SIST EN ISO 21068-3:2008
(Main)Chemical analysis of silicon-carbide-containing raw materials and refractory products - Part 3: Determination of nitrogen, oxygen and metallic and oxidic constituents (ISO21068-3:2008)
Chemical analysis of silicon-carbide-containing raw materials and refractory products - Part 3: Determination of nitrogen, oxygen and metallic and oxidic constituents (ISO21068-3:2008)
This part of ISO 21068 specifies methods for the determination of total nitrogen and nitrogen calculated as silicon nitride, total oxygen, and free metallic and oxidic components in silicon carbide raw materials and refractory products. It applies only to silicon carbide materials that are not bonded with nitrogen. Nitride-bonded silicon carbide refractories are covered in EN 12698-1.
Chemische Analyse von Siliciumcarbid enthaltenden Rohstoffen und feuerfesten Erzeugnissen - Teil 3: Bestimmung des Gehaltes an Stickstoff, Sauerstoff sowie metallenen und oxidischen Bestandteilen (ISO 21068-3:2008)
Dieser Teil von ISO 21068 beschreibt Verfahren für die Bestimmung von Gesamtstickstoff und als Siliciumnitrid berechnetem Stickstoff, Gesamtsauerstoff sowie freien metallenen und sauerstoffhaltigen Bestandteilen.
Analyse chimique des matières premières et des produits réfractaires contenant du carbure de silicium - Partie 3: Dosage de l'azote, de l'oxygène et des constituants métalliques et oxydés (ISO 21068-3:2008)
L'ISO 21068-3:2008 spécifie des méthodes permettant de doser l'azote total et l'azote calculés comme le nitrure de silicium, l'oxygène total et les composés libres métalliques et contenant de l'oxyde dans les matières premières et produits réfractaires de carbure de silicium.
Elle s'applique uniquement aux matériaux contenant du carbure de silicium qui ne sont pas liés à l'azote. Les matériaux contenant du carbure de silicium qui sont liés à l'azote sont couverts par l'EN 12698-1.
Kemijska analiza surovin in ognjevzdržnih izdelkov s silicijevim karbidom - 3.del: Določevanje dušika, kisika in kovin in oksidnih sestavin (ISO 21068-3:2008)
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
SIST EN ISO 21068-3:2008
01-december-2008
.HPLMVNDDQDOL]DVXURYLQLQRJQMHY]GUåQLKL]GHONRYVVLOLFLMHYLPNDUELGRPGHO
'RORþHYDQMHGXãLNDNLVLNDLQNRYLQLQRNVLGQLKVHVWDYLQ ,62
Chemical analysis of silicon-carbide-containing raw materials and refractory products -
Part 3: Determination of nitrogen, oxygen and metallic and oxidic constituents (ISO21068
-3:2008)
Chemische Analyse von Siliciumcarbid enthaltenden Rohstoffen und feuerfesten
Erzeugnissen - Teil 3: Bestimmung des Gehaltes an Stickstoff, Sauerstoff sowie
metallenen und oxidischen Bestandteilen (ISO 21068-3:2008)
Analyse chimique des matières premières et des produits réfractaires contenant du
carbure de silicium - Partie 3: Dosage de l'azote, de l'oxygène et des constituants
métalliques et oxydés (ISO 21068-3:2008)
Ta slovenski standard je istoveten z: EN ISO 21068-3:2008
ICS:
81.080 Ognjevzdržni materiali Refractories
SIST EN ISO 21068-3:2008 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST EN ISO 21068-3:2008
---------------------- Page: 2 ----------------------
SIST EN ISO 21068-3:2008
EUROPEAN STANDARD
EN ISO 21068-3
NORME EUROPÉENNE
EUROPÄISCHE NORM
August 2008
ICS 81.080
English Version
Chemical analysis of silicon-carbide-containing raw materials
and refractory products - Part 3: Determination of nitrogen,
oxygen and metallic and oxidic constituents (ISO 21068-3:2008)
Analyse chimique des matières premières et des produits Chemische Analyse von Siliciumcarbid enthaltenden
réfractaires contenant du carbure de silicium - Partie 3: Rohstoffen und feuerfesten Erzeugnissen - Teil 3:
Dosage de l'azote, de l'oxygène et des constituants Bestimmung des Gehaltes an Stickstoff, Sauerstoff sowie
métalliques et oxydés (ISO 21068-3:2008) metallischen und oxidischen Bestandteilen (ISO 21068-
3:2008)
This European Standard was approved by CEN on 11 July 2008.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the
official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,
France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36 B-1050 Brussels
© 2008 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 21068-3:2008: E
worldwide for CEN national Members.
---------------------- Page: 3 ----------------------
SIST EN ISO 21068-3:2008
EN ISO 21068-3:2008 (E)
Contents Page
Foreword.3
2
---------------------- Page: 4 ----------------------
SIST EN ISO 21068-3:2008
EN ISO 21068-3:2008 (E)
Foreword
This document (EN ISO 21068-3:2008) has been prepared by Technical Committee ISO/TC 33 "Refractories"
in collaboration with Technical Committee CEN/TC 187 “Refractory products and materials” the secretariat of
which is held by BSI.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by February 2009, and conflicting national standards shall be withdrawn
at the latest by February 2009.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech
Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,
Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
Sweden, Switzerland and the United Kingdom.
Endorsement notice
The text of ISO 21068-3:2008 has been approved by CEN as a EN ISO 21068-3:2008 without any
modification.
3
---------------------- Page: 5 ----------------------
SIST EN ISO 21068-3:2008
---------------------- Page: 6 ----------------------
SIST EN ISO 21068-3:2008
INTERNATIONAL ISO
STANDARD 21068-3
First edition
2008-08-01
Chemical analysis of silicon-carbide-
containing raw materials and refractory
products —
Part 3:
Determination of nitrogen, oxygen
and metallic and oxidic constituents
Analyse chimique des matières premières et des produits réfractaires
contenant du carbure de silicium —
Partie 3: Dosage de l'azote, de l'oxygène et des constituants
métalliques et oxydés
Reference number
ISO 21068-3:2008(E)
©
ISO 2008
---------------------- Page: 7 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
COPYRIGHT PROTECTED DOCUMENT
© ISO 2008
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2008 – All rights reserved
---------------------- Page: 8 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
Contents Page
Foreword .iv
Introduction.v
1 Scope.1
2 Normative references.1
3 Terms and definitions .2
4 Determination of nitrogen and oxygen .2
4.1 General .2
4.2 Combined determination of nitrogen and oxygen by an analyser with thermal
conductivity (CR) and infrared absorption (IR) detection.2
5 Determination of nitrogen calculated as Si N .4
3 4
5.1 General .4
5.2 Acid decomposition — Titration method.5
5.3 Acid decomposition — Photometry method .9
5.4 Inert-gas fusion — Thermal conductivity method .12
5.5 Determination of total nitrogen.17
6 Determination of free Iron by Inductively Coupled Plasma Atomic Emission Spectrometry
(ICP-AES).17
6.1 General .17
6.2 Copper sulfate method .18
6.3 Bromine/methanol method.19
7 Determination of free aluminium and free magnesium.22
7.1 General .22
7.2 Acid decomposition — Inductively coupled plasma atomic emission spectroscopy
(ICP-AES).22
7.3 Acid decomposition — Flame Atomic Absorption Spectrometry (FAAS).24
7.4 Hydrogen generating method .25
8 Analysis of oxides .26
8.1 General .26
8.2 Wet methods .26
8.3 Flame atomic absorption and/or inductively coupled plasma atomic emission
spectrometer.26
8.4 XRF fusion method after ignition of the sample .27
8.5 Determination of silicon(IV) oxide, aluminium oxide, iron(III) oxide, titanium(IV) oxide,
calcium oxide, magnesium oxide, sodium oxide, potassium oxide, chromium(III) oxide,
zirconium oxide, and boron oxide .29
9 Expression of results.31
10 Test report.31
Annex A (informative) Statistical results obtained with analysis of refractories containing carbon
and/or silicon carbide .32
Bibliography.37
© ISO 2008 – All rights reserved iii
---------------------- Page: 9 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 21068-3 was prepared by Technical Committee ISO/TC 33, Refractories.
ISO 21068 consists of the following parts, under the general title Chemical analysis of silicon-carbide-
containing raw materials and refractory products:
⎯ Part 1: General information and sample preparation
⎯ Part 2: Determination of loss on ignition, total carbon, free carbon and silicon carbide, total and free silica
and total and free silicon
⎯ Part 3: Determination of nitrogen, oxygen and metallic and oxidic constituents
iv © ISO 2008 – All rights reserved
---------------------- Page: 10 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
Introduction
[8]
ISO 21068, Parts 1 to 3, have been developed from the combination of a Japanese standard JIS 2011 and
work items originally developed within CEN. Because there is a wide variety of laboratory equipment in use,
the most commonly used methods are described.
This part of ISO 21068 is applicable to the analysis of all refractory products as classified in
[3], [4], [5], [6] [1]
ISO 10081 (all parts) (shaped) and ISO 1927 (unshaped) and raw materials containing carbon
and/or silicon carbide. Therefore, this part of ISO 21068 covers the full range of analysis from pure silicon
carbide to oxidic refractory composition with a low content of silicon carbide and/or nitrides. Primarily, this part
of ISO 21068 provides methods to distinguish between different carbon bound types like total carbon (C )
total
and free carbon (C ) and derives from these two the silicon carbide content.
free
If free carbon is present, this part of ISO 21068 includes different types of temperature treatment in order to
determine the mass changes gravimetrically. Frequently, the resulting residue is used for other determinations.
The determination of other groups of analytes described in this part of ISO 21068 are free metals, free silicon
(Si ), free aluminum (Al ), free magnesium (Mg ), free iron (Fe ) and the group of oxides from main to
free free free free
trace components.
This part of ISO 21068 also describes the chemical analysis of SiO , total Si, oxygen and nitrogen and other
2
oxidic bound metals which typically occur in the materials.
This part of ISO 21068 represents a listing of analytical methods which is approximately structured according
to material composition. However, it is still the user who should prove the applicability of the method
depending on the material and analytical requirements.
© ISO 2008 – All rights reserved v
---------------------- Page: 11 ----------------------
SIST EN ISO 21068-3:2008
---------------------- Page: 12 ----------------------
SIST EN ISO 21068-3:2008
INTERNATIONAL STANDARD ISO 21068-3:2008(E)
Chemical analysis of silicon-carbide-containing raw materials
and refractory products —
Part 3:
Determination of nitrogen, oxygen and metallic and oxidic
constituents
1 Scope
This part of ISO 21068 specifies methods for the determination of total nitrogen and nitrogen calculated as
silicon nitride, total oxygen, and free metallic and oxidic components in silicon carbide raw materials and
refractory products.
It applies only to silicon carbide materials that are not bonded with nitrogen. Nitride-bonded silicon carbide
refractories are covered in EN 12698-1.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 10058-1, Chemical analysis of magnesite and dolomite refractory products (alternative to the X-ray
fluorescence method) — Part 1: Apparatus, reagents, dissolution and gravimetric silica
ISO 10058-2, Chemical analysis of magnesite and dolomite refractory products (alternative to the X-ray
fluorescence method) — Part 2: Wet chemical analysis
ISO 10058-3, Chemical analysis of magnesite and dolomite refractory products (alternative to the X-ray
fluorescence method) — Part 3: Flame atomic absorption spectrometry (FAAS) and inductively coupled
plasma emission spectrometry (ICP-AES)
ISO 12677, Chemical analysis of refractory products by XRF — Fused cast bead method
ISO 20565-1, Chemical analysis of chrome-bearing refractory products and chrome-bearing raw materials
(alternative to the X-ray fluorescence method) — Part 1: Apparatus, reagents, dissolution and gravimetric
silica
ISO 20565-2, Chemical analysis of chrome-bearing refractory products and chrome-bearing raw materials
(alternative to the X-ray fluorescence method) — Part 2: Wet chemical analysis
ISO 20565-3, Chemical analysis of chrome-bearing refractory products and chrome-bearing raw materials
(alternative to the X-ray fluorescence method) — Part 3: Flame atomic absorption spectrometry (FAAS) and
inductively coupled plasma emission spectrometry (ICP-AES)
ISO 21068-1:2008, Chemical analysis of silicon-carbide-containing raw materials and refractory products —
Part 1: General information and sample preparation
© ISO 2008 – All rights reserved 1
---------------------- Page: 13 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
ISO 21068-2:2008, Chemical analysis of silicon-carbide-containing raw materials and refractory products —
Part 2: Determination of loss on ignition, total carbon, free carbon and silicon carbide, total and free silica and
total and free silicon
ISO 21079-1, Chemical analysis of refractories containing alumina, zirconia and silica — Refractories
containing 5 % to 45 % of ZrO (alternative to the X-ray fluorescence method) — Part 1: Apparatus, reagents
2
and dissolution
ISO 21079-2, Chemical analysis of refractories containing alumina, zirconia and silica — Refractories
containing 5 % to 45 % of ZrO (alternative to the X-ray fluorescence method) — Part 2: Wet chemical
2
analysis
ISO 21079-3, Chemical analysis of refractories containing alumina, zirconia and silica — Refractories
containing 5 % to 45 % of ZrO (alternative to the X-ray fluorescence method) — Part 3: Flame atomic
2
absorption spectrometry (FAAS) and inductively coupled plasma emission spectrometry (ICP-AES)
ISO 21587-1, Chemical analysis of aluminosilicate refractory products (alternative to the X-ray fluorescence
method) — Part 1: Apparatus, reagents, dissolution and gravimetric silica
ISO 21587-2, Chemical analysis of aluminosilicate refractory products (alternative to the X-ray fluorescence
method) — Part 2: Wet chemical analysis
ISO 21587-3, Chemical analysis of aluminosilicate refractory products (alternative to the X-ray fluorescence
method) — Part 3: Inductively coupled plasma and atomic absorption spectrometry methods
ISO 26845, Chemical analysis of refractories — General requirements for wet chemical analysis, atomic
absorption spectrometry (AAS) and inductively coupled plasma atomic emission spectrometry (ICP-AES)
methods
EN 12698-1:2007, Chemical analysis of nitride bonded silicon carbide refractories — Part 1: Chemical
methods
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 21068-1 apply.
4 Determination of nitrogen and oxygen
4.1 General
For oxygen only, the IR detection method is given; for nitrogen, several different methods are described,
calculated nominally as Si N .
3 4
NOTE The calculation of nitrogen as Si N is only applicable in the case where other nitride species are absent or
3 4
too low to detect by XRD, see ISO 21068-1. Otherwise, nitrogen is reported as total nitrogen.
4.2 Combined determination of nitrogen and oxygen by an analyser with thermal
conductivity (CR) and infrared absorption (IR) detection
4.2.1 Principle
The method uses inert-gas fusion analysis. A preweighed sample is placed in a graphite crucible positioned
between the electrodes of an impulse furnace. 5 kW of power (typically) is passed through the crucible
generating a temperature of approximately 2 800 °C.
NOTE 1 Furnace temperatures can be varied by increasing and decreasing current/voltage.
2 © ISO 2008 – All rights reserved
---------------------- Page: 14 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
The sample decomposes, releasing any oxygen and nitrogen present. The nitrogen released remains as
elemental nitrogen, while oxygen combines with the carbon of the graphite crucible to form carbon monoxide.
The sample gases are carried on a helium carrier gas either to a rare-earth copper catalyst, which converts
carbon monoxide to carbon dioxide, and then to an infrared cell which measures the carbon dioxide present or
are measured directly without catalyst as carbon monoxide. The gas stream is then passed through sodium
hydroxide to remove carbon dioxide, and magnesium perchlorate to remove any moisture present, and finally
through a thermal conductivity cell or other suitable analyser to quantify the nitrogen.
[7]
NOTE 2 A method for the determination of oxygen contents less than 3 % is given in EN 725-3 .
Because the sample will invariably be in the form of a powder, it should be enclosed in a small nickel capsule
before placing it in the graphite crucible to prevent any loss of sample during analysis.
When materials with dissociation temperatures higher than 2 400 °C ± 25 °C are being analysed, it is
recommended that a fluxing agent is also included with the sample. A suitable agent would be a nickel wire
basket.
4.2.2 Reagents
4.2.2.1 Nickel or tin capsule, of suitable dimensions and oxygen and nitrogen free.
4.2.2.2 Nickel basket, of suitable dimensions and oxygen and nitrogen free.
4.2.2.3 Carbon dioxide, 99,998 % pure.
4.2.2.4 Nitrogen, 99,998 % pure.
4.2.2.5 Helium, 99,998 % pure.
4.2.3 Apparatus
Ordinary laboratory apparatus and the following.
4.2.3.1 Combined nitrogen/oxygen analyser, commercially available.
NOTE If no combined analyser for nitrogen and oxygen is available, a separate nitrogen and/or oxygen analyser can
be used.
4.2.4 Calibration
Referring to the instrument operation manual, the calibration can be achieved by two methods:
a) using certified reference materials (preferably primary);
b) by injection of known volumes of pure carbon dioxide and nitrogen into the detection system.
If b) is used, it is recommended that a standard reference material be analysed to verify the performance of
the electrode furnace, associated chemicals and detection system.
For both methods, a minimum of three calibration points and a zero shall be used to establish the calibration.
4.2.5 Procedure
4.2.5.1 General
Operate the instrument in accordance with the instrument operation manual.
© ISO 2008 – All rights reserved 3
---------------------- Page: 15 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
4.2.5.2 Determination
Dry and grind the sample (see Clause 4 of ISO 21068-1:2008). Weigh it, to the nearest 0,1 mg, into the nickel
capsule and seal it, taking care to expel any air present.
NOTE A typical sample mass is approximately 50 mg ± 1 mg. However, in practice, the sample mass is determined
by a combination of the dynamic range of the analyser and the magnitude of the concentration of oxygen and nitrogen
present.
Put the nickel capsule into the loading-mechanism analyser.
Carry out the analysis in two stages:
a) heat the graphite crucible to a temperature at least as high as that used for the analysis, for a period of
time sufficient to allow any entrapped oxygen and nitrogen to be expelled;
b) drop the sample into the graphite crucible and perform the analysis.
Because of the sample masses involved, report results as the mean of at least three determinations.
4.2.5.3 Blank determinations
Although any oxygen and nitrogen present in the graphite crucible is removed prior to the analysis being
carried out [see 4.2.5.2 a)], there may still be oxygen and nitrogen present in the tin capsule and nickel basket.
Make blank determinations and subtract them from subsequent analyses. The blank shall be the mean of at
least three determinations.
Prepare a solution containing approximately 75 ml of acetic acid, 25 ml of nitric acid and 1,5 ml of hydrochloric
acid. In a well-ventilated fume cupboard, heat the solution to a temperature of 55 °C ± 5 °C, immerse the
nickel basket in the heated solution for 30 s to 60 s, remove the nickel basket from the solution and rinse
immediately in running water. Immerse the nickel basket in chemically pure acetone, dry thoroughly and place
the cleaned nickel basket in a desiccator.
4.2.5.4 Calculation
Calculate the mass fraction of nitrogen or oxygen, w , expressed as a percentage, using Equation (1).
a
wwb=− (1)
am
where
w is the mass fraction of nitrogen or oxygen, respectively, measured in the sample, expressed as a
m
percentage;
b is the average blank determination of nitrogen or oxygen respectively, expressed as a percentage by
mass.
Report the results as the mean of three determinations.
5 Determination of nitrogen calculated as Si N
3 4
5.1 General
The nitrogen determined is calculated as silicon nitride. The determination of silicon nitride is carried out using
one of the following methods:
a) acid decomposition with pressurization/separation by the steam distillation/neutralization titration method;
4 © ISO 2008 – All rights reserved
---------------------- Page: 16 ----------------------
SIST EN ISO 21068-3:2008
ISO 21068-3:2008(E)
b) acid decomposition with pressurization/separation by steam distillation/indophenol blue absorption
spectroscopy; this method should be used for samples containing silicon nitride whose percentage is less
than 2 % by mass;
c) inert-gas fusion-thermal conductivity method.
The calculation of Si N by using the measured nitrogen content is only justified and expedient if nitrogen is
3 4
chemically bonded as silicon nitride quantitatively. The methods described in Clause 4 are, in principle,
applicable for the determination of total nitrogen. When method 5.2 or 5.3 is used for determining total
nitrogen, the obtained result should be verified by a method as described in Clause 4 or 5.4. This is because
of the high chemical resistance of nitrides, particularly with regard to unknown nitrides, besides Si N ,
3 4
contained in the sample.
5.2 Acid decomposition — Titration method
5.2.1 Principle
A sample is decomposed with sulfuric acid and hydrofluoric acid in a pressurization container, so that silicon
nitride changes to ammonium salt, and boric acid is then added to it. The resulting solution is transferred into
a distillation flask. Sodium hydroxide is added to the flask and steam distillation is carried out, and the
ammonia distillate is absorbed into an appropriate amidosulfonic acid. The remaining amidosulfonic acid is
titrated with sodium hydroxide.
5.2.2 Reagents
Solutions 5.2.2.1, 5.2.2.2 and 5.2.2.7 shall be stored in plastics bottles.
5.2.2.1 Hydrofluoric acid.
5.2.2.2 Sulfuric acid (1+1).
5.2.2.3 Boric acid.
5.2.2.4 Sodium hydroxide (500 g/l).
5.2.2.5 Ammonium sulfate, purity more than 99,9 % by mass. Heat at 110 °C ± 10 °C for 3 h and cool in
a desiccator.
5.2.2.6 Amidosulfuric acid solution, 0,1 mol/l.
Weigh 10,0 g, to the nearest 0,1 mg, of amidosulfuric acid (reference material for volumetric analysis, or high-
purity reagent above 99,99 % by mass). Dissolve in water, transfer to a 1 000 ml volumetric flask, and dilute to
the mark with water.
Calculate the factor, F, for the 0,1 mol/l amidosulfuric acid solution using Equation (2).
mP×
a
F = (2)
9,709 5 ×
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.