EN 12390-3:2019
(Main)Testing hardened concrete - Part 3: Compressive strength of test specimens
Testing hardened concrete - Part 3: Compressive strength of test specimens
This document specifies a method for the determination of the compressive strength of test specimens of hardened concrete.
Prüfung von Festbeton - Teil 3: Druckfestigkeit von Probekörpern
Diese Europäische Norm legt ein Verfahren für die Bestimmung der Druckfestigkeit von Probekörpern aus Festbeton fest.
Essais pour béton durci - Partie 3 : Résistance à la compression des éprouvettes
Le présent document spécifie une méthode qui permet de déterminer la résistance à la compression d’échantillons de béton durci.
Preskušanje strjenega betona - 3. del: Tlačna trdnost preskušancev
Ta evropski standard določa metodo za ugotavljanje tlačne trdnosti preskušancev iz strjenega betona.
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
01-oktober-2019
Nadomešča:
SIST EN 12390-3:2009
SIST EN 12390-3:2009/AC:2011
Preskušanje strjenega betona - 3. del: Tlačna trdnost preskušancev
Testing hardened concrete - Part 3: Compressive strength of test specimens
Prüfung von Festbeton - Teil 3: Druckfestigkeit von Probekörpern
Essai pour béton durci - Partie 3 : Résistance à la compression des éprouvettes
Ta slovenski standard je istoveten z: EN 12390-3:2019
ICS:
91.100.30 Beton in betonski izdelki Concrete and concrete
products
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
EN 12390-3
EUROPEAN STANDARD
NORME EUROPÉENNE
June 2019
EUROPÄISCHE NORM
ICS 91.100.30 Supersedes EN 12390-3:2009
English Version
Testing hardened concrete - Part 3: Compressive strength
of test specimens
Essais pour béton durci - Partie 3 : Résistance à la Prüfung von Festbeton - Teil 3: Druckfestigkeit von
compression des éprouvettes Probekörpern
This European Standard was approved by CEN on 29 April 2019.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this
European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references
concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN
member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by
translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management
Centre has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway,
Poland, Portugal, Republic of North Macedonia, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and
United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
CEN-CENELEC Management Centre: Rue de la Science 23, B-1040 Brussels
© 2019 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 12390-3:2019 E
worldwide for CEN national Members.
Contents Page
European foreword . 3
1 Scope . 5
2 Normative references . 5
3 Terms and definitions . 5
4 Principle . 5
5 Apparatus . 5
6 Test specimens . 5
7 Procedure. 6
7.1 Specimen preparation and positioning . 6
7.2 Loading. 6
7.3 Assessment of type of failure . 7
8 Expression of results . 7
9 Test report . 7
10 Precision . 11
Annex A Adjustment of test specimens. 12
Annex B Procedure for testing specimens with dimensions which are outside the
tolerances of the designated sizes of EN 12390-1 . 18
European foreword
This document (EN 12390-3:2019) has been prepared by Technical Committee CEN/TC 104 “Concrete
and related products”, the secretariat of which is held by SN.
This European Standard shall be given the status of a national standard, either by publication of an
identical text or by endorsement, at the latest by December 2019, and conflicting national standards
shall be withdrawn at the latest by December 2019.
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. CEN shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN 12390-3:2009.
It is recognized good practice to include measurement of density prior to the determination of
compressive strength.
The methods for adjusting the ends of test specimens, given in Annex A, have been validated in a
laboratory inter-comparison, part-funded by the EC under the Measurement and Testing Programme;
contract MATI-CT-94-0043.
This standard is one of a series on testing concrete.
EN 12390, Testing hardened concrete, consists of the following parts:
— Part 1: Shape, dimensions and other requirements of specimens and moulds;
— Part 2: Making and curing specimens for strength tests;
— Part 3: Compressive strength of test specimens;
— Part 4: Compressive strength – Specification for testing machines;
— Part 5: Flexural strength of test specimens;
— Part 6: Tensile splitting strength of test specimens;
— Part 7: Density of hardened concrete;
— Part 8: Depth of penetration of water under pressure;
— Part 11: Determination of the chloride resistance of concrete, unidirectional diffusion;
— Part 12: Determination of the potential carbonation resistance of concrete: Accelerated carbonation
method (in preparation);
— Part 13: Determination of secant modulus of elasticity in compression;
— Part 14: Semi-adiabatic method for the determination of heat released by concrete during its
hardening process;
— Part 15: Adiabatic method for the determination of heat released by concrete during its hardening
process;
— Part 16: Determination of the shrinkage of concrete (in preparation);
— Part 17: Determination of creep of concrete in compression (in preparation);
— Part 18: Determination of the chloride migration coefficient (in preparation).
This edition includes the following significant technical changes with respect to EN 12390-3:2009:
— editorial revision;
— technical corrections;
— clarification of acceptable tolerances of test specimen size or diameter;
— clarification of procedure from when the specimen is removed from curing until being tested for
strength.
According to the CEN-CENELEC Internal Regulations, the national standards organisations of the
following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria,
Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia,
France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta,
Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland,
Turkey and the United Kingdom.
1 Scope
This document specifies a method for the determination of the compressive strength of test specimens
of hardened concrete.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
EN 197-1, Cement — Part 1: Composition, specifications and conformity criteria for common cements
EN 12350-1, Testing fresh concrete — Part 1: Sampling
EN 12390-1, Testing hardened concrete — Part 1: Shape, dimensions and other requirements for
specimens and moulds
EN 12390-2, Testing hardened concrete — Part 2: Making and curing specimens for strength tests
EN 12390-4, Testing hardened concrete — Part 4: Compressive strength — Specification for testing
machines
EN 12390-7, Testing hardened concrete — Part 7: Density of hardened concrete
EN 12504-1, Testing concrete in structures — Part 1: Cored specimens — Taking, examining and testing
in compression
ISO 3310-1, Test sieves — Technical requirements and testing — Part 1: Test sieves of metal wire cloth
3 Terms and definitions
No terms and definitions are listed in this document.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— IEC Electropedia: available at http://www.electropedia.org/
— ISO Online browsing platform: available at http://www.iso.org/obp
4 Principle
Specimens are loaded to failure in a compression testing machine conforming to EN 12390-4. The
maximum load sustained by the specimen is recorded and the compressive strength of the concrete is
calculated.
5 Apparatus
Compression testing machine, conforming to EN 12390-4.
6 Test specimens
The test specimen shall be a cube, cylinder or core meeting the requirements of EN 12350-1,
EN 12390-1, EN 12390-2, or EN 12504-1.
If the dimension of the test specimen does not conform to the tolerances for designated size or diameter
in EN 12390-1, it shall be rejected, adjusted or tested in accordance with the procedure given in
Annex B.
One of the methods given in Annex A shall be used to adjust the specimen.
If damaged specimens or specimens which are honeycombed are tested, their condition shall be noted
in the test report in Clause 9, c).
7 Procedure
7.1 Specimen preparation and positioning
The load bearing surfaces of the specimen shall be moulded in the case of cube specimens or ground or
capped in accordance with Annex A in the case of cylinder, core or adjusted specimens.
After removal of the specimen from curing, the specimens shall be tested for strength as soon as
practicable, but within 10 hours. The test facility shall be at a temperature of (20 ± 5) °C (or (25 ± 5) °C
in hot climates). Where specimens are to be stored in the testing facility for more than 4 hours they
shall be protected from moisture loss e.g. by covering with wet hessian or impermeable membrane.
Wipe all testing machine bearing surfaces clean and remove any loose grit or other extraneous material
from the surfaces of the specimen that will be in contact with the platens.
Do not use packing, other than auxiliary platens or spacing blocks (see EN 12390-4) between the
specimen and the platens of the testing machine.
With two-column testing machines, cubic specimens should be placed with the trowelled surface not in
contact with the platens and facing a column.
Wipe the excess moisture from the surface of the specimen before placing in the testing machine.
Position the cube specimens so that the load is applied perpendicularly to the direction of casting.
Centre the specimen with respect to the lower platen to an accuracy of 1 % of the designated size of
cubic, or designated diameter of cylindrical specimens.
If auxiliary platens are used, align them with the top and bottom face of the specimen.
7.2 Loading
Select a constant rate of loading within the range 0,6 ± 0,2 MPa/s (N/mm ·s). After the application of
the initial load, which does not exceed approximately 30 % of the failure load, apply the load to the
specimen without shock and increase continuously at the selected constant rate ± 10 %, until no greater
load can be sustained.
The initial load should be applied as close as possible to the selected rate of loading.
When using manually controlled testing machines, correct any tendency for the selected rate of loading
to decrease, as specimen failure is approached by appropriate adjustment of the controls.
During the final stages of the test, the load rate can be affected by the failure mode of the specimen.
Nevertheless every effort should be made to maintain the selected loading rate as close as possible.
Record the maximum load indicated in kN.
NOTE Further guidance on loading rates for high and low strength concrete e.g. above 80 MPa (N/mm ) and
below 20 MPa (N/mm ) cube strengths, may be given in provisions valid in the place of use of the concrete.
7.3 Assessment of type of failure
Examples of the failure of specimen showing that the tests have proceeded satisfactorily are given in
Figure 1 for cubes and in Figure 3 for cylinders.
Examples for unsatisfactory failure of specimens are shown in Figure 2 for cubes and in Figure 4 for
cylinders. If failure is unsatisfactory this shall be recorded with reference to the pattern letter according
to Figure 2 or 4 closest to that observed.
NOTE Unsatisfactory failures can be caused by many different factors.
For cylindrical specimens, failure of the capping before the concrete is an unsatisfactory failure.
8 Expression of results
The compressive strength is given b
...
SLOVENSKI STANDARD
01-oktober-2019
Nadomešča:
SIST EN 12390-3:2009
SIST EN 12390-3:2009/AC:2011
Preskušanje strjenega betona - 3. del: Tlačna trdnost preskušancev
Testing hardened concrete - Part 3: Compressive strength of test specimens
Prüfung von Festbeton - Teil 3: Druckfestigkeit von Probekörpern
Essai pour béton durci - Partie 3 : Résistance à la compression des éprouvettes
Ta slovenski standard je istoveten z: EN 12390-3:2019
ICS:
91.100.30 Beton in betonski izdelki Concrete and concrete
products
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
EN 12390-3
EUROPÄISCHE NORM
EUROPEAN STANDARD
Juni 2019
NORME EUROPÉENNE
ICS 91.100.30 Ersatz für EN 12390-3:2009
Deutsche Fassung
Prüfung von Festbeton - Teil 3: Druckfestigkeit von
Probekörpern
Testing hardened concrete - Part 3: Compressive Essais pour béton durci - Partie 3 : Résistance à la
strength of test specimens compression des éprouvettes
Diese Europäische Norm wurde vom CEN am 29. April 2019 angenommen.
Die CEN-Mitglieder sind gehalten, die CEN/CENELEC-Geschäftsordnung zu erfüllen, in der die Bedingungen festgelegt sind, unter
denen dieser Europäischen Norm ohne jede Änderung der Status einer nationalen Norm zu geben ist. Auf dem letzten Stand
befindliche Listen dieser nationalen Normen mit ihren bibliographischen Angaben sind beim CEN-CENELEC-Management-
Zentrum oder bei jedem CEN-Mitglied auf Anfrage erhältlich.
Diese Europäische Norm besteht in drei offiziellen Fassungen (Deutsch, Englisch, Französisch). Eine Fassung in einer anderen
Sprache, die von einem CEN-Mitglied in eigener Verantwortung durch Übersetzung in seine Landessprache gemacht und dem
Management-Zentrum mitgeteilt worden ist, hat den gleichen Status wie die offiziellen Fassungen.
CEN-Mitglieder sind die nationalen Normungsinstitute von Belgien, Bulgarien, Dänemark, Deutschland, Estland, Finnland,
Frankreich, Griechenland, Irland, Island, Italien, Kroatien, Lettland, Litauen, Luxemburg, Malta, den Niederlanden, Norwegen,
Österreich, Polen, Portugal, der Republik Nordmazedonien, Rumänien, Schweden, der Schweiz, Serbien, der Slowakei, Slowenien,
Spanien, der Tschechischen Republik, der Türkei, Ungarn, dem Vereinigten Königreich und Zypern.
EUROPÄISCHES KOMITEE FÜR NORMUNG
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
CEN-CENELEC Management-Zentrum: Rue de la Science 23, B-1040 Brüssel
© 2019 CEN Alle Rechte der Verwertung, gleich in welcher Form und in welchem Ref. Nr. EN 12390-3:2019 D
Verfahren, sind weltweit den nationalen Mitgliedern von CEN
vorbehalten.
Inhalt
Seite
Europäisches Vorwort . 3
1 Anwendungsbereich . 5
2 Normative Verweisungen . 5
3 Begriffe . 5
4 Kurzbeschreibung . 5
5 Prüfeinrichtung . 5
6 Probekörper . 6
7 Durchführung . 6
7.1 Vorbereitung und Anordnung der Probekörper. 6
7.2 Belastung . 7
7.3 Beurteilung der Bruchbilder . 7
8 Angabe der Ergebnisse . 7
9 Prüfbericht . 8
10 Präzision . 11
Anhang A (normativ) Angleichen der Probekörper . 12
A.1 Allgemeines . 12
A.2 Abschleifen . 12
A.3 Aufbringen des Abgleichmaterials (unter Verwendung von Tonerdeschmelzzement) . 12
A.4 Aufbringen des Abgleichmaterials — Schwefelmischung . 13
A.5 Aufbringen des Abgleichmaterials — Sandkastenverfahren — Verwendung von
Sandkästen für Zylinderproben . 14
A.5.1 Vorbereitung . 14
A.5.2 Prüfeinrichtung . 14
A.5.3 Durchführung . 15
Anhang B (normativ) Prüfung von Probekörpern mit Maßen außerhalb der Toleranzen der
Nennmaße nach EN 12390-1 . 18
B.1 Kurzbeschreibung . 18
B.2 Gerät . 18
B.3 Durchführung . 18
B.3.1 Würfel . 18
B.3.2 Zylinder oder Bohrkerne . 18
B.3.3 Druckfestigkeitsprüfung . 19
Literaturhinweise . 20
Europäisches Vorwort
Dieses Dokument (EN 12390-3:2019) wurde vom Technischen Komitee CEN/TC 104 „Beton und zugehörige
Produkte“ erarbeitet, dessen Sekretariat von SN gehalten wird.
Diese Europäische Norm muss den Status einer nationalen Norm erhalten, entweder durch Veröffentlichung
eines identischen Textes oder durch Anerkennung bis Dezember 2019, und etwaige entgegenstehende
nationale Normen müssen bis Dezember 2019 zurückgezogen werden.
Es wird auf die Möglichkeit hingewiesen, dass einige Elemente dieses Dokuments Patentrechte berühren
können. CEN ist nicht dafür verantwortlich, einige oder alle diesbezüglichen Patentrechte zu identifizieren.
Dieses Dokument ersetzt EN 12390-3:2009.
Es ist allgemein üblich, dass vor der Druckfestigkeitsprüfung eine Bestimmung der Rohdichte erfolgt.
Die in Anhang A angegebenen Verfahren zum Abgleichen der Probekörper wurden in einem Laborringver-
such, der teilweise von der Europäischen Gemeinschaft unter dem EG-Mess- und Prüfprogramm gefördert
wurde (Vertragsnummer MATI-CT-94-0043), validiert.
Diese Norm ist Bestandteil einer Normenreihe für die Prüfung von Beton.
EN 12390, Prüfung von Festbeton, besteht aus den folgenden Teilen:
Teil 1: Form, Maße und andere Anforderungen für Probekörpern und Formen
Teil 2: Herstellung und Lagerung von Probekörpern für Festigkeitsprüfungen
Teil 3: Druckfestigkeit von Probekörpern
Teil 4: Bestimmung der Druckfestigkeit — Anforderungen an Prüfmaschinen
Teil 5: Biegezugfestigkeit von Probekörpern
Teil 6: Spaltzugfestigkeit von Probekörpern
Teil 7: Dichte von Festbeton
Teil 8: Wassereindringtiefe unter Druck
Teil 11: Bestimmung des Chloridwiderstandes von Beton — Einseitig gerichtete Diffusion
Teil 12: Bestimmung des Karbonatisierungswiderstandes von Beton — Beschleunigtes Karbonatisierungs-
verfahren (in Vorbereitung)
Teil 13: Bestimmung des Elastizitätsmoduls unter Druckbelastung (Sekantenmodul)
Teil 14: Teiladiabatisches Verfahren zur Bestimmung der Wärme, die während des Erhärtungsprozesses
von Beton freigesetzt wird
Teil 15: Adiabatisches Verfahren zur Bestimmung der Wärme, die während des Erhärtungsprozesses von
Beton freigesetzt wird
Teil 16: Bestimmung des Schwindens von Beton (in Vorbereitung)
Teil 17: Bestimmung des Kriechens von Beton unter Druckspannung (in Vorbereitung)
Teil 18: Bestimmung des Chloridmigrationskoeffizienten (in Vorbereitung)
Diese Fassung beinhaltet die folgenden wesentlichen technischen Änderungen gegenüber EN 12390-3:2009:
redaktionelle Überarbeitung;
technische Korrekturen;
Erläuterung von zulässigen Toleranzen der Größe oder des Durchmessers von Probekörpern;
Erläuterung der Verfahrensweise vom Zeitpunkt der Entnahme der Probekörper aus der Lagerung bis
zur Festigkeitsprüfung.
Entsprechend der CEN-CENELEC-Geschäftsordnung sind die nationalen Normungsinstitute der folgenden
Länder gehalten, diese Europäische Norm zu übernehmen: Belgien, Bulgarien, Dänemark, Deutschland, die
ehemalige jugoslawische Republik Mazedonien, Estland, Finnland, Frankreich, Griechenland, Irland, Island,
Italien, Kroatien, Lettland, Litauen, Luxemburg, Malta, Niederlande, Norwegen, Österreich, Polen, Portugal,
Rumänien, Schweden, Schweiz, Serbien, Slowakei, Slowenien, Spanien, Tschechische Republik, Türkei,
Ungarn, Vereinigtes Königreich und Zypern.
1 Anwendungsbereich
Dieses Dokument legt ein Verfahren für die Bestimmung der Druckfestigkeit von Probekörpern aus Fest-
beton fest.
2 Normative Verweisungen
Die folgenden Dokumente werden im Text in solcher Weise in Bezug genommen, dass einige Teile davon
oder ihr gesamter Inhalt Anforderungen des vorliegenden Dokuments darstellen. Bei datierten
Verweisungen gilt nur die in Bezug genommene Ausgabe. Bei undatierten Verweisungen gilt die letzte
Ausgabe des in Bezug genommenen Dokuments (einschließlich aller Änderungen).
EN 197-1, Zement — Teil 1: Zusammensetzung, Anforderungen und Konformitätskriterien von Normalzement
EN 12350-1, Prüfung von Frischbeton — Teil 1: Probenahme und Prüfgeräte
EN 12390-1, Prüfung von Festbeton — Teil 1: Form, Maße und andere Anforderungen für Probekörper und
Formen
EN 12390-2, Prüfung von Festbeton — Teil 2: Herstellung und Lagerung von Probekörpern für
Festigkeitsprüfungen
EN 12390-4, Prüfung von Festbeton — Teil 4: Bestimmung der Druckfestigkeit — Anforderungen an
Prüfmaschinen
EN 12390-7, Prüfung von Frischbeton — Teil 7: Dichte von Festbeton
EN 12504-1, Prüfung von Beton in Bauwerken — Teil 1: Bohrkernproben — Herstellung, Untersuchung und
Prüfung der Druckfestigkeit
ISO 3310-1, Test sieves — Technical requirements and testing — Part 1: Test sieves of metal wire cloth
3 Begriffe
In diesem Dokument werden keine Begriffe aufgeführt.
ISO und IEC stellen terminologische Datenbanken für die Verwendung in der Normung unter den folgenden
Adressen bereit:
IEC Electropedia: verfügbar unter http://www.electropedia.org/
ISO Online Browsing Platform: verfügbar unter http://www.iso.org/obp
4 Kurzbeschreibung
Die Probekörper werden bis zum Bruch in einer Druckprüfmaschine nach EN 12390-4 belastet. Die erreichte
Höchstlast wird aufgezeichnet und die Druckfestigkeit des Betons wird berechnet.
5 Prüfeinrichtung
Druckprüfmaschine nach EN 12390-4.
6 Probekörper
Die Probekörper müssen Würfel, Zylinder oder Bohrkerne sein und den Anforderungen von EN 12350-1,
EN 12390-1, EN 12390-2 oder EN 12504-1 entsprechen.
Wenn die Maße des Probekörpers nicht den Toleranzen hinsichtlich des Nennmaßes oder -durchmessers
nach EN 12390-1 entsprechen, muss der Probekörper verworfen, abgeglichen oder entsprechend des in
Anhang B angegebenen Verfahrens geprüft werden.
Zum Abgleichen des Probekörpers ist eines der im Anhang A angegebenen Verfahren anzuwenden.
Wenn Probekörper geprüft werden, die Beschädigungen oder Fehlstellen aufweisen, muss ihre
Beschaffenheit in den Prüfbericht in Abschnitt 9, c) angegeben werden.
7 Durchführung
7.1 Vorbereitung und Anordnung der Probekörper
Die Lastaufnahmeflächen des Probekörpers müssen im Falle von Würfelproben geschalt werden oder im
Falle von Zylinder-, Bohrkern- oder abgeglichenen Proben nach Anhang A geschli
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.