Hardmetals - Vickers hardness test (ISO 3878:1983)

This second edition cancels and replaces the first edition (i.e. ISO 3878:1976). Specifies principle, symbols and designations, apparatus, test pieces, procedure, expression of results and test report.

Hartmetalle - Vickers-Härteprüfung (ISO 3878:1983)

Métaux-durs - Essai de dureté Vickers (ISO 3878:1983)

La présente Norme internationale spécifie une méthode d'essai de dureté Vickers pour les métaux-durs.

Hardmetals - Vickers hardness test (ISO 3878:1983)

General Information

• Status: Published
• Publication Date: 30-Nov-2000
• ICS: 77.040.10 - Mechanical testing of metals
• ICS: 77.160 - Powder metallurgy
• Technical Committee: SS SPL - Technical Board for the general field
• Current Stage: 6060 - National Implementation/Publication (Adopted Project)
• Start Date: 01-Dec-2000
• Due Date: 01-Dec-2000
• Completion Date: 01-Dec-2000
• Ref Project: EN 23878:1993 - Hardmetals - Vickers hardness test (ISO 3878:1983)

Standards Content (Sample)

2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Hardmetals - Vickers hardness test (ISO 3878:1983)Hartmetalle - Vickers-Härteprüfung (ISO 3878:1983)Métaux-durs - Essai de dureté Vickers (ISO 3878:1983)Hardmetals - Vickers hardness test (ISO 3878:1983)77.160Metalurgija prahovPowder metallurgy77.040.10Mehansko preskušanje kovinMechanical testing of metalsICS:Ta slovenski standard je istoveten z:EN 23878:1993SIST EN 23878:2000en01-december-2000SIST EN 23878:2000SLOVENSKI
STANDARD



SIST EN 23878:2000



SIST EN 23878:2000



SIST EN 23878:2000



SIST EN 23878:2000



SIST EN 23878:2000



International Standard INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONWlE~YHAPO~HAR OPrAHWAL&lR fl0 CTAH~PTH3AL&lM.ORGANISATION INTERNATIONALE DE NORMALISATION Hardmetals - Vickers hardness test Mtaux-durs - Essai de durete Vickers Second edition - 1983-08-15 UDC 669.018.25 : 620.178.152.341 Ref. No. ISO 38784983 (E) Descriptors : powder metallurgy, hardmetals, carbides, tests, hardness tests, Vickers hardness. Price based on 2 pages SIST EN 23878:2000



Foreword ISO (the International Organization for Standardization) is a worldwide federation of national Standards bodies (ISO member bedies). The work of developing International Standards is carried out through ISO technical committees. Every member body interested in a subject for which a technical committee has been authorized has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. Draft International Standards adopted by the technical committees are circulated to the member bodies for approval before their acceptance as International Standards by the ISO Council. International Standard ISO 3378 was developed by Technical Committee ISO/TC 119, Powder metahrgy, and was circulated to the member bodies in August 1982. lt has been approved by the member bodies of the following countries : Austria Italy China Korea, Rep. of Czechoslovakia Poland Egypt, Arab Rep. of Romania France South Africa, Rep. of Germany, F. R. Spain Sweden Switzerland Thailand United Kingdom USA USSR No member body expressed disapproval of the document. This second edition cancels and replaces the first edition (i.e. ISO 3878-1976). 0 International Organkation for Standardkation, 1983 Printed in Switzerland SIST EN 23878:2000



INTERNATIONAL STANDARD ISO 3878-1983 (EI Hardmetals - Vickers hardness test 1 Scope and field of application This International Standard specifies the method of Vickers hardness test for hardmetals. 5.3 Measuring device, capable of measuring indentation diagonals to the following accuracy : d < 100 Pm : Z!I 0,2 Pm; 100 pm G d < 200 Fm : + 1,0 Pm; 2 References d > 200 Pm : rt 0,5 %. I S 0 146, Metallic ma terials - Hardness test - Verifica tion of Vickers hardness testing machines HV 0,2 to HV 100.1) ISO 409, Metallic materials - Hardness test - Tables of Vickers hardness values for use in tests made on flat surfaces - Part 7 : HV 5 to HV 100. - Part 2 : HV 0,2 to less than HV 5. ISO 4565, Hardmetals - Me tallographic de termina tion o f porosity and uncombined carbon. I S 0 6567, Metallic ma terials - Hardness tes t - Vickers tes t - Part 7 ; HV 5 to HV 100. - Part 2 : HV 0,2 to less than HV 5. 3 Principle See ISO 6507/1 and ISO 6507/2. 4 Symbols and designations See ISO 6507/1 and ISO 6507/2. 6 Test pieces 6.1 The thickness of the layer removed from the surface of the test piece shall be not less than 0,2 mm. The test shall be carried out on a surface which is free from foreign matter and, in particular, completely free from lubricants. The
...