Standard Test Methods for Coated Fabrics Used for Oil Spill Control and Storage

Standard Test Methods for Coated Fabrics Used for Oil Spill Control and Storage

SCOPE
1.1 These test methods cover laboratory-conducted performance tests for coated fabrics used in spill control barriers or in temporary storage devices.  
1.2  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
14-May-1995
Technical Committee
F20 - Hazardous Substances and Oil Spill Response
Drafting Committee
F20.11 - Control
Current Stage
Ref Project

Relations

Replaces
ASTM F715-95 - Standard Test Methods for Coated Fabrics Used for Oil Spill Control and Storage
Effective Date
15-May-1995
Replaced By
ASTM F715-95(2002) - Standard Test Methods for Coated Fabrics Used for Oil Spill Control and Storage
Effective Date
10-Oct-2002
Referred By
ASTM F1599-95(2018) - Standard Guide for Collecting Performance Data on Temporary Storage Devices
Effective Date
15-May-1995
Referred By
ASTM F1523-94(2023) - Standard Guide for Selection of Booms in Accordance With Water Body Classifications
Effective Date
15-May-1995
Referred By
ASTM F2152-07(2021) - Standard Guide for In-Situ Burning of Spilled Oil: Fire-Resistant Boom
Effective Date
15-May-1995

Buy Standard

ASTM F715-95(2001) - Standard Test Methods for Coated Fabrics Used for Oil Spill Control and StorageASTM F715-95(2001) - Standard Test Methods for Coated Fabrics Used for Oil Spill Control and Storage
PreviousNext
Standard
ASTM F715-95(2001) - Standard Test Methods for Coated Fabrics Used for Oil Spill Control and Storage
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Designation: F 715 – 95 (Reapproved 2001)
Standard Test Methods for
Coated Fabrics Used for Oil Spill Control and Storage
This standard is issued under the fixed designation F 715; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope D 751 Test Methods for Coated Fabrics
D 975 Specification for Diesel Fuel Oils
1.1 These test methods cover laboratory-conducted perfor-
D 1149 Test Method for Rubber Deterioration—Surface
mance tests for coated fabrics used in spill control barriers or
Ozone Cracking in a Chamber
in temporary storage devices.
D 1266 Test Method for Sulfur in Petroleum Products
1.2 This standard does not purport to address all of the
(Lamp Method)
safety concerns, if any, associated with its use. It is the
D 1298 Practice for Density, Relative Density (Specific
responsibility of the user of this standard to establish appro-
Gravity), or API Gravity of Crude Petroleum and Liquid
priate safety and health practices and determine the applica-
Petroleum Products by Hydrometer Method
bility of regulatory limitations prior to use.
D 1319 Test Method for Hydrocarbon Types in Liquid
2. Referenced Documents Petroleum Products by Fluorescent Indicator Adsorption
D 1796 Test Method for Water and Sediment in Fuel Oils by
2.1 ASTM Standards:
the Centrifuge Method (Laboratory Procedure)
D 86 Test Method for Distillation of Petroleum Products at
D 2425 Test Method for Hydrocarbon Types in Middle
Atmospheric Pressure
Distillates by Mass Spectrometry
D 93 Test Methods for Flash Point by Pensky-Martens
D 2500 Test Method for Cloud Point of Petroleum Oils
Closed Cup Tester
D 2644 Tolerances for Yarns Spun on the Woolen System
D 97 Test Method for Pour Point of Petroleum Products
D 3117 Test Method for Wax Appearance Point of Distillate
D 129 Test Method for Sulfur in Pretroleum Products (Gen-
Fuels
eral Bomb Method)
D 4157 Test Method for Abrasion Resistance of Textile
D 130 Test Method for Detection of Copper Corrosion from
Fabrics (Oscillatory Cylinder Method)
Petroleum Products by the Copper Strip Tarnish Test
G 26 Practice for Operating Light-Exposure Apparatus
D 287 Test Method for API Gravity of Crude Petroleum and
(Xenon-Arc Type) With and Without Water for Exposure
Petroleum Products (Hydrometer Method)
of Nonmetallic Materials
D 445 Test Method for Kinematic Viscosity of Transparent
2.2 Federal Standard:
and Opaque Liquids (The Calculation of Dynamic Viscos-
Fed. Std. No. 191A Textile Test Methods
ity)
2.3 Military Specification:
D 482 Test Method for Ash from Petroleum Products
MIL-T-6396 E Tank, Fuel, Oil, Water-Alcohol, Coolant
D 524 Test Method for Ramsbottom Carbon Residue of
Fluid, Non-Self-Sealing, Removable, Internal
Petroleum Products
D 543 Practices for Evaluating the Resistance of Plastics to
3. Significance and Use
Chemical Reagents
3.1 Membrane materials are subjected to these tests in order
D 613 Test Method for Cetane Number of Diesel Fuel Oil
to provide data that reasonably relate to membrane response
D 664 Test Method for Acid Number of Petroleum Products
under the actual conditions of spill control barrier or storage
by Potentiometric Titration
device use.
3.2 Although these test methods provide data on individual
performance of membrane materials, all combinations of actual
These test methods are under the jurisdiction of ASTM Committee F20 on
Hazardous Substances and Oil Spill Response and are the direct responsibility of
Subcommittee F20.11 on Control. Annual Book of ASTM Standards, Vol 09.02.
Current edition approved May 15, 1995. Published July 1995. Originally Annual Book of ASTM Standards, Vol 09.01.
e1 8
published as F 715 – 81. Last previous edition F 715 – 81 (1994) . Annual Book of ASTM Standards, Vol 07.01.
2 9
Annual Book of ASTM Standards, Vol 05.01. Annual Book of ASTM Standards, Vol 05.02.
3 10
Annual Book of ASTM Standards, Vol 05.04. Annual Book of ASTM Standards, Vol 07.02.
4 11
Annual Book of ASTM Standards, Vol 08.01. Annual Book of ASTM Standards, Vol 14.04.
5 12
Annual Book of ASTM Standards, Vol 05.05. Available from Standardization Documents Order Desk, Bldg. 4 Section D,
700 Robbins Ave., Philadelphia, PA 19111-5098, Attn: NPODS.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
F 715
conditions of spill control barrier or storage device use are not sandpaper as the abradant. Cycle continuously to exposure of
simulated in this sequence of tests. threads.
4.8 Seam Strength—Test Methods D 751. Perform test with
4. Base Line Tests
seam orientation as in device design.
4.1 Number of Specimens—Subject specimens of spill con-
4.9 Seam Adhesion—Repeat adhesion test (see 4.5) for
trol membrane materials to the tests prescribed in 4.2-4.11.
specimens containing a seam.
Perform all tests in the direction of both the warp and fill of the
4.10 Blocking Resistance—Test Methods D 751.
fabric. The number of specimens to be tested are as specified in
4.11 Mildew—Fed. Std. No. 191A, Method 5762 (Mixed
the proced
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D6152/D6152M-12(2024)(Specification)
Standard Specification for SEBS-Modified Mopping Asphalt Used in Roofing

ABSTRACT
This specification covers SEBS (styrene-ethylenebutylene-styrene)-modified mopping asphalt intended for use in built-up roof construction, construction of some modified bitumen systems, construction of bituminous vapor retarder systems, and for adhering insulation boards used in various types of roofing systems. This specification is intended as a material specification and issues regarding the suitability of specific roof constructions or application techniques are beyond its scope. The specified tests and property values are intended to establish minimum properties. In place system design criteria or performance attributes are factors beyond the scope of this specification. The base asphalt shall be prepared from crude petroleum and the SEBS-modified asphalt shall incorporate sufficient SEBS as the primary polymeric modifier. The SEBS modified asphalt shall be homogeneous and free of water and shall conform to the prescribed physical properties including (1) softening point before and after heat exposure, (2) softening point change, (3) flash point, (4) penetration before and after heat exposure, (5) penetration change, (6) solubility in trichloroethylene, (7) tensile elongation, (8) elastic recovery, and (9) low temperature flexibility. The sampling and test methods to determine compliance with the specified physical properties, as well as the evaluation for stability during heat exposure are detailed.
SCOPE
1.1 This specification covers SEBS (styrene-ethylene-butylene-styrene)-modified asphalt intended for use in built-up roof construction, construction of some modified bitumen systems, construction of bituminous vapor retarder systems, and for adhering insulation boards used in various types of roof systems.  
1.2 This specification is intended as a material specification. Issues regarding the suitability of specific roof constructions or application techniques are beyond its scope.  
1.3 The specified tests and property values used to characterize SEBS-modified asphalt are intended to establish minimum properties. In-place system design criteria or performance attributes are factors beyond the scope of this specification.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM D5643/D5643M-06(2024)(Specification)
Standard Specification for Coal Tar Roof Cement, Asbestos Free

ABSTRACT
This specification covers coal tar roof cement suitable for trowel application in coal tar roofing and flashing systems. The chemical composition of coal tar roof cement shall conform to the requirements prescribed. The water, non-volatile matter, insoluble matter, behaviour at 60 deg. C, adhesion to wet surfaces, and flash point shall be tested to meet the requirements prescribed.
SCOPE
1.1 This specification covers coal tar roof cement suitable for trowel application in coal tar roofing and flashing systems.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM D396-24(Specification)
Standard Specification for Fuel Oils

ABSTRACT
This specification covers grades of fuel oil intended for use in various types of fuel-oil-burning equipment under various climatic and operating conditions. These grades include the following: Grades No. 1 S5000, No. 1 S500, No. 2 S5000, and No. 2 S500 for use in domestic and small industrial burners; Grades No. 1 S5000 and No. 1 S500 adapted to vaporizing type burners or where storage conditions require low pour point fuel; Grades No. 4 (Light) and No. 4 (Heavy) for use in commercial/industrial burners; and Grades No. 5 (Light), No. 5 (Heavy), and No. 6 for use in industrial burners. Preheating is usually required for handling and proper atomization. The grades of fuel oil shall be homogeneous hydrocarbon oils, free from inorganic acid, and free from excessive amounts of solid or fibrous foreign matter. Grades containing residual components shall remain uniform in normal storage and not separate by gravity into light and heavy oil components outside the viscosity limits for the grade. The grades of fuel oil shall conform to the limiting requirements prescribed for: (1) flash point, (2) water and sediment, (3) physical distillation or simulated distillation, (4) kinematic viscosity, (5) Ramsbottom carbon residue, (6) ash, (7) sulfur, (8) copper strip corrosion, (9) density, and (10) pour point. The test methods for determining conformance to the specified properties are given.
SCOPE
1.1 This specification (see Note 1) covers grades of fuel oil intended for use in various types of fuel-oil-burning equipment under various climatic and operating conditions. These grades are described as follows:  
1.1.1 Grades No. 1 S5000, No. 1 S500, No. 1 S15, No. 2 S5000, No. 2 S500, and No. 2 S15 are middle distillate fuels for use in domestic and small industrial burners. Grades No. 1 S5000, No. 1 S500, and No. 1 S15 are particularly adapted to vaporizing type burners or where storage conditions require low pour point fuel.  
1.1.2 Grades B6–B20 S5000, B6–B20 S500, and B6–B20 S15 are middle distillate fuel/biodiesel blends for use in domestic and small industrial burners.  
1.1.3 Grades No. 4 (Light) and No. 4 are heavy distillate fuels or middle distillate/residual fuel blends used in commercial/industrial burners equipped for this viscosity range.  
1.1.4 Grades No. 5 (Light), No. 5 (Heavy), and No. 6 are residual fuels of increasing viscosity and boiling range, used in industrial burners. Preheating is usually required for handling and proper atomization.  
Note 1: For information on the significance of the terminology and test methods used in this specification, see Appendix X1.
Note 2: A more detailed description of the grades of fuel oils is given in X1.3.  
1.2 This specification is for the use of purchasing agencies in formulating specifications to be included in contracts for purchases of fuel oils and for the guidance of consumers of fuel oils in the selection of the grades most suitable for their needs.  
1.3 Nothing in this specification shall preclude observance of federal, state, or local regulations which can be more restrictive.  
1.4 The values stated in SI units are to be regarded as standard.  
1.4.1 Non-SI units are provided in Table 1 and Table 2 and in 7.1.2.1/7.1.2.2 because these are common units used in the industry.
Note 3: The generation and dissipation of static electricity can create problems in the handling of distillate burner fuel oils. For more information on the subject, see Guide D4865.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    13 pages
    English language
    sale 15% off
  • Technical specification
    13 pages
    English language
    sale 15% off
ASTM
ASTM D8165-24(Test Method)
Standard Test Method for Evaluation of Load-Carrying Capacity of Lubricants Used in Hypoid Final-Drive Axles Operated under Low-Speed and High-Torque Conditions

SIGNIFICANCE AND USE
5.1 This test method measures a lubricant's ability to protect hypoid final drive axles from abrasive wear, adhesive wear, plastic deformation, and surface fatigue when subjected to low-speed, high-torque conditions. Lack of protection can lead to premature gear or bearing failure, or both.  
5.2 This test method is used, or referred to, in specifications and classifications of rear-axle gear lubricants such as:  
5.2.1 Specification D7450.  
5.2.2 American Petroleum Institute (API) Publication 1560.  
5.2.3 SAE J308.  
5.2.4 SAE J2360.
SCOPE
1.1 This test method, commonly referred to as the L-37-1 test, describes a test procedure for evaluating the load-carrying capacity, wear performance, and extreme pressure properties of a gear lubricant in a hypoid axle under conditions of low-speed, high-torque operation.3  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.2.1 Exceptions—Where there is no direct SI equivalent such as National Pipe threads/diameters, tubing size, or where there is a sole source supply equipment specification.
1.2.1.1 The drawing in Annex A6 is in inch-pound units.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific warning statements are provided in 7.2 and 10.1.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    18 pages
    English language
    sale 15% off
  • Standard
    18 pages
    English language
    sale 15% off
ASTM
ASTM D6416/D6416M-16(2024)(Test Method)
Standard Test Method for Two-Dimensional Flexural Properties of Simply Supported Sandwich Composite Plates Subjected to a Distributed Load

SIGNIFICANCE AND USE
5.1 This test method simulates the hydrostatic loading conditions which are often present in actual sandwich structures, such as marine hulls. This test method can be used to compare the two-dimensional flexural stiffness of a sandwich composite made with different combinations of materials or with different fabrication processes. Since it is based on distributed loading rather than concentrated loading, it may also provide more realistic information on the failure mechanisms of sandwich structures loaded in a similar manner. Test data should be useful for design and engineering, material specification, quality assurance, and process development. In addition, data from this test method would be useful in refining predictive mathematical models or computer code for use as structural design tools. Properties that may be obtained from this test method include:  
5.1.1 Panel surface deflection at load,  
5.1.2 Panel face-sheet strain at load,  
5.1.3 Panel bending stiffness,  
5.1.4 Panel shear stiffness,  
5.1.5 Panel strength, and  
5.1.6 Panel failure modes.
SCOPE
1.1 This test method determines the two-dimensional flexural properties of sandwich composite plates subjected to a distributed load. The test fixture uses a relatively large square panel sample which is simply supported all around and has the distributed load provided by a water-filled bladder. This type of loading differs from the procedure of Test Method C393, where concentrated loads induce one-dimensional, simple bending in beam specimens.  
1.2 This test method is applicable to composite structures of the sandwich type which involve a relatively thick layer of core material bonded on both faces with an adhesive to thin-face sheets composed of a denser, higher-modulus material, typically, a polymer matrix reinforced with high-modulus fibers.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text the inch-pound units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    12 pages
    English language
    sale 15% off
ASTM
ASTM D3019/D3019M-17(2024)(Specification)
Standard Specification for Lap Cement Used with Asphalt Roll Roofing, Non-Fibered, and Fibered

ABSTRACT
This specification covers the physical requirements and testing of three types of lap cement for use with asphalt roll roofing. Type I is a brushing consistency lap cement intended for use in the exposed-nailing method of roll roofing application, and contains no mineral or other stabilizers. This type is further divided into two grades, as follows: Grade 1, which is made with an air-blown asphalt; and Grade 2, which is made with a vacuum-reduced or steam-refined asphalt. Both Types II and III, on the other hand, are heavy brushing or light troweling consistency lap cement intended for use in the concealed-nailing method of roll roofing application, only that Type II cement contains a quantity of short-fibered asbestos, while Type III cement contains a quantity of mineral or other stabilizers, or both, but contains no asbestos. The lap cements shall be sampled for testing, and shall adhere to specified values of the following properties: water content; distillation (total distillate at given temperatures); softening point of residue; solubility in trichloroethylene; and strength at indicated age.
SCOPE
1.1 This specification covers lap cement consisting of asphalt dissolved in a volatile petroleum solvent with or without mineral or other stabilizers, or both, for use with roll roofing. The fibered version of these cements excludes the use of asbestos fibers.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following precautionary caveat applies only to the test method portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4586/D4586M-07(2024)(Specification)
Standard Specification for Asphalt Roof Cement, Asbestos-Free

ABSTRACT
This specification covers the testing and requirements for two types and two classes of asbestos-free asphalt roof cement consisting of an asphalt base, volatile petroleum solvents, and mineral and/or other stabilizers, mixed to a smooth, uniform consistency suitable for trowel application to roofing and flashing. Type I is made from asphalts characterized as self-healing, adhesive, and ductile, while Type II is made from asphalt characterized by high softening point and relatively low ductility. Class I is used for application to essentially dry surfaces, while Class II is used for application to damp, wet, or underwater surfaces. The roof cements shall comply with composition limits for water, nonvolatile matter, mineral and/or other stabilizers, and bitumen (asphalt). They shall also meet physical requirements such as uniformity, workability, and pliability and behavior at given temperatures.
SCOPE
1.1 This specification covers asbestos-free asphalt roof cement suitable for trowel application to roofings and flashings.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following precautionary caveat pertains only to the test method portion, Section 8 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM C1178/C1178M-24(Specification)
Standard Specification for Coated Glass Mat Water-Resistant Gypsum Backing Panel

ABSTRACT
This specification covers coated glass mat water-resistant gypsum backing panel designed for use on ceilings and walls in bath and shower areas as a base for the application of ceramic or plastic tile. Coated glass mat water-resistant gypsum backing panel shall consist of a noncombustible water-resistant gypsum core, surfaced with glass mat, partially or completely embedded in the core, and with a water-resistant coating on one surface. The specimens shall be tested for flexural strength, humidified deflection, core hardness, end hardness, edge hardness, nail pull resistance, water resistance, and surface water absorption. Coated glass mat water-resistant gypsum backing panel shall have surfaces true and free of imperfections that render the panel unfit for its designed use.
SCOPE
1.1 This specification covers coated glass mat water-resistant gypsum backing panel designed for use on ceilings and walls in bath and shower areas as a base for the application of ceramic or plastic tile.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Within the text, the SI units are shown in brackets.  
1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM D43/D43M-00(2024)(Specification)
Standard Specification for Coal Tar Primer Used in Roofing, Dampproofing, and Waterproofing

ABSTRACT
This specification covers coal tar primer suitable for use with coal tar pitch in roofing, dampproofing, and waterproofing below or above ground level, for application to concrete, masonry, and coal tar surfaces. Different tests shall be conducted in order to determine the following physical properties of coal tar primer: water content, consistency, specific gravity, matter insoluble in benzene, distillation, and coke residue content.
SCOPE
1.1 This specification covers coal tar primer suitable for use with coal tar pitch in roofing, dampproofing, and waterproofing below or above ground level, for application to concrete, masonry, and coal tar surfaces.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM A456/A456M-24(Specification)
Standard Specification for Magnetic Particle Examination of Large Crankshaft Forgings

ABSTRACT
This test method deals with the acceptance criteria for the magnetic particle examination of forged steel crankshafts and forgings having large main bearing journal or crankpin diameters. Covered here are three classes of forgings, which shall be evaluated under two areas of inspection, namely: major critical areas, and minor critical areas. During inspection, magnetic particle indications shall be classified as: surface indications, which include nonmetallic inclusions or stringers, open or twist cracks, flakes, or pipes; open or pinpoint indications; and non-open indications. Procedures for dimpling, depressing, inspection, and product marking are also mentioned.
SCOPE
1.1 This is an acceptance specification for the magnetic particle inspection of forged steel crankshafts having main bearing journals or crankpins 4 in. [200 mm] or larger in diameter.  
1.2 There are three classes, with acceptance standards of increasing severity:  
1.2.1 Class 1.  
1.2.2 Class 2 (originally the sole acceptance standard of this specification).  
1.2.3 Class 3 (formerly covered in Supplementary Requirement S1 of Specification A456 – 64 (1970)).  
1.3 This specification is not intended to cover continuous grain flow crankshafts (see Specification A983/A983M); however, Specification A986/A986M may be used for this purpose.
Note 1: Specification A668/A668M is a product specification which may be used for slab-forged crankshaft forgings that are usually twisted in order to set the crankpin angles, or for barrel forged crankshafts where the crankpins are machined in the appropriate configuration from a cylindrical forging.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.5 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch units.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off