ASTM D3381/D3381M-13

Standard Specification for Viscosity-Graded Asphalt Cement for Use in Pavement Construction

ABSTRACT
This specification covers three sets of physical requirement limits for asphalt cements graded by viscosity at a specified temperature for use in pavement construction. The purchaser shall indicate the applicable table of limits. The cements shall be prepared from crude petroleum by suitable methods, and if needed, volume corrections should be made as well. The properties for which the materials shall be tested on and should conform to are water content, viscosity, penetration, Cleveland open cup flash point, solubility in trichloroethylene, ductility, and behavior during thin-film oven and rolling thin-film oven tests on residue.
SCOPE
1.1 This specification covers asphalt cements graded by viscosity at 60°C [140°F] for use in pavement construction. Four sets of limits are offered in this specification. The purchaser shall specify the applicable table of limits. In the event the purchaser does not specify limits, Table 1 shall apply. For asphalt cements graded by penetration at 25°C [77°F]. See Specification D946. If needed, volume corrections for asphalt cements should be made according to Practice D4311.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

General Information

• Status: Historical
• Publication Date: 31-May-2013
• ICS: 93.080.20 - Road construction materials
• Technical Committee: D04 - Road and Paving Materials
• Drafting Committee: D04.40 - Asphalt Specifications

Relations

• Replaces: ASTM D3381/D3381M-12 - Standard Specification for Viscosity-Graded Asphalt Cement for Use in Pavement Construction
• Effective Date: 01-Jun-2013
• Referred By: ASTM D6373-23 - Standard Specification for Performance-Graded Asphalt Binder
• Effective Date: 01-Jun-2013
• Referred By: ASTM D8239-23 - Standard Specification for Performance-Graded Asphalt Binder Using the Multiple Stress Creep and Recovery (MSCR) Test
• Effective Date: 01-Jun-2013
• Referred By: ASTM D6114/D6114M-19 - Standard Specification for Asphalt-Rubber Binder
• Effective Date: 01-Jun-2013
• Referred By: ASTM D6140-22 - Standard Test Method to Determine Asphalt Retention of Paving Fabrics Used in Asphalt Paving for Full-Width Applications
• Effective Date: 01-Jun-2013
• Referred By: ASTM D946/D946M-20 - Standard Specification for Penetration-Graded Asphalt Binder for Use in Pavement Construction
• Effective Date: 01-Jun-2013
• Referred By: ASTM D4887/D4887M-11(2021)e1 - Standard Practice for Preparation of Viscosity Blends for Hot Recycled Asphalt Materials
• Effective Date: 01-Jun-2013
• Referred By: ASTM D6932/D6932M-21 - Standard Guide for Materials and Construction of Open-Graded Friction Course Plant Asphalt Mixtures
• Effective Date: 01-Jun-2013
• Referred By: ASTM D7064/D7064M-21 - Standard Practice for Open-Graded Friction Course (OGFC) Asphalt Mixture Design
• Effective Date: 01-Jun-2013
• Referred By: ASTM D4552/D4552M-20 - Standard Classification for Hot-Mix Recycling Agents
• Effective Date: 01-Jun-2013
• Referred By: ASTM D5329-20 - Standard Test Methods for Sealants and Fillers, Hot-Applied, for Joints and Cracks in Asphalt Pavements and Portland Cement Concrete Pavements
• Effective Date: 01-Jun-2013

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D3381/D3381M −13
Standard Specification for
Viscosity-Graded Asphalt Cement for Use in Pavement
1
Construction
This standard is issued under the fixed designation D3381/D3381M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope D1754 Test Method for Effects of Heat andAir onAsphaltic
Materials (Thin-Film Oven Test)
1.1 This specification covers asphalt cements graded by
D2042 Test Method for Solubility of Asphalt Materials in
viscosity at 60°C [140°F] for use in pavement construction.
Trichloroethylene
Four sets of limits are offered in this specification. The
D2170 Test Method for Kinematic Viscosity of Asphalts
purchaser shall specify the applicable table of limits. In the
(Bitumens)
event the purchaser does not specify limits, Table 1 shall apply.
D2171 Test Method for Viscosity of Asphalts by Vacuum
For asphalt cements graded by penetration at 25°C [77°F]. See
Capillary Viscometer
Specification D946. If needed, volume corrections for asphalt
D2872 Test Method for Effect of Heat and Air on a Moving
cements should be made according to Practice D4311.
Film of Asphalt (Rolling Thin-Film Oven Test)
1.2 The values stated in either SI units or inch-pound units
D4311 Practice for Determining Asphalt Volume Correction
are to be regarded separately as standard. The values stated in
to a Base Temperature
each system may not be exact equivalents; therefore, each
D7553 Test Method for Solubility of Asphalt Materials in
system shall be used independently of the other. Combining
N-Propyl Bromide
values from the two systems may result in non-conformance
with the standard. 3. Manufacture
3.1 The asphalt cement shall be prepared from crude petro-
2. Referenced Documents
leum by suitable methods.
2
2.1 ASTM Standards:
D5 Test Method for Penetration of Bituminous Materials 4. Physical Requirements
D92 Test Method for Flash and Fire Points by Cleveland
4.1 The asphalt cement shall be homogeneous, free from
Open Cup Tester
water, and shall not foam when heated to 177°C [350°F].
D36 Test Method for Softening Point of Bitumen (Ring-and-
4.2 The asphalt cements shall conform to the requirements
Ball Apparatus)
given in Table 1, Table 2, Table 3,or Table 4, as specified by
D70 Test Method for Density of Semi-Solid Bituminous
the purchaser.
Materials (Pycnometer Method)
D95 Test Method for Water in Petroleum Products and
5. Methods of Sampling and Testing
Bituminous Materials by Distillation
5.1 Sample and test asphalt cements in accordance with the
D113 Test Method for Ductility of Bituminous Materials
following methods:
D140 Practice for Sampling Bituminous Materials
5.1.1 Sampling—Practice D140.
D946 Specification for Penetration-Graded Asphalt Cement
5.1.2 Water—Test Method D95.
for Use in Pavement Construction
5.1.3 Viscosity at 60°C [140°F]—Test Method D2171.
5.1.4 Viscosity at 135°C [275°F]—Test Method D2170.
1
This specification is under the jurisdiction of ASTM Committee D04 on Road
5.1.5 Penetration— Test Method D5.
and Paving Materials and is the direct responsibility of Subcommittee D04.40 on
5.1.6 Flash Point, Cleveland Open Cup—Test Method D92.
Asphalt Specifications.
5.1.7 Solubility in Trichloroethylene—Test Method D2042.
CurrenteditionapprovedJune1,2013.PublishedJuly2013.Originallyapproved
5.1.8 Thin-Film Oven Test—Test Method D1754 (see Table
in 1975. Last previous edition approved in 2012 as D3381/D3381M – 12. DOI:
10.1520/D3381_D3381M-13.
1 and Table 2).
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
5.1.9 Rolling Thin-Film Oven Test—Test Method D2872
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
(see Table 3 and Table 4).
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. 5.1.10 Ductility—Test Method D113.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D3381/D3381M − 13
TABLE 1 Requirements for Asphalt Cement, Viscosity Graded at 60°C [140°F] Based on Original Asphalt
Viscosity Grade
Test
AC-2.5 AC-5 AC-10 AC-20 AC-30 AC-40
Viscosity, 60°C [140°F], Pa·s 25 ± 5 50 ± 10 100 ± 20 200 ± 40 300 ± 60 400 ± 80
2
Viscosity, 135°C [275°F], min, mm /s 80 110 150 210 250 300
Penetration, 25°C [77°F], 100 g, 5 s, min 200 120 70 40 30 20
Flash point, Cleveland open cup, min,°C [°F] 165 [325] 175 [350] 220 [425] 230 [450] 230 [450] 230 [450]
A
Solubility in trichloroethylene, min, % 99.0 99.0 99.
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D3381/D3381M − 12 D3381/D3381M − 13
Standard Specification for
Viscosity-Graded Asphalt Cement for Use in Pavement
1
Construction
This standard is issued under the fixed designation D3381/D3381M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope
1.1 This specification covers asphalt cements graded by viscosity at 60°C [140°F] for use in pavement construction. ThreeFour
sets of limits are offered in this specification. The purchaser shall specify the applicable table of limits. In the event the purchaser
does not specify limits, Table 1 shall apply. For asphalt cements graded by penetration at 25°C [77°F]. See Specification D946.
If needed, volume corrections for asphalt cements should be made according to Practice D4311.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
2. Referenced Documents
2
2.1 ASTM Standards:
D5 Test Method for Penetration of Bituminous Materials
D92 Test Method for Flash and Fire Points by Cleveland Open Cup Tester
D36 Test Method for Softening Point of Bitumen (Ring-and-Ball Apparatus)
D70 Test Method for Density of Semi-Solid Bituminous Materials (Pycnometer Method)
D95 Test Method for Water in Petroleum Products and Bituminous Materials by Distillation
D113 Test Method for Ductility of Bituminous Materials
D140 Practice for Sampling Bituminous Materials
D946 Specification for Penetration-Graded Asphalt Cement for Use in Pavement Construction
D1754 Test Method for Effects of Heat and Air on Asphaltic Materials (Thin-Film Oven Test)
D2042 Test Method for Solubility of Asphalt Materials in Trichloroethylene
D2170 Test Method for Kinematic Viscosity of Asphalts (Bitumens)
D2171 Test Method for Viscosity of Asphalts by Vacuum Capillary Viscometer
D2872 Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test)
D4311 Practice for Determining Asphalt Volume Correction to a Base Temperature
D7553 Test Method for Solubility of Asphalt Materials in N-Propyl Bromide
3. Manufacture
3.1 The asphalt cement shall be prepared from crude petroleum by suitable methods.
4. Physical Requirements
4.1 The asphalt cement shall be homogeneous, free from water, and shall not foam when heated to 175°C177°C [350°F].
4.2 The asphalt cements shall conform to the requirements given in Table 1, Table 2, Table 3, or Table 4, as specified by the
purchaser.
1
This specification is under the jurisdiction of ASTM Committee D04 on Road and Paving Materials and is the direct responsibility of Subcommittee D04.40 on Asphalt
Specifications.
Current edition approved Dec. 1, 2012June 1, 2013. Published December 2012July 2013. Originally approved in 1975. Last previous edition approved in 20092012 as
D3381 – 09a.D3381/D3381M – 12. DOI: 10.1520/D3381_D3381M-12.10.1520/D3381_D3381M-13.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D3381/D3381M − 13
TABLE 1 Requirements for Asphalt Cement, Viscosity Graded at 60°C [140°F] Based on Original Asphalt
NOTE 1—Grading based on original asphalt.
Viscosity Grade
Test
AC-2.5 AC-5 AC-10 AC-20 AC-30 AC-40
Viscosity, 60°C [140°F], Pa·s 25 ± 5 50 ± 10 100 ± 20 200 ± 40 300 ± 60 400 ± 80
2
Viscosity, 135°C [275°F], min, mm /s 80 110 150 210 250 300
Penetration, 25°C [77°F], 100 g, 5 s, min 200 120 70 40 30 20
Flash point, Cleveland open cup, min,°C [°F] 165 [325] 175 [350] 220 [425] 230 [450] 230 [450] 230 [450]
A
Solubility in trichloroethylene, min, % 99.0 99.0 99.0 99.0 99.0 99.0
Tests on residue from thin-film oven test:
Viscosity, 60°C [140°F], max, Pa·s 125 250 500 1000 1500 2000
A
Ductility, 25°C [77°F], 5 cm/min, min, cm 100 100 50 20 15
...