ISO 12192:2002

Paper and board — Compressive strength — Ring crush method

ISO 12192:2002 specifies a method for the determination of the edgewise compressive strength (ring crush resistance) of paper and paperboard, especially board used in the manufacture of cartons and packing cases. ISO 12192:2002 applies to all paper and paperboard with a thickness in the range of 280 micrometres to 580 micrometres. It may also be used for paper and board having a thickness less than 280 micrometres but those results are more a reflection of the paper's stiffness than its compressive strength. For paper and board having a thickness exceeding 580 micrometres, it may be impossible to bend them to the circumference without disturbing the structure.

Papier et carton — Résistance à la compression — Méthode d'écrasement avec anneau

L'ISO 12192:2002 spécifie une méthode pour la détermination de la résistance à la compression sur chant (résistance à la compression avec anneau) des papiers et cartons, notamment des cartons utilisés dans la fabrication des boîtes en carton et des caisses d'emballage. L'ISO 12192:2002 est applicable à tous les papiers et cartons dont l'épaisseur est comprise entre 280 micromètres et 580 micromètres. Elle peut également être utilisée pour des papiers et cartons d'épaisseur inférieure à 280 micromètres, mais les résultats obtenus reflètent davantage la rigidité du papier que sa résistance à la compression. Pour les papiers et cartons d'épaisseur supérieure à 580 micromètres, il peut s'avérer impossible d'obtenir une courbure correspondant à la circonférence sans porter atteinte à la structure.

General Information

• Status: Withdrawn
• Publication Date: 12-Nov-2002
• Withdrawal Date: 12-Nov-2002
• ICS: 85.060 - Paper and board
• Technical Committee: ISO/TC 6/SC 2 - Test methods and quality specifications for paper and board
• Drafting Committee: ISO/TC 6/SC 2 - Test methods and quality specifications for paper and board
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 12-Sep-2011

Relations

• Revised: ISO 12192:2011 - Paper and board — Determination of compressive strength — Ring crush method
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 12192
First edition
2002-11-01

Paper and board — Compressive
strength — Ring crush method
Papier et carton — Résistance à la compression — Méthode d'écrasement
avec anneau




Reference number
ISO 12192:2002(E)
©
 ISO 2002

---------------------- Page: 1 ----------------------
ISO 12192:2002(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not
be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this
file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this
area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters
were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event
that a problem relating to it is found, please inform the Central Secretariat at the address given below.


©  ISO 2002
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's member body
in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Printed in Switzerland

ii © ISO 2002 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 12192:2002(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this International Standard may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
International Standard ISO 12192 was prepared by Technical Committee ISO/TC 6, Paper, board and pulps,
Subcommittee SC 2, Test methods and quality specifications for paper and board.
© ISO 2002 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 12192:2002(E)
Introduction
Fibreboard shipping containers are frequently subjected to in-plane compressive forces during shipment or storage.
Therefore, resistance to crushing is an important measure of the performance characteristics of the container.
The resistance to crushing depends on the design of the containers and on the in-plane crush resistance of the
components of the board from which it is made. The in-plane crush resistance of these components can be
measured by the ring crush test.

iv © ISO 2002 – All rights reserved

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 12192:2002(E)

Paper and board — Compressive strength — Ring crush method
1 Scope
This International Standard specifies a method for the determination of the edgewise compressive strength (ring
crush resistance) of paper and paperboard, especially board used in the manufacture of cartons and packing
cases.
This International Standard applies to all paper and paperboard with a thickness in the range of 280 µm to 580 µm.
It may also be used for paper and board having a thickness less than 280 µm but those results are more a
reflection of the paper's stiffness than its compressive strength. For paper and board having a thickness exceeding
580 µm, it may be impossible to bend them to the circumference without disturbing the structure.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this International Standard. For dated references, subsequent amendments to, or revisions of, any of these
publications do not apply. However, parties to agreements based on this International Standard are encouraged to
investigate the possibility of applying the most recent editions of the normative documents indicated below. For
undated references, the latest edition of the normative document referred to applies. Members of ISO and IEC
maintain registers of currently valid International Standards.
ISO 186, Paper and board — Sampling to determine average quality
ISO 187, Paper, board and pulps — Standard atmosphere for conditioning and testing and procedure for
monitoring the atmosphere and conditioning of samples
ISO 534, Paper and board — Determination of thickness and apparent bulk density or apparent sheet density
ISO 13820, Paper, board and corrugated fibreboard — Description and calibration of compression-testing
equipment
3 Principle
A test piece of paper or board, in the form of a narrow strip held in a ring form, is subjected to an increasing
edgewise compressive force until collapse occurs.
4 Apparatus
4.1 Cutting device, consisting of a die cutter, capable of accurately cutting the test pieces to the specified
dimensions with clean, sharp, parallel and straight edges.
Other cutting devices such as a double-knife cutter may be used, provided they can be shown to give similar test
results. The parallelism of the test piece will be determined by the quality of the cutting device. The width of the
male die or the anvil of the double-knife cutter shall be 12,7 mm ± 0,1 mm, and parallel to within 0,015 mm over its
entire length.
© ISO 2002 – All rights reserved 1

---------------------- Page: 5 ----------------------
ISO 12192:2002(E)
4.2 Test-piece holder, consisting of a block, preferably cylindrical, having a cylindrical recession which, together
with a removable central disc, forms an annular groove.
The recession shall have an inside diameter of 49,30 mm ± 0,05 mm and be 6,35 mm ± 0,25 mm deep with its
bottom parallel to the base of the block to within 0,01 mm. The disc is 6,35 mm ± 0,25 mm in thickness. Table 1
gives recommended diameters for the various discs to accommodate the range of thicknesses for this test. A
centring pin of approximately 6,35 mm in diameter is fixed in the exact centre of the cylindrical recess. The pin can
be recessed from the base of the block but shall not protrude from the bottom. Each disc shall have a hole of
slightly larger diameter at its exact centre to accommodate the pin, which will then correctly centralize the disc and
provide a uniform annular groove. See Figure 1.
It is essential that the area of contact between the bottom of the cylindrical recess and its side be a right angle. Any
radius at this point prevents the test strip from resting squarely on the bottom and gives rise to erroneous results.
Dimensions in millimetres


Key
1 Base block
2 Gap to allow d
...

NORME ISO
INTERNATIONALE 12192
Première édition
2002-11-01

Papier et carton — Résistance à la
compression — Méthode d'écrasement
avec anneau
Paper and board — Compressive strength — Ring crush method




Numéro de référence
ISO 12192:2002(F)
©
 ISO 2002

---------------------- Page: 1 ----------------------
ISO 12192:2002(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier peut
être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence autorisant
l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées acceptent de fait la
responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute responsabilité en la
matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du
fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation de
ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer le
Secrétariat central à l'adresse donnée ci-dessous.


©  ISO 2002
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque
forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l’ISO à
l’adresse ci-après ou du comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Imprimé en Suisse

ii © ISO 2002 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 12192:2002(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux de
normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 3.
La tâche principale des comités techniques est d’élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur publication
comme Normes internationales requiert l’approbation de 75 % au moins des comités membres votants.
L’attention est appelée sur le fait que certains des éléments de la présente Norme internationale peuvent faire
l’objet de droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable de
ne pas avoir identifié de tels droits de propriété et averti de leur existence.
L’ISO 12192 a été élaborée par le comité technique ISO/TC 6, Papiers, cartons et pâtes, sous-comité SC 2,
Méthodes d’essais et spécifications de qualité des papiers et cartons.

© ISO 2002 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 12192:2002(F)
Introduction
Les emballages d’expédition en carton dur sont fréquemment soumis à des forces de compression à plat au cours
de leur expédition ou de leur stockage. Par conséquent, la résistance à l’écrasement constitue une mesure
importante des propriétés mécaniques des emballages.
La résistance à l’écrasement dépend de la conception de l’emballage et de la résistance à l’écrasement à plat des
composants du carton dont l’emballage est constitué. La résistance de ces composants à l’écrasement à plat peut
être mesurée au moyen de l’essai d’écrasement avec anneau.

iv © ISO 2002 – Tous droits réservés

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 12192:2002(F)

Papier et carton — Résistance à la compression — Méthode
d'écrasement avec anneau
1 Domaine d’application
La présente Norme internationale spécifie une méthode pour la détermination de la résistance à la compression
sur chant (résistance à la compression avec anneau) des papiers et cartons, notamment des cartons utilisés dans
la fabrication des boîtes en carton et des caisses d’emballage.
La présente Norme internationale est applicable à tous les papiers et cartons dont l’épaisseur est comprise entre
280 µm et 580 µm. La présente Norme internationale peut également être utilisée pour des papiers et cartons
d’épaisseur inférieure à 280 µm, mais les résultats obtenus reflètent davantage la rigidité du papier que sa
résistance à la compression. Pour les papiers et cartons d’épaisseur supérieure à 580 µm, il peut s’avérer
impossible d’obtenir une courbure correspondant à la circonférence sans porter atteinte à la structure.
2 Références normatives
Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,
constituent des dispositions valables pour la présente Norme internationale. Pour les références datées, les
amendements ultérieurs ou les révisions de ces publications ne s’appliquent pas. Toutefois, les parties prenantes
aux accords fondés sur la présente Norme internationale sont invitées à rechercher la possibilité d’appliquer les
éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière
édition du document normatif en référence s’applique. Les membres de l’ISO et de la CEI possèdent le registre des
Normes internationales en vigueur.
ISO 186, Papier et carton — Échantillonnage pour déterminer la qualité moyenne
ISO 187, Papier, carton et pâtes — Atmosphère normale de conditionnement et d’essai et méthode de surveillance
de l’atmosphère et de conditionnement des échantillons
ISO 534, Papier et carton — Détermination de l’épaisseur et de la masse volumique des feuilles uniques ou des
feuilles en liasses
ISO 13820, Papier, carton et carton ondulé — Description et étalonnage du matériel pour essai de compression
3 Principe
Une éprouvette constituée de papier ou de carton, ayant la forme d’une bande étroite, maintenue dans un gabarit
en forme d’anneau, est soumise à une force croissante de compression sur chant, jusqu’à l’affaissement de la
bande.
4 Appareillage
4.1 Appareil de découpage, constitué d’un emporte-pièce, permettant de découper avec précision les
éprouvettes aux dimensions spécifiées, en produisant des bords propres, nets, parallèles et droits.
© ISO 2002 – Tous droits réservés 1

---------------------- Page: 5 ----------------------
ISO 12192:2002(F)
Il est également possible d’utiliser d’autres appareils de découpage comme un massicot à deux lames, à condition
qu’il soit démontré qu’ils permettent d’obtenir des résultats d’essai similaires. Le parallélisme de l’éprouvette est
déterminé par la qualité de l’appareil de découpage. La largeur de la partie mâle de la forme de découpe ou de la
contre-pièce du massicot à deux lames doit être de 12,7 mm ± 0,1 mm; elle doit être parallèle sur toute sa
longueur, à 0,015 mm près.
4.2 Porte-éprouvette, constitué d’un support, de préférence cylindrique, comportant un évidement cylindrique
qui, avec un disque central amovible, forme une gorge annulaire.
L’évidement doit avoir un diamètre intérieur de 49,30 mm ± 0,05 mm et une profondeur de 6,35 mm ± 0,25 mm, et
son fond doit être parallèle à la base du support, à 0,01 mm près. Le disque a une épaisseur de
6,35 mm ± 0,25 mm. Le Tableau 1 indique les diamètres recommandés pour les différents disques, en fonction des
épaisseurs, pour cet essai. Un goujon de centrage d’environ 6,35 mm de diamètre est fixé exactement au centre
de l’évidement cylindrique. Le goujon peut être en retrait de la base du support, mais il ne doit pas dépasser de
celle-ci. Chaque disque doit comporter un trou exactement centré et de diamètre légèrement supérieur à celui du
goujon pour permettre son passage, ce qui permettra d’obtenir un centrage correct du disque et une gorge
annulaire uniforme. Voir la Figure 1.
Il est essentiel que la zone de contact entre le fond de l’évidement cylindrique et le côté de celui-ci forme un angle
droit. Tout rayon à ce niveau empêche la bande d’essai de reposer entièrement sur le fond de l’évidement et
fausse les résultats.
Dimensions en millimètres

Légende
1 Base du support
2 Jeu permettant la rotation libre des disques
3 Disque
4 Goujon de cent
...