Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service

Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service

SCOPE
1.1 This specification covers hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties are developed by suitable heat treatment, as indicated for each alloy.
1.2 Where strength at temperature is a factor, these steels are generally limited to a maximum service temperature of 1200F [650C]. For oxidation (scaling) resistance and at low stresses, these steels are useful to 1450F [790C].
1.3 This specification is expressed in both inch-pound units and SI units; however, unless the purchase order or contract specifies the applicable M specification designation (SI units), the inch-pound units shall apply. The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

General Information

Status
Historical
Publication Date
28-Feb-2005
ICS
77.140.60 - Steel bars and rods
77.140.85 - Iron and steel forgings
Technical Committee
A01 - Steel, Stainless Steel and Related Alloys
Drafting Committee
A01.17 - Flat-Rolled and Wrought Stainless Steel
Current Stage
Ref Project

Relations

Replaces
ASTM A565-03b - Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service
Effective Date
01-Mar-2005
Replaced By
ASTM A565/A565M-05a - Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service
Effective Date
01-Sep-2005
Referred By
ASTM A484/A484M-23 - Standard Specification for General Requirements for Stainless Steel Bars, Billets, and Forgings
Effective Date
01-Mar-2005

Buy Standard

ASTM A565/A565M-05 - Standard Specification for Martensitic Stainless Steel Bars for High-Temperature ServiceASTM A565/A565M-05 - Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service
PreviousNext
Technical specification
ASTM A565/A565M-05 - Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
Designation: A 565/A 565M – 05
Standard Specification for
Martensitic Stainless Steel Bars for High-Temperature
1
Service
This standard is issued under the fixed designationA 565/A 565M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (ϵ) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* SAE J1086 Recommended Practice for Numbering Metals
3
and Alloys (UNS)
1.1 This specification covers hot-finished and cold-finished
martensitic chromium steel bars for high-temperature service.
3. Ordering Information
The mechanical properties are developed by suitable heat
3.1 It is the responsibility of the purchaser to specify all
treatment, as indicated for each alloy.
requirements that are necessary for material ordered under this
1.2 Where strength at temperature is a factor, these steels
specification. Such requirements may include, but are not
are generally limited to a maximum service temperature of
limited to, the following:
1200°F [650°C]. For oxidation (scaling) resistance and at low
3.1.1 Quantity (weight or number of pieces);
stresses, these steels are useful to 1450°F [790°C].
3.1.2 Name of material (martensitic stainless steel);
1.3 This specification is expressed in both inch-pound units
3.1.3 Form (bar, etc.);
and SI units; however, unless the purchase order or contract
3.1.4 Condition;
specifies the applicable M specification designation (SI units),
3.1.5 Finish;
the inch-pound units shall apply. The values stated in either
3.1.6 Size, or applicable dimension including diameter,
inch-pound units or SI units are to be regarded separately as
thickness, width, length, etc.;
standard. Within the text, the SI units are shown in brackets.
3.1.7 Grade designation (Table 1); and
The values stated in each system may not be exact equivalents;
3.1.8 ASTM designation number and date of issue.
therefore,eachsystemshallbeusedindependentlyoftheother.
Combining values from the two systems may result in noncon-
4. General Requirements
formance with the specification.
4.1 Product furnished to this specification shall conform to
the requirements of Specification A 484A 484/A 484M/
2. Referenced Documents
2 A 484M, including any supplementary requirements indicated
2.1 ASTM Standards:
in the purchase order. Failure to comply with the general
A 370 Test Methods and Definitions for MechanicalTesting
requirements of Specification A 484A 484/A 484M/A 484M
of Steel Products
constitutes nonconformance with this specification. In case of
A 484/A 484M Specification for General Requirements for
conflict between the requirements of this specification and
Stainless Steel Bars, Billets, and Forgings
Specification A 484A 484/A 484M/A 484M, this specification
A 751 Test Methods, Practices, and Terminology for
shall prevail.
Chemical Analysis of Steel Products
A 994 Guide for Editorial Procedures and Form of Product
5. Manufacture
SpecificationsforSteel,StainlessSteel,andRelatedAlloys
5.1 Heat Treatment:
E 527 Practice for Numbering Metals and Alloys (UNS)
5.1.1 The product forms covered in this specification may
2.2 Other Documents:
be furnished in one of the following conditions:
5.1.1.1 Condition A—Annealed,
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel, 5.1.1.2 Condition T—Heat treated (for machining),
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
5.1.1.3 Condition HT—Heat treated (for high-temperature
A01.17 on Flat-Rolled and Wrought Stainless Steel.
service), or
Current edition approved March 1, 2005. Published March 2005. Originally
5.1.1.4 Condition H—Heat treated.
approved in 1966. Last previous edition approved in 2003 as A 565 – 03b.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
3
Standards volume information, refer to the standard’s Document Summary page on Available from Society of Automotive Engineers (SAE), 400 Commonwealth
the ASTM website. Dr., Warrendale, PA 15096-0001.
*ASummary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A 565/A 565M – 05
TABLE 1 Chemical Requirements
Grade UNS Carbon Man- Phos- Sulfur Silicon Chromium Nickel Molyb- Vana- Tungsten Nitrogen Alumi- C
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM A638/A638M-23(Specification)
Standard Specification for Precipitation Hardening Iron Base Superalloy Bars, Forgings, and Forging Stock for High-Temperature Service

ABSTRACT
This specification covers hot-finished or cold-finished precipitation hardening iron base superalloy bars, forgings, and forging stock for high-temperature service. The mechanical properties of these alloys are developed by suitable solution treating and precipitation hardening treatments. Two grades of iron base alloy are covered; Grade 660 and Grade 662 (bars and forgings). The material shall meet the requirements as to stress rupture properties specified. The material shall conform to the chemical, mechanical, and metallurgical properties requirements specified.
SCOPE
1.1 This specification2 covers hot-finished or cold-finished precipitation hardening iron base superalloy bars, forgings, and forging stock for high-temperature service. The mechanical properties of these alloys are developed by suitable solution treating and precipitation hardening treatments.  
1.2 Two grades of iron base alloy are covered. Selection will depend upon design, service conditions, mechanical properties, and elevated temperature characteristics.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. SI units are shown in brackets. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 Unless the order specifies an “M” designation, the material shall be furnished to inch-pound units.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM A565/A565M-10(2017)e1(Specification)
Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service

ABSTRACT
This guide covers standard specification for hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties shall be developed by suitable heat treatment, as indicated for each alloy. The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, vanadium, tungsten, nitrogen, aluminum, columbium, and copper. The microstructure shall not contain more than 5% delta-ferrite after full heat treatment. The material shall conform to the required mechanical properties such as tensile strength, yield strength, elongation, impact strength, and Brinell hardness. The material shall also undergo stress rupture testing using a combination test bar.
SCOPE
1.1 This specification covers hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties are developed by suitable heat treatment, as indicated for each alloy.  
1.2 Where strength at temperature is a factor, these steels are generally limited to a maximum service temperature of 1200°F [650°C]. For oxidation (scaling) resistance and at low stresses, these steels are useful to 1450°F [790°C].  
1.3 This specification is expressed in both inch-pound units and SI units; however, unless the purchase order or contract specifies the applicable M specification designation (SI units), the inch-pound units shall apply. The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM A638/A638M-23(Specification)
Standard Specification for Precipitation Hardening Iron Base Superalloy Bars, Forgings, and Forging Stock for High-Temperature Service

ABSTRACT
This specification covers hot-finished or cold-finished precipitation hardening iron base superalloy bars, forgings, and forging stock for high-temperature service. The mechanical properties of these alloys are developed by suitable solution treating and precipitation hardening treatments. Two grades of iron base alloy are covered; Grade 660 and Grade 662 (bars and forgings). The material shall meet the requirements as to stress rupture properties specified. The material shall conform to the chemical, mechanical, and metallurgical properties requirements specified.
SCOPE
1.1 This specification2 covers hot-finished or cold-finished precipitation hardening iron base superalloy bars, forgings, and forging stock for high-temperature service. The mechanical properties of these alloys are developed by suitable solution treating and precipitation hardening treatments.  
1.2 Two grades of iron base alloy are covered. Selection will depend upon design, service conditions, mechanical properties, and elevated temperature characteristics.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. SI units are shown in brackets. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 Unless the order specifies an “M” designation, the material shall be furnished to inch-pound units.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B639-02(2018)(Specification)
Standard Specification for Precipitation Hardening Cobalt-Containing Alloys (UNS R30155 and UNS R30816) Rod, Bar, Forgings, and Forging Stock for High-Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation hardenable cobalt-containing alloys (UNS R30155 and UNS R30816) rod, bar, forgings, and forging stock for high temperature service. The material shall conform to the required chemical composition for carbon, manganese, silicon, phosphorus, sulfur, chromium, nickel, molybdenum, columbium, tantalum, iron, cobalt, and nitrogen. The materials shall conform to the required tensile and hardness properties such namely tensile strength, yield strength, alongation and Brinell hardness. The alloys shall also conform to the required stress-rupture properties. Dimensions such as diameter, thickness, or width, out-of-round, corners, cut lengths, straightness for cold-worked and hot-worked rod and bar shall be measured.
SCOPE
1.1 This specification covers hot- and cold-worked precipitation hardenable cobalt-containing alloys (UNS R30155 and UNS R30816)2 rod, bar, forgings, and forging stock for high-temperature service.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM A565/A565M-10(2017)e1(Specification)
Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service

ABSTRACT
This guide covers standard specification for hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties shall be developed by suitable heat treatment, as indicated for each alloy. The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, vanadium, tungsten, nitrogen, aluminum, columbium, and copper. The microstructure shall not contain more than 5% delta-ferrite after full heat treatment. The material shall conform to the required mechanical properties such as tensile strength, yield strength, elongation, impact strength, and Brinell hardness. The material shall also undergo stress rupture testing using a combination test bar.
SCOPE
1.1 This specification covers hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties are developed by suitable heat treatment, as indicated for each alloy.  
1.2 Where strength at temperature is a factor, these steels are generally limited to a maximum service temperature of 1200°F [650°C]. For oxidation (scaling) resistance and at low stresses, these steels are useful to 1450°F [790°C].  
1.3 This specification is expressed in both inch-pound units and SI units; however, unless the purchase order or contract specifies the applicable M specification designation (SI units), the inch-pound units shall apply. The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM F1210-23(Guide)
Standard Guide for Ecological Considerations for the Use of Oil Spill Dispersants in Freshwater and Other Inland Environments, Lakes and Large Water Bodies

SIGNIFICANCE AND USE
3.1 This guide is meant to aid response teams who may use it during spill response planning and spill events.  
3.2 This guide should be adapted to site specific circumstance.
SCOPE
1.1 This guide covers the use of oil spill dispersants to assist in the control of oil spills. The guide is written with the goal of minimizing the environmental impacts of oil spills; this goal is the basis on which the recommendations are made. Aesthetic and socioeconomic factors are not considered, although these and other factors are often important in spill response.  
1.2 Spill responders have available several means to control or clean up spilled oil. Chemical dispersants should be given equal consideration with other spill countermeasures.  
1.3 This is a general guide only. Oil, as used in this guide, includes crude oils and refined petroleum products. Differences between individual dispersants or between different oil products are not considered. The dispersibility of the oil with the chosen dispersant should be evaluated.  
1.4 The guide is organized by habitat type, for example, small ponds and lakes, rivers and streams, and land. It considers the use of dispersants primarily to protect habitats from impact (or to minimize impacts).  
1.5 This guide applies only to freshwater and other inland environments. It does not consider the direct application of dispersants to subsurface waters.  
1.6 In making dispersant use decisions, appropriate government authorities should be consulted as required by law.  
1.7 This guide does not address getting regulatory approval.  
1.8 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM C596-23(Test Method)
Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement

SIGNIFICANCE AND USE
4.1 This test method establishes a selected set of conditions of temperature, relative humidity and rate of evaporation of the environment to which a mortar specimen of stated composition shall be subjected for a specified period of time during which its change in length is determined and designated “drying shrinkage.”  
4.2 The drying shrinkage of mortar as determined by this test method has a linear relation to the drying shrinkage of concrete made with the same cement and exposed to the same drying conditions.4 Hence this test method may be used when it is desired to develop data on the effect of a hydraulic cement on the drying shrinkage of concrete made with that cement.
SCOPE
1.1 This test method determines the change in length on drying of mortar bars containing hydraulic cement and graded standard sand.  
1.2 The values stated in SI units are to be regarded as standard. When combined standards are referenced, the selection of measurement system is at the user’s discretion subject to the requirements of the referenced standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure).2  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1751-23(Specification)
Standard Specification for Preformed Expansion Joint Filler for Concrete Paving and Structural Construction (Nonextruding and Resilient Asphalt Types)

SCOPE
1.1 This specification covers preformed expansion joint filler having relatively little extrusion and substantial recovery after release from compression.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
Note 1: Attention is called to Specifications D1752 and D994/D994M.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM B637-23(Specification)
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for high-temperature service. Chemical analysis shall be performed on the alloy and shall conform to the chemical composition requirement in carbon, manganese, silicon, phosphorus, sulfur, chromium, cobalt, molybdenum, columbium, tantalum, titanium, aluminum, zirconium, boron, iron, copper, and nickel. The material shall follow recommended annealing treatment, solution treatment, stabilizing treatment, and precipitation hardening treatment. Tension testing, hardness testing and stress-rupture testing shall be performed on the material and shall comply to the required tensile strength, yield strength, elongation, reduction in area, and Brinell hardness.
SCOPE
1.1 This specification2 covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for moderate or high temperature service (Table 1).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM D8139-23(Specification)
Standard Specification for Semi-Rigid, Closed-Cell Polypropylene Foam, Preformed Expansion Joint Fillers for Concrete Paving and Structural Construction

SCOPE
1.1 This specification covers preformed expansion joint fillers made from closed-cell polypropylene foam materials having suitable compressibility, recovery from compression, nonextruding, and weather-resistant characteristics.  
1.1.1 Type I, closed-cell polypropylene foam.  
1.2 These joint fillers are intended for use in concrete pavements in full-depth joints. There are several variations in size with typical thicknesses of 1/2 in. (12.7 mm), 3/4 in. (19.05 mm), and 1 in. (25.4 mm); typical widths of 31/2 in. (88.9 mm), 4 in. (101.6 mm), 5 in. (127 mm), 6 in. (152.5 mm), 7 in. (177.8 mm), 8 in. (203.2 mm), or 48 in. (1.2 m) sheet; and typical lengths of 5 ft (1.52 m) and 10 ft (3.05 m).  
1.3 The values stated in inch-pound units are to be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off