ASTM G95-07(2021)
(Test Method)Standard Test Method for Cathodic Disbondment Test of Pipeline Coatings (Attached Cell Method) (Withdrawn 2024)
Standard Test Method for Cathodic Disbondment Test of Pipeline Coatings (Attached Cell Method) (Withdrawn 2024)
SIGNIFICANCE AND USE
4.1 Damage to pipe coating is almost unavoidable during transportation and construction. Breaks or holidays in pipe coatings may expose the pipe to possible corrosion since, after a pipe has been installed underground, the surrounding earth will be moisture-bearing and will constitute an effective electrolyte. Applied cathodic protection potentials may cause loosening of the coating, beginning at holiday edges. Spontaneous holidays may also be caused by such potentials. This test method provides accelerated conditions for cathodic disbondment to occur and provides a measure of resistance of coatings to this type of action.
4.2 The effects of the test are to be evaluated by physical examinations and monitoring the current drawn by the test specimen. Usually there is no correlation between the two methods of evaluation, but both methods are significant. Physical examination consists of assessing the effective contact of the coating with the metal surface in terms of observed differences in the relative adhesive bond. It is usually found that the cathodically disbonded area propagates from an area where adhesion is zero to an area where adhesion reaches the original level. An intermediate zone of decreased adhesion may also be present.
4.3 Assumptions associated with test results include:
4.3.1 Maximum adhesion, or bond, is found in the coating that was not immersed in the test liquid, and
4.3.2 Decreased adhesion in the immersed test area is the result of cathodic disbondment.
4.4 Ability to resist disbondment is a desired quality on a comparative basis, but disbondment in this test method is not necessarily an adverse indication of coating performance. The virtue of this test method is that all dielectric-type coatings now in common use will disbond to some degree, thus providing a means of comparing one coating to another.
4.5 The current density appearing in this test method is much greater than that usually required for cathodic protection in nat...
SCOPE
1.1 This test method covers accelerated procedures for simultaneously determining comparative characteristics of coating systems applied to steep pipe exterior for the purpose of preventing or mitigating corrosion that may occur in underground service where the pipe will be in contact with natural soils and will receive cathodic protection. They are intended for use with samples of coated pipe taken from commercial production and are applicable to such samples when the coating is characterized by function as an electrical barrier.
1.2 This test method is intended to facilitate testing of coatings where the test cell is cemented to the surface of the coated pipe specimen. This is appropriate when it is impractical to submerge or immerse the test specimen as required by Test Methods G8, G42, or G80. Coating sample configuration such as flat plate and small diameter pipe may be used, provided that the test procedure remains unchanged.2
1.3 This test method allows options that must be identified in the report.
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
WITHDRAWN RATIONALE
This test method covered accelerated procedures for simultaneously determining comparative characteristics of coating systems applied to ste...
General Information
Relations
Buy Standard
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: G95 − 07 (Reapproved 2021)
Standard Test Method for
Cathodic Disbondment Test of Pipeline Coatings (Attached
1
Cell Method)
ThisstandardisissuedunderthefixeddesignationG95;thenumberimmediatelyfollowingthedesignationindicatestheyearoforiginal
adoptionor,inthecaseofrevision,theyearoflastrevision.Anumberinparenthesesindicatestheyearoflastreapproval.Asuperscript
epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope mendations issued by the World Trade Organization Technical
Barriers to Trade (TBT) Committee.
1.1 This test method covers accelerated procedures for
simultaneously determining comparative characteristics of
2. Referenced Documents
coating systems applied to steep pipe exterior for the purpose
3
2.1 ASTM Standards:
of preventing or mitigating corrosion that may occur in
G8Test Methods for Cathodic Disbonding of Pipeline Coat-
underground service where the pipe will be in contact with
ings
natural soils and will receive cathodic protection. They are
G12Test Method for Nondestructive Measurement of Film
intended for use with samples of coated pipe taken from
Thickness of Pipeline Coatings on Steel (Withdrawn
commercial production and are applicable to such samples
4
2013)
when the coating is characterized by function as an electrical
G42Test Method for Cathodic Disbonding of Pipeline
barrier.
Coatings Subjected to Elevated Temperatures
1.2 This test method is intended to facilitate testing of
G62Test Methods for Holiday Detection in Pipeline Coat-
coatings where the test cell is cemented to the surface of the
ings
coated pipe specimen. This is appropriate when it is impracti-
G80Test Method for Specific Cathodic Disbonding of Pipe-
4
cal to submerge or immerse the test specimen as required by
line Coatings (Withdrawn 2013)
Test Methods G8, G42,or G80. Coating sample configuration
such as flat plate and small diameter pipe may be used,
3. Summary of Test Method
2
provided that the test procedure remains unchanged.
3.1 The test method described subjects the coating on the
1.3 This test method allows options that must be identified testspecimentoelectricalstressinahighlyconductivealkaline
in the report. electrolyte. Electrical stress is obtained from an impressed
direct-current system. An intentional holiday is to be made in
1.4 The values stated in SI units are to be regarded as the
the coating prior to starting of test.
standard. The values given in parentheses are for information
3.1.1 Electrical instrumentation is provided for measuring
only.
the current and the potential throughout the test cycle. At the
1.5 This standard does not purport to address all of the
conclusion of the test period, the test specimen is physically
safety concerns, if any, associated with its use. It is the
examined.
responsibility of the user of this standard to establish appro-
3.1.2 Physical examination is conducted by comparing the
priate safety, health, and environmental practices and deter-
extent of loosened or disbonded coating at the intentional
mine the applicability of regulatory limitations prior to use.
holiday in the immersed area with extent of loosened or
1.6 This international standard was developed in accor-
disbondedcoatingatareferenceholidaymadeinthecoatingin
dance with internationally recognized principles on standard-
an area that was not immersed.
ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom- 4. Significance and Use
4.1 Damage to pipe coating is almost unavoidable during
transportation and construction. Breaks or holidays in pipe
1
This test method is under the jurisdiction of ASTM Committee D01 on Paint
and Related Coatings, Materials, andApplications and is the direct responsibility of
3
Subcommittee D01.48 on Durability of Pipeline Coating and Linings. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Nov. 1, 2021. Published November 2021. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approvedin1987.Lastpreviouseditionapprovedin2013asG95–07(2013).DOI: Standards volume information, refer to the standard’s Document Summary page on
10.1520/G0095-07R21. the ASTM website.
2 4
For other cathodic disbondment testing procedures, consult Test Methods G8, The last approved version of this historical standard is referenced on
G42, and G80. www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
G95 − 07 (2021)
coatings may expose the pipe to possible corrosion since, aft
...
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: G95 − 07 (Reapproved 2021)
Standard Test Method for
Cathodic Disbondment Test of Pipeline Coatings (Attached
1
Cell Method)
This standard is issued under the fixed designation G95; the number immediately following the designation indicates the year of original
adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript
epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope mendations issued by the World Trade Organization Technical
Barriers to Trade (TBT) Committee.
1.1 This test method covers accelerated procedures for
simultaneously determining comparative characteristics of
2. Referenced Documents
coating systems applied to steep pipe exterior for the purpose
3
2.1 ASTM Standards:
of preventing or mitigating corrosion that may occur in
G8 Test Methods for Cathodic Disbonding of Pipeline Coat-
underground service where the pipe will be in contact with
ings
natural soils and will receive cathodic protection. They are
G12 Test Method for Nondestructive Measurement of Film
intended for use with samples of coated pipe taken from
Thickness of Pipeline Coatings on Steel (Withdrawn
commercial production and are applicable to such samples
4
2013)
when the coating is characterized by function as an electrical
G42 Test Method for Cathodic Disbonding of Pipeline
barrier.
Coatings Subjected to Elevated Temperatures
1.2 This test method is intended to facilitate testing of
G62 Test Methods for Holiday Detection in Pipeline Coat-
coatings where the test cell is cemented to the surface of the
ings
coated pipe specimen. This is appropriate when it is impracti-
G80 Test Method for Specific Cathodic Disbonding of Pipe-
4
cal to submerge or immerse the test specimen as required by
line Coatings (Withdrawn 2013)
Test Methods G8, G42, or G80. Coating sample configuration
such as flat plate and small diameter pipe may be used,
3. Summary of Test Method
2
provided that the test procedure remains unchanged.
3.1 The test method described subjects the coating on the
1.3 This test method allows options that must be identified
test specimen to electrical stress in a highly conductive alkaline
in the report. electrolyte. Electrical stress is obtained from an impressed
direct-current system. An intentional holiday is to be made in
1.4 The values stated in SI units are to be regarded as the
the coating prior to starting of test.
standard. The values given in parentheses are for information
3.1.1 Electrical instrumentation is provided for measuring
only.
the current and the potential throughout the test cycle. At the
1.5 This standard does not purport to address all of the
conclusion of the test period, the test specimen is physically
safety concerns, if any, associated with its use. It is the
examined.
responsibility of the user of this standard to establish appro-
3.1.2 Physical examination is conducted by comparing the
priate safety, health, and environmental practices and deter-
extent of loosened or disbonded coating at the intentional
mine the applicability of regulatory limitations prior to use.
holiday in the immersed area with extent of loosened or
1.6 This international standard was developed in accor-
disbonded coating at a reference holiday made in the coating in
dance with internationally recognized principles on standard-
an area that was not immersed.
ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom- 4. Significance and Use
4.1 Damage to pipe coating is almost unavoidable during
transportation and construction. Breaks or holidays in pipe
1
This test method is under the jurisdiction of ASTM Committee D01 on Paint
and Related Coatings, Materials, and Applications and is the direct responsibility of
3
Subcommittee D01.48 on Durability of Pipeline Coating and Linings. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Nov. 1, 2021. Published November 2021. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1987. Last previous edition approved in 2013 as G95 – 07 (2013). DOI: Standards volume information, refer to the standard’s Document Summary page on
10.1520/G0095-07R21. the ASTM website.
2 4
For other cathodic disbondment testing procedures, consult Test Methods G8, The last approved version of this historical standard is referenced on
G42, and G80. www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
G95 − 07 (2021)
coatings may expose the pipe to possible corrosion since, after 4.3.2 Decreased adhesion in the immersed test area is the
a pipe h
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.