ASTM D1465-90(2000)
(Test Method)Standard Test Method for Blocking and Picking Points of Petroleum Wax
Standard Test Method for Blocking and Picking Points of Petroleum Wax
SCOPE
1.1 This test method covers the determination of the blocking point and picking point of petroleum wax.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
An American National Standard
Designation:D1465–90(Reapproved 2000) Technical Association of Pulp and Paper Industry
Suggested Method T 652
Standard Test Method for
1
Blocking and Picking Points of Petroleum Wax
This standard is issued under the fixed designation D1465; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This test method was prepared jointly by the Technical Association of the Pulp and Paper Industry and the American Society for Testing
and Materials.
1. Scope disruption (picking point) and where 50% of the specimen
width is disrupted (50% blocking point) are noted. The
1.1 This test method covers the determination of the block-
temperatures of corresponding points on the blocking plate are
ing point and picking point of petroleum wax.
reported as the picking point and blocking point or blocking
1.2 This standard does not purport to address all of the
range.
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appro-
5. Significance and Use
priate safety and health practices and determine the applica-
5.1 Blocking of waxed paper, because of the relatively low
bility of regulatory limitations prior to use.
temperatures at which it may occur, can be a major problem to
2. Referenced Documents the paper-coating industry. For example, when the waxed
surfaces in a roll of waxed paper stick together, upon separa-
2.1 ASTM Standards:
tion the surface films are marred and the glossy finish is
D87 Test Method for Melting Point of Petroleum Wax
2
destroyed. The wax picking point and the wax blocking point
(Cooling Curve)
indicate an approximate temperature range at or above which
D2423 Test Method for Surface Wax on Waxed Paper or
2
waxed surfaces in contact with each other are likely to cause
Paperboard
3
surface film injury.
E1 Specification for ASTM Thermometers
6. Apparatus
3. Terminology
6.1 Wax Coating Device—Any manual- or machine-driven
3.1 Definitions:
waxer that gives uniform coatings of the desired weights to a
3.1.1 wax blocking point—the lowest temperature at which
strip of paper not less than 51 mm (2 in.) wide.
film disruption occurs across 50% of the waxed paper surface
6.2 Trimming Board,orotherdeviceforcuttingpaperstrips.
when the test strips are separated.
6.3 Paper Scales, sensitive to 0.002 g, or suitable balance
3.1.2 wax picking point—the temperature at which the first
for measuring basis weights of unwaxed and waxed paper.
film disruption occurs on the waxed paper when test strips are
6.4 Blocking PlateAssembly,consistingofametalplate305
separated.
1
mm (12 in.) wide, 13 to 51 mm ( ⁄2 to 2 in.) thick, and 559 to
4. Summary of Test Method 914 mm (22 to 36 in.) long. It is heated at one end and cooled
at the other end to provide a 457 to 762-mm (18 to 30-in.) test
4.1 Paper test specimens are coated with the wax sample,
section having an average temperature gradient of 0.8 to 2.2°C
folded with the waxed surfaces together, and placed on a
(1.5 to 4.0°F)/in. The temperature gradient across the width of
blocking plate.The plate is heated at one end and cooled at the
the plate from the longitudinal axis to 25 mm (1 in.) from the
other end to impose a measured temperature gradient along its
edge must not exceed 0.3°C (0.5°F). The temperature at any
length.After a conditioning period on the plate, the specimens
point should not vary more than 0.3°C (0.5°F). Details of two
areremoved,unfolded,andexamined.Thepointsofinitialfilm
acceptable blocking plates are given in Fig. 1 and Fig. 2.
1
6.4.1 Eight Foam Rubber Strips,25to38mm(1to1 ⁄2 in.)
1
1 1
This test method is under the jurisdiction of ASTM Committee D02 on
wide by 6 to 13 mm ( ⁄4 to ⁄2 in.) thick, extending the length
Petroleum Products and Lubricantsand is the direct responsibility of Subcommittee
of the test section on the blocking plate.
D02.10.0Aon Physical and Chemical Properties.
6.4.2 Eight Sets of Steel Weights, 25 by 25 mm (1 by 1 in.)
Current edition approved April 27, 1990. Published June 1990. Originally
e1
in cross section made from stock having a density range from
published as D1465–57T. Last previous edition D1465–80 (1985) .
2 3 3
Annual Book of ASTM Standards, Vol 05.01.
7800 to 8000 kg/m (0.28 to 0.29 lb/in ). The weights may be
3
Annual Book of ASTM Standards, Vol 14.03.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
D1465
FIG. 1 Type A Blocking Plate
FIG. 2 Type B Blocking Plate
in single lengths or in sections to give sets equa
...