(Practice)

Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal

Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal

SIGNIFICANCE AND USE
Primers and primer surfacers may be used over many different surfaces top coated with one or more of a variety of coatings and subjected to many kinds of wear and exposure.
The selection of the tests to be used for any given product or system must be governed by experience and by the requirement agreed upon between the producer and the user.
SCOPE
1.1 This practice covers the selection and use of procedures for testing primers and primer surfacers. The test methods included are listed in Table 1.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
14-May-2005
ICS
87.040 - Paints and varnishes
Technical Committee
D01 - Paint and Related Coatings, Materials, and Applications
Drafting Committee
D01.55 - Factory Applied Coatings on Preformed Products
Current Stage
Ref Project

Relations

Replaces
ASTM D3322-82(2001) - Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal
Effective Date
15-May-2005
Replaced By
ASTM D3322-82(2011) - Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal
Effective Date
01-Jun-2011

Buy Standard

ASTM D3322-82(2005) - Standard Practice for Testing Primers and Primer Surfacers Over Preformed MetalASTM D3322-82(2005) - Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal
PreviousNext
Standard
ASTM D3322-82(2005) - Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D3322–82(Reapproved2005)
Standard Practice for
Testing Primers and Primer Surfacers Over Preformed
1
Metal
This standard is issued under the fixed designation D3322; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope D661 Test Method for Evaluating Degree of Cracking of
Exterior Paints
1.1 This practice covers the selection and use of procedures
D714 Test Method for Evaluating Degree of Blistering of
for testing primers and primer surfacers. The test methods
Paints
included are listed in Table 1.
D823 Practices for Producing Films of Uniform Thickness
1.2 The values stated in SI units are to be regarded as the
of Paint, Varnish, and Related Products on Test Panels
standard. The values given in parentheses are for information
D870 Practice for Testing Water Resistance of Coatings
only.
Using Water Immersion
1.3 This standard does not purport to address all of the
D968 Test Methods for Abrasion Resistance of Organic
safety concerns, if any, associated with its use. It is the
Coatings by Falling Abrasive
responsibility of the user of this standard to establish appro-
D1005 Test Method for Measurement of Dry-Film Thick-
priate safety and health practices and determine the applica-
ness of Organic Coatings Using Micrometers
bility of regulatory limitations prior to use.
D1186 Test Methods for Nondestructive Measurement of
2. Referenced Documents Dry Film Thickness of Nonmagnetic Coatings Applied to
3
2
a Ferrous Base
2.1 ASTM Standards:
D1308 Test Method for Effect of Household Chemicals on
B117 Practice for Operating Salt Spray (Fog) Apparatus
Clear and Pigmented Organic Finishes
C540 Test Method for Image Gloss of Porcelain Enamel
3
D1400 Test Method for Nondestructive Measurement of
Surfaces
DryFilmThicknessofNonconductiveCoatingsAppliedto
D16 Terminology for Paint, Related Coatings, Materials,
3
a Nonferrous Metal Base
and Applications
D1474 Test Methods for Indentation Hardness of Organic
D522 Test Methods for Mandrel Bend Test of Attached
Coatings
Organic Coatings
D1640 TestMethodsforDrying,Curing,orFilmFormation
D523 Test Method for Specular Gloss
of Organic Coatings at Room Temperature
D609 Practice for Preparation of Cold-Rolled Steel Panels
D1729 Practice for Visual Appraisal of Colors and Color
for Testing Paint, Varnish, Conversion Coatings, and
Differences of Diffusely-Illuminated Opaque Materials
Related Coating Products
D1730 Practices for Preparation of Aluminum and
D610 Practice for Evaluating Degree of Rusting on Painted
Aluminum-Alloy Surfaces for Painting
Steel Surfaces
D1731 Practices for Preparation of Hot-Dip Aluminum
D658 Test Method for Abrasion Resistance of Organic
3
Surfaces for Painting
Coatings by Air Blast Abrasive
D1732 Practices for Preparation of Magnesium Alloy Sur-
D660 Test Method for Evaluating Degree of Checking of
faces for Painting
Exterior Paints
D1733 Method of Preparation of Aluminum Alloy Panels
3
for Testing Paint, Varnish, Lacquer, and Related Products
1
This practice is under the jurisdiction of ASTM Committee D01 on Paint and D1735 Practice for Testing Water Resistance of Coatings
Related Coatings, Materials, and Applications and is the direct responsibility of
Using Water Fog Apparatus
Subcommittee D01.55 on Factory Applied Coatings on Preformed Products.
D1737 Test Method for Elongation of Attached Organic
Current edition approved May 15, 2005. Published June 2005. Originally
3
Coatings with Cylindrical Mandrel Apparatus
approved in 1974. Last previous edition approved in 2001 as D3322 – 82 (2001).
DOI: 10.1520/D3322-82R05.
D2091 Test Method for Print Resistance of Lacquers
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
D2092 Guide for Preparation of Zinc-Coated (Galvanized)
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
3
Steel Surfaces for Painting
Standards volume information, refer to the standard’s Document Summary page on
D2197 Test Method for Adhesion of Organic Coatings by
the ASTM website.
3
Withdrawn. The last approved version of this historical standard is referenced
Scrape Adhesion
on www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
D3322–82 (2005)
TABLE 1 Test Methods
D2201 Practice for Preparation of Zinc-Coated and Zinc-
Alloy-Coated Steel Panels for Testing Paint and Related
Property Section ASTM Federal Test
Coating Products
Method Method
D2244 Practice for Calculation of Color Tolerances and
Specification
No. 141B
Color Diffe
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D7190-10(2023)(Practice)
Standard Practice to Evaluate Leaching of Water-Soluble Materials from Latex Paint Films

SIGNIFICANCE AND USE
4.1 Surfactant staining is a common problem with exterior house paints, particularly when subjected to humid environments (such as morning dew) shortly after application.  
4.2 Interior paints used in humid areas such as kitchens and bathrooms may also experience surfactant staining.  
4.3 Leaching of water-soluble materials may be dependent on colorant dispersions that are mixed into tint base paints. Other paint components may also affect the leaching of water-soluble materials.
SCOPE
1.1 This practice covers the ability of a latex paint film to resist staining caused by the leaching of water-soluble materials when contacted with water shortly after application.  
1.2 Water staining is attributed to the leaching of surfactants or other water-soluble materials from a paint film.  
1.3 The values stated in SI units are to be regarded as standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4214-23(Test Method)
Standard Test Methods for Evaluating the Degree of Chalking of Exterior Paint Films

SIGNIFICANCE AND USE
4.1 The procedures provide a broad range of techniques and photographic references to evaluate chalking of exterior paints.
SCOPE
1.1 These test methods cover the evaluation of the degree of chalking on white or tinted exterior paint films. These test methods describe the procedures recommended for transferring the chalk to a fabric or fingertip, which is then compared to photographic reference standards, or in the case of adhesive tapes, compared to a reflectance table or photographic reference standards, to determine the degree of chalking.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D4147-18(2023)(Practice)
Standard Practice for Applying Coil Coatings Using Wire-Wound Drawdown Bars

SIGNIFICANCE AND USE
3.1 This practice is useful in the laboratory to simulate roll-coated films.
SCOPE
1.1 This practice covers a procedure for applying a coil coating film of uniform thickness on a flat metal panel using wire-wound drawdown bars.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4287-00(2023)(Test Method)
Standard Test Method for High-Shear Viscosity Using a Cone/Plate Viscometer

SIGNIFICANCE AND USE
4.1 The viscosity value obtained by this test method gives information about the flow properties of the material under high-shear conditions similar to those encountered during application: brushing (see Test Method D4958), spraying, electrostatic disk, or roll coating.  
4.2 This test method is suitable for all paints and varnishes whether they are Newtonian in behavior or not. However, due to the narrow gap between the stationary and rotary parts of high-shear viscometers, this test method is more reproducible for paints having finer pigment dispersions as determined by Test Method D1210.
SCOPE
1.1 This test method covers the determination of the viscosity of paints, varnishes, and related products at a rate of shear of 12 000 s−1.  
1.2 Paints and varnishes that dry very rapidly may not give reproducible results with this test method. Measurements made at elevated temperatures may also give poor precision due to loss of volatiles and to drying.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D16-23(Terminology)
Standard Terminology for Paint, Related Coatings, Materials, and Applications

SCOPE
1.1 This standard consists of technical terms used in standards under the jurisdiction of ASTM Committee D01 (on Paint and Related Coatings, Materials, and Applications), and of definitions suitable for use in these standards.
Note 1: When any definition in this standards is quoted or published out of the context of this standard, editorially insert the following delimiting statement “for paints and related coatings, materials, and applications” after the dash following the term (in the absence of an existing delimiting statement). This will limit the filed of application of the term and definition to that approved by this committee.  
1.2 In this terminology standard, definitions used in other ASTM standards are indicated by following the definition with the designation of that standard. In some cases, a relevant D01 subcommittee is also listed. Definitions influenced by those used by other organizations are indicated by the acronym of the organization. Primary terms are given in bold, while narrower and unapproved terms are given in italics.  
1.3 There are several specialized terminology standards under the jurisdiction of Committee D01, as follows: D804, D1695, D6440, D6488, and D7188. Few definitions from those standards are included in Terminology D16. Therefore, in searches for definitions of paints and coatings terms, these standards should be included where appropriate.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    10 pages
    English language
    sale 15% off
  • Standard
    10 pages
    English language
    sale 15% off
ASTM
ASTM D6762-18(2023)(Test Method)
Standard Test Method for Determining the Hiding Power of Paint by Visual Evaluation of Spray Applied Coatings

SIGNIFICANCE AND USE
5.1 This test method determines hiding power of a test paint by visual evaluation of a spray applied coating.
Note 1: Test Method D2805 describes an instrumental method for determining hiding power. The paint film is applied at a uniform thickness (for example with a doctor blade), the film thickness is measured rigorously, and the opacity is determined photometrically. Hiding power is thereby determined with a high degree of precision.  
5.2 Test Method D6762 is less precise than Test Method D2805, but is commonly used since it is more closely related to the application characteristics of the paint and is simpler in concept and evaluation.
SCOPE
1.1 This test method provides for the quantitative visual determination of the film thickness required to achieve full hiding. This film thickness is considered to be the hiding power of a test paint.  
1.2 This method applies only to spray applied coatings but its concepts are valid for other methods of application as well.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D2805-11(2023)(Test Method)
Standard Test Method for Hiding Power of Paints by Reflectometry

SIGNIFICANCE AND USE
5.1 This is a precise instrumental method giving results having an absolute physical significance without reference to a comparison paint. It should be used when maximum precision and minimum subjectivity are required, as in testing specification coatings or evaluating the hiding efficiency of pigments.  
5.2 Hiding power Test Method D344 is visual instead of instrumental, and gives results that are relative to a material standard instead of absolute. It is less precise than Test Method D2805 but more closely aligned with practical painting procedures.
SCOPE
1.1 This test method covers the determination, without reference to a material paint standard, of the hiding power of air dry coatings with Y tristimulus values greater than 15 %. With appropriate modification, it can also be used to test baking finishes.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D3732-23(Practice)
Standard Practice for Reporting Cure Times of Ultraviolet-Cured Coatings

SIGNIFICANCE AND USE
4.1 This practice provides a guide whereby all pertinent variables relating to the ultraviolet cure of a coating are described.
SCOPE
1.1 This practice applies to all coatings cured by ultraviolet energy.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D1644-01(2023)(Test Method)
Standard Test Methods for Nonvolatile Content of Varnishes

SIGNIFICANCE AND USE
2.1 These test methods are applicable to varnish and are useful to producers and users in determining nonvolatile content and are sometimes an appropriate measure of the film-forming matter in varnish.
SCOPE
1.1 These test methods determine the fraction of a varnish that is nonvolatile at the temperature of the test while volatile solvents are driven off. It is sometimes an approximate measure of the film-forming matter in a varnish.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For a specific statement, see Section 3.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D6486-23(Practice)
Standard Practice for Short Term Vehicle Service Exposure of Automotive Coatings

SIGNIFICANCE AND USE
4.1 Since the exposure of automotive coatings to the various mechanical and chemical stresses encountered in actual operations, is very opportunistic, obtaining statistically significant data from which valid conclusions can be drawn, requires rigorous attention to the experimental designs and conditions of exposure.
SCOPE
1.1 This practice covers the protocol for vehicle service exposure testing of automotive coatings. Such exposure testing is valuable for the verification of the performance of automotive coatings and correlation with laboratory test data. Vehicle service exposure is intended to provide short term (2 to 20 weeks) exposure to the stress factors associated with vehicle operation. Factors included are scratch, mar, impact, stone chipping, insect impact, bird dropping, tree sap and staining, environmental fallout, etc.
Note 1: Vehicle service exposure is not intended to provide the conditions that are needed for characterizing the long term effects of weathering or corrosion exposure.  
1.2 The exposure conditions are produced by the placement of multiple test panels of automotive finishes on automotive test fleets that traverse a defined road course. Exposure to the operating environment can be 20 h/day, 7 days/week allowing for accumulation of over 100 000 miles in 10 weeks of exposure.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off