Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Polyester Reinforcements

ABSTRACT
This specification covers Grades G (granule surfaced) and S (smooth surfaced) prefabricated bituminous sheet materials reinforced with polyester fabric and modified by styrene butadiene styrene (SBS) thermoplastic elastomer, intended for use in the fabrication of multiple ply roofing and waterproofing membranes. The sheet materials shall meet dimensional requirements such as thickness and net mass per unit area, as well as physical requirements such as peak load before and after heat conditioning, elongation at peak load, ultimate elongation, tear strength, low temperature flexibility, dimensional stability, compound stability, and granule embedment.
SCOPE
1.1 This specification covers prefabricated modified bituminous sheet materials reinforced with polyester fabric as the primary reinforcement, (see Note 1) with or without granules, which use styrene butadiene styrene (SBS) thermoplastic elastomer as the primary modifier and are intended for use in the fabrication of multiple ply roofing and waterproofing membranes.
Note 1: Many modified bituminous sheets are currently marketed with polyester mat reinforced with glass yarns to improve processing in the manufacture of the finished modified bitumen product and to reduce distortions that may be introduced during production. These glass yarns are typically a small percentage of the reinforcement and do not contribute to the physical properties of the finished product so much as to make these products be classified by Specification D6162/D6162M.  
1.2 This specification is intended as a material specification only. Issues regarding the suitability of the specific roof constructions or application techniques are beyond this scope.  
1.3 The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties. In-place roof system design criteria, such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift resistance, and others, are factors beyond the scope of this material specification.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

General Information

Status
Historical
Publication Date
31-Oct-2016
Current Stage
Ref Project

Buy Standard

Technical specification
ASTM D6164/D6164M-16 - Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Polyester Reinforcements
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview
Technical specification
REDLINE ASTM D6164/D6164M-16 - Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Polyester Reinforcements
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D6164/D6164M −16
Standard Specification for
Styrene Butadiene Styrene (SBS) Modified Bituminous
1
Sheet Materials Using Polyester Reinforcements
This standard is issued under the fixed designation D6164/D6164M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope D5147/D5147M Test Methods for Sampling and Testing
Modified Bituminous Sheet Material
1.1 This specification covers prefabricated modified bitumi-
D6162/D6162M Specification for Styrene Butadiene Sty-
nous sheet materials reinforced with polyester fabric as the
rene (SBS) Modified Bituminous Sheet Materials Using a
primary reinforcement, (see Note 1) with or without granules,
Combination of Polyester and Glass Fiber Reinforcements
which use styrene butadiene styrene (SBS) thermoplastic
elastomer as the primary modifier and are intended for use in
3. Terminology
the fabrication of multiple ply roofing and waterproofing
3.1 Definitions—For definitions of terms used in this
membranes.
specification, refer to Terminology D1079.
NOTE1—Manymodifiedbituminoussheetsarecurrentlymarketedwith
polyester mat reinforced with glass yarns to improve processing in the
4. Classification
manufacture of the finished modified bitumen product and to reduce
distortions that may be introduced during production. These glass yarns
4.1 Modified bituminous sheet materials reinforced with
are typically a small percentage of the reinforcement and do not contribute
polyester fabric, Type I and Type II, are covered by this
to the physical properties of the finished product so much as to make these
specification.
products be classified by Specification D6162/D6162M.
4.2 The following grades are used to describe the material
1.2 This specification is intended as a material specification
surfacing:
only. Issues regarding the suitability of the specific roof
4.2.1 Grade G—Granule Surfaced.
constructions or application techniques are beyond this scope.
4.2.2 Grade S—Smooth Surfaced.
1.3 The specified tests and property limits used to charac-
5. Material and Manufacture
terize the sheet materials are intended to establish minimum
properties. In-place roof system design criteria, such as fire
5.1 In the process of manufacture, the reinforcement is
resistance, field strength, impact/puncture resistance, material
saturated with asphalt or modified asphalt and is impregnated
compatibility, uplift resistance, and others, are factors beyond
and coated on both sides with an SBS modified bituminous
the scope of this material specification.
coating. The SBS modified bituminous coating shall be per-
1.4 The values stated in either SI units or inch-pound units mitted to be compounded with a mineral stabilizer.
are to be regarded separately as standard. The values stated in
5.2 The Grade G sheet is surfaced on the weather side with
each system may not be exact equivalents; therefore, each
mineralgranules,exceptforanyselvage.Topreventstickingin
system shall be used independently of the other. Combining
the roll, the reverse side and any selvage shall be permitted to
values from the two systems may result in non-conformance
be covered with a fine mineral surfacing or any other surfacing
with the standard.
that will not interfere with adhesion or bonding of the lap
during application.
2. Referenced Documents
2
5.3 Sheet material intended for application by heat welding
2.1 ASTM Standards:
(torching) shall meet the minimum bottom coating requirement
D1079 Terminology Relating to Roofing and Waterproofing
found in Table 1.
1
This specification is under the jurisdiction of ASTM Committee D08 on
6. Physical Properties
Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.04
on Felts, Fabrics and Bituminous Sheet Materials.
6.1 The sheet shall conform to the minimum physical
Current edition approved Nov. 1, 2016. Published November 2016. Originally
properties prescribed in Table 2.
approved in 1997. Last previous edition approved in 2011 as D6164/D6164M – 11.
DOI: 10.1520/D6164_D6164M-16.
6.2 The finished product shall not crack nor be so sticky as
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
to cause tearing or other material damage upon being unrolled
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
at any product temperature between 4 and 60°C [40 and
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. 140°F].
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D6164/D616
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D6164/D6164M − 11 D6164/D6164M − 16
Standard Specification for
Styrene Butadiene Styrene (SBS) Modified Bituminous
1
Sheet Materials Using Polyester Reinforcements
This standard is issued under the fixed designation D6164/D6164M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This specification covers prefabricated modified bituminous sheet materials reinforced with polyester fabric as the primary
reinforcement, (see Note 1) with or without granules, which use styrene butadiene styrene (SBS) thermoplastic elastomer as the
primary modifier and are intended for use in the fabrication of multiple ply roofing and waterproofing membranes.
NOTE 1—Many modified bituminous sheets are currently marketed with polyester mat reinforced with glass yarns to improve processing in the
manufacture of the finished modified bitumen product and to reduce distortions that may be introduced during production. These glass yarns are typically
a small percentage of the reinforcement and do not contribute to the physical properties of the finished product so much as to make these products be
classified by Specification D6162D6162/D6162M.
1.2 This specification is intended as a material specification only. Issues regarding the suitability of the specific roof
constructions or application techniques are beyond this scope.
1.3 The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties.
In-place roof system design criteria, such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift
resistance, and others, are factors beyond the scope of this material specification.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each
system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the
two systems may result in non-conformance with the standard.
2. Referenced Documents
2
2.1 ASTM Standards:
D1079 Terminology Relating to Roofing and Waterproofing
D5147D5147/D5147M Test Methods for Sampling and Testing Modified Bituminous Sheet Material
D6162D6162/D6162M Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using a
Combination of Polyester and Glass Fiber Reinforcements
3. Terminology
3.1 Definitions—For definitions of terms used in this specification, refer to Terminology D1079.
4. Classification
4.1 Modified bituminous sheet materials reinforced with polyester fabric, Type I and Type II, are covered by this specification.
4.2 The following grades are used to describe the material surfacing:
4.2.1 Grade G—Granule Surfaced.
4.2.2 Grade S—Smooth Surfaced.
5. Material and Manufacture
5.1 In the process of manufacture, the reinforcement is saturated with asphalt or modified asphalt and is impregnated and coated
on both sides with an SBS modified bituminous coating. The SBS modified bituminous coating shall be permitted to be
compounded with a mineral stabilizer.
1
This specification is under the jurisdiction of ASTM Committee D08 on Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.04 on Felts
and FabricsFelts, Fabrics and Bituminous Sheet Materials.
Current edition approved Jan. 1, 2011Nov. 1, 2016. Published January 2011November 2016. Originally approved in 1997. Last previous edition approved in 20052011
ε1
as D6164 – 05D6164/D6164M – 11. . DOI: 10.1520/D6164_D6164M-11.10.1520/D6164_D6164M-16.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D6164/D6164M − 16
5.2 The Grade G sheet is surfaced on the weather side with mineral granules, except for any selvage. To prevent sticking in the
roll, the reverse side and any selvage shall be permitted to be covered with a fine mineral surfacing or any other surfacing that will
not interfere with adhesion or bonding of the lap during application.
5.3 Sheet materia
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.