SIST ISO 6507-1:1995
(Main)Metallic materials -- Hardness test -- Vickers test -- Part 1: HV 5 to HV 100
Metallic materials -- Hardness test -- Vickers test -- Part 1: HV 5 to HV 100
Matériaux métalliques -- Essai de dureté -- Essai Vickers -- Partie 1: HV 5 à HV 100
Kovinska gradiva - Preskus trdote - Preskus trdote po Vickersu - 1. del: HV 5 do HV 100
General Information
Relations
Buy Standard
Standards Content (Sample)
International Standard @ 650711
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION*MEXAYHAPOAHAR OPrAHH3AUMR il0 CTAHAAPTH3AUHM*ORGANlSATlON INTERNATIONALE DE NORMALISATION
Metallic materials - Hardness test - Vickers test -
Part 1 : HV 5 to HV 100
Matériaux métalliques - Essai de dureté - Essai Vickers - Partie 1 :
First edition - 1982-07-01
-
y UDC 620.178.152.341 Ref. No. IS0 6507/1-1982 (E)
f!
Descriptors : metal products, tests, hardness tests, Vickers hardness, designation, test specimens, test equipment.
-
Price based on 6 pages
8
---------------------- Page: 1 ----------------------
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards institutes (IS0 member bodies). The work of developing Inter-
national Standards is carried out through IS0 technical committees. Every member
body interested in a subject for which a technical committee has been set up has the
right to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with EO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 6507/1 was developed by Technical Committee
ISO/TC 164, Mechanical testing of metals, and was circulated to the member bodies in
June 1981.
It has been approved by the member bodies of the following countries :
Hungary Romania
Australia
Austria India South Africa, Rep. of
Brazil Japan Spain
Canada Korea, Rep. of Sweden
China Mexico Switzerland
Czechoslovakia Netherlands USA
Egypt, Arab Rep. of Norway USSR
France Poland
Germany, F. R. Portugal
The member body of the following country expressed disapproval of the document on
technical grounds :
United Kingdom
This International Standard cancels and replaces IS0 Recommendations R 81-1967,
R 192-1971 and R 399-1964, of which it constitutes a technical revision.
O International Organization for Standardization, 1982 O
---------------------- Page: 2 ----------------------
IS0 6507/1-1982 (E)
INTERNATIONAL STANDARD
Metallic materials - Hardness test - Vickers test -
Part I : HV 5 to HV 100
IS0 64û, Calibration of standardized blocks to be used for
O Introduction
Vickers hardness testing machines. 3)
Three types of Vickers hardness test exist, characterized by dif-
ferent ranges of test forces. See table 1. IS0 3878, Hardmetals - Vickers hardness test.4)
IS0 44981 1, Sintered metal materials, excluding hardmetals -
NOTE - In general, decreasing test force increases the scatter of
results of the measurements. This is particularly true for low load
Determination of apparent hardness - Pari I : Materials of
Vickers hardness tests and for Vickers microhardness tests.
essentially uniform section hardness.
IS0 650712, Metallic materials - Hardness test - Vickers test
- Part 2 : HV 0,2 to less than HV 5.5)
1 Scope and field of application
IS0 650713, Metallic materials - Hardness test - Vickers test
This Part of IS0 6507 specifies the method of Vickers hardness
- Part 3 : Less than HV 0,2.5)
test HV 5 to HV 100 (test forces from 49,03 to 980,7 NI for
metallic materials.
3 Principle
For specific materials andlor products particular International
Standards exist. (See clause 2.)
Forcing a diamond indenter in the form of a right pyramid with
a square base and with a specified angle between opposite
faces at the vertex into the surface of a test piece and measur-
ing the diagonals of the indentation left in the surface after
2 References
removal of the test force, F. (See figure 1.)
IS0 146, Verification of Vickers hardness testing machines. 1)
The Vickers hardness is proportional to the quotient obtained
IS0 40911, Metallic materials - Hardness test - Tables of by dividing the test force by the sloping area of the indentation
which is assumed to be a right pyramid with a square base, and
Vickers hardness values for use in tests made on flat surfaces
having at the vertex the same angle as the indenter.
- Part 1 : HV 5 to HV 100.2)
Low load Vickers
HV 0,2 to < HV 5 1,961 to < @,O3
1) At present at the stage of draft. (Revision of ISO/R 146-1968.1
2) At present at the stage of draft. (Revision of ISO/R 409-1964.)
3) At present at the stage of draft. (Revision of ISO/R 640-1967.)
4) At present at the stage of draft. (Revision of IS0 378-1978.]
5) At present at the stage of draft.
1
---------------------- Page: 3 ----------------------
6.3 The thickness of the test piece or of the layer under test
4 Symbols and designations
shall be at least 1,5 times the diagonal of the indentation. (See
annex A.)
4.1 See table 2 and figures 1 and 2.
No deformation shall be visible at the back of the test piece
Table 2
after the test.
Symbol Designation
a Angle between the opposite faces at the vertex of the
6.4 For tests on curved surfaces the corrections given in
pyramidal indenter (136O)
annex B, tables 4 to 9 shall be applied.
F Test force, in newtons
d Arithmetic mean, in millimetres, of the two diagonals
6.5 For test pieces of small cross-section or of irregular
dl and d2
shape, it may be necessary to provide some form of additional
support, for example mounting in plastics material.
HV Vickers hardness
Test force
= Constant x
Surface area of indentation
7 Procedure
1360
2Fsin-
2 F
7.1 In general, the test is carried out at ambient temperature
= 0,102 = 0,189 1 -
within the limits of 10 to 35 OC. Tests carried out under con-
d2 d2
trolled conditions shall be made at a temperature of 23 f 5 OC.
1 1
NOTE - Constant = I = - = 0,102
g, 9,806 65
7.2 The following test forces shall be used.
4.2 The Vickers hardness is denoted by the symbol HV
preceded by the hardness value and completed by :
Table 3
a) a number representing the test force (see table 3);
Test force
Hardness symbol F
b) the duration of loading, in seconds, if different from the Nominal value
time specified in 7.4.
HV 5 @,O3 N
HV 10 98.07 N
Examples :
HV 20 196,l N
HV 30 294,2 N
640 HV 30 = Vickers hardness of 640 determined with a test
HV 50 490,3 N
force of 294,2 N applied for 10 to 15 s. HV 100 980,7 N
640 HV 30120 = Vickers hardness of 640 determined with a
test force of 294,2 N applied for 20 s.
7.3 The test piece shall be placed on a rigid support. The
contact surfaces shall be clean and free from foreign matter
5 Apparatus (scale, oil, dirt etc.). It is important that the test piece lies firmly
on the support so that displacement cannot occur during the
5.1 Testing machine, capable of applying a predetermined test.
force or forces within the range of &,O3 to 980,7 N, in accord-
ance with IS0 146.
7.4 Bring the indenter into contact with the test surface and
apply the test force in a direction perpendicular to the surface,
5.2 Indenter, a diamond in the shape of a right pyramid with without shock or vibration, until the applied force attains the
a square base, as specified in IS0 146. specified value. The time from the initial application of the force
until the full test force is reached shall not be less than
2 s nor greater than 8 s. The duration of the test force shall
5.3 Measuring device, as specified in IS0 146.
be 10 to 15 s. For particular materials a longer time for main-
...
SLOVENSKI STANDARD
SIST ISO 6507-1:1995
01-november-1995
Kovinska gradiva - Preskus trdote - Preskus trdote po Vickersu - 1. del: HV 5 do
HV 100
Metallic materials -- Hardness test -- Vickers test -- Part 1: HV 5 to HV 100
Matériaux métalliques -- Essai de dureté -- Essai Vickers -- Partie 1: HV 5 à HV 100
Ta slovenski standard je istoveten z: ISO 6507-1:1982
ICS:
77.040.10 Mehansko preskušanje kovin Mechanical testing of metals
SIST ISO 6507-1:1995 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST ISO 6507-1:1995
---------------------- Page: 2 ----------------------
SIST ISO 6507-1:1995
International Standard @ 650711
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION*MEXAYHAPOAHAR OPrAHH3AUMR il0 CTAHAAPTH3AUHM*ORGANlSATlON INTERNATIONALE DE NORMALISATION
Metallic materials - Hardness test - Vickers test -
Part 1 : HV 5 to HV 100
Matériaux métalliques - Essai de dureté - Essai Vickers - Partie 1 :
First edition - 1982-07-01
-
y UDC 620.178.152.341 Ref. No. IS0 6507/1-1982 (E)
f!
Descriptors : metal products, tests, hardness tests, Vickers hardness, designation, test specimens, test equipment.
-
Price based on 6 pages
8
---------------------- Page: 3 ----------------------
SIST ISO 6507-1:1995
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards institutes (IS0 member bodies). The work of developing Inter-
national Standards is carried out through IS0 technical committees. Every member
body interested in a subject for which a technical committee has been set up has the
right to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with EO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 6507/1 was developed by Technical Committee
ISO/TC 164, Mechanical testing of metals, and was circulated to the member bodies in
June 1981.
It has been approved by the member bodies of the following countries :
Hungary Romania
Australia
Austria India South Africa, Rep. of
Brazil Japan Spain
Canada Korea, Rep. of Sweden
China Mexico Switzerland
Czechoslovakia Netherlands USA
Egypt, Arab Rep. of Norway USSR
France Poland
Germany, F. R. Portugal
The member body of the following country expressed disapproval of the document on
technical grounds :
United Kingdom
This International Standard cancels and replaces IS0 Recommendations R 81-1967,
R 192-1971 and R 399-1964, of which it constitutes a technical revision.
O International Organization for Standardization, 1982 O
---------------------- Page: 4 ----------------------
SIST ISO 6507-1:1995
IS0 6507/1-1982 (E)
INTERNATIONAL STANDARD
Metallic materials - Hardness test - Vickers test -
Part I : HV 5 to HV 100
IS0 64û, Calibration of standardized blocks to be used for
O Introduction
Vickers hardness testing machines. 3)
Three types of Vickers hardness test exist, characterized by dif-
ferent ranges of test forces. See table 1. IS0 3878, Hardmetals - Vickers hardness test.4)
IS0 44981 1, Sintered metal materials, excluding hardmetals -
NOTE - In general, decreasing test force increases the scatter of
results of the measurements. This is particularly true for low load
Determination of apparent hardness - Pari I : Materials of
Vickers hardness tests and for Vickers microhardness tests.
essentially uniform section hardness.
IS0 650712, Metallic materials - Hardness test - Vickers test
- Part 2 : HV 0,2 to less than HV 5.5)
1 Scope and field of application
IS0 650713, Metallic materials - Hardness test - Vickers test
This Part of IS0 6507 specifies the method of Vickers hardness
- Part 3 : Less than HV 0,2.5)
test HV 5 to HV 100 (test forces from 49,03 to 980,7 NI for
metallic materials.
3 Principle
For specific materials andlor products particular International
Standards exist. (See clause 2.)
Forcing a diamond indenter in the form of a right pyramid with
a square base and with a specified angle between opposite
faces at the vertex into the surface of a test piece and measur-
ing the diagonals of the indentation left in the surface after
2 References
removal of the test force, F. (See figure 1.)
IS0 146, Verification of Vickers hardness testing machines. 1)
The Vickers hardness is proportional to the quotient obtained
IS0 40911, Metallic materials - Hardness test - Tables of by dividing the test force by the sloping area of the indentation
which is assumed to be a right pyramid with a square base, and
Vickers hardness values for use in tests made on flat surfaces
having at the vertex the same angle as the indenter.
- Part 1 : HV 5 to HV 100.2)
Low load Vickers
HV 0,2 to < HV 5 1,961 to < @,O3
1) At present at the stage of draft. (Revision of ISO/R 146-1968.1
2) At present at the stage of draft. (Revision of ISO/R 409-1964.)
3) At present at the stage of draft. (Revision of ISO/R 640-1967.)
4) At present at the stage of draft. (Revision of IS0 378-1978.]
5) At present at the stage of draft.
1
---------------------- Page: 5 ----------------------
SIST ISO 6507-1:1995
6.3 The thickness of the test piece or of the layer under test
4 Symbols and designations
shall be at least 1,5 times the diagonal of the indentation. (See
annex A.)
4.1 See table 2 and figures 1 and 2.
No deformation shall be visible at the back of the test piece
Table 2
after the test.
Symbol Designation
a Angle between the opposite faces at the vertex of the
6.4 For tests on curved surfaces the corrections given in
pyramidal indenter (136O)
annex B, tables 4 to 9 shall be applied.
F Test force, in newtons
d Arithmetic mean, in millimetres, of the two diagonals
6.5 For test pieces of small cross-section or of irregular
dl and d2
shape, it may be necessary to provide some form of additional
support, for example mounting in plastics material.
HV Vickers hardness
Test force
= Constant x
Surface area of indentation
7 Procedure
1360
2Fsin-
2 F
7.1 In general, the test is carried out at ambient temperature
= 0,102 = 0,189 1 -
within the limits of 10 to 35 OC. Tests carried out under con-
d2 d2
trolled conditions shall be made at a temperature of 23 f 5 OC.
1 1
NOTE - Constant = I = - = 0,102
g, 9,806 65
7.2 The following test forces shall be used.
4.2 The Vickers hardness is denoted by the symbol HV
preceded by the hardness value and completed by :
Table 3
a) a number representing the test force (see table 3);
Test force
Hardness symbol F
b) the duration of loading, in seconds, if different from the Nominal value
time specified in 7.4.
HV 5 @,O3 N
HV 10 98.07 N
Examples :
HV 20 196,l N
HV 30 294,2 N
640 HV 30 = Vickers hardness of 640 determined with a test
HV 50 490,3 N
force of 294,2 N applied for 10 to 15 s. HV 100 980,7 N
640 HV 30120 = Vickers hardness of 640 determined with a
test force of 294,2 N applied for 20 s.
7.3 The test piece shall be placed on a rigid support. The
contact surfaces shall be clean and free from foreign matter
5 Apparatus (scale, oil, dirt etc.). It is important that the test piece lies firmly
on the support so that displacement cannot occur during the
5.1 Testing machine, capable of applying a predetermined test.
force or forces within the range of &,O3 to 980,7 N, in accord-
ance with IS0 146.
7.4 Bring the indenter into contact with the test surface and
apply the test force in a direction perpendicular to the surface,
5.2 Indenter, a diamond in the shape of a right pyramid with without shock or vibration, until the applied force attains
...
Norme internationale
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION*MEXAYHAPO~HAfl OPïAHH3AUblR fl0 CTAHAAPTH3AUHi4*ORGANlSATlON INTERNATIONALE DE NORMALISATION
Matériaux métalliques - Essai de dureté - Essai Vickers -
Partie 1 : HV 5 à HV 100
Metallic materials - Hardness test - Vickers test - Part 1 :
Première édition - 1982-07-01
C D U 620.178.152.341 Réf. no : IS0 6507/1-1982 (FI
Descripteurs : produit métallurgique, essai, essai de dureté, dureté Vickers, désignation, spécimen d'essai, matériel d'essai, résultats d'essai.
Prix basé sur 6 pages
---------------------- Page: 1 ----------------------
Avant-propos
L‘ISO (Organisation internationale de normalisation) est une fédération mondiale
d‘organismes nationaux de normalisation (comités membres de I’ISO). L‘élaboration
des Normes internationales est confiée aux comités techniques de I’ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I’ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I‘ISO.
La Norme internationale IS0 6507/1 a été élaborée par le comité technique
ISO/TC 164, Essais mécaniques des métaux, et a été soumise aux comités membres
en juin 1981.
Les comités membres des pays suivants l‘ont approuvée :
Portugal
Afrique du Sud, Rép. d’ Espagne
Allemagne, R. F. France Roumanie
Suède
Australie Hongrie
Autriche Inde Suisse
Brésil Japon Tchécoslovaquie
Mexique URSS
Canada
Chine Norvège USA
Pays-Bas
Corée, Rép. de
Égypte, Rép. arabe d’ Pologne
Le comité membre du pays suivant l’a désapprouvée pour des raisons techniques :
Royaume-Uni
Cette Norme internationale annule et remplace les Recommandations ISO/R 81-1967,
ISO/R 192-1971 et ISO/R 399-1964, dont elle constitue une révision technique.
O Organisation internationale de normalisation, 1982 O
Imprimé en Suisse
---------------------- Page: 2 ----------------------
NORME INTERNATIONALE IS0 6507/1-1982 (F)
Matériaux métalliques - Essai de dureté - Essai Vickers -
Partie I : HV 5 à HV I00
O Introduction IS0 640, Matériaux métalliques - Essai de dureté - Etalon-
à utiliser pour les machines d'essai
nage des blocs de référence
Il existe trois types d'essai de dureté VickerS, caractérisés par de dureté Vickers.3)
différents domaines de charges d'essai. Voir tableau 1.
IS0 3878, Métaux durs - Essai de dureté Vickers.4)
NOTE - En général, plus la charge d'essai devient faible, plus la dis-
persion des mesures devient grande. Ceci est notable pour les essais de IS0 44981 1, Matériaux métalliques frittés à l'exclusion des
dureté Vickers sous charge réduite et les essais de microdureté Vickers.
métaux durs - Détermination de la dureté apparente -
Partie I : Matériaux ayant essentiellement une dureté uniforme
dans la section.
1 Objet et domaine d'application
IS0 650712, Matériaux métalliques - Essai de dureté - Essai
Vickers - Partie 2 : HV 0,2 à HV 5 exclu.5)
La présente partie de I'ISO 6507 spécifie la méthode d'essai de
dureté Vickers HV 5 à HV 100 (charge d'essai de 49.03 à
IS0 650713, Matériaux métalliques - Essai de dureté - Essai
980,7 N) pour les matériaux métalliques.
Vickers - Partie 3 : Jusqu'à HV 0,2 exclu.5)
Des Normes internationales particulières existent pour les maté-
riaux etlou pour les produits spécifiques (voir chapitre 2).
3 Principe
Impression, à la surface d'une éprouvette, d'un pénétrateur en
forme de pyramide droite à base carrée, d'angle au sommet
prescrit, et mesurage des diagonales de l'empreinte laissée sur
2 Références
la surface après enlèvement de la charge d'essai F (voir
figure 1).
IS0 146, Contrôle des machines d'essai de dureté Vickers. 1)
La dureté Vickers est proportionnelle au quotient de la charge
IS0 4091 1, Matériaux métalliques - Essai de dureté -
d'essai par l'aire de l'empreinte qui est considérée comme une
Tableaux des valeurs de dureté Vickers pour utilisation dans les
pyramide droite à base carrée et ayant au sommet le même
essais effectués sur surfaces planes - Partie I : HV 5 à HV
angle que le pénétrateur.
100.2)
Tableau 1
Charge d'essai, F Méthode
Désignation Symbole de dureté
N d'essai
Essai de dureté Vickers HV5 à HVIMI @,O3 à 980,7 IS0 6537/1
Essai de dureté Vickers
HV0.2à < HV 5 1,961 A < &,O3 IS0 6507/2
sous charge réduite
Essai de microdureté Vickers < HV 0,2 < 1,961 IS0 6507/3
1) Actuellement au stade de projet. (Révision de I'ISO/R 146-1968.)
2) Actuellement au stade de projet. (Révision de I'ISO/R 409-1964)
3) Actuellement au stade de projet. (Révision de I'ISO/R 640-1967.)
4) Actuellement au stade de projet. (Révision de I'ISO 3878-1978.)
5) Actuellement au stade de projet.
1
---------------------- Page: 3 ----------------------
IS0 6507/1-1982 (FI
6.2 La préparation doit être effectuée de manière que toute
4 Symboles et désignations
altération de la dureté de surface, par exemple, par échauffe-
ment ou par écrouissage, soit minimisée.
4.1 Voir tableau 2 et figures 1 et 2.
6.3 L'épaisseur de l'éprouvette ou de la couche superficielle à
Tableau 2
essayer ne doit pas être inférieure à 1,5 fois la diagonale de
l'empreinte. (Voir annexe A.)
Symbole Désignation
a Angle entre les deux faces opposées au sommet du
Après l'essai, aucune déformation ne doit être visible sur la face
pénétrateur pyramidal (136')
opposée de l'éprouvette.
Charge d'essai, en newtons
F
Moyenne arithmétique, en millimètres, des deux dia-
d
6.4 Pour les essais effectués sur des surfaces courbes, les
gonales dl et d2
coefficients de correction donnés dans les tableaux 4 à 9 de
Dureté Vickers
HV
l'annexe B doivent être appliqués.
Charge d'essai
= Constante x
Aire de l'empreinte
6.5 Pour les éprouvettes de petite section ou de forme irrégu-
136O
lière il peut être nécessaire de prévoir des formes de support
2 F sin -
2 F complémentaire, par exemple, par enrobage dans des maté-
= 0,189 1 -
= 0,102
riaux plastiques.
d2 LI2
1 1
NOTE - Constante = .L = - = 0,102
g, 9,806 65
7 Mode opératoire
7.1 En règle général, l'essai est effectué à la température
4.2 La dureté Vickers est désignée par le symbole HV pré-
ambiante dans les limites comprises entre 10 et 35 OC. Les
cédé par la valeur de dureté et complété par :
essais effectués sous conditions surveillées doivent être effec-
tués à une température de 23 tr 5 OC.
a) un nombre représentant la charge d'essai (voir
tableau 3);
7.2 Les charges d'essai suivantes doivent être utilisées.
b) la durée d'application de la charge, en secondes, si elle
diffère du temps spécifié en 7.4.
Tableau 3
Exemples :
Charge d'essai
Symbole de dureté F
Valeur nominale
640 HV 30 = Dureté Vickers de 640, déterminée sous une
charge d'essai de 294.2 N appliquée durant 10 à 15 s.
98,07 N
640 HV 30120 = Dureté Vickers de 640, déterminée SOUS 196,l N
HV 30 294,2 N
une charge d'essai de 294,2 N appliquée durant 20 s.
490,3 N
HV 100 980,7 N
5 Appareillage
7.3 L'éprouvette doit être placée sur un support rigide. Les
5.1 Machine d'essai, permettant l'application d'une charge
surfaces de contact doivent être propres et exemptes de corps
d'essai prédéterminée ou, d'autres charges comprises entre
étrangers (calamine, huile, saleté, etc.). II est important que
49,03 et 980,7 N, conformément à I'ISO 146.
l'éprouvette soit maintenue solidement sur le support de facon
ait pas de déplacement pendant l'essai.
qu'il n'y
5.2 Pénétrateur, diamant de la forme d'une pyramide droite
à base carrée comme spécifié dans I'ISO 146.
7.4 Amener le pénétrateur en contact avec la surface d'essai
et appliquer la charge perpendiculairement à la surface, sans
5.3 Dispositif de mesure, conforme aux spécifications de
choc ni vibration, jusqu'à ce que la charge appliquée atteigne la
I'ISO 146.
valeur spécifiée. La durée s'éc
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.