ISO 26443:2023

Fine ceramics (advanced ceramics, advanced technical ceramics) - Rockwell indentation test for evaluation of adhesion of ceramic coatings

This document specifies a method for the qualitative evaluation of the adhesion of ceramic coatings up to 20 μm thick by indentation with a Rockwell diamond indenter. The formation of cracks after indentation can also reveal cohesive failure. The indentations are made with a Rockwell hardness test instrument. The method described in this document can also be suitable for evaluating the adhesion of metallic coatings. The test is not suitable for elastic coatings on hard substrates.

Céramiques techniques — Évaluation de l'adhérence des revêtements céramiques par l'essai de pénétration Rockwell

Le présent document spécifie une méthode permettant l’évaluation qualitative de l’adhérence de revêtements céramiques jusqu’à 20 μm d’épaisseur par indentation à l’aide d’un pénétrateur diamanté de Rockwell. La formation de fissures après l’indentation peut également révéler une rupture cohésive. Les indentations sont réalisées à l’aide d’un instrument d’essai de dureté Rockwell. La méthode décrite dans le présent document peut également être adaptée à l’évaluation de l’adhérence de revêtements métalliques. L’essai n’est pas adapté aux revêtements élastiques sur des substrats durs.

General Information

• Status: Published
• Publication Date: 30-Oct-2023
• ICS: 81.060.30 - Advanced ceramics
• Technical Committee: ISO/TC 206 - Fine ceramics
• Drafting Committee: ISO/TC 206 - Fine ceramics
• Current Stage: 6060 - International Standard published
• Start Date: 31-Oct-2023
• Due Date: 24-Jul-2024
• Completion Date: 31-Oct-2023

Relations

• Consolidates: ISO 8013:2019 - Rubber, vulcanized - Determination of creep in compression or shear
• Effective Date: 11-Feb-2023
• Revises: ISO 26443:2008 - Fine ceramics (advanced ceramics, advanced technical ceramics) - Rockwell indentation test for evaluation of adhesion of ceramic coatings
• Effective Date: 28-Jan-2023

Overview

ISO 26443:2023 - "Fine ceramics (advanced ceramics, advanced technical ceramics) - Rockwell indentation test for evaluation of adhesion of ceramic coatings" specifies a qualitative adhesion test for ceramic coatings (and some metallic coatings) up to 20 μm thickness. The standard defines using a Rockwell diamond indenter on a Rockwell hardness tester to produce indentations, then inspects the indent and surrounding area microscopically to classify adhesion and reveal cohesive failure (cracking). The test is not suitable for elastic coatings on hard substrates.

Key topics and technical requirements

• Scope: Adhesion evaluation for coatings ≤ 20 μm; also applicable to some metallic coatings. Not for elastic coatings on hard substrates.
• Test principle: Indentation with Rockwell diamond indenter followed by optical microscopy to detect cracking, flaking or delamination.
• Equipment & references:
  • Use Rockwell procedures per ISO 6508-1 (test method).
  • Machine/indenter verification per ISO 6508-2.
  • Regular indenter contour checks recommended (optical magnification ≥ ×200 to detect ring cracks/microwear).
• Loading rules (select by substrate/coating):
  • Metallic substrates harder than 54 HRC: 1 471.5 N (Rockwell C scale).
  • Metallic substrates softer than 54 HRC and medium case‑hardened steel: 981 N (Rockwell D).
  • Other substrates (ceramics, cermets, thin/soft substrates): 588.6 N (Rockwell A).
• Timing: Loading time 1–8 s and hold time (4 ± 2) s (per ISO 6508-1) - keep constant for repeatability.
• Classification: Results are categorized into Class 0–3:
  • Class 0: No cracking/delamination (acceptable).
  • Class 1: Cracking without adhesive delamination (acceptable).
  • Class 2: Partial adhesive delamination (unacceptable; report % area delaminated).
  • Class 3: Complete adhesive delamination (unacceptable; report r/a ratio).
• Inspection: Use optical microscopy (×100) and optional contrast techniques (e.g., Nomarski) to reveal cracks.
• Reporting: Include equipment, calibration, specimen description, load used, at least three test results, and detailed descriptions for class 2/3 failures.

Applications and who uses it

ISO 26443:2023 is intended for:

• Coating engineers, materials scientists, and R&D developing thin ceramic or metallic coatings.
• Quality control and industrial test laboratories performing coating adhesion tests on advanced ceramics, cermets, cemented carbides, and coated metals.
• Failure analysis and comparative evaluation of coating/substrate systems during process development or production qualification.

Practical uses: production QA, comparative adhesion assessment across substrates or coatings, early-stage screening of coating adhesion, and documenting adhesion performance for supplier/customer agreements.

Related standards

• ISO 6508-1 - Metallic materials - Rockwell hardness test - Part 1: Test method
• ISO 6508-2 - Metallic materials - Rockwell hardness test - Part 2: Verification and calibration of testing machines and indenters

Keywords: ISO 26443, Rockwell indentation test, adhesion of ceramic coatings, fine ceramics, Rockwell diamond indenter, coating adhesion test, ceramic coating evaluation.

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 26443
Second edition
2023-10
Fine ceramics (advanced ceramics,
advanced technical ceramics) —
Rockwell indentation test for
evaluation of adhesion of ceramic
coatings
Céramiques techniques — Évaluation de l'adhérence des revêtements
céramiques par l'essai de pénétration Rockwell
Reference number
© ISO 2023
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 1
6 Sampling and preparation of test specimens . 2
7 Procedure .2
8 Limits . 3
9 Test report . 3
Annex A (informative) Pictorial representations and sample photographs of the classes
defined in Table 1 . .4
Bibliography . 6
iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO document should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use
of (a) patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed
patent rights in respect thereof. As of the date of publication of this document, ISO had not received
notice of (a) patent(s) which may be required to implement this document. However, implementers are
cautioned that this may not represent the latest information, which may be obtained from the patent
database available at www.iso.org/patents. ISO shall not be held responsible for identifying any or all
such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 206, Fine ceramics, in collaboration
with the European Committee for Standardization (CEN) Technical Committee CEN/TC 184, Advanced
technical ceramics, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
This second edition cancels and replaces the first edition (ISO 26443:2008), of which it constitutes a
minor revision. The changes are as follows:
— table of contents was added;
— normative reference titles were updated;
— units for loads in kgf were deleted.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
INTERNATIONAL STANDARD ISO 26443:2023(E)
Fine ceramics (advanced ceramics, advanced technical
ceramics) — Rockwell indentation test for evaluation of
adhesion of ceramic coatings
1 Scope
This document specifies a method for the qualitative evaluation of the adhesion of ceramic coatings
up to 20 μm thick by indentation with a Rockwell diamond indenter. The formation of cracks after
indentation can also reveal cohesive failure. The indentations are made with a Rockwell hardness test
instrument.
The method described in this document can also be suitable for evaluating the adhesion of metallic
coatings.
The test is not suitable for elastic coatings on hard substrates.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requireme
...

NORME ISO
INTERNATIONALE 26443
Deuxième édition
2023-10
Céramiques techniques — Évaluation
de l'adhérence des revêtements
céramiques par l'essai de pénétration
Rockwell
Fine ceramics (advanced ceramics, advanced technical ceramics) —
Rockwell indentation test for evaluation of adhesion of ceramic
coatings
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2023
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 1
4 Principe. 1
5 Appareillage . 1
6 Échantillonnage et préparation des éprouvettes . 2
7 Mode opératoire . 2
8 Limites . 3
9 Rapport d’essai . 3
Annexe A (informative) Représentation schématique et exemples de photographie des
classes définies dans le Tableau 1 . 5
Bibliographie . 7
iii
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner
l’utilisation d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité
et à l’applicabilité de tout droit de brevet revendiqué à cet égard. À la date de publication du présent
document, l’ISO n'avait pas reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa
mise en application. Toutefois, il y a lieu d’avertir les responsables de la mise en application du présent
document que des informations plus récentes sont susceptibles de figurer dans la base de données de
brevets, disponible à l'adresse www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne
pas avoir identifié tout ou partie de tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 206, Céramiques techniques, en
collaboration avec le comité technique CEN/TC 184, Céramiques techniques, du Comité européen de
normalisation (CEN), conformément à l'Accord de coopération technique entre l'ISO et le CEN (Accord
de Vienne).
Cette deuxième édition annule et remplace la première édition (ISO 26443:2008), dont elle constitue
une révision mineure. Les modifications sont les suivantes:
— le sommaire a été ajouté;
— les titres des références normatives ont été mis à jour;
— les unités de charge en kgf ont été supprimées.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/members.html.
iv
NORME INTERNATIONALE ISO 26443:2023(F)
Céramiques techniques — Évaluation de l'adhérence
des revêtements céramiques par l'essai de pénétration
Rockwell
1 Domaine d’application
Le présent document spécifie une méthode permettant l’évaluation qualitative de l’adhérence de
revêtements céramiques jusqu’à 20 μm d’épaisseur par indentation à l’aide d’un pénétrateur diamanté
de Rockwell. La formation de fissures après l’indentation peut également révéler une rupture cohésive.
Les indentations sont réalisées à l’aide d’un instrument d’essai de dureté Rockwell.
La méthode décrite dans le présent document peut également être adaptée à l’évaluation de l’adhérence
de revêtements métalliques.
L’essai n’est pas adapté aux revêtements élastiques sur des substrats durs.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition de la publication à laquelle il est fait référence (y
compris tous les amendements) s'applique.
ISO 6508-1, Matériaux métalliques — Essai de dureté Rockwell — Partie 1: Méthode d’essai
ISO 6508-2, Matériaux métalliques — Essai de dureté Rockwell — Pa
...