranges specified below. The blocks shall be chosen so that at least one
reference block in each hardness range is used for the verification.
⎯ u 225 HV
⎯ 400 HV to 600 HV
⎯ > 700 HV
5.4 When verifying testing machines using only one test force, three
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.