ASTM B209/B209M-21

Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate

SCOPE
1.1 This specification2 covers aluminum and aluminum-alloy flat sheet, coiled sheet, and plate in the alloys (Note 1) and tempers shown in Tables 2, 3, 4, and 5, and in the following finishes:  
1.1.1 Plate in all alloys and sheet in heat-treatable alloys: mill finish.  
1.1.2 Sheet in nonheat-treatable alloys: mill finish, one-side bright mill finish, standard one-side bright finish, and standard two-sides bright finish.  
1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1M. The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527.
Note 1: Throughout this specification, use of the term alloy in the general sense includes aluminum as well as aluminum alloy.
Note 2: See Specification B632/B632M for tread plate.
Note 3: See Specification B928/B928M for 5xxx-H116 and 5xxx-H321 aluminum alloys containing 3 % or more nominal magnesium and intended for marine service and similar environments. Other alloy-temper products listed in this specification, which do not require the additional corrosion testing/capability called out in Specification B928/B928M, may be suitable for marine and similar environment applications.  
1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

• Status: Historical
• Publication Date: 30-Apr-2021
• ICS: 77.150.10 - Aluminium products
• Technical Committee: B07 - Light Metals and Alloys
• Drafting Committee: B07.03 - Aluminum Alloy Wrought Products

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B209/B209M −21
Standard Specification for
1
Aluminum and Aluminum-Alloy Sheet and Plate
This standard is issued under the fixed designation B209/B209M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope* responsibility of the user of this standard to establish appro-
2 priate safety, health, and environmental practices and deter-
1.1 This specification covers aluminum and aluminum-
mine the applicability of regulatory limitations prior to use.
alloy flat sheet, coiled sheet, and plate in the alloys (Note 1)
1.6 This international standard was developed in accor-
and tempers shown in Tables 2, 3, 4, and 5, and in the
dance with internationally recognized principles on standard-
following finishes:
ization established in the Decision on Principles for the
1.1.1 Plate in all alloys and sheet in heat-treatable alloys:
Development of International Standards, Guides and Recom-
mill finish.
mendations issued by the World Trade Organization Technical
1.1.2 Sheet in nonheat-treatable alloys: mill finish, one-side
Barriers to Trade (TBT) Committee.
bright mill finish, standard one-side bright finish, and standard
two-sides bright finish.
2. Referenced Documents
1.2 Alloy and temper designations are in accordance with
2.1 The following documents of the issue in effect on date
ANSI H35.1/H35.1M. The equivalent Unified Numbering
of material purchase form a part of this specification to the
SystemalloydesignationsarethoseofTable1precededbyA9,
extent referenced herein:
for example, A91100 for aluminum 1100 in accordance with
3
2.2 ASTM Standards:
Practice E527.
B548Test Method for Ultrasonic Inspection of Aluminum-
NOTE 1—Throughout this specification, use of the term alloy in the
Alloy Plate for Pressure Vessels
general sense includes aluminum as well as aluminum alloy.
B557Test Methods for Tension Testing Wrought and Cast
NOTE 2—See Specification B632/B632M for tread plate.
NOTE 3—See Specification B928/B928M for 5xxx-H116 and 5xxx- Aluminum- and Magnesium-Alloy Products
H321 aluminum alloys containing 3% or more nominal magnesium and
B557MTest Methods forTensionTestingWrought and Cast
intended for marine service and similar environments. Other alloy-temper
Aluminum- and Magnesium-Alloy Products (Metric)
products listed in this specification, which do not require the additional
B594Practice for Ultrasonic Inspection ofAluminum-Alloy
corrosion testing/capability called out in Specification B928/B928M, may
Wrought Products
be suitable for marine and similar environment applications.
B632/B632M Specification for Aluminum-Alloy Rolled
1.3 For acceptance criteria for inclusion of new aluminum
Tread Plate
and aluminum alloys in this specification, see Annex A2.
B660Practices for Packaging/Packing of Aluminum and
1.4 The values stated in either SI units or inch-pound units
Magnesium Products
are to be regarded separately as standard. The values stated in
B666/B666MPractice for Identification Marking of Alumi-
each system are not necessarily exact equivalents; therefore, to
num and Magnesium Products
ensure conformance with the standard, each system shall be
B881Terminology Relating toAluminum- and Magnesium-
used independently of the other, and values from the two
Alloy Products
systems shall not be combined.
B918/B918MPractice for Heat Treatment of Wrought Alu-
1.5 This standard does not purport to address all of the minum Alloys
safety concerns, if any, associated with its use. It is the B928/B928M Specification for High Magnesium
Aluminum-AlloyProductsforMarineServiceandSimilar
Environments
1
This specification is under the jurisdiction ofASTM Committee B07 on Light
B947Practice for Hot Rolling Mill Solution HeatTreatment
Metals and Alloys and is the direct responsibility of Subcommittee B07.03 on
Aluminum Alloy Wrought Products.
Current edition approved May 1, 2021. Published June 2021. Originally
3
approved in 1946. Last previous edition approved in 2014 as B209–14. DOI: For referenced ASTM standards, visit the ASTM website, www.astm.org, or
10.1520/B0209_B0209M-21. contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
2
For ASME Boiler and Pressure Vessel Code applications see related Specifi- Standards volume information, refer to the standard’s Document Summary page on
cation SB-209 in Section II of that Code. the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: B209 − 14 B209/B209M − 21
Standard Specification for
1
Aluminum and Aluminum-Alloy Sheet and Plate
This standard is issued under the fixed designation B209;B209/B209M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope*
2
1.1 This specification covers aluminum and aluminum-alloy flat sheet, coiled sheet, and plate in the alloys (Note 1) and tempers
shown in Tables 2 and 3,2, 3, 4, and 5, and in the following finishes:
1.1.1 Plate in all alloys and sheet in heat-treatable alloys: mill finish.
1.1.2 Sheet in nonheat-treatable alloys: mill finish, one-side bright mill finish, standard one-side bright finish, and standard
two-sides bright finish.
1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1(M).H35.1/H35.1M. The equivalent Unified
Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance
with Practice E527.
NOTE 1—Throughout this specification, use of the term alloy in the general sense includes aluminum as well as aluminum alloy.
NOTE 2—See Specification B632/B632M for tread plate.
NOTE 3—See Specification B928/B928M for 5xxx-H116 and 5xxx-H321 aluminum alloys containing 3 % or more nominal magnesium and intended for
marine service and similar environments. Other alloy-temper products listed in this specification, which do not require the additional corrosion
testing/capability called out in ASTMSpecification B928/B928M, may be suitable for marine and similar environment applications.
1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.
1.4 This specification is the inch-pound companion to SpecificationThe values stated in either SI units or inch-pound units are to
be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure
conformance with the standard, each system shall B209M; therefore, no SI equivalents are presented in the specification.be used
independently of the other, and values from the two systems shall not be combined.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety safety, health, and healthenvironmental practices and determine the
applicability of regulatory limitations prior to use.
1
This specification is under the jurisdiction of ASTM Committee B07 on Light Metals and Alloys and is the direct responsibility of Subcommittee B07.03 on Aluminum
Alloy Wrought Products.
Current edition approved Nov. 1, 2014May 1, 2021. Published November 2014June 2021. Originally approved in 1946. Last previous edition approved in 20102014 as
B209 – 10.B209 – 14. DOI: 10.1520/B0209-14.10.1520/B0209_B0209M-21.
2
For ASME Boiler and Pressure Vessel Code applications see related Specification SB-209 in Section II of that Code.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
B209/B209M − 21
1.6 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2.1 The following documents of the issue in effect on date of material purchase form a part of this specificationspecification to
the extent referenced herein:
3
2.2 ASTM Standards:
B548 Test Method for Ultrasonic Inspection of Aluminum-Alloy Plate for Pressure Vessels
B557 Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
B557M Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric)
B594 Practice for Ultrasonic Inspection of Aluminum-Alloy Wrought Products
B632/B632M Specification for Aluminum-Alloy Rolled Tread Plate
B660 Practices for Packaging/Packing of Aluminum and Magnesium Products
B666/B
...