ISO/TR 8461:1984

Rubber, vulcanized — Classification — Rubber materials

Caoutchouc vulcanisé — Classification — Matériaux caoutchouc

General Information

• Status: Withdrawn
• Publication Date: 31-Aug-1984
• Withdrawal Date: 31-Aug-1984
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45 - Rubber and rubber products
• Drafting Committee: ISO/TC 45 - Rubber and rubber products
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 18-Sep-2000

Standards Content (Sample)

TECHNICAL REPORT 8461
Published 1984-10-01
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION. MEXAYHAPOjJHAF1 OPTAHM3AQMfl IlO CTAHflAPTM3A~VlLt.ORGANlSATlON INTERNATIONALE DE NORMALISATION
.h
Rubber, vulcanized - Classification - Rubber materials
Caoutchouc vulcanis~ - Classification - Ma thriaux caoutchouc
IS0 (International Organization for Standardization) is a worldwide federation of national standards bodies (IS0 member bodies). The
work of preparing International Standards is normally carried out through IS0 technical committees. Each member body interested in
a subject for which a technical committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
The main task of IS0 technical committees is to prepare International Standards. In exceptional circumstances a technical committee
may propose the publication of a technical report of one of the following types :
-
type 1, when the necessary support within the technical committee cannot be obtained for the publication of an International
Standard, despite repeated efforts;
-
type 2, when the subject is still under technical development requiring wider exposure;
-
type 3, when a technical committee has collected data of a different kind from that which is normally published as an
International Standard (“state of the art”, for example).
Technical reports are accepted for publication directly by IS0 Council. Technical reports types 1 and 2 are subject to review within
three years of publication, to decide if they can be transformed into International Standards. Technical reports type 3 do not
necessarily have to be reviewed until the data they provide is considered no longer valid or useful.
ISO/TR 8461 was prepared by Technical Committee lSO/TC 45, Rubber and rubber products.
The reasons which led to the decision to publish this document in the form of a technical report type 2 are explained in the
Introduction.
0 Introduction
Work on the classification of vulcanized rubber was carried out by Working Group 8 of Technical Committee ISO/TC 45, Rubber and
rubber products, over many years. This resulted in the circulation in 1980 of ISO/DIS 4632, Rubber, vulcanized - Classification
system. This large document covered both the classification system and an extensive number of tables of rubber materials.
iii
UDC 678.063.001.33 Ref. No. ISO/TR 84614984 (E)
Descriptors : rubber, vulcanized rubber, physical properties, classification.
a International Organization for Standardization, 1984 0
“sglb 2L
Printed in Switzerland Price based on 46 pages

---------------------- Page: 1 ----------------------
ISO/TR 8461-1984 E)
The comments on DIS 4632 were examined by WG 8 at its 1980 meeting in Dubrovnik. The comment that the document was too
complicated for use by industry was accepted and it was resolved by TC 45 that ISO/DIS 4632 be divided into two parts
Part 7 : Description of the classification system.
Part 2: Rubber materials.
IS0 4632/l was published in 1982.
It was agreed that the second part should be issued as a type 2 Technical Report, (TC 45 Resolution 1293) and Working Group 8/TG 2
was formed for the purpose of examining the text of this report. The amended draft was circulated in 1981 and the comments
Following extensive discussion, many of the comments, including some of those
discussed at the 1981 meeting in Boston.
accompanying the United Kingdom disapproval, were taken into account. As a result it was agreed that the second part, as amended
by the Task Group and duly edited be submitted to IS0 Central Secretariat for issue as a Technical Report. The amendments included
a reconsideration by the Czechoslovak, Swedish, United Kingdom and USA national bodies of the standard vulcanizates submitted
by them in the light of comments received.
The reasons for publication as a Technical Report are as follows:
it is hoped tha
the list of rubber materials is complex and extensive. It has already been simplified and t during the next 3 years
a)
rther steps taken to eliminate little used grades and combine grades having sim ilar properties;
fu can be
materials submitted by Czechoslovakia, Sweden and USA only. It is necessary to ensure that the list of
b) table 1 contains
materials represents those required in all national standards;
c) table 1 does not include materials described in documents under the jurisdiction of ISO/TC 45. Consequently WG 8/TG 2 will
seek out such materials and solicit further national rubber materials to be included in the proper format for the intended
transformation of ISO/TR 8461 into IS0 4632/2.
1 Scope and field of application
This Technical Report contains the list of properties of rubber materials submitted by member bodies of lSO/TC 45. They are
classified and designated by the methods described in IS0 4632/l.
NOTE - The tests employed in this system have been chosen for their reproducibility and ability to control the properties of elastomeric materials.
They are not intended to simulate service tests which, because of variability in test conditions, may be unsatisfactory for control purposes. It is rec-
ommended that the selection of a rubber material for a given application should be discussed between the user and the supplier so that all relevant
operating factors may be considered.
2 References
IS0 1433, Rubber, vulcanized - Preferred gradation of properties.
IS0 1629, Rubbers and latices - Nomenclature.
Part 7 : Description of the classification system.
IS0 463211, Rubber, vulcanized - Classification -
3 Outline
3.1 Sources and classification
3.1.1 The properties of certain commercially available solid vulcanized rubber materials based upon various national standards are
listed in table 1. These materials are intended to cover the majority of applications. The sources of the standards are indicated in
table 1 under the following code:
CS Czechoslovakia
SE Sweden
US United States of America
3.1.2 The classification system, methods of test, test conditions and properties to be tested are specified in IS0 4632/l.
2

---------------------- Page: 2 ----------------------
ISO/TR 8461-1984 (El
3.1.3 As far as possible the values of properties given in this Technical Report have been brought into line with the list of preferred
gradations in IS0 1433.
listed in table 1 has i ts own code consisting of a combinatio n of letters l and digits. This code can be used for
3.1.4 Each material
in the figu
information retrieval by punched cards or digital computer. An example is shown re.
c
BCD denotes
- a material designation based on the three classifi-
cation criteria of heat, oil and low temperature
resistance
- a four digit numerical code for the basic physical
properties of hardness, tensile strength,
elongation at break and compression set
a suffix grade number representing additional
properties
Figure
32 . Composition and manufacture
This classification system applies to materials manufactured from natural rubber, synthetic rubber or reclaimed rubber, alone or in
combination, together with added compounding ingredients of such nature and quantity as to produce vulcanizates that comply with
the specified requirements. All materials and workmanship shall be in accordance with good commercial practice, and the resulting
product shall be free of porous area, weak sections, bubbles, foreign matter or other defects affecting serviceability.
.
33 Sampling and inspection
3.3.1 A lot, unless specified otherwise, shall consist of all products of the same material submitted for inspection at the same time.
3.3.2 When proof of conformance with a specification based on this classification system is required, the supplier shall, upon
request of the purchaser at the time of ordering, furnish a sufficient number of samples to perform the required tests. Test pieces shall
be prepared as specified in IS0 4632/l. The samples shall be warranted to have equivalent cure and to be from the same run or batch
of compound used in the lot.
3.3.3 When differences arise due to the method of processing or to the difficulty in obtaining suitable test pieces from a finished
rubber product the values of properties may differ from those obtained from standard test pieces. Such differences in the values of
properties for the rubber product shall be reported in an appropriate manner as agreed between the supplier and purchaser. Such dif-
ferences in values can be determined by comparing results from standard test pieces with those obtained on actual rubber products.
3.4 Reporting
The specification code of a material taken from this Technical Report shall be prefaced by a reference to lSO/TR 8461. An example is
as follows :
Rubber material, lSO/TR 8461 BAD 5373-3
or if the full line call out designation is required
Rubber material, ISO/TR 8461 BAD 5373-3 Al4 C42 EA14 FlO F70 F80
4 Rubber materials
Rubber materials are listed in table 1.
NOTE - It is intended that rubber materials specified in any documents under the jurisdiction of ISO/TC 45 will be included in table 1.
3

---------------------- Page: 3 ----------------------
Table 1 - Standard rubber materials
Classification criteria : AAC
Suffix
Basic
grade Grade Grade Grade Grade
Grade
physical Suffix Requirements
Grade No. 1 Grade No. 7
numbers
No. 2 No. 3 No. 4 No. 5 No. 6
properties
available
cs 4163 Al3 Heat resistance, 70 h at 70 OC
No. 4
cs 5153 No. 4 - hardness change, IRHD, max.
+ 10 + 15 + 10 + 10 + 10
-
CS 6162 tensile change, %, max.
Nos. 4; 5 - 20 - 30 - 30 - 20
- 20
-
elongation change, %, max.
cs 7373 No. 6 -20 -40
- 30 - 20 - 20
CS 8143 No. 7
A23 Heat resistance, 7 days at 70 OC
SE 9323
No. 2
- hardness change, IRHD, max.
+ 10 + 10
cs 9323 No. 3
-
tensile change, %, max.
-30 - 30
-
elongation change, %, max.
-40 - 30
Cl2 Ozone resistance, 50 pphm, 96 h at 40 OC
-
threshold strain, %, min.
20
C42
Ozone resistance, 200 pphm, 96 h at 40 OC
-
threshold strain, %, min.
40
FlO Low temperature resistance
.
- brittleness temperature, OC, max.
- 30
F70 Low temperature resistance
-
Basic properties
retraction temperature, TR-10, OC, max.
- 35
only - no
F80 Low temperature resistance
additional
-
retraction temperature, TR-30, OC, max.
- 10
requirements
Gil Tear strength
-
crescent, kN/m, min.
60
60
011 Electrical resistivity
- SZcm
5 x 10” to 5 x 10’4
021 Electrical insulation
-
resistance, Ma, min.
1 x 10’0
031 Breakdown voltage
- kV/mm, min.
15
Rll Resilience
- Lupke, %, max.
20
s71 Compression flexometer
- temperature rise, OC, max. 80
-
creep, %, max.
60
-
set, Oh, max.
20

---------------------- Page: 4 ----------------------
Table 1 - Standard rubber materials (cohwed)
Classification criteria : AAD
Suffix
Basic
grade Grade Grade Grade Grade Grade
physical Suffix Requirements Grade No. 1
No. 4 No. 5 No. 6
No. 2 No. 3
properties numbers
available
SE 3483 No. 3 Al3 Heat resistance, 70 h at 70 OC
SE 4586 - hardness + 10
+ 10
change, IRHD, max.
No. 2
- tensile change, %, max. 30
us 4793 - 30 -
No. 4
us 5573 No. - elongation change, max. - 30
- 30
4 %,
SE 5586 No. 5
US 6353 No. 2 A23 Heat resistance, 7 days at 70 OC
+ 10 + 10 + 10 + 10
No. 5 - hardness change, IRHD, max.
SE 6576
- 30 - 30
- 30 - 30
- tensile change, %, max.
us 6673 No. 4
- 40
-40 - 40 - 30
No. 6 - elongation change, %, max.
SE 7143
SE 7343 No. 6
SE 7566 No. 5 B13 Compression set, 22 h at 70 OC
- max. 25 25
No. 2 %,
US 8543
Cl2 Ozone resistance, 50 pphm, 96 h at 40 OC
20 10
20 10 10
- threshold strain, %, min.
C42 Ozone resistance, 200 pphm, 96 h at 40 OC
- Basic properties
threshold strain, %, min.
40
only - no
EA14 Aqueous fluid resistance, distilled water,
additional
70 h at 100 OC requirements
10 10
- volume change, %, max.
FlO Low temperature resistance
- - 50
-50 50
- brittleness temperature, OC, max.
F70 Low temperature resistance
- - - 30
45 -50 40 -40
- retraction temperature, TR-10, OC, max.
F80 Low temperature resistance
-40 - 30 - 25 - 20
- 35
- retraction temperature, TR-30, OC, max.
Gil Tear strength
60
90 60 120
- crescent, kN/m, min.
Kll Adhesion to metals
* *
- -
- two plate method, MPa, min.
L
* Materials can be bonded to metal during vulcanization. Because of the wide variety of compounds in use and manifold end-use requirements, values should be agreed between supplier and user.
f

---------------------- Page: 5 ----------------------
Table 1 - Standard rubber materials (continued)
Classification criteria : AAE
Suffix
Basic
grade
Grade No. 2
physical Suffix Requirements Grade No. 1
number
properties
available
SE 3483 No. 2
Al3 Heat resistance, 70 h at 70 OC
-
+ 10
hardness change, IRHD, max.
-
tensile change, %, max. - 20
-
- 20
elongation change, %, max.
A23 Heat resistance, 7 days at 70 OC
-
+ 10
hardness change, IRHD, max.
-
tensile change, %, max. - 30
-
-40
elongation change, %, max.
Basic properties
only - no
Cl2 Ozone resistance, 50 pphm, 96 h at 40 OC
additional
-
10
threshold strain, %, min.
requirements
F70 Low temperature resistance
-
retraction temperature, TR-10, OC, max. - 50
F80 Low temperature resistance
-
retraction temperature, TR-30, OC, max. - 40
Gil Tear strength
-
60
crescent, kN/m, min.

---------------------- Page: 6 ----------------------
Table 1 - Standard rubber materials (continued)
Classification criteria : ABD
Suffix
Basic
Grade Grade Grade Grade Grade
grade
physical Suffix Requirements Grade No. 1
numbers No. 2 No. 3 No. 4 No. 5 No. 6
properties
available
cs 5383 No. 1 Al3 Heat resistance, 70 h at 70 OC
cs 6473 Nos. 4; 6 - hardness change, IRHD, max.
+ 10 + 15 + 10 + 10 +5
CS 6585 Nos. 3; 5 - tensile change, %, max. - 20 - 30 - 20 -40 - 20
CS 7363 No. 2 - elongation change, %, max. - 30 - 30 - 20 - 40 - 20
cs 7574 No. 3
C42 Ozone resistance, 200 pphm, 96 h at 40 OC
- threshold strain, %, min. 120
G21 Tear strength
- angle, kN/m, min. 5
Hll Resistance to flex cracking (De Mattia)
- kilocycles, min.
10
Basic properties
Jll Abrasion resistance
only - no
- index, min. additional 60
requirements
011 Electrical resistivity
- acrn 5 x 106 to 1 x 10’0
021 Electrical insulation
- resistance, Ma, min.
5 x 10’0
Rll Resilience
- Lupke, %, min. 20
50
s71 Compression f lexometer
- temperature rise, OC, max. 60 60
- creep, %, max. 60
40
- set, %, max. 20 15

---------------------- Page: 7 ----------------------
Table 1 - Standard rubber materials (conthued)
Classification criteria : ABE
Suffix
Basic
grade Grade Grade
physical Suffix Requirements Grade No. 1
numbers No. 2 No. 3
properties
available
cs 4483
No. 2 Al3 Heat resistance, 70 h at 70 OC
cs 4583 No. 2 - hardness change, IRHD, max. + 15 + 10
-
CS 6574 No. 3 tensile change, %, max. - 10 - 20
-
elongation change, %, max. - 30 - 20
Basic properties
G21 Tear strength
only - no
-
angle, kN/m, min. 20
additional
requirements
Hll Resistance to flex cracking (De Mattia)
- kilocycles, min. 60
Jll Abrasion resistance
-
index, min. 90

---------------------- Page: 8 ----------------------
Table 1 - Standard rubber materials (conhued)
Classification criteria : ACD
1
Suffix
Basic
grade
Grade
Grade
physical
Suffix
Requirements
Grade No. 1
numbers
No. 2
No. 3
properties
available
cs 5373 Nos. 2; 3
Al3 Heat resistance, 70 h at 70 OC
- hardness change, IRHD, max.
+ 10
+ 10
- tensile change, %, max.
- 30
- 30
-
elongation change, %, max.
- 30
- 30
Cl2 Ozone resistance, 50 pphm, 96 h at 40 OC
-
threshold strain, %, min.
20
EFll Resistance to hydrocarbon liquids, liquid A, 70 h
at 23 OC
- hardness change, IRHD, max.
- 10
- tensile change, %, max.
- 20
-
elongation change, %, max.
- 30
-
volume change, %, max.
+ 15
EF21 Resistance to hydrocarbon liquids, liquid B, 70 h
at 23 OC
- hardness change, IRHD, max.
- 20
- tensile change, %, max.
Basic properties
-40
-
elongation change, %, max.
only - no -50
-
volume change, %, max.
additional
+80
requirements
E013
Oil resistance, oil No. 1, 70 h at 70 OC
- hardness change, IRHD
-5to +lO
- tensile change, %, max.
- 20
-
elongation change, %, max.
- 30
-
volume change, %
- 15 to + 10
E014 Oil resistance, oil No. 1, 70 h at 100 OC
- hardness change, IRHD
- 10 to + 10
- tensile change, %, max.
- 30
-
elongation change, %, max.
- 30
-
volume change, %
-1oto +20
E033 Oil resistance, oil No. 3, 70 h at 70 OC
- hardness change, IRHD, max.
- 15
- tensile change, %, max.
- 30
-
elongation change, %, max.
-40
-
volume change, %, max.
+50
m

---------------------- Page: 9 ----------------------
Table 1 - Standard rubber materials (conhued)
Classification criteria : AHC
Suffix
Basic
grade
physical Suffix Requirements Grade No. 1 Grade No. 2 Grade No. 3 Grade No. 4
numbers
m
properties
available
CS 6253 Heat resistance, 70 h at 70 OC
No. 3 Al3
CS 6365 No. 2 - hardness change, IRHD, max. + 10 + 10 + 10
-
cs 8536 No. 4 tensile change, %, max. - 20 - 20 - 10
-
elongation change, %, max.
- 20 - 20 - 30
EFll Resistance to hydrocarbon liquids, liquid A, 70 h
at 23 OC
- hardness change, IRHD (max.) -5to0 Oto -5
b- 10)
-
tensile change, %, max. - 10 - 10 - 20
-
elongation change, %, max. - 10 - 10
- 20
-
volume change, %, max. +5 +5 + 10
EF21 Resistance to hydrocarbon liquids, liquid B, 70 h
at 23 OC
- hardness change, IRHD (max.) ( - 20) b-20) 0 to - 20
-
tensile change, %, max. -40 - 35
-40
-
elongation change, %, max. -40 - 35 -40
-
volume change, %, max. +40 + 40
+ 50
Basic properties
only - no
E013 Oil resistance, oil No. 1, 70 h at 70 OC
additional
- hardness change, IRHD - 10 to + 10
-5to +lO - 10 to + 10
requirements
-
tensile change, %, max. - 20 - 20
- 20
-
elongation change, %, max.
- 20 - 20 - 30
-
volume change, % -15to +5 -1oto +5
-15to +5
E014 Oil resistance, oil No. 1, 70 h at 100 OC
- hardness change, IRHD -5to +15
-5to +5 - 10 to + 10
-
tensile change, %, max. - 20 - 10 - 20
-
elongation change, %, max. - 30
- 10 - 30
-
volume change, % - 20 to + 5 -5 to + 10 -15to +5
E033 ‘Oil resistance, oil No. 3, 70 h at 70 OC
- hardness change, IRHD -1oto +5 - 10 to + 10
-
tensile change, %, max. - 20 - 20
-
elongation change, %, max. - 20 - 30
-
volume change, %, max. + 15 + 20
FlO Low temperature resistance
- brittleness temperature, OC, max. - 15

---------------------- Page: 10 ----------------------
Table 1 - Standard rubber materials (conhued)
Classification criteria : AKB
\
Suffix
Basic
grade
physical
Suffix Requirements Grade No. 1 Grade No. 2
number
properties
available
CS 9424 No. 2
Al3 Heat resistance, 70 h at 70 OC
- hardness change, IRHD, max.
+ 10
- tensile change, %, max. - 20
-
elongation change, %, max.
- 20
EFll
Resistance to hydrocarbon liquids, liquid A, 70 h
at 23 OC
- hardness change, IRHD
-5to +lO
- tensile change, %, max.
- 20
-
elongation change, %, max.
- 20
-
volume change, %
-1oto +5
EF21 Resistance to hydrocarbon liquids, liquid B, 70 h
at 23 OC
- hardness change, IRHD
-1otoo
- tensile change, %, max.
- 30
-
elongation change, %, max.
- 30
-
volume change, %, max.
+ 30
Basic properties
only - no
E013 Oil resistance, oil No. 1, 70 h at 70 OC
additional
- hardness change, IRHD
-5to +lO
requirements
- tensile change, %, max.
- 20
-
elongation change, %, max.
- 20
-
volume change, %
-1oto +5
E014 Oil resistance, oil No. 1, 70 h at 100 OC
- hardness change, IRHD
-- 20 to + 5
- tensile change, %, max.
- 20
-
elongation change, %, max.
-30
-
volume change, %
-15to +5
E033 Oil resistance, oil No. 3, 70 h at 70 OC
- hardness change, IRHD
- 10 to + 10
- tensile change, %, max.
- 20
-
elongation change, %, max.
- 30
-
volume change, %
- 10 to + 10
FlO Low temperature resistance
- brittleness temperature, OC, max.
- 20
m

---------------------- Page: 11 ----------------------
Table 1 - Standard rubber materials (contl’nued)
Classification criteria : AKC
Suffix
Basic
grade
physical
Suffix Requirements Grade No. 2 Grade No. 3 Grade No. 4
Grade No. 1
numbers
properties
available
us 4173
No. 2 Al3 Heat resistance, 70 h at 70 OC
us 5173 - hardness change, IRHD, max.
No. 2 + 10
+ 10
US 6263
No. 2 - tensile change, %, max.
- 20 - 20
-
CS 6263 No. 3 elongation change, %, max.
- 30
-40
US 7323
No. 2
Al4 Heat resistance, 70 h at 100 OC
cs 8434 No. 4
- hardness change, IRHD, max.
+ 15
- tensile change, %, max.
- 20
-
elongation change, %, max.
-40
EFll Resistance to hydrocarbon liquids, liquid A, 70 h
at 23 OC
- hardness change, IRHD, max.
-5
-5
- tensile change, %, max.
- 10 - 10
-
elongation change, %, max.
- 10
- 10
-
volume change, %, max.
+5 +5
EF21 Resistance to hydrocarbon liquids, liquid B, 70 h
at 23 OC
- hardness change, IRHD, max.
- 10
- tensile change, %, max.
- 20
-
elongation change, %, max.
- 30
-
volume change, %, max.
+ 30 + 15
Basic properties
only - no
E013
Oil resistance, oil No. 1, 70 h at 70 OC
additional
- hardness change, IRHD (max.)
+ 10 to - 10
(-- 15)
requirements
- tensile change, %, max.
- 20 - 30
-
elongation change, %, max.
- 30
-40
-
volume change, %
0 to - 20 +5to -15
E014 Oil resistance, oil No. 1, 70 h at 100 OC
- hardness change, IRHD, max.
- 15 + 15
- tensile change, %, max.
- 20 - 30
-
elongation change, %, max.
- 30
-40
-
volume change, %
-5to +5
0 to - 20 0 to - 15
E033 Oil resistance, oil No. 3, 70 h at 70 OC
- hardness change, IRHD
-5to +lO + 10 to - 10
- tensile change, %, max.
- 20
- 30
-
elongation change, %, max.
- 20 - 30
-
volume change, %
-1oto +5 + 10 to - 10
E034 Oil resistance, oil No. 3, 70 h at 100 OC
- hardness change, IRHD -5to +lO
- tensile change, %, max.
- 30
-
elongation change, %, max. -50
FlO Low temperature resistance
- brittleness temperature, OC, max. -40

---------------------- Page: 12 ----------------------
Table 1 - Standard rubber materials (contr’nued)
Classification criteria : AKD
Suffix
Basic
grade
physical
Suffix
Requirements
Grade No. 1 Grade No. 2
number
properties
available
CS 7323 No. 2 Al3 Heat resistance, 70 h at 70 OC
- hardness change, IRHD, max.
+ 10
- tensile change, %, max.
- 20
-
elongation change, %, max.
-40
EFll Resistance to hydrocarbon liquids, liquid A, 70 h
at 23 OC
- hardness change, IRHD, max.
-5
- tensile change, %, max.
- 10
-
elongation change, %, max.
- 10
-
volume change, %
+5
EF21
Resistance to hydrocarbon liquids, liquid B, 70 h
at 23 OC
- hardness change, IRHD, max.
- 15
- tensile change, %, max.
- 30
-
elongation change, %, max. Basic properties
- 30
-
volume change, %, max.
only - no
+ 30
additional
E013 Oil resistance, oil No. 1, 70 h at 70 OC
requirements
- hardness change, IRHD, max.
+ 10
- tensile change, %, max.
- 30
-
elongation change, %, max.
- 30
-
volume change, %
- 10 too
E014
Oil resistance, oil No. 1, 70 h at 100 OC
- hardness change, IRHD, max.
+ 15
- tensile change, %, max.
- 30
-
elongation change, %, max.
-40
-
volume change, %
-15to0
E033
Oil resistance, oil No. 3, 70 h at 70 OC
- hardness change, IRHD
+5to -5
- tensile change, %, max.
- 10
-
elongation change, %, max.
- 10
-
volume change, %
+5to -5
m

---------------------- Page: 13 ----------------------
Table 3 - Standard rubber materials (continued)
Classification criteria : BAC
Suffix
Basic
grade
Grade Grade
physical Suffix Requirements
Grade No. 1
numbers No. 2 No. 3
properties
available
us 3473” Al4 Heat resistance, 70 h at 100 OC
No. 2
us 4473” - hardness change, IRHD, max. + 10 + 10
No. 2
-
tensile change, %, max.
us 5473” No. 2 - 30 - 30
-
us 6463* elongation change, %, max. - 30 - 30
No. 2
Basic properties
us 7453”
No. 2
only - no
B13 Compression set, 22 h at 70 OC
us 7563”
No. 2
- additional
%, max. 25
US 8423”
No. 3
requirements
US 9423” No. 3
FlO Low temperature resistance
- brittleness temperature, OC, max.
- 40 -40
Compression set is based on 22 h at 70 OC.

---------------------- Page: 14 ----------------------
Table 1 - Standard rubber materials (continued)
Classification criteria : BAD
Suffix
Basic
Grade Grade
Grade Grade Grade Grade
grade
physical Suffix Requirements Grade No. 1
No. 4 No. 5 No. 6 No. 7
numbers No. 2 No. 3
properties
available
us 3373” Al4 Heat resistance, 70 h at 100 OC
No. 4
+ 10 + 10 + 10 + 10
+ 15 + 10
- hardness change, IRHD, max.
us 3473” No. 4
- 30 - 30
- 30 - 30 - 30 - 30
- tensile change, %, max.
us 4473” No. 4
- 30 - 50 -50 - 30
- 30 -50
- elongation change, %, max.
cs 5373 Nos. 2; 3; 7
SE 5373 No. 5
B13 Compression set, 22 h at 70 OC
CS 6363 Nos. 3; 7
25
SE 6363 No. 5 - %, max.
US 6573 No. 4
pphm, OC
SE 7343 No. 5 C42 Ozone resistance, 200 96 h at 40
40 40
40 40
- threshold strain, %, min.
us 7563 No. 4
EA14 Aqueous fluid resistance, distilled water, 70 h
SE 8323 No. 6
Basic properties
at 100 OC
only - no
Oto +5 Oto +5
- volume change, % (max.) (+ 10) (+ 10)
additional
requirements
FlO Low temperature resistance
-50 - 55 -50 -50
- brittleness temperature, OC, max.
F70 Low temperature resistance
- - 45 -40
45
- retraction temperature, TR- 10, OC, max.
F80 Low temperature resistance
- 25
- 30 - 30
max.
- retraction temperature, TR-30, OC,
Gil Tear strength
60 60
- crescent, kN/m, min.
It Compression set is based on 22 h at 70 OC.
m

---------------------- Page: 15 ----------------------
Table 1 - Standard rubber materials (conhued)
Classification criteria : BAE
Suffix
Basic
grade
Grade No. 1 Grade No. 2 Grade No. 3 Grade No. 4
physical Suffix Requirements
numbers
properties
available
us 3473* Al4 Heat resistance, 70 h at 100 OC
No. 2
us 4473” - hardness change, IRHD, max. + 10 - 10 - 10
No. 2
- 30 - 30 - 30
us 5473” No. 2 - tensile change, %, max.
-
-40 - 30
cs 6473 elongation change, %, max. - 30
No. 4
CS 6772 No. 3
B13 Compression set, 22 h at 70 OC
-
%, max. 25
FlO Low temperature resistance
- 60
- brittleness temperature, OC, max.
Basic properties
only - no
Tear strength
G21
additional
-
20 15
angle, kN/m, min.
requirements
Hll Resistance to flex cracking (De Mattia)
- kilocycles, min. 100 100
Jll’ Abrasion resistance
-
90 90
index, min.
K21 Adhesion to metals
*+
-
-
one plate method, MPa, min.
* Compression set is based on 22 h at 70 OC.
** Materials can be bonded to metal during vulcanization. Because of the wide variety of compounds in use and manifold end-use requirements, values should be agreed between supplier
and user.

---------------------- Page: 16 ----------------------
Table 1 - Standard rubber materials (contr’nued)
Classification criteria : BCD
Suffix
Basic
grade
physical
Suffix Requirements Grade No. 2 Grade No. 3
Grade No. 1 Grade No. 4
numbers
properties
available
US 3161 No. 2 Al4 Heat resistance, 70 h at 100 OC
us 3481 No. 2 - hardness change, IRHD, max. +15 . + 15 + 15
us 4371 No. 2 - tensile change, %, max. - 20 - 20 - 20
us 4481 No. 2 - elongation change, %, max. -40 -40 - 40
US 5161 No. 2
us 5461 No. 2 B14 Compression set, 22 h at 100 OC
us 5681 No. 2 - %, max. 35 35 35
us 6161 No. 3
us 6461 No. 3 E014 Oil resistance, oil No. 1, 70 h at 100 OC
us 6671 No. 3 - hardness change, IRHD Basic properties - 10 to + 10 - 10 to + 10 - 10 to + 10
- tensile max.
us 7141 No. 3 change, %, only no - 30 - 30 - 30
-
us 7441 No. 3 - elongation change, %, max. additional -30 - 30 - 30
US 7661 No. 3 - volume change, % requirements - 10 to + 15 - 10 to + 15 + 10 to + 15
US 8221 No. 4 E034 Oil resistance, oil No. 3, 70 h at 100 OC
us 8421 No. 4 - tensile change, %, max. - 70 -60
-50
us 9321 No. 4 - elongation change, %, max. -60
-50 -30
us 9421 No. 4 - volume change, %, max. + 120 +loo + 80
K21 Adhesion to metals
* *
- - *
- -
one plate method, MPa, min.
* Materials can be bonded to metal during vulcanization. Because of the wide variety of compounds in use and manifold end-use requirements, values should be agreed between supplier
and user.

---------------------- Page: 17 ----------------------
Table 1 - Standard rubber materials (conhued)
Classification criteria : BCE
Suffix
Basic
grade
physical
Suffix Requirements Grade No. 1 Grade No. 2
number
properties
available
US 3161 Al4 Heat resistance, 70 h at 100 OC
No. 2
us 3481 - hardness change, IRHD, max. + 15
No. 2
-
us 4371 No. 2 tensile change, %, max. - 20
-
us 4481 elongation change, %, max. -40
No. 2
US 5361 No. 2
B14 Compression set, 22 h at 100 OC
us 5461 No. 2
-
%, max. 35
us 6161 No. 2
us 6461 No. 2
E014 Oil resistance, oil No. 1, 70 h at 100 OC
us 7147
No. 2
- hardness change, IRHD
- 10 to + 10
Basic properties
us 7451 No. 2
-
tensile change, %, max. - 30
only - no
-
elongation change, %, max.
- 30
additional
-
volume change, % - 10 to + 15
requirements
E034 Oil resistance, oil No. 3, 70 h at 100 OC
-
tensile change, %, max.
-60
-
elongation change, %, max. -60
-
volume change, %, max.
+lOo
K21 Adhesion to metals
it
- -
one plate method, MPa, min.
* Materials can be bonded to metal during vulcanization. Because of the wide variety of compounds in use and manifold end-use
requirements, values should be agreed between supplier and user.

---------------------- Page: 18 ----------------------
Table 1 - Standard rubber materials (conthued)
Classification criteria : BDC
Suffix
Basic
grade Grade Grade Grade Grade Grade
physical
Suffix Requirements Grade No. 1
No. 6
No. 2 No. 3 No. 4 No. 5
properties numbers
available
...

RAPPORT TECHNIQUE 8461
Publié 1984-10-01
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION. MEXflYHAPOflHAR OPTAHMJA~MA no CTAHflAPTM3A~MM * ORGANISATION INTERNATIONALE DE NORMALISATION
X
Caoutchouc vulca,iisé - Classification - Matéria
caoutchouc
Rubber, vulcanized - Classification - Rubber materials
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de normalisation (comités
membres de I'ISO). L'élaboration des Normes internationales est confiée aux comités techniques de I'ISO. Chaque comité membre
intéressé par une étude a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec I'ISO, participent également aux travaux.
La tâche principale des comités techniques de 1'1S0 est d'élaborer les Normes internationales. Exceptionnellement, un comité
technique peut proposer la publication d'un rapport technique de l'un des types suivants:
-
type 1 : lorsque, en dépit de maints efforts au sein d'un comité technique, l'accord requis ne peut être réalisé en faveur de la
publication d'une Norme internationale;
-
type 2: lorsque le sujet en question est encore en cours de développement technique et requiert une plus grande expérience;
-
type 3: lorsqu'un comité technique a réuni des données de nature différente de celles qui sont normalement publiées comme
Normes internationales (ceci pouvant comprendre des informations sur l'état de la technique, par exemple).
La publication des rapports techniques dépend directement de l'acceptation du Conseil de I'ISO. Les rapports techniques des types 1
et 2 font l'objet d'un nouvel examen trois ans au plus tard après leur publication afin de décider éventuellementde leur transformation
en Normes internationales. Les rapports techniques du type 3 ne doivent pas nécessairement être révisés avant que les données
fournies ne soient plus jugées valables ou utiles.
L'ISO/TR 8461 a été préparé par le comité technique ISO/TC 45, Élastomères et produits à base d'élastomères.
Les raisons justifiant la décision de publier le présent document sous forme de rapport technique du type 2 sont exposées dans
l'introduction.
O introduction
L'étude sur la classification des élastomères vulcanisés entreprise par le groupe de travail GT 8 du comité technique ISO/TC 45,
Élastomères et produits à base d'élastomères, a duré de nombreuses années. II en est résulté la diffusion en 1980 de I'ISO/DIS 4632,
Caoutchouc vulcanisé - Système de ciassification. Ce document volumineux contenait à la fois le système de classification et un
grand nombre de tableaux des matériaux caoutchouc.
CDU 678.063.001.33 Réf. no : ISO/TR 8461-1984 (FI
Descripteurs : caoutchouc, caoutchouc vulcanisé, propriété physique, classification.
0 Organization internationale de normalisation, 1984 O
Imprimé en Suisse
Prix basé sur 46 pages

---------------------- Page: 1 ----------------------
ISO/TR 8461-1984 (F)
Les commentaires sur le DIS 4632 furent examinés par le GT 8 à sa réunion de 1980 à Dubrovnik. Le commentaire selon lequel le
document était trop compliqué pour être employé par l'industrie fut admis et le TC 45 décida que I'ISOIDIS 4632 serait divisé en deux
parties.
Partie 7 : Description du système de classification.
Partie 2: Matériaux caoutchouc.
L'ISO 463211 a été publiée en 1982.
II fut décidé que la seconde partie serait publiée comme rapport technique du type 2 (résolution 1293 du TC 451, et le groupe de tra-
vail 81GE 2 fut constitué dans le but d'examiner le texte de ce rapport. Le projet modifié fut diffusé en 1981 et ies commentaires
discutés à la réunion de 1981 à Boston. Après une longue discussion, de nombreux commentaires furent pris en considération, y
compris certains commentaires qui accompagnaient le vote négatif du Royaume-Uni. II fut finalement décidé que la seconde partie,
modifiée par le groupe réduit et dûment diffusée, serait soumise au Secrétariat central de I'ISO en vue de sa publication comme
rapport technique. Les modifications comprenaient la révision par les comités membres de Tchécoslovaquie, Suède, Royaume-Uni et
États-Unis, en fonction des commentaires recus, de leur présentation de vulcanisats normalisés.
Les raisons de la publication comme rapport technique sont les suivantes:
a) la liste des matériaux caoutchouc est complexe et longue. Elle a déjà été simplifiée et il est espéré que pendant les trois
prochaines années, des dispositions complémentaires permettront d'éliminer les grades peu utilisés et de regrouper les grades
ayant des propriétés similaires.
b) le tableau 1 contient seulement des matériaux proposés par la Tchécoslovaquie, la Suède et les Etats-Unis. Il est nécessaire de
s'assurer que la liste de matériaux répond bien aux besoins de toutes les normes nationales.
c) le tableau 1 ne contient pas les matériaux décrits dans les documents sous la juridiction de I'ISO/TC 45. En conséquence,
GT 8/GE 2 procèdera à la recherche de ces matériaux et appellera à la soumission de matériaux complémentaires pour les inclure
SOUS une forme convenable dans la future transformation de I'ISOITR 8461 en IS0 4632/2.
1 Objet et domaine d'application
Le présent Rapport technique contient la liste des propriétés des matériaux caoutchouc soumis par les comités membres de
I'ISOITC 45. Ces matériaux sont classés et désignés au moyen des méthodes décrites dans I'ISO 4632/ 1.
NOTE - Les essais employés dans ce document ont été choisis pour leur reproductibilité et leur aptitude à contrôler les propriétés des matériaux
élastomères. Ils ne sont pas destinés à simuler des essais de fonctionnement qui, en raison de la variabilité des conditions d'essai, peuvent ne pas être
satisfaisants pour les besoins du contrôle. II est recommandé que la sélection d'un matériau caoutchouc pour une application donnée fasse l'objet
d'une discussion entre l'utilisateur et le fournisseur, afin que tous les facteurs relatifs au fonctionnement puissent être considérés.
2 Références
IS0 1433, Caoutchouc vulcanisé - Gradations préférées des propriétés.
IS0 1629, Caoutchouc et latex de caoutchouc - Nomenclature.
IS0 46321 1, Caoutchouc vulcanisé - Classification - Partie 7 : Description du système de classification.
3 Éléments de base
3.1 Sources et classification
3.1.1 Les propriétés de certains matériaux en caoutchouc vulcanisé, commercialement disponibles et basés sur diverses normes
le tableau 1. Ces matériaux sont destinés à couvrir la majorité des applications. Les origines des
nationales, sont rassemblées dans
normes sont indiquées dans le tableau 1 au moyen du code suivant :
CS Tchécoslovaquie
SE Suède
US États-Unis
3.1.2 Le système de classification, les méthodes d'essai, les conditions d'essai et les propriétés à déterminer sont en conformité avec
I'ISO 463211.
3.1.3 Dans la mesure du possible, les valeurs des propriétés données dans le présent Rapport technique ont été mises en accord
avec la liste des gradations préférées figurant dans I'ISO 1433.
2

---------------------- Page: 2 ----------------------
ISO/TR 8461-1984 (FI
3.1.4 Chaque matériau figurant dans le tableau 1 possède son propre code constitué par une combinaison de lettres et de chiffres.
Ce code peut être utilisé pour la recherche d’informations au moyen de cartes perforées ou d‘un ordinateur affichage numérique. Un
exemple est représenté sur la figure.
signifie :
une désignation de matériau basée sur les trois
critères de classification : résistance à la chaleur, à
l’huile et aux basses températures.
I I
un code de quatre chiffres pour les propriétés
physiques de base : dureté, résistance à la
traction, allongement à la rupture et DRC.
un numéro suffixe de grade représentant des
propriétés additionnelles.
Figure
3.2 Composition et fabrication
Ce système de classification s’applique aux matériaux fabriqués à partir de caoutchouc naturel, de caoutchouc synthétique ou de
caoutchouc régénéré, seuls ou en combinaison, associés à des ingrédients de mélange, leur nature et leur proportion étant choisies
pour donner des vulcanisats répondant aux exigences spécifiées. Tous les matériaux et les conditions de fabrication doivent être en
accord avec la bonne pratique commerciale, et le produit résultant ne doit pas comporter de zones poreuses, de zones de faiblesse, de
bulles, de corps étrangers ou d’autres défauts affectant l’aptitude en service.
3,3 Échantillonnage et contrôle
3.3.1 lot, sauf spécification contraire, doit être constitué par l’ensemble des produits faits à partir du même matériau et présentés
Un
simultanément au contrôle.
3.3.2 Lorsqu’une preuve de conformité à une spécification basée sur ce système de classification est requise, cette demande devant
être formulée par l’acheteur à la commande, le fournisseur doit fournir un nombre d’échantillons suffisant pour procéder aux essais
exigés. Les éprouvettes doivent être préparées comme spécifié dans I‘ISO 4632/1. II devra être attesté que les échantillons ont une
vulcanisation équivalent à celle des produits du lot et qu‘ils ont été faits à partir de la même série de mélanges.
3.3.3 En raison de différences dans la méthode de mise en œuvre ou de la difficulté d‘obtenir des éprouvettes satisfaisantes à partir
e
d’un produit fini en caoutchouc, les valeurs des propriétés mesurées à partir du produit peuvent différer de celles obtenues en utilisant
des éprouvettes normalisées. Ces différences de valeurs doivent être signalées d’une facon appropriée, comme défini entre le fournis-
I seur et l‘acheteur. Ces différences peuvent être déterminées en comparant les résultats obtenus à partir d’éprouvettes normalisées à
I
ceux obtenus à partir des produits en caoutchouc.
3.4 Désignation
i
Le code de spécification d‘un matériau choisi dans le présent Rapport technique doit être précédé de la référence à I’ISO/TR 8461.
À titre d‘exemple :
Matériau caoutchouc, ISO/TR 8461 BAD 5373-3
ou, si le ((code descriptif ~1) complet est nécessaire :
Matériau caoutchouc, ISO/TR 8461 BAD 5373-3 A14 C42 EA14 FI0 WO F80
I
4 Matériaux caoutchouc
Les matériaux caoutchouc sont rassemblés dans le tableau 1.
NOTE - Il est prévu que les matériaux caoutchouc spécifiés dans tout document sous la juridiction de I’ISO/TC 45 seront inclus dans le tableau 1
_-
I) En anglais ’‘line call-out”.
3

---------------------- Page: 3 ----------------------
ISO/TR 8461-1984 (F)
4
0
h
O
Z8R
al
U +I I
e
8
0
U-
288
m
8% +I I
al
UV)
E88
8% +I I
al
U-
mo
8'
4-
mo
8
8'
0)
UN
088
8328
5%
+I I I I I
O
a
O
c
O
ci
a
O
m
O
4

---------------------- Page: 4 ----------------------
ISO/TR 8461-1984 (FI
8Rg
E88
E
I I
+I I
4m i38!No
E88
R
I I IN
+I I
QC
*
88
E88
NE E I
I I
+I I
$888
E88
E I I I
+I I
O
UN i3dR$*,
08% E88 N 8
E I I I
+II +II
QC
.-
O
O
m,
O
mNbdmNmdwwmN
000000000000
zzzzzzzzzzzz

---------------------- Page: 5 ----------------------
ISO/TR 8461-1984 (F)
N
O
O>
U
8
r
O
al
U
8
xx xx
EE EE
,oe oeoè

---------------------- Page: 6 ----------------------
ISO/TR 8461-1984 (FI
o
E
xo
-E
rm
wx
EL"
X
L"
E88
+I I
ZRR
R 88s
+I I
EBB
fi:
.,E8
+I I
t'
ZR8
40
+I I -
t'
xx
mm
EE
x
E
9
(Dm
-""him
O8800
zzzzz
7

---------------------- Page: 7 ----------------------
ISO/TR 8461-1984 (FI
E88 <
w 8
+I I
4EB
+I I
C
O
.-
2
I)
mc
Ë
.ni
al>
va
cx
,m .E
m
v I
'al
a

---------------------- Page: 8 ----------------------
ISO/TR 8461-1984 (FI
Z8i-3
+I I
I I l I
E88 8
+I I
r
O
P)
U
L!
U
O
N
8
z
UJ
O
9

---------------------- Page: 9 ----------------------
I ISO/TR 8461-1984 (F)
w
O
Q)
U
L
Q
m
O
P)
U
e
0
N
O
Q)
U
e
Q
c
O
C
0
U