ASTM D709-01

(Specification)

Standard Specification for Laminated Thermosetting Materials

Standard Specification for Laminated Thermosetting Materials

SCOPE
1.1 This specification covers laminated thermosetting materials consisting of two or more plies or layers of reinforcing material bonded by a thermosetting synthetic resin. Examples of such reinforcement are cellulose paper, cotton fabric, glass fabric, and synthetic fiber fabrics. These materials are available in the form of sheets, rolled and molded tubes, and molded rods.
1.2 The values stated in inch-pound units are to be regarded as the standard. Note 1—This specification resembles IEC 60893-3 in title only. The content is significantly different.
1.3 The following safety hazards caveat pertains only to the test methods described in this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
09-Sep-2001
ICS
83.140.20 - Laminated sheets
Technical Committee
D09 - Electrical and Electronic Insulating Materials
Drafting Committee
D09.07 - Electrical Insulating Materials
Current Stage
Ref Project

Relations

Replaces
ASTM D709-00 - Standard Specification for Laminated Thermosetting Materials
Effective Date
10-Sep-2001
Replaced By
ASTM D709-01(2007) - Standard Specification for Laminated Thermosetting Materials
Effective Date
01-May-2007
Referred By
ASTM D2132-23 - Standard Test Method for Dust-and-Fog Tracking and Erosion Resistance of Electrical Insulating Materials
Effective Date
10-Sep-2001
Referred By
ASTM F992-17(2022) - Standard Specification for Valve Label Plates
Effective Date
10-Sep-2001
Referred By
ASTM D618-21 - Standard Practice for Conditioning Plastics for Testing
Effective Date
10-Sep-2001

Buy Standard

ASTM D709-01 - Standard Specification for Laminated Thermosetting MaterialsASTM D709-01 - Standard Specification for Laminated Thermosetting Materials
PreviousNext
Technical specification
ASTM D709-01 - Standard Specification for Laminated Thermosetting Materials
English language
34 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
An American National Standard
Designation: D 709 – 01
Standard Specification for
1
Laminated Thermosetting Materials
This standard is issued under the fixed designation D 709; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
2
1. Scope Rods and Tubes Used for Electrical Insulation
D 785 Test Method for Rockwell Hardness of Plastics and
1.1 This specification covers laminated thermosetting mate-
4
Electrical Insulating Materials
rials consisting of two or more plies or layers of reinforcing
4
D 883 Terminology Relating to Plastics
material bonded by a thermosetting synthetic resin. Examples
D 1180 Test Method for Bursting Strength of Round Rigid
of such reinforcement are cellulose paper, cotton fabric, glass
5
Plastic Tubing
fabric, and synthetic fiber fabrics.These materials are available
2
D 1711 Terminology Relating to Electrical Insulation
in the form of sheets, rolled and molded tubes, and molded
D 2303 Test Method for Liquid-Contaminant, Inclined-
rods.
2
Plane Tracking and Erosion of Insulating Materials
1.2 The values stated in inch-pound units are to be regarded
D 2304 Test Method for Thermal Endurance of Rigid Elec-
as the standard.
2
trical Insulating Materials
NOTE 1—This specification resembles IEC 60893-3 in title only. The
D 3636 Practice for Sampling and Judging Quality of Solid
content is significantly different.
6
Electrical Insulating Materials
1.3 The following safety hazards caveat pertains only to the
D 6054 Practice for Conditioning Electrical Insulating Ma-
6
test methods described in this specification. This standard does
terials for Testing
7
not purport to address all of the safety concerns, if any,
2.2 IEEE Standards:
associated with its use. It is the responsibility of the user of this
1 GeneralPrinciplesforTemperatureLimitsintheRatingof
standard to establish appropriate safety and health practices
Electric Equipment
and determine the applicability of regulatory limitations prior
98 Guide for the Preparation of Test Procedures for the
to use.
Thermal Evaluation and Establishment of Temperature
Indices of Solid Electrical Insulating Materials
2. Referenced Documents
99 Guide for the Preparation of Test Procedures for the
2.1 ASTM Standards:
Thermal Evaluation of Insulation Systems for Electric
D 229 Test Methods for Rigid Sheet and Plate Materials
Equipment
2
Used for Electrical Insulation
101 Guide for the Statistical Analysis of Thermal Life Test
D 257 Test Methods for DC Resistance or Conductance of
Data
2
8
Insulating Materials
2.3 NEMA Standards:
D 348 Test Methods for Rigid Tubes Used for Electrical
LI 1-1971 Industrial Laminated Thermosetting Products
2
Insulation
LI 5-1969 Temperature Indices of Industrial Thermosetting
D 349 Test Methods for Laminated Round Rods Used for
Laminates
2
Electrical Insulation
LI 3-1961 High-Temperature Properties of Industrial Ther-
D 495 Test Method for High-Voltage, Low-Current, Dry
mosetting Laminates
2
9
Arc Resistance of Solid Electrical Insulation
2.4 Military Specifications:
D 621 Test Methods for Deformation of Plastics Under
MIL-P-997 Plastic Material, Laminated, Thermosetting,
3
Load
D 668 Test Methods for Measuring Dimensions of Rigid
4
Annual Book of ASTM Standards, Vol 08.01.
5
Discontinued—See 1989 Annual Book of ASTM Standards, Vol 08.04.
1 6
This specification is under the jurisdiction of ASTM Committee D09 on Annual Book of ASTM Standards, Vol 10.02.
7
Electrical and Electronic Insulating Materials and is the direct responsibility of Available from the Institute of Electrical and Electronics Engineers, 345 E. 47
Subcommittee D09.07 on Flexible and Rigid Insulating Materials. St., New York, NY 10017.
8
Current edition approved Sept. 10, 2001. Published November 2001. Originally Available from the National Electrical Manufacturers Association, 2101 L
published as D 709 – 43 T. Last previous edition D 709 – 00. Street, NW, Washington, DC, 20037.
2 9
Annual Book of ASTM Standards, Vol 10.01. AvailablefromStandardizationDocumentsOrderDesk,Bldg.4SectionD,700
3
Discontinued—See 1993 Annual Book of ASTM Standards, Vol 08.01. Robbins Ave., Philadelphia, PA 19111-5094 Attn: NPODS.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
D709–01
Machined rods, manufactured from certain grades of sheet material, are
Electric Insulation, Sheets, Glass Cloth, Silicone Resin
not covered by this specification. In rods machined from sheets, the
M
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D709-17(Specification)
Standard Specification for Laminated Thermosetting Materials

ABSTRACT
This specification establishes the manufacture, property requirements, and testing of several grades of laminated thermosetting materials consisting of two or more plies or layers of reinforcing material such as cellulose paper, cotton fabric, glass fabric, and synthetic fiber fabrics, bonded by a thermosetting synthetic resin. These materials are available in the form of sheets, rolled and molded tubes, and molded rods.
SCOPE
1.1 This specification covers laminated thermosetting materials consisting of two or more plies or layers of reinforcing material bonded by a thermosetting synthetic resin. Examples of such reinforcement are cellulose paper, cotton fabric, glass fabric, and synthetic fiber fabrics. These materials are available in the form of sheets, rolled and molded tubes, and molded rods.  
1.2 The values stated in inch-pound units are to be regarded as the standard.  
Note 1: This specification resembles IEC 60893-3 in title only. The content is significantly different.  
1.3 The following safety hazards caveat pertains only to the test methods described in this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.    
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    35 pages
    English language
    sale 15% off
  • Technical specification
    35 pages
    English language
    sale 15% off
ASTM
ASTM D3917-23(Specification)
Standard Specification for Dimensional Tolerance of Thermosetting Glass-Reinforced Plastic Pultruded Shapes

ABSTRACT
This specification defines the dimensional tolerances of standard rods, bars, and shapes pultruded from thermosetting glass-reinforced plastics. Tolerances cover dimensional criteria for cross sections, width or diameter, straightness, twist, surface flatness, angularity, and camber.
SCOPE
1.1 This specification defines production tolerances applicable to standard rods, bars, shapes, and flat sheet pultruded from thermosetting glass-reinforced plastics.  
1.2 These dimensional tolerances apply to all shapes specified as “standard” by the pultrusion industry.  
1.3 Custom shapes and products designed for special applications may carry specific tolerances that vary from the standard.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 The following safety hazards caveat pertains only to the test methods portion, Section 5, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM D3479/D3479M-19(2023)(Test Method)
Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 This test method is designed to yield tensile fatigue data for material specifications, research and development, quality assurance, and structural design and analysis. The primary test result is the fatigue life of the test specimen under a specific loading and environmental condition. Replicate tests may be used to obtain a distribution of fatigue life for specific material types, laminate stacking sequences, environments, and loading conditions. Guidance in statistical analysis of fatigue life data, such as determination of linearized stress life (S-N) or strain-life (ε-N) curves, can be found in Practice E739.  
5.2 This test method can be utilized in the study of fatigue damage in a polymer matrix composite such as the occurrence of microscopic cracks, fiber fractures, or delaminations.3 The specimen's residual strength or stiffness, or both, may change due to these damage mechanisms. The loss in stiffness may be quantified by discontinuing cyclic loading at selected cycle intervals to obtain the quasi-static axial stress-strain curve using modulus determination procedures found in Test Method D3039/D3039M. The loss in strength associated with fatigue damage may be determined by discontinuing cyclic loading to obtain the static strength using Test Method D3039/D3039M.  
Note 1: This test method may be used as a guide to conduct tension-tension variable amplitude loading. This information can be useful in the understanding of fatigue behavior of composite structures under spectrum loading conditions, but is not covered in this test method.
SCOPE
1.1 This test method determines the fatigue behavior of polymer matrix composite materials subjected to tensile cyclic loading. The composite material forms are limited to continuous-fiber or discontinuous-fiber reinforced composites for which the elastic properties are specially orthotropic with respect to the test direction. This test method is limited to unnotched test specimens subjected to constant amplitude uniaxial in-plane loading where the loading is defined in terms of a test control parameter.  
1.2 This test method presents two procedures where each defines a different test control parameter.  
1.2.1 Procedure A—A system in which the test control parameter is the load (stress) and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude load cycles. In this procedure, the test control parameter may be described using either engineering stress or applied load as a constant amplitude fatigue variable.  
1.2.2 Procedure B—A system in which the test control parameter is the strain in the loading direction and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude strain cycles. In this procedure, the test control parameter may be described using engineering strain in the loading direction as a constant amplitude fatigue variable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D8387/D8387M-23(Test Method)
Standard Test Method for High Bypass – Low Bearing Interaction Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This test method determines the uniaxial high bypass - low bearing interaction response of multi-directional polymer matrix composite laminates reinforced by high-modulus fibers using a two-fastener hard point joint specimen. The scope of this test method is limited to net section (bypass) failure modes. Standard specimen configurations using fixed values of test parameters are described for this procedure. A number of test parameters may be varied within the scope of the standard, provided that the parameters are fully documented in the test report. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced composites for which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1. This test method was previously published under Test Method D7248/D7248M-17 Procedure C.  
1.2 This test method is consistent with the recommendations of Composite Materials Handbook, CMH-17, which describes the desirable attributes of a bearing/bypass interaction response test method.  
1.3 The two-fastener test configurations described in this test method are intended to provide data in the relatively high bypass, low bearing part of the composite bolted joint bearing-bypass interaction diagram. This data complements the data from filled hole tension and compression (Practice D6742/D6742M), bearing (Test Method D5961/D5961M), and low bypass/high bearing interaction (Test Method D7248/D7248M) tests.  
1.4 This test method requires careful specimen design, instrumentation, data measurement, and data analysis. The use of this test method requires close coordination between the test requestor and the test lab personnel. Test requestors need to be familiar with the data analysis procedures of this test method and should not expect test labs who are unfamiliar with this test method to be able to produce acceptable results without close coordination.  
1.5 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5.1 Within the text, the inch-pound units are shown in brackets.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    27 pages
    English language
    sale 15% off
  • Standard
    27 pages
    English language
    sale 15% off
ASTM
ASTM D6873/D6873M-23(Practice)
Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This practice provides instructions for modifying static bearing test methods to determine the fatigue behavior of composite materials subjected to cyclic bearing forces. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.  
1.2 This practice supplements Test Method D5961/D5961M with provisions for testing specimens under cyclic loading. Several important test specimen parameters (for example, fastener selection, fastener installation method, and fatigue force/stress ratio) are not mandated by this practice; however, repeatable results require that these parameters be specified and reported.  
1.3 This practice is limited to test specimens subjected to constant amplitude uniaxial loading, where the machine is controlled so that the test specimen is subjected to repetitive constant amplitude force (stress) cycles. Either engineering stress or applied force may be used as a constant amplitude fatigue variable. The repetitive loadings may be tensile, compressive, or reversed, depending upon the test specimen and procedure utilized.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D4762-23(Guide)
Standard Guide for Testing Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
4.1 This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.
SCOPE
1.1 This guide summarizes the application of ASTM standard test methods (and other supporting standards) to continuous-fiber reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included, emphasizing use of standards of Committee D30 on Composite Materials.  
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including non-ASTM test methods, is included in the Composite Materials Handbook (CMH-17).2 Additional specific recommendations for testing textile (fabric, braided) composites are contained in Guide D6856.  
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards with SI units listed first.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    27 pages
    English language
    sale 15% off
  • Guide
    27 pages
    English language
    sale 15% off
ASTM
ASTM D8131/D8131M-23(Practice)
Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This test practice is designed to produce tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the tensile response and should therefore be reported include the following: materials (laminates and adhesive), methods of material preparation including surface preparation prior to bonding, lay-ups, specimen stacking sequence, joint taper ratio or step length, ply overlap length, material relative thicknesses and stiffness of the parent and repair laminates, adhesive bond stiffness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Properties in the test direction, which may be obtained from this test practice, include the following:  
5.1.1 Ultimate tensile strength (based on the nominal parent material thickness), (Fptu).  
5.1.2 Ultimate tensile strength (based on the nominal repair material thickness), (Frtu).  
5.1.3 Ultimate running force per repair ply, (Nj).
SCOPE
1.1 This test practice defines the procedure for determination of the tensile strength of a tapered or stepped joint of polymer matrix composite materials. It is applicable to secondary bonded or co-bonded laminates with either unidirectional plies or woven fabric reinforcements. The materials to be bonded may be different material systems. In the bondline, a separate adhesive material may or may not be used (example: adhesives may be used with a prepreg system or may not be used with a wet lay-up repair system). The range of acceptable test laminates and thicknesses is described in 8.2.1.  
1.2 This practice supplements Test Method D3039/D3039M for tensile loading. Several important test specimen parameters (for example, joint length, ply overlaps, step depth, and taper ratio) are not mandated by this practice, however, these parameters are required to be specified and reported to support repeatable results.  
1.3 Unidirectional (0° ply orientation) tape composites, textile composites, as well as multidirectional composite laminates, can be tested.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM D8484-23(Specification)
Standard Specification for Plastic Lumber Materials and Wood-Plastic Composite Materials Used as Exterior Wall Coverings

SCOPE
1.1 This specification is applicable to the use of plastic lumber materials and of wood-plastic composite materials, and no other plastic composite materials, used as exterior wall coverings, as part of an exterior wall assembly.  
1.2 This specification is not applicable to the use of plastic lumber materials or of wood-plastic composite materials contained in exterior wall assemblies when not used as part of the exterior wall covering.  
1.3 This specification is not applicable to the use of any of the following types of materials:
(a) poly(vinyl chloride) (PVC) siding (see Specification D3679, for standard vinyl siding, or Specification D7793, for insulated vinyl siding),
(b) polypropylene siding (see Specification D7254),
(c) wood (including lumber, plywood, engineered wood, coated wood, or painted wood).  
1.4 This specification is not applicable to the use of plastic lumber materials or of wood-plastic composite materials in any application other than the one addressed in 1.1. In particular, this specification is not applicable to the use of plastic lumber materials or of wood-plastic composite materials as exterior deck boards, stair treads, handrails, guards, or soffits.  
1.5 The values stated in inch-pound units are to be regarded as standard. Any SI units given in parentheses are for information only.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM D8066/D8066M-23(Practice)
Standard Practice Unnotched Compression Testing of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This practice provides supplemental instructions for the use of Test Method D6484/D6484M to determine unnotched compressive strength data for material specifications, research and development, material design allowables, and quality assurance. Factors that influence compressive strengths and shall therefore be reported include the following: material, methods of material fabrication, accuracy of lay-up, laminate stacking sequence and overall thickness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Composite properties in the test direction that may be obtained from this test method include:  
5.1.1 Unnotched compressive (UNC) strength, Fxunc,  
5.1.2 Ultimate compressive strain,  
5.1.3 Compressive (linear or chord) modulus of elasticity, Ec, and  
5.1.4 Poisson's ratio in compression.  
5.2 This practice provides a compression test method for laminates containing fibers in multiple fiber directions, particularly those combining axial (0 degree) fibers and off-axis (± θ degree) fibers. Other compression strength test methods include SACMA SRM-1 (also known as the modified D695), D3410/D3410M, D5467/D5467M, D6641/D6641M, and D7249/D7249M. The SRM-1 test uses 12.6 mm [0.50 in.] wide specimens, which is only appropriate for unidirectional tape, cross-ply [0/90]ns tape, or small unit-cell-size fabrics (e.g. 3K-70-P). Larger cell-size fabrics (for example, spread-tow 12K fabrics) should be tested with wider specimens. The standard D3410/D3410M and D6641/D6641M test fixtures do permit the use of wider specimens, for example, 25.4 mm [1.0 in.] wide, and thus can be used to test laminates containing both axial and off-axis fibers; however their gage lengths are relatively short. Test Method D5467/D5467M is intended to obtain the compressive strength of unidirectional laminates, but is expensive due to the sandwich beam confi...
SCOPE
1.1 This practice provides instructions for using the Test Method D6484/D6484M open hole compression test fixture to determine unnotched compressive strength of multi-directional laminates. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.2.1 Within the text the inch-pound units are shown in brackets.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM C582-23(Specification)
Standard Specification for Contact-Molded Reinforced Thermosetting Plastic (RTP) Laminates for Corrosion-Resistant Equipment

ABSTRACT
This specification covers composition, thickness, fabricating procedures, and physical property requirements for glass fiber reinforced thermoset polyester, vinyl ester, or other qualified thermosetting resin laminates comprising the materials of construction for RTP corrosion-resistant tanks, piping, and equipment. This specification is limited to fabrication by contact molding. Laminates shall be classified according to type, class, and grade: Types I and II; Classes P and V. Tensile strength and tangent modulus of elasticity, flexural strength, glass content, thickness, hardness, chemical resistance, and surface flame-spread classification tests shall be performed to conform to the specified requirements.
SCOPE
1.1 This specification covers composition, thickness, fabricating procedures, and physical property requirements for glass fiber reinforced thermoset polyester, vinyl ester, or other qualified thermosetting resin laminates comprising the materials of construction for RTP corrosion-resistant tanks, piping, and equipment. This specification is limited to fabrication by contact molding.  
Note 1: The laminates covered by this specification are manufactured during fabrication of contact-molded RTP tanks, piping, and other equipment.
Note 2: There is no known ISO equivalent to this standard.  
1.2 The values stated in inch-pound units are to be regarded as standard. The SI values given in parentheses are conversions from inch-pound units and are for information only.  
1.3 The following safety hazards caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off