Standard Guide for Testing Polymer Matrix Composite Materials

Standard Guide for Testing Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.
SCOPE
1.1 This guide summarizes the application of ASTM standard test methods (and other supporting standards) to continuous-fiber reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included, emphasizing use of standards of Committee D30 on Composite Materials.
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including non-ASTM test methods, is included in the Composite Materials Handbook (MIL-HDBK-17). Additional specific recommendations for testing textile (fabric, braided) composites are contained in Guide D 6856.
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards with SI units listed first.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Apr-2004
ICS
83.140.20 - Laminated sheets
Technical Committee
D30 - Composite Materials
Drafting Committee
D30.01 - Editorial and Resource Standards
Current Stage
Ref Project

Relations

Replaces
ASTM D4762-88(2001) - Standard Guide for Testing Automotive/Industrial Composite Materials
Effective Date
01-May-2004
Replaced By
ASTM D4762-08 - Standard Guide for Testing Polymer Matrix Composite Materials
Effective Date
01-Apr-2008
Referred By
ASTM D8509/D8509M-23 - Standard Guide for Test Method Selection and Test Specimen Design for Bolted Joint Related Properties
Effective Date
01-May-2004
Referred By
ASTM E2533-21 - Standard Guide for Nondestructive Examination of Polymer Matrix Composites Used in Aerospace Applications
Effective Date
01-May-2004
Referred By
ASTM D8069-17a - Standard Test Method for Determining Flexural Modulus of Full Section Pultruded Fiber Reinforced Polymer (FRP) Composite Members with Doubly Symmetric Cross Sections under Bending
Effective Date
01-May-2004

Buy Standard

ASTM D4762-04 - Standard Guide for Testing Polymer Matrix Composite MaterialsASTM D4762-04 - Standard Guide for Testing Polymer Matrix Composite Materials
PreviousNext
Guide
ASTM D4762-04 - Standard Guide for Testing Polymer Matrix Composite Materials
English language
16 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D4762–04
Standard Guide for
1
Testing Polymer Matrix Composite Materials
This standard is issued under the fixed designation D 4762; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope C 480 Test Method for Flexure Creep of Sandwich Con-
structions
1.1 This guide summarizes the application of ASTM stan-
C 613/C 613M Test Method for Constituent Content of
dard test methods (and other supporting standards) to
Composite Prepreg by Soxhlet Extraction
continuous-fiber reinforced polymer matrix composite materi-
D 2344/D 2344M Test Method for Short Beam Strength of
als. The most commonly used or most applicable ASTM
Composite Materials and Their Laminates
standards are included, emphasizing use of standards of Com-
D 3039/D 3039M Test Method for Tensile Properties of
mittee D30 on Composite Materials.
Polymer Matrix Composite Materials
1.2 This guide does not cover all possible standards that
D 3171 Test Method for Constituent Content of Composite
could apply to polymer matrix composites and restricts discus-
Materials
sion to the documented scope. Commonly used but non-
D 3410/D 3410M Test Method for Compressive Properties
standard industry extensions of test method scopes, such as
of Polymer Matrix Composite Materials with Unsupported
application of static test methods to fatigue testing, are not
Gage Section by Shear Loading
discussed. A more complete summary of general composite
D 3479/D 3479M Test Method for Tension-Tension Fatigue
testing standards, including non-ASTM test methods, is in-
of Polymer Matrix Composite Materials
cluded in the Composite Materials Handbook (MIL-HDBK-
2
D 3518/D 3518M TestMethodforIn-PlaneShearResponse
Additional specific recommendations for testing textile
17).
of Polymer Matrix Composite Materials by Tensile Test of
(fabric, braided) composites are contained in Guide D 6856.
a 645 Laminate
1.3 This guide does not specify a system of measurement;
D 3529/D 3529M Test Method for Matrix Solids Content
the systems specified within each of the referenced standards
and Matrix Content of Composite Prepreg
shall apply as appropriate. Note that the referenced standards
D 3530/D 3530M Test Method for Volatiles Content of
ofASTM Committee D30 are either SI-only or combined-unit
Composite Material Prepreg
standards with SI units listed first.
D 3531 TestMethodforResinFlowofCarbonFiber-Epoxy
1.4 This standard does not purport to address all of the
Prepreg
safety concerns, if any, associated with its use. It is the
D 3532 Test Method for Gel Time of Carbon Fiber-Epoxy
responsibility of the user of this standard to establish appro-
Prepreg
priate safety and health practices and determine the applica-
D 3544 Guide for Reporting Test Methods and Results on
bility of regulatory limitations prior to use.
4
High Modulus Fibers
2. Referenced Documents
D 3800 Test Method for Density of High-Modulus Fibers
3
D 3878 Terminology of Composite Materials
2.1 ASTM Standards:
D 4018 TestMethodsforPropertiesofContinuousFilament
2.1.1 Standards of Committee D30 on Composite Materials
Carbon and Graphite Fiber Tows
C 393 Test Method for Flexural Properties of Sandwich
D 4102 Test Method for Thermal Oxidative Resistance of
Constructions
Carbon Fibers
D 4255/D 4255M Test Method for In-Plane Shear Proper-
ties of Polymer Matrix Composite Materials by the Rail
1
This guide is under the jurisdiction of ASTM Committee D30 on Composite
Shear Method
Materials and is the direct responsibility of Subcommittee D30.01 on Editorial and
Resource Standards.
D 5229/D 5229M Test Method for Moisture Absorption
Current edition approved May 1, 2004. Published May 2004. Originally
Properties and Equilibrium Conditioning of Polymer Ma-
approved in 1988. Last previous edition approved in 2001 as D 4762 – 88 (2001).
2 trix Composite Materials
AvailablefromASTM,andalsofromtheU.S.DoDStandardizationDocuments
D 5379/D 5379M Test Method for Shear Properties of
Order Desk, Bldg. 4 Section D, 700 Robbins Ave., Philadelphia, PA 19111-5094,
Attn: NPODS.
Composite Materials by the V-Notched Beam Method
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
4
the ASTM website.
Withdrawn.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
D4762–04
D 5448/D 5448M Test Method for In-Plane Shear Proper- C 581 Practice for Determining
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D8387/D8387M-23(Test Method)
Standard Test Method for High Bypass – Low Bearing Interaction Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This test method determines the uniaxial high bypass - low bearing interaction response of multi-directional polymer matrix composite laminates reinforced by high-modulus fibers using a two-fastener hard point joint specimen. The scope of this test method is limited to net section (bypass) failure modes. Standard specimen configurations using fixed values of test parameters are described for this procedure. A number of test parameters may be varied within the scope of the standard, provided that the parameters are fully documented in the test report. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced composites for which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1. This test method was previously published under Test Method D7248/D7248M-17 Procedure C.  
1.2 This test method is consistent with the recommendations of Composite Materials Handbook, CMH-17, which describes the desirable attributes of a bearing/bypass interaction response test method.  
1.3 The two-fastener test configurations described in this test method are intended to provide data in the relatively high bypass, low bearing part of the composite bolted joint bearing-bypass interaction diagram. This data complements the data from filled hole tension and compression (Practice D6742/D6742M), bearing (Test Method D5961/D5961M), and low bypass/high bearing interaction (Test Method D7248/D7248M) tests.  
1.4 This test method requires careful specimen design, instrumentation, data measurement, and data analysis. The use of this test method requires close coordination between the test requestor and the test lab personnel. Test requestors need to be familiar with the data analysis procedures of this test method and should not expect test labs who are unfamiliar with this test method to be able to produce acceptable results without close coordination.  
1.5 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5.1 Within the text, the inch-pound units are shown in brackets.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    27 pages
    English language
    sale 15% off
  • Standard
    27 pages
    English language
    sale 15% off
ASTM
ASTM D3479/D3479M-19(2023)(Test Method)
Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 This test method is designed to yield tensile fatigue data for material specifications, research and development, quality assurance, and structural design and analysis. The primary test result is the fatigue life of the test specimen under a specific loading and environmental condition. Replicate tests may be used to obtain a distribution of fatigue life for specific material types, laminate stacking sequences, environments, and loading conditions. Guidance in statistical analysis of fatigue life data, such as determination of linearized stress life (S-N) or strain-life (ε-N) curves, can be found in Practice E739.  
5.2 This test method can be utilized in the study of fatigue damage in a polymer matrix composite such as the occurrence of microscopic cracks, fiber fractures, or delaminations.3 The specimen's residual strength or stiffness, or both, may change due to these damage mechanisms. The loss in stiffness may be quantified by discontinuing cyclic loading at selected cycle intervals to obtain the quasi-static axial stress-strain curve using modulus determination procedures found in Test Method D3039/D3039M. The loss in strength associated with fatigue damage may be determined by discontinuing cyclic loading to obtain the static strength using Test Method D3039/D3039M.  
Note 1: This test method may be used as a guide to conduct tension-tension variable amplitude loading. This information can be useful in the understanding of fatigue behavior of composite structures under spectrum loading conditions, but is not covered in this test method.
SCOPE
1.1 This test method determines the fatigue behavior of polymer matrix composite materials subjected to tensile cyclic loading. The composite material forms are limited to continuous-fiber or discontinuous-fiber reinforced composites for which the elastic properties are specially orthotropic with respect to the test direction. This test method is limited to unnotched test specimens subjected to constant amplitude uniaxial in-plane loading where the loading is defined in terms of a test control parameter.  
1.2 This test method presents two procedures where each defines a different test control parameter.  
1.2.1 Procedure A—A system in which the test control parameter is the load (stress) and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude load cycles. In this procedure, the test control parameter may be described using either engineering stress or applied load as a constant amplitude fatigue variable.  
1.2.2 Procedure B—A system in which the test control parameter is the strain in the loading direction and the machine is controlled so that the test specimen is subjected to repetitive constant amplitude strain cycles. In this procedure, the test control parameter may be described using engineering strain in the loading direction as a constant amplitude fatigue variable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D6873/D6873M-23(Practice)
Standard Practice for Bearing Fatigue Response of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 Refer to Guide D8509.
SCOPE
1.1 This practice provides instructions for modifying static bearing test methods to determine the fatigue behavior of composite materials subjected to cyclic bearing forces. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.  
1.2 This practice supplements Test Method D5961/D5961M with provisions for testing specimens under cyclic loading. Several important test specimen parameters (for example, fastener selection, fastener installation method, and fatigue force/stress ratio) are not mandated by this practice; however, repeatable results require that these parameters be specified and reported.  
1.3 This practice is limited to test specimens subjected to constant amplitude uniaxial loading, where the machine is controlled so that the test specimen is subjected to repetitive constant amplitude force (stress) cycles. Either engineering stress or applied force may be used as a constant amplitude fatigue variable. The repetitive loadings may be tensile, compressive, or reversed, depending upon the test specimen and procedure utilized.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D4762-23(Guide)
Standard Guide for Testing Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
4.1 This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.
SCOPE
1.1 This guide summarizes the application of ASTM standard test methods (and other supporting standards) to continuous-fiber reinforced polymer matrix composite materials. The most commonly used or most applicable ASTM standards are included, emphasizing use of standards of Committee D30 on Composite Materials.  
1.2 This guide does not cover all possible standards that could apply to polymer matrix composites and restricts discussion to the documented scope. Commonly used but non-standard industry extensions of test method scopes, such as application of static test methods to fatigue testing, are not discussed. A more complete summary of general composite testing standards, including non-ASTM test methods, is included in the Composite Materials Handbook (CMH-17).2 Additional specific recommendations for testing textile (fabric, braided) composites are contained in Guide D6856.  
1.3 This guide does not specify a system of measurement; the systems specified within each of the referenced standards shall apply as appropriate. Note that the referenced standards of ASTM Committee D30 are either SI-only or combined-unit standards with SI units listed first.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    27 pages
    English language
    sale 15% off
  • Guide
    27 pages
    English language
    sale 15% off
ASTM
ASTM D8066/D8066M-23(Practice)
Standard Practice Unnotched Compression Testing of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This practice provides supplemental instructions for the use of Test Method D6484/D6484M to determine unnotched compressive strength data for material specifications, research and development, material design allowables, and quality assurance. Factors that influence compressive strengths and shall therefore be reported include the following: material, methods of material fabrication, accuracy of lay-up, laminate stacking sequence and overall thickness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Composite properties in the test direction that may be obtained from this test method include:  
5.1.1 Unnotched compressive (UNC) strength, Fxunc,  
5.1.2 Ultimate compressive strain,  
5.1.3 Compressive (linear or chord) modulus of elasticity, Ec, and  
5.1.4 Poisson's ratio in compression.  
5.2 This practice provides a compression test method for laminates containing fibers in multiple fiber directions, particularly those combining axial (0 degree) fibers and off-axis (± θ degree) fibers. Other compression strength test methods include SACMA SRM-1 (also known as the modified D695), D3410/D3410M, D5467/D5467M, D6641/D6641M, and D7249/D7249M. The SRM-1 test uses 12.6 mm [0.50 in.] wide specimens, which is only appropriate for unidirectional tape, cross-ply [0/90]ns tape, or small unit-cell-size fabrics (e.g. 3K-70-P). Larger cell-size fabrics (for example, spread-tow 12K fabrics) should be tested with wider specimens. The standard D3410/D3410M and D6641/D6641M test fixtures do permit the use of wider specimens, for example, 25.4 mm [1.0 in.] wide, and thus can be used to test laminates containing both axial and off-axis fibers; however their gage lengths are relatively short. Test Method D5467/D5467M is intended to obtain the compressive strength of unidirectional laminates, but is expensive due to the sandwich beam confi...
SCOPE
1.1 This practice provides instructions for using the Test Method D6484/D6484M open hole compression test fixture to determine unnotched compressive strength of multi-directional laminates. The composite material forms are limited to continuous-fiber reinforced polymer matrix composites in which the laminate is both symmetric and balanced with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.2.1 Within the text the inch-pound units are shown in brackets.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D8131/D8131M-23(Practice)
Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates

SIGNIFICANCE AND USE
5.1 This test practice is designed to produce tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the tensile response and should therefore be reported include the following: materials (laminates and adhesive), methods of material preparation including surface preparation prior to bonding, lay-ups, specimen stacking sequence, joint taper ratio or step length, ply overlap length, material relative thicknesses and stiffness of the parent and repair laminates, adhesive bond stiffness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Properties in the test direction, which may be obtained from this test practice, include the following:  
5.1.1 Ultimate tensile strength (based on the nominal parent material thickness), (Fptu).  
5.1.2 Ultimate tensile strength (based on the nominal repair material thickness), (Frtu).  
5.1.3 Ultimate running force per repair ply, (Nj).
SCOPE
1.1 This test practice defines the procedure for determination of the tensile strength of a tapered or stepped joint of polymer matrix composite materials. It is applicable to secondary bonded or co-bonded laminates with either unidirectional plies or woven fabric reinforcements. The materials to be bonded may be different material systems. In the bondline, a separate adhesive material may or may not be used (example: adhesives may be used with a prepreg system or may not be used with a wet lay-up repair system). The range of acceptable test laminates and thicknesses is described in 8.2.1.  
1.2 This practice supplements Test Method D3039/D3039M for tensile loading. Several important test specimen parameters (for example, joint length, ply overlaps, step depth, and taper ratio) are not mandated by this practice, however, these parameters are required to be specified and reported to support repeatable results.  
1.3 Unidirectional (0° ply orientation) tape composites, textile composites, as well as multidirectional composite laminates, can be tested.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4.1 Within the text the inch-pound units are shown in brackets.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM D2344/D2344M-22(Test Method)
Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates

SIGNIFICANCE AND USE
5.1 In most cases, because of the complexity of internal stresses and the variety of failure modes that can occur in this specimen, it is not generally possible to relate the short-beam strength to any one material property. However, failures are normally dominated by resin and interlaminar properties, and the test results have been found to be repeatable for a given specimen geometry, material system, and stacking sequence  (4).  
5.2 Short-beam strength determined by this test method can be used for quality control and process specification purposes. It can also be used for comparative testing of composite materials, provided that failures occur consistently in the same mode (5) .  
5.3 This test method is not limited to specimens within the range specified in Section 8, but is limited to the use of a loading span length-to-specimen thickness ratio of 4.0 and a minimum specimen thickness of 2.0 mm [0.08 in.].
SCOPE
1.1 This test method determines the short-beam strength of high-modulus fiber-reinforced composite materials. The specimen is a short beam machined from a curved or a flat laminate up to 6.00 mm [0.25 in.] thick. The beam is loaded in three-point bending.  
1.2 Application of this test method is limited to continuous- or discontinuous-fiber-reinforced polymer matrix composites, for which the elastic properties are balanced and symmetric with respect to the longitudinal axis of the beam.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM E1922/E1922M-22(Test Method)
Standard Test Method for Translaminar Fracture Toughness of Laminated and Pultruded Polymer Matrix Composite Materials

SIGNIFICANCE AND USE
5.1 The parameter KTL  determined by this test method is a measure of the resistance of a polymer matrix composite laminate to notch-tip damage and effective translaminar crack growth under opening mode loading. The result is valid only for conditions in which the damage zone at the notch tip is small compared with the notch length and the in-plane specimen dimensions. Alternately, for materials exhibiting distributed damage in a larger volume, observed force-displacement and discrete damage events are still valid structural responses for certain specific engineering applications.  
5.2 This test method can serve the following purposes. In research and development, (a) KTL data can quantitatively establish the effects of fiber and matrix variables and stacking sequence of the laminate on the translaminar fracture resistance of composite laminates; and (b) quantified distributed damage measurements can be used to validate progressive composite damage models. In structural design, KTL data can, within the constraints of the specimen geometry and loading, be used to assess composite laminate resistance to damage growth from edge flaws and notches.  
5.3 The translaminar fracture toughness,  KTL, as well as distributed damage observations, determined by this test method may be a function of the testing speed and temperature. This test method is intended for room temperature and quasi-static conditions, but it can apply to other test conditions provided that the requirements of 13.2 and 13.3 are met. Application of KTL in the design of service components should be made with awareness that the test parameters specified by this test may differ from service conditions, possibly resulting in a different material response than that seen in service. Distributed damage observations are also limited to the material and geometry tested, but may be more generally applied to a variety of structural analysis validation applications.  
5.4 Not all types of laminated polymer matrix...
SCOPE
1.1 This test method covers the determination of translaminar fracture toughness, KTL, for laminated, molded, or pultruded polymer matrix composite materials of various fiber orientations using test results from monotonically loaded notched specimens. If the material response is such that the KTL calculation is not valid, alternate reporting methods are provided.  
1.2 This test method is applicable to room temperature laboratory air environments.  
1.3 Composite materials that can be tested by this test method are not limited by thickness or by type of polymer matrix or fiber, provided that the specimen sizes and the test results meet the requirements of this test method. This test method was developed primarily from test results of various carbon fiber – epoxy matrix laminates and from additional results of glass fiber – epoxy matrix, glass fiber-polyester matrix pultrusions and carbon fiber – bismaleimide matrix laminates (1-4, 5, 6).2  
1.4 A range of eccentrically loaded, single-edge-notch tension, ESE(T), specimen sizes with proportional planar dimensions is provided, but planar size may be variable and adjusted, with associated changes in the applied test load. Specimen thickness is a variable, independent of planar size.  
1.5 Specimen configurations other than those contained in this test method may be used. It is particularly important that the requirements discussed in 5.1 and 5.4 regarding contained notch-tip damage be met when using alternative specimen configurations in conjunction with the KTL calculation.  
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.6.1 Within the text, the inch-pound units are shown ...

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM D5449/D5449M-22(Test Method)
Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is designed to produce transverse compressive property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the transverse compressive response and should therefore be reported are: material, method of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties in the test direction that may be obtained from this test method are:  
5.1.1 Transverse compressive strength, σ22uc,  
5.1.2 Transverse compressive strain at failure, ε22uc,  
5.1.3 Transverse compressive modulus of elasticity, E22, and  
5.1.4 Poisson's ratio, γ21.
SCOPE
1.1 This test method determines the transverse compressive properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial compression for determination of transverse compressive properties.  
1.2 The technical content of this test method has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this test method, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The test method, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the test method will only be in response to specific requests and performed only as technical support allows.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D5450/D5450M-22(Test Method)
Standard Test Method for Transverse Tensile Properties of Hoop Wound Polymer Matrix Composite Cylinders

SIGNIFICANCE AND USE
5.1 This test method is used to produce transverse tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors which influence the transverse tensile response and should, therefore, be reported are: material, methods of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties, in the test direction, which may be obtained from this test method include:  
5.1.1 Transverse Tensile Strength,    
5.1.2 Transverse Tensile Strain at Failure,    
5.1.3 Transverse Tensile Modulus of Elasticity,  E22, and  
5.1.4 Poisson's Ratio,  υ21.
SCOPE
1.1 This test method determines the transverse tensile properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial tension for determination of transverse tensile properties.  
1.2 The technical content of this test method has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this test method, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The test method, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the test method will only be in response to specific requests and performed only as technical support allows.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.3.1 Within the text, the inch-pound units are shown in brackets.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off