ASTM

ASTM B462-10e1

(Specification)

Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service

Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service

ABSTRACT
This specification covers nickel-chromium-molybdenum-columbium (UNS N06625), nickel-chromium-molybdenum-silicon alloy (UNS N06219), and nickel-chromium-molybdenum-tungsten alloy (UNS N06650) in the form of hot-worked rod and bar and cold-worked rod. The matreial shall conform to the required chemical composition for carbon, manganese, silicon, phosphorus, sulfur, chromium, columbium, tantalum, cobalt, molybdenum, iorn, aluminum, titanium, copper, nickel, tungsten, and nitrogen. The materials shall conform to the the heat treatment and room temperature tensile properties such as tensile strength, yield strength, and elongation. Dimensions of the alloys such as diameter, thickness, or width, length and straightness shall also be determined.
SCOPE
1.1 This specification covers forged or rolled UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033* pipe flanges, forged fittings, and valves and parts intended for corrosive high-temperature service.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Sep-2010
ICS
77.150.40 - Nickel and chromium products
77.150.99 - Other products of non-ferrous metals
Technical Committee
B02 - Nonferrous Metals and Alloys
Drafting Committee
B02.07 - Refined Nickel and Cobalt and Their Alloys
Current Stage
Ref Project

Relations

Replaced By
ASTM B462-10e2 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045,
Effective Date
01-Oct-2010

Buy Standard

ASTM B462-10e1 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature ServiceASTM B462-10e1 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service
PreviousNext
Technical specification
ASTM B462-10e1 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM B462-10e1 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature ServiceREDLINE ASTM B462-10e1 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service
PreviousNext
Technical specification
REDLINE ASTM B462-10e1 - Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service
English language
6 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
´1
Designation:B462 −10
StandardSpecification for
Forged or Rolled UNS N06030, UNS N06022, UNS N06035,
UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS
N08020, UNS N08024, UNS N08026, UNS N08367, UNS
N10276, UNS N10665, UNS N10675, UNS N10629, UNS
N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe
Flanges, Forged Fittings, and Valves and Parts for
1
Corrosive High-Temperature Service
This standard is issued under the fixed designation B462; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1
´ NOTE—The chromium range for UNS N06022 in Table 1 was corrected editorially in January 2011.
1. Scope* 2. Referenced Documents
2 3
1.1 This specification covers forged or rolled UNS 2.1 ASTM Standards:
N06030, UNS N06035, UNS N06022, UNS N06200, UNS A262 Practices for Detecting Susceptibility to Intergranular
N06059, UNS N10362, UNS N06686, UNS N08020, UNS Attack in Austenitic Stainless Steels
N08024, UNS N08026, UNS N08367, UNS N10276, UNS B166 Specification for Nickel-Chromium-IronAlloys (UNS
N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06600, N06601, N06603, N06690, N06693, N06025,
N06045, UNS N06025, and UNS R20033* pipe flanges, N06045, and N06696), Nickel-Chromium-Cobalt-
forged fittings, and valves and parts intended for corrosive Molybdenum Alloy (UNS N06617), and Nickel-Iron-
high-temperature service. Chromium-Tungsten Alloy (UNS N06674) Rod, Bar, and
Wire
1.2 The values stated in inch-pound units are to be regarded
B335 Specification for Nickel-Molybdenum Alloy Rod
as standard. The values given in parentheses are mathematical
B408 Specification for Nickel-Iron-Chromium Alloy Rod
conversions to SI units that are provided for information only
and Bar
and are not considered standard.
B472 Specification for Nickel Alloy Billets and Bars for
1.3 This standard does not purport to address all of the
Reforging
safety concerns, if any, associated with its use. It is the
B473 Specification for UNS N08020, UNS N08024, and
responsibility of the user of this standard to become familiar
UNS N08026 Nickel Alloy Bar and Wire
with all hazards including those identified in the appropriate
B574 Specification for Low-Carbon Nickel-Chromium-
Material Safety Data Sheet (MSDS) for this product/material
Molybdenum, Low-Carbon Nickel-Molybdenum-
as provided by the manufacturer, to establish appropriate
Chromium, Low-Carbon Nickel-Molybdenum-
safety and health practices, and determine the applicability of
Chromium-Tantalum, Low-Carbon Nickel-Chromium-
regulatory limitations prior to use.
Molybdenum-Copper, and Low-Carbon Nickel-
Chromium-Molybdenum-Tungsten Alloy Rod
1 B581 Specification for Nickel-Chromium-Iron-
This specification is under the jurisdiction of ASTM Committee B02 on
Molybdenum-Copper Alloy Rod
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
B02.07 on Refined Nickel and Cobalt and Their Alloys.
B649 Specification for Ni-Fe-Cr-Mo-Cu-N Low-CarbonAl-
Current edition approved Oct. 1, 2010. Published October 2010. Originally
loys (UNS N08925, UNS N08031, UNS N08354, and
approved in 1967. Last previous edition approved in 2006 as B462 – 06. DOI:
10.1520/B0462-10E01.
2 3
For ASME Boiler and Pressure Vessel Code applications see related Specifi- For referenced ASTM standards, visit the ASTM website, www.astm.org, or
cation SB-462 in Section II of that Code. contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
* NewdesignationestablishedinaccordancewithPracticeE527andSAEJ1086, Standards volume information, refer to the standard’s Document Summary page on
Practice for Numbering Metals and Alloys (UNS). the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
´1
B462−10
UNS N08926), and Cr-Ni-Fe-N Low-CarbonAlloy (UNS 5.2.1 Material for forging shall consist of a billet, bar, or
R20033) Bar and Wire, and Ni-Cr-Fe-Mo-N Alloy (UNS forging produced in accordance with Specifications B166,
N08936) Wire B335, B408, B 462, B472, B473, B574, B581, B649,or B691.
B691 Specification for Iron-Nickel-Chromium- 5.2.2 The material shall be forged by hammering, pressing,
Molybdenum Alloys (UNS N08366 and UNS N08367) rolling, extruding, or upsetting; it shall be brought as nearly as
Rod, Bar, and Wire practicable to the finished shape and size by hot working; and
B880 Specification for General Requirements for Chemical shall be so processed as to cause metal flow during the
Check Analysis Limits for
...

This document is not anASTM standard and is intended only to provide the user of anASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´1
Designation:B462–10 Designation: B462 – 10
Standard Specification for
Forged or Rolled UNS N06030, UNS N06022, UNS N06035,
UNS N06200, UNS N06059, UNS N10362, UNS N06686, UNS
N08020, UNS N08024, UNS N08026, UNS N08367, UNS
N10276, UNS N10665, UNS N10675, UNS N10629, UNS
N08031, UNS N06045, UNS N06025, UNS R20033 Alloy Pipe
Flanges, Forged Fittings, and Valves and Parts for
1
Corrosive High-Temperature Service
This standard is issued under the fixed designation B462; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1
´ NOTE—The chromium range for UNS N06022 in Table 1 was corrected editorially in January 2011.
1. Scope*
2
1.1 This specification covers forged or rolled UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N06059, UNS
N10362, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675,
UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033* pipe flanges, forged fittings, and valves and parts
intended for corrosive high-temperature service.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical
conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data
Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and
determine the applicability of regulatory limitations prior to use.
2. Referenced Documents
3
2.1 ASTM Standards:
A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels
B166 Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, N06045,
and N06696), Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617), and Nickel-Iron-Chromium-Tungsten Alloy
(UNS N06674) Rod, Bar, and Wire
B335 Specification for Nickel-Molybdenum Alloy Rod
B408 Specification for Nickel-Iron-Chromium Alloy Rod and Bar
B472 Specification for Nickel Alloy Billets and Bars for Reforging
B473 Specification for UNS N08020, UNS N08024, and UNS N08026 Nickel Alloy Bar and Wire
B574 Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium, Low-
Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon
Nickel-Chromium-Molybdenum-tTungsten Alloy Rod
B581 Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Rod
B649 Specification for Ni-Fe-Cr-Mo-Cu-N Low-Carbon Alloys (UNS N08925, UNS N08031, UNS N08354, and UNS
N08926), and Cr-Ni-Fe-N Low-Carbon Alloy (UNS R20033) Bar and Wire, and Ni-Cr-Fe-Mo-N Alloy (UNS N08936) Wire
B691 Specification for Iron-Nickel-Chromium-Molybdenum Alloys (UNS N08366 and UNS N08367) Rod, Bar, and Wire
1
ThisspecificationisunderthejurisdictionofASTMCommitteeB02onNonferrousMetalsandAlloysandisthedirectresponsibilityofSubcommitteeB02.07onRefined
Nickel and Cobalt and Their Alloys.
Current edition approved Oct. 1, 2010. Published October 2010. Originally approved in 1967. Last previous edition approved in 2006 as B462 – 06. DOI:
10.1520/B0462-10E01.
2
For ASME Boiler and Pressure Vessel Code applications see related Specification SB-462 in Section II of that Code.
* New designation established in accordance with Practice E527 and SAE J1086, Practice for Numbering Metals and Alloys (UNS).
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright ©ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA19428-2959, United States.
1

---------------------- Page: 1 ----------------------
´1
B462 – 10
B880 Specification for General Requirements for Chemical CheckAnalysis Limits for Nickel, NickelAlloys and CobaltAlloys
E8 Test Methods for Tension Testing of Metallic Materials
E527 Practice for Numbering Metals and Alloys
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM F1210-23(Guide)
Standard Guide for Ecological Considerations for the Use of Oil Spill Dispersants in Freshwater and Other Inland Environments, Lakes and Large Water Bodies

SIGNIFICANCE AND USE
3.1 This guide is meant to aid response teams who may use it during spill response planning and spill events.  
3.2 This guide should be adapted to site specific circumstance.
SCOPE
1.1 This guide covers the use of oil spill dispersants to assist in the control of oil spills. The guide is written with the goal of minimizing the environmental impacts of oil spills; this goal is the basis on which the recommendations are made. Aesthetic and socioeconomic factors are not considered, although these and other factors are often important in spill response.  
1.2 Spill responders have available several means to control or clean up spilled oil. Chemical dispersants should be given equal consideration with other spill countermeasures.  
1.3 This is a general guide only. Oil, as used in this guide, includes crude oils and refined petroleum products. Differences between individual dispersants or between different oil products are not considered. The dispersibility of the oil with the chosen dispersant should be evaluated.  
1.4 The guide is organized by habitat type, for example, small ponds and lakes, rivers and streams, and land. It considers the use of dispersants primarily to protect habitats from impact (or to minimize impacts).  
1.5 This guide applies only to freshwater and other inland environments. It does not consider the direct application of dispersants to subsurface waters.  
1.6 In making dispersant use decisions, appropriate government authorities should be consulted as required by law.  
1.7 This guide does not address getting regulatory approval.  
1.8 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM C596-23(Test Method)
Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement

SIGNIFICANCE AND USE
4.1 This test method establishes a selected set of conditions of temperature, relative humidity and rate of evaporation of the environment to which a mortar specimen of stated composition shall be subjected for a specified period of time during which its change in length is determined and designated “drying shrinkage.”  
4.2 The drying shrinkage of mortar as determined by this test method has a linear relation to the drying shrinkage of concrete made with the same cement and exposed to the same drying conditions.4 Hence this test method may be used when it is desired to develop data on the effect of a hydraulic cement on the drying shrinkage of concrete made with that cement.
SCOPE
1.1 This test method determines the change in length on drying of mortar bars containing hydraulic cement and graded standard sand.  
1.2 The values stated in SI units are to be regarded as standard. When combined standards are referenced, the selection of measurement system is at the user’s discretion subject to the requirements of the referenced standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure).2  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1751-23(Specification)
Standard Specification for Preformed Expansion Joint Filler for Concrete Paving and Structural Construction (Nonextruding and Resilient Asphalt Types)

SCOPE
1.1 This specification covers preformed expansion joint filler having relatively little extrusion and substantial recovery after release from compression.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
Note 1: Attention is called to Specifications D1752 and D994/D994M.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM B637-23(Specification)
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for high-temperature service. Chemical analysis shall be performed on the alloy and shall conform to the chemical composition requirement in carbon, manganese, silicon, phosphorus, sulfur, chromium, cobalt, molybdenum, columbium, tantalum, titanium, aluminum, zirconium, boron, iron, copper, and nickel. The material shall follow recommended annealing treatment, solution treatment, stabilizing treatment, and precipitation hardening treatment. Tension testing, hardness testing and stress-rupture testing shall be performed on the material and shall comply to the required tensile strength, yield strength, elongation, reduction in area, and Brinell hardness.
SCOPE
1.1 This specification2 covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for moderate or high temperature service (Table 1).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM D8139-23(Specification)
Standard Specification for Semi-Rigid, Closed-Cell Polypropylene Foam, Preformed Expansion Joint Fillers for Concrete Paving and Structural Construction

SCOPE
1.1 This specification covers preformed expansion joint fillers made from closed-cell polypropylene foam materials having suitable compressibility, recovery from compression, nonextruding, and weather-resistant characteristics.  
1.1.1 Type I, closed-cell polypropylene foam.  
1.2 These joint fillers are intended for use in concrete pavements in full-depth joints. There are several variations in size with typical thicknesses of 1/2 in. (12.7 mm), 3/4 in. (19.05 mm), and 1 in. (25.4 mm); typical widths of 31/2 in. (88.9 mm), 4 in. (101.6 mm), 5 in. (127 mm), 6 in. (152.5 mm), 7 in. (177.8 mm), 8 in. (203.2 mm), or 48 in. (1.2 m) sheet; and typical lengths of 5 ft (1.52 m) and 10 ft (3.05 m).  
1.3 The values stated in inch-pound units are to be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM F3337-23(Guide)
Standard Guide for Taking Property and Behavior Measurements on Weathered Fractions of Oil

SIGNIFICANCE AND USE
5.1 A standard procedure is necessary to establish property changes for spilled oils or petroleum products at different oil weathering stages.  
5.2 This procedure employs standardized equipment, and test procedures.  
5.3 This procedure should be performed at the stages of weathering corresponding to the spill conditions of interest.
SCOPE
1.1 This guide summarizes methods to fractionate oil by evaporative weathering and then measure the properties and behavior of the weathered oil. The results of this guide can provide oil behavior data for input into oil spill models and response method selection.  
1.2 This guide covers general procedures for oil weathering and behavior and does not cover all possible procedures which may be applicable to this topic.  
1.3 The results obtained using this guide are intended to provide baseline data for the behavior of oil and petroleum products when spilled and input to oil spill models.  
1.4 The results obtained using this guide can be used directly to predict certain facets of oil spill behavior or as input to oil spill models.  
1.5 The accuracy of the guide depends very much on the representative nature of the oil sample used. Certain oils can have different properties depending on their chemical contents at the moment a sample is taken.  
1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    4 pages
    English language
    sale 15% off
  • Guide
    4 pages
    English language
    sale 15% off
ASTM
ASTM D6390-23(Test Method)
Standard Test Method for Determination of Draindown Characteristics in Uncompacted Asphalt Mixtures

SIGNIFICANCE AND USE
5.1 This test method can be used to determine whether the amount of draindown measured for a given asphalt mixture is within specified acceptable levels. The test provides an evaluation of the draindown potential of an asphalt mixture during mixture design and/or during field production. This test is primarily used for mixtures with high coarse aggregate content such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the amount of draindown in an uncompacted asphalt mixture sample when the sample is held at elevated temperatures comparable to those encountered during the production, storage, transport, and placement of the mixture. The test is particularly applicable to mixtures such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM B472-23(Specification)
Standard Specification for Nickel Alloy Billets and Bars for Reforging

ABSTRACT
This specification covers UNS N06002, UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N06230, UNS N06600, UNS N06617, UNS N06625, UNS N08020, UNS N08026, UNS N08024, UNS N08120, UNS N08926, UNS N08367, UNS N10242, UNS N10276, UNS N10665, UNS N10675, UNS N12160, UNS R20033, UNS N06059, UNS N06686, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R30556 nickel alloy billets and bars for reforging. The products shall be hot worked from ingots by rolling, forging, extruding, hammering, or pressing. The material shall conform to the chemical composition requirements prescribed by the reference material. The chemical composition of the material shall be determined by chemical analysis in accordance with test method E1473.
SCOPE
1.1 This specification covers UNS N06002, UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N10362, UNS N06230, UNS N06600, UNS N06617, UNS N06625, UNS N08020, UNS N08026, UNS N08024, UNS N08120, UNS N08926, UNS N08367, UNS N10242, UNS N10276, UNS N10665, UNS N10675, UNS N12160, UNS R20033, UNS N06059, UNS N06686, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS N06699, and UNS R305562 billets and bars for reforging.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM D545-23(Test Method)
Standard Test Methods for Preformed Expansion Joint Fillers for Concrete Construction (Nonextruding and Resilient Types)

SIGNIFICANCE AND USE
3.1 The compression resistance perpendicular to the faces, the resistance to the extrusion during compression, and the ability to recover after release of the load are indicative of a joint filler's ability to continuously fill a concrete expansion joint and thereby prevent damage that might otherwise occur during thermal expansion. The asphalt content is a measure of the fiber-type joint filler's durability and life expectancy. In the case of cork-type fillers, the resistance to water absorption and resistance to boiling hydrochloric acid are relative measures of durability and life expectancy.
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 These test methods cover the physical properties associated with preformed expansion joint fillers. The test methods include:    
Property  
Section  
Expansion in Boiling Water  
7.1  
Recovery and Compression  
7.2  
Extrusion  
7.3  
Boiling in Hydrochloric Acid  
7.4  
Asphalt Content  
7.5  
Water Absorption  
7.6  
Density  
7.7
Note 1: Specific test methods are applicable only to certain types of joint fillers, as stated herein.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D517-23(Specification)
Standard Specification for Asphalt Plank

ABSTRACT
This specification covers asphalt plank used for bridge decks as well as for industrial floors. Asphalt planks shall be classified according to usage: Type Ia; Type Ib; and Type II. Asphalt plank shall be formed from a mixture of asphalt, fibers, modifiers, or a combination thereof, and mineral filler in such a manner as to produce a uniformly dense mass. The following test methods shall be intended to measure those attributes necessary to measure the ability of asphalt plank to provide a reasonably long and satisfactory service: absorption; brittleness; dimensions; and hardness.
SCOPE
1.1 This specification covers asphalt plank used for bridge decks as well as for industrial floors.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off