ASTM A516/A516M-01

Standard Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- and Lower-Temperature Service

SCOPE
1.1 This specification covers carbon steel plates intended primarily for service in welded pressure vessels where improved notch toughness is important.
1.2 Plates under this specification are available in four grades having different strength levels as follows:Tensile Strength,Grade U.S. [SI]ksi [MPa]55 [380]55-75 [380-515]60 [415]60-80 [415-550]65 [450]65-85 [450-585]70 [485]70-90 [485-620]
1.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness of plates furnished under this specification as follows: Maximum Thickness,Grade U.S. [SI]in. [mm] 55 [380]12 [305]60 [415]8 [205]65 [450]8 [205]70 [485]8 [205]
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

General Information

• Status: Historical
• Publication Date: 09-Sep-2001
• ICS: 77.140.30 - Steels for pressure purposes
• Technical Committee: A01 - Steel, Stainless Steel and Related Alloys
• Drafting Committee: A01.11 - Steel Plates for Boilers and Pressure Vessels

Relations

• Replaces: ASTM A516/A516M-90(2001) - Standard Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- and Lower-Temperature Service
• Effective Date: 10-Sep-2001
• Replaced By: ASTM A516/A516M-03 - Standard Specification for Pressure Vessel Plates, Carbon Steel, for Moderate- and Lower-Temperature Service
• Effective Date: 10-Sep-2003
• Referred By: ASTM A671/A671M-20 - Standard Specification for Electric-Fusion-Welded Steel Pipe for Atmospheric and Lower Temperatures
• Effective Date: 10-Sep-2001
• Referred By: ASTM A285/A285M-17 - Standard Specification for Pressure Vessel Plates, Carbon Steel, Low- and Intermediate-Tensile Strength
• Effective Date: 10-Sep-2001
• Referred By: ASTM A672/A672M-19 - Standard Specification for Electric-Fusion-Welded Steel Pipe for High-Pressure Service at Moderate Temperatures
• Effective Date: 10-Sep-2001
• Referred By: ASTM A20/A20M-20 - Standard Specification for General Requirements for Steel Plates for Pressure Vessels
• Effective Date: 10-Sep-2001
• Referred By: ASTM F1603-17(2023) - Standard Specification for Kettles, Steam-Jacketed, 32 oz to 20 gal (1 to 75.7 L), Tilting, Table Mounted, Direct Steam, Gas and Electric Heated
• Effective Date: 10-Sep-2001
• Referred By: ASTM F1565-00(2019) - Standard Specification for Pressure-Reducing Valves for Steam Service
• Effective Date: 10-Sep-2001
• Referred By: ASTM A1097/A1097M-22 - Standard Specification for Steel Casing Pipe, Carbon, Electric-Fusion (Arc)-Welded (NPS 10 and Larger)
• Effective Date: 10-Sep-2001
• Referred By: ASTM F1602-12(2023) - Standard Specification for Kettles, Steam-Jacketed, 20 to 200 gal (75.7 to 757 L), Floor or Wall Mounted, Direct Steam, Gas and Electric Heated
• Effective Date: 10-Sep-2001

Standards Content (Sample)

NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Used in USDOE-NE Standards
Designation: A 516/A 516M – 01
Standard Specification for
Pressure Vessel Plates, Carbon Steel, for Moderate- and
1
Lower-Temperature Service
This standard is issued under the fixed designation A 516/A 516M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope 2. Referenced Documents
2
1.1 This specification covers carbon steel plates intended 2.1 ASTM Standards:
primarily for service in welded pressure vessels where im- A 20/A20M Specification for General Requirements for
3
proved notch toughness is important. Steel Plates for Pressure Vessels
1.2 Plates under this specification are available in four A 435/A435M Specification for Straight-Beam Ultrasonic
3
grades having different strength levels as follows: Examination of Steel Plates
A 577/A577M Specification for Ultrasonic Angle-Beam
Tensile Strength,
3
Grade U.S. [SI] ksi [MPa]
Examination of Steel Plates
A 578/A578M Specification for Straight-Beam Ultrasonic
55 [380] 55–75 [380–515]
Examination of Plain and Clad Steel Plates for Special
60 [415] 60–80 [415–550]
3
65 [450] 65–85 [450–585]
Applications
70 [485] 70–90 [485–620]
3. General Requirements and Ordering Information
1.3 The maximum thickness of plates is limited only by the
capacity of the composition to meet the specified mechanical 3.1 Material supplied to this material specification shall
property requirements; however, current practice normally
conform to Specification A 20/A 20M. These requirements
limits the maximum thickness of plates furnished under this outline the testing and retesting methods and procedures,
specification as follows:
permissible variations in dimensions, and mass, quality and
repair of defects, marking, loading, etc.
Maximum Thickness,
Grade U.S. [SI] in. [mm]
3.2 Specification A 20/A20M also establishes the rules for
the ordering information that should be complied with when
55 [380] 12 [305]
60 [415] 8 [205] purchasing material to this specification.
65 [450] 8 [205]
3.3 In addition to the basic requirements of this specifica-
70 [485] 8 [205]
tion, certain supplementary requirements are available when
1.4 For plates produced from coil, the additional require-
additional control, testing, or examination is required to meet
ments, including additional testing requirements and the re-
end use requirements. These include:
porting of additional test results of Specification A 20/A 20M
3.3.1 Vacuum treatment,
apply.
3.3.2 Additional or special tension testing,
1.5 The values stated in either inch-pound units or SI units
3.3.3 Impact testing, and
are to be regarded separately as standard. Within the text, the
3.3.4 Nondestructive examination.
SI units are shown in brackets. The values stated in each
3.4 The purchaser is referred to the listed supplementary
system are not exact equivalents; therefore, each system must
requirements in this specification and to the detailed require-
be used independently of the other. Combining values from the
ments in Specification A 20/A20M.
two systems may result in nonconformance with the specifi-
3.5 Coiled product is excluded from qualification to this
cation.
specification until it is decoiled, leveled, and cut to length.
Plate produced from coil means plate that has been cut to
individual lengths from a coiled product and is furnished
without heat treatment. The processor decoils, levels, cuts to
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
length, and marks the product. Except as allowed by Section 6
Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee
A01.11 on Steel Plates for Boilers and Pressure Vessels. in Specification A 20/A 20M, the processor is responsible for
Current edition approved Sept. 10, 2001. Published Sept. 2001. Originally
published as A 516 – 64. Last previous edition A 516/A 516M – 90 (2001).
2
For ASME Boiler and Pressure Vessel Code applications, see related Specifi-
3
cation SA-516/SA-516M in Section II of that Code. Annual Book of ASTM Standards, Vol 01.04.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
A 516/A 516M – 01
1
performing and certifying all tests, examinations, repairs, 5.3 When notch-toughness tests are required on plates 1 ⁄2
inspecti
...