ISO 535:2023

Paper and board — Determination of water absorptiveness — Cobb method

This document specifies a method for determining the water absorptiveness of paper and board, including corrugated fibreboard, under standard conditions. This document is not applicable for paper of grammage less than 50 g/m2 or embossed paper. It is not applicable for porous papers such as newsprint or papers such as blotting paper or other papers having a relatively high-water absorptiveness for which ISO 8787 is more suitable.

Papier et carton — Détermination de la capacité d'absorption d'eau — Méthode de Cobb

Le présent document spécifie une méthode de détermination de la capacité d’absorption d’eau du papier et du carton, y compris du carton ondulé, dans des conditions normalisées. Le présent document ne s’applique pas aux types de papiers suivants: papier de grammage inférieur à 50 g/m2, papier gaufré, papiers poreux tels que le papier journal, papiers tels que le papier buvard ou d’autres papiers ayant une capacité d’absorption d’eau relativement élevée, l’ISO 8787 étant mieux adaptée dans ces cas.

General Information

• Status: Published
• Publication Date: 12-Mar-2023
• ICS: 85.060 - Paper and board
• Technical Committee: ISO/TC 6/SC 2 - Test methods and quality specifications for paper and board
• Drafting Committee: ISO/TC 6/SC 2/WG 47 - Water absorptiveness of paper and board
• Current Stage: 6060 - International Standard published
• Start Date: 13-Mar-2023
• Due Date: 21-Nov-2022
• Completion Date: 13-Mar-2023

Relations

• Revises: ISO 535:2014 - Paper and board — Determination of water absorptiveness — Cobb method
• Effective Date: 23-Apr-2020

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 535
Fourth edition
2023-03
Paper and board — Determination of
water absorptiveness — Cobb method
Papier et carton — Détermination de la capacité d'absorption d'eau
— Méthode de Cobb
Reference number
ISO 535:2023(E)
© ISO 2023

---------------------- Page: 1 ----------------------
ISO 535:2023(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2023
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
  © ISO 2023 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 535:2023(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Reagents and materials . 2
6 Apparatus . 2
7 Sampling . 3
8 Conditioning . 3
9 Preparation of test pieces .3
10 Procedure .3
10.1 General . 3
10.2 Mounting of the test pieces . . 3
10.3 Exposure to water and blotting . 3
10.4 Times of test . 5
10.5 Rejection of test pieces . 5
11 Expression of results . 5
12 Precision . 6
13 Test report . 6
Annex A (informative) Precision . 7
Annex B (informative) Suitable blotting paper . 9
Bibliography .10
iii
© ISO 2023 – All rights reserved

---------------------- Page: 3 ----------------------
ISO 535:2023(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 6, Paper, board and pulps, Subcommittee
SC 2, Test methods and quality specifications for paper and board, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 172, Pulp, paper and board, in
accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This fourth edition cancels and replaces the third edition (ISO 535:2014), which has been technically
revised.
The main changes are as follows:
— requirements in 5.1 and 5.2 added;
— Clause 6 and 6.2 revised;
— preparation of test pieces added in Clause 9;
— Subclauses 10.3 and 10.4 revised and requirements added;
— several additional explanations added in 10.5.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
  © ISO 2023 – All rights reserved

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 535:2023(E)
Paper and board — Determination of water absorptiveness
— Cobb method
1 Scope
This document specifies a method for determining the water absorptiveness of paper and board,
including corrugated fibreboard, under standard conditions.
2
This document is not applicable for paper of grammage less than 50 g/m or embossed paper. It is not
applicable for porous papers such as newsprint or papers such as blotting paper or other papers having
a relatively high-water absorptiveness for which ISO 8787 is more suitable.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 186, Paper and board — Sampling to determine average quality
ISO 187, Paper, board and pulps — Standard atmosphere for conditioning and testing and procedure for
monitoring the atmosphere and conditioning of samples
ISO 14487, Pulps — Standard water for physical testing
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
water absorptiveness
Cobb value
2
calculated mass of water absorbed in a specified time by 1 m of paper or board under specified
conditions
2
Note 1 to entry: The test area is normally 100 cm .
4 Principle
A test piece is weighed immediately before and after exposure for a specified time of one surface to
water, followed by blotting. The result of the increase in mass is expressed in grams per square
2
metre (g/m ).
The test piece shall not show any sign of penetration through or leakage outside the test ring (see 10.5).
1
© ISO 2023 – All rights reserved

---------------------- Page: 5 ----------------------
ISO 535:2023(E)
5 Reagents and materials
5.1 Water, distilled or deionized, at the laboratory conditioning temperature, i.e. 23 °C ± 1 °C or
27 °C ± 1 °C in tropical countries. The water shall fulfil the requirements of ISO 14487.
2 2
5.2 Blotting paper, having a grammage of 250 g/m ± 25 g/m .
The blotting paper shall have dimensions of at least 140 mm × 140 mm either circular or rectangular.
Blotting papers in accordance with ISO 5269-1 are suitable, see Annex B.
6 Apparatus
6.1 Absorptiveness tester for the determination of water absorptiveness.
Any type of apparatus may be used which permits
— an immediate and uniform contact of the water with the part of the test piece submitted to the test,
— controlled rapid removal of the unabsorbed water from the test piece at the end of the contact
period, and
— the rapid removal of the test piece without the risk of water contacting the test piece outside the test
area.
In its simplest form, the apparatus consists of a rigid base with a smooth, planar surface, and a rigid
2
metal cylinder of 112,8 mm ± 0,2 mm internal diameter (corresponding to a test area of 100 cm ) and
with a means of clamping it firmly to the base plate. The edge of the cylinder in contact with the test
piece shall be flat and machined smooth with a thickness sufficient to prevent the cylinder cutting into
the test piece. The height of the cylinder is not important, provided it is sufficient to contain a water
depth of 10 mm.
For materials where leakage between the cylinder and the upper surface of the test piece can occur
during the test, a soft, elastic, non-absorbent gasket may be interposed to prevent this. This gasket shall
have the same internal diameter as the cylinder after clamping.
If a gasket is used, it shall be used for all test pieces.
The diameter of the compressed gasket can be tested as follows: mount a piece of carbonless paper
which has roughly the same dimensions as the test piece, into the absorptiveness tester, and close
the cylinder as for the test. If the pressure is not high enough for an adequate impression, use a usual
test piece and the carbonless paper to increase the thickness of the arrangement. In some cases, a
compressible, blotter-like paper or other papers can be more suitable to test the diameter of the gasket.
To prevent damage to the machined edge of the cylinder caused by clamping it upside down it is
recommended to mark the top in some way so that it can be identified readily. If a cylinder of a small
2
area is used it should not be less than 50 cm . The water depth shall still be 10 mm.
When testing corrugated fibreboard, it is recommended to use an apparatus with adjustable pressure
to adjust the cylinder according to the structural conditions of the test piece.
6.2 Metal roller, with a smooth face, 200 mm ± 10 mm wide, a diameter of 90 mm ± 10 mm and a
mass of 10 kg ± 0,5 kg.
6.3 Balance, which can be read to the nearest 1 mg.
6.4 Timer, reading in seconds and capable of timing up to at least 30 min.
2
  © ISO 2023 – All rights reserved

---------------------- Page: 6 ----------------------
ISO 535:2023(E)
6.5 Graduated cylinder, or other means of measuring appropriate aliquots.
7 Sampling
If the tests are made to evaluate a lot, the sample shall be selected in accordance with ISO 186. If the
tests are made on another type of sample, the test pieces shall be representative of the sample received.
8 Conditioning
Condition the sample as specified in ISO 187. Keep it in the conditioning atmosphere throughout the
test.
9 Preparation of test pieces
Prepare the test pieces in the atmospheric conditions identical to those used to condition the samples.
...

NORME ISO
INTERNATIONALE 535
Quatrième édition
2023-03
Papier et carton — Détermination
de la capacité d'absorption d'eau —
Méthode de Cobb
Paper and board — Determination of water absorptiveness — Cobb
method
Numéro de référence
ISO 535:2023(F)
© ISO 2023

---------------------- Page: 1 ----------------------
ISO 535:2023(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2023
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
  © ISO 2023 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 535:2023(F)
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 1
4 Principe. 1
5 Réactifs et matériaux . 2
6 Appareillage . 2
7 Échantillonnage .3
8 Conditionnement .3
9 Préparation des éprouvettes . 3
10 Mode opératoire . 3
10.1 Généralités . 3
10.2 Mise en place des éprouvettes . 3
10.3 Exposition à l’eau et essuyage . 3
10.4 Durées d’essai . 5
10.5 Rejet des éprouvettes . 5
11 Expression des résultats . 6
12 Fidélité . 6
13 Rapport d’essai . 6
Annexe A (informative) Fidélité .8
Annexe B (informative) Papier buvard adapté .10
Bibliographie .11
iii
© ISO 2023 – Tous droits réservés

---------------------- Page: 3 ----------------------
ISO 535:2023(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 6, Papiers, cartons et pâtes, sous-
comité SC 2, Méthodes d'essais et spécifications de qualité des papiers et cartons, en collaboration avec
le comité technique CEN/TC 172, Pâtes, papier et carton, du Comité européen de normalisation (CEN)
conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette quatrième édition annule et remplace la troisième édition (ISO 535:2014), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— ajout d’exigences aux paragraphes 5.1 et 5.2;
— révision de l’Article 6 et du paragraphe 6.2;
— ajout d’informations sur la préparation des éprouvettes à l’Article 9;
— révision des paragraphes 10.3 et 10.4 et ajout d’exigences dans ceux-ci;
— ajout de nombreuses explications supplémentaires dans le paragraphe 10.5.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.html.
iv
  © ISO 2023 – Tous droits réservés

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 535:2023(F)
Papier et carton — Détermination de la capacité
d'absorption d'eau — Méthode de Cobb
1 Domaine d’application
Le présent document spécifie une méthode de détermination de la capacité d’absorption d’eau du papier
et du carton, y compris du carton ondulé, dans des conditions normalisées.
Le présent document ne s’applique pas aux types de papiers suivants: papier de grammage inférieur
2
à 50 g/m , papier gaufré, papiers poreux tels que le papier journal, papiers tels que le papier buvard
ou d’autres papiers ayant une capacité d’absorption d’eau relativement élevée, l’ISO 8787 étant mieux
adaptée dans ces cas.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 186, Papier et carton — Échantillonnage pour déterminer la qualité moyenne
ISO 187, Papier, carton et pâtes — Atmosphère normale de conditionnement et d'essai et méthode de
surveillance de l'atmosphère et de conditionnement des échantillons
ISO 14487, Pâtes — Eau normalisée pour essais physiques
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
3.1
capacité d’absorption de l’eau
indice de Cobb
résultat du calcul de la masse d’eau absorbée par mètre carré de papier ou de carton, pendant un temps
défini et dans des conditions spécifiées
2
Note 1 à l'article: D’ordinaire, la zone d’essai mesure 100 cm .
4 Principe
Une éprouvette est pesée immédiatement avant et immédiatement après exposition à l’eau d’une de
ses faces pendant un temps défini, suivi d’un essuyage. Le résultat de l’accroissement de la masse est
2
exprimé en grammes par mètre carré (g/m ).
L’éprouvette ne doit présenter aucun signe de transpercement ou de fuite à l’extérieur du cylindre
(voir 10.5).
1
© ISO 2023 – Tous droits réservés

---------------------- Page: 5 ----------------------
ISO 535:2023(F)
5 Réactifs et matériaux
5.1 Eau distillée ou déionisée, à la température de conditionnement du laboratoire, c’est-à-dire
(23 ± 1) °C, ou (27 ± 1) °C dans les pays tropicaux. L’eau doit respecter les exigences de l’ISO 14487.
2
5.2 Papier buvard, de grammage égal à (250 ± 25) g/m .
Le papier buvard doit être de forme circulaire ou rectangulaire et mesurer au moins 140 mm × 140 mm.
Les papiers buvards conformes à l’ISO 5269-1 sont adaptés (voir l’Annexe B).
6 Appareillage
6.1 Appareil d’essai de capacité d’absorption pour déterminer la capacité d’absorption de l’eau.
Tout type d’appareil permettant d’effectuer les actions suivantes peut être utilisé:
— la mise en contact immédiate et uniforme de l’eau avec la partie de l’éprouvette soumise à essai;
— le retrait rapide et contrôlé de l’eau non absorbée par l’éprouvette à la fin de la période de mise en
contact;
— le retrait rapide de l’éprouvette sans qu’il existe un risque de contact de l’eau avec une surface
extérieure à la surface d’essai.
Sous sa forme la plus simple, l’appareil se compose d’une embase rigide à surface lisse et plane et d’un
cylindre métallique rigide de diamètre intérieur égal à (112,8 ± 0,2) mm (correspondant à une surface
2
d’essai d’environ 100 cm ), muni d’un dispositif permettant de le fixer solidement à l’embase. Le bord du
cylindre qui vient au contact de l’éprouvette doit être plat et poli par usinage, et posséder une épaisseur
suffisante pour ne pas entailler l’éprouvette. La hauteur du cylindre importe peu pourvu qu’il puisse
contenir une hauteur d’eau de 10 mm.
Si des fuites sont susceptibles de se produire en cours d’essai entre le cylindre et la face supérieure de
l’éprouvette en raison du matériau utilisé, celles-ci peuvent être évitées par l’interposition d’un joint
mou, élastique et non absorbant. Ce joint doit avoir le même diamètre intérieur que celui du cylindre
après fixation.
Si un joint est utilisé, il doit l’être pour toutes les éprouvettes.
Le diamètre du joint comprimé peut être soumis à essai comme suit: mettre en place, sur l’appareil
d’essai de capacité d’absorption, un morceau de papier autocopiant de dimensions approximativement
identiques à celles de l’éprouvette et fermer le cylindre comme pour l’essai. Si la pression n’est pas
assez élevée pour que l’impression soit suffisante, utiliser une éprouvette habituelle en plus du papier
autocopiant afin d’augmenter l’épaisseur de l’ensemble. Dans certains cas, un papier de type buvard
compressible ou d’autres papiers peuvent se révéler plus adaptés pour soumettre à essai le diamètre du
joint.
Pour éviter d’endommager le bord usiné du cylindre si ce dernier est fixé à l’envers, il est conseillé
de marquer la face supérieure du cylindre de façon à pouvoir l’identifier facilement. Si un cylindre de
2
section réduite est utilisé, il convient que celle-ci ne soit pas inférieure à 50 cm . La hauteur d’eau doit
toujours être de 10 mm.
Si du carton ondulé est utilisé, il est recommandé d’utiliser un appareil dont la pression est réglable afin
d’adapter le cylindre aux conditions structurelles de l’éprouvette.
6.2 Rouleau métallique, présentant une face polie, d’une largeur de (200 ± 10) mm, d’un diamètre de
(90 ± 10) mm et d’une masse de (10 ± 0,5) kg.
2
  © ISO 2023 – Tous droits réservés

---------------------- Page: 6 ----------------------
ISO 535:2023(F)
6.3 Balance, pouvant indiquer une masse à 1 mg près.
6.4 Chronomètre, permettant la lecture en secondes d’une durée d’au moins 30 min.
6.5 Éprouvette graduée, ou autre moyen permettant de mesurer des aliquotes appropriées.
7 Échantillonnage
Si les essais sont effectués pour évaluer un lot, l’échantillon doit être choisi conformément à l’ISO 186. Si
les essais sont effectués sur un autre type d’échantillon, les éprouvettes doivent être représentatives de
l’échantillon reçu.
8 Conditionnement
Conditionner l’échantillon comme spécifié dans l’ISO 187. Le conserver dans l’atmosphère de
conditionnement pendant toute la durée de l’essai.
9 Préparation des éprouvettes
Préparer les éprouvettes dans les mêmes conditions atmosphériques que celles utilisées pour les
échantillons. Dans les échantillons, découper un minimum de cinq éprouvettes pour chacune des
faces à soumettre à essai en évitant tout contact de la surface d’essai avec les mains ou les doigts. Les
éprouvettes doiv
...

ISO/FDIS 535: ####2022 (E)
ISO TC 6/SC 2/WG 47
Date: 2022-10-0711-03
Secretariat: SIS
Paper and board — Determination of water absorptiveness — Cobb method
© ISO 2022 – All rights reserved

---------------------- Page: 1 ----------------------
ISO/FDIS 535: #### 2022(E)
© ISO 20XX2022
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no
part of this publication may be reproduced or utilized otherwise in any form or by any means,
electronic or mechanical, including photocopying, or posting on the internet or an intranet, without
prior written permission. Permission can be requested from either ISO at the address below or
ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Fax: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
© ISO 2022 – All rights reserved
ii © ISO 2022 – All rights reserved

---------------------- Page: 2 ----------------------
ISO/FDIS 535: #### 2022(E)
Contents
Foreword . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Reagents and materials . 2
5.1 Water, distilled or deionized . 2
5.2 Blotting paper . 2
6 Apparatus . 2
6.1 Absorptiveness tester . 2
6.2 Metal roller . 3
6.3 Balance . 3
6.4 Timer, . 3
6.5 Graduated cylinder, . 3
7 Sampling . 3
8 Conditioning . 3
9 Preparation of test pieces . 3
10 Procedure . 3
10.1 General . 3
10.2 Mounting of the test pieces . 4
10.3 Exposure to water and blotting . 4
10.4 Times of test . 5
10.5 Rejection of test pieces . 6
11 Expression of results . 6
12 Precision . 7
13 Test report . 7
Annex A (informative) Precision . 8
Annex B (informative) Suitable blotting paper . 11
Bibliography . 12

© ISO 2022 – All rights reserved
© ISO 2022 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO/FDIS 535: #### 2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any
patent rights identified during the development of the document will be in the Introduction and/or on
the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the World
Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 6, Paper, board and pulps, Subcommittee
SC 2, Test methods and quality specifications for paper and board, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 172, Pulp, paper and board, in
accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This fourth edition cancels and replaces the third edition (ISO 535:2014), which has been technically
revised.
The main changes are as follows:
— requirements in 5.1 and 5.2 added;
— Clause 6 and 6.2 revised;
— preparation of test pieces added in Clause 9;
— Subclauses 10.3 and 10.4 revised and requirements added;
— several additional explanations added in 10.5;
© ISO 2022 – All rights reserved
iv © ISO 2022 – All rights reserved

---------------------- Page: 4 ----------------------
ISO/FDIS 535: #### 2022(E)
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
© ISO 2022 – All rights reserved
© ISO 2022 – All rights reserved v

---------------------- Page: 5 ----------------------
ISO/FDIS 535: #### (E)
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 535:2022(E)

Paper and board — Determination of water absorptiveness —
Cobb method
1 Scope
This document specifies a method for determining the water absorptiveness of paper and board,
including corrugated fibreboard, under standard conditions.
2
This document is not applicable for paper of grammage less than 50 g/m or embossed paper. It is not
applicable for porous papers such as newsprint or papers such as blotting paper or other papers having
a relatively high-water absorptiveness for which ISO 8787 is more suitable.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 186, Paper and board — Sampling to determine average quality
ISO 187, Paper, board and pulps — Standard atmosphere for conditioning and testing and procedure for
monitoring the atmosphere and conditioning of samples
ISO 5269-1, Pulps — Preparation of laboratory sheets for physical testing — Part 1: Conventional sheet-
former method
ISO 14487, Pulps — Standard water for physical testing
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https://www.iso.org/obp
— IEC Electropedia: available at https://www.electropedia.org/
3.1
water absorptiveness
Cobb value
2
calculated mass of water absorbed in a specified time by 1 m of paper or board under specified
conditions
© ISO 2022 – All rights reserved 1

---------------------- Page: 6 ----------------------
ISO/FDIS 535:2022(E)
2
Note 1 to entry: The test area is normally 100 cm .
4 Principle
A test piece is weighed immediately before and after exposure for a specified time of one surface to water,
2
followed by blotting. The result of the increase in mass is expressed in grams per square metre (g/m ).
The test piece shall not show any sign of penetration through or leakage outside the test ring (see 10.5).
5 Reagents and materials
5.1 Water, distilled or deionized, at the laboratory conditioning temperature, i.e. 23 °C ± 1 °C or
27 °C ± 1 °C in tropical countries. The water shall fulfil the requirements of ISO 14487.
2 2
5.2 Blotting paper, having a grammage of 250 g/m ± 25 g/m .
The blotting paper shall have dimensions of at least 140 mm × 140 mm either circular or rectangular.
Blotting papers in accordance with ISO 5269-1 are suitable, see .Annex B.
6 Apparatus
6.1 Absorptiveness tester for the determination of water absorptiveness.
Any type of apparatus may be used which permits
— an immediate and uniform contact of the water with the part of the test piece submitted to the test,
— controlled rapid removal of the unabsorbed water from the test piece at the end of the contact period,
and
— the rapid removal of the test piece without the risk of water contacting the test piece outside the test
area.
In its simplest form, the apparatus consists of a rigid base with a smooth, planar surface, and a rigid metal
2
) and with a
cylinder of 112,8 mm ± 0,2 mm internal diameter (corresponding to a test area of 100 cm
means of clamping it firmly to the base plate. The edge of the cylinder in contact with the test piece shall
be flat and machined smooth with a thickness sufficient to prevent the cylinder cutting into the test piece.
The height of the cylinder is not important, provided it is sufficient to contain a water depth of 10 mm.
For materials where leakage between the cylinder and the upper surface of the test piece can occur during
the test, a soft, elastic, non-absorbent gasket may be interposed to prevent this. This gasket shall have the
same internal diameter as the cylinder after clamping.
If a gasket is used, it shall be used for all test pieces.
The diameter of the compressed gasket can be tested as follows: mount a piece of carbonless paper which
has roughly the same dimensions as the test piece, into the absorptiveness tester, and close the cylinder
as for the test. If the pressure is not high enough for an adequate impression, use a usual test piece and
© ISO 2022 – All rights reserved
2 © ISO 2022 – All rights reserved

---------------------- Page: 7 ----------------------
ISO/FDIS 535:2022(E)
the carbonless paper to increase the thickness of the arrangement. In some cases, a compressible, blotter-
like paper or other papers can be more suitable to test the diameter of the gasket.
To prevent damage to the machined edge of the cylinder caused by clamping it upside down it is
recommended to mark the top in some way so that it can be identified readily. If a cylinder of a small area
2
is used it should not be less than 50 cm . The water depth shall still be 10 mm.
When testing corrugated fibreboard, it is recommended to use an apparatus with adjustable pressure to
adjust the cylinder according to the structural conditions of the test piece.
6.2 Metal roller, with a smooth face, 200 mm ± 10 mm wide, a diameter of 90 mm ± 10 mm and a mass
of 10 kg ± 0,5 kg.
6.3 Balance, which can be read to the nearest 1 mg.
6.4 Timer, reading in seconds and capable of timing up to at least 30 min.
6.5 Graduated cylinder, or other means of measuring appropriate aliquots.
7 Sampling
If the tests are made to evaluate a lot, the sample shall be selected in accordance with ISO 186. If the tests
are made on another type of sample, the test pieces shall be representative of the sample received.
8 Conditioning
Condition the sample as specified in ISO 187. Keep them in the conditioning atmosphere throughout the
test.
9 Preparation of test pieces
Prepare the test pieces in the atmospheric conditions identical to those used to condition them. Avoiding
contact of the test area with hands or fingers, cut from the sample at least 5five test pieces for each face
to be tested. The test pieces shall be of suffi
...

FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 535
ISO/TC 6/SC 2
Paper and board — Determination of
Secretariat: SIS
water absorptiveness — Cobb method
Voting begins on:
2022-11-17
Papier et carton — Détermination de la capacité d'absorption d'eau
— Méthode de Cobb
Voting terminates on:
2023-01-12
ISO/CEN PARALLEL PROCESSING
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 535:2022(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
NATIONAL REGULATIONS. © ISO 2022

---------------------- Page: 1 ----------------------
ISO/FDIS 535:2022(E)
FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 535
ISO/TC 6/SC 2
Paper and board — Determination of
Secretariat: SIS
water absorptiveness — Cobb method
Voting begins on:
Papier et carton — Détermination de la capacité d'absorption d'eau
— Méthode de Cobb
Voting terminates on:
COPYRIGHT PROTECTED DOCUMENT
© ISO 2022
ISO/CEN PARALLEL PROCESSING
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
RECIPIENTS OF THIS DRAFT ARE INVITED TO
ISO copyright office
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
CP 401 • Ch. de Blandonnet 8
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
CH-1214 Vernier, Geneva
DOCUMENTATION.
Phone: [phone]
IN ADDITION TO THEIR EVALUATION AS
Reference number
Email: [e-mail]
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO­
ISO/FDIS 535:2022(E)
Website: www.iso.org
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
Published in Switzerland
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN­
DARDS TO WHICH REFERENCE MAY BE MADE IN
ii
  © ISO 2022 – All rights reserved
NATIONAL REGULATIONS. © ISO 2022

---------------------- Page: 2 ----------------------
ISO/FDIS 535:2022(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Reagents and materials . 2
6 Apparatus . 2
7 Sampling . 3
8 Conditioning . 3
9 Preparation of test pieces .3
10 Procedure .3
10.1 General . 3
10.2 Mounting of the test pieces . . 3
10.3 Exposure to water and blotting . 3
10.4 Times of test . 5
10.5 Rejection of test pieces . 5
11 Expression of results . 5
12 Precision . 6
13 Test report . 6
Annex A (informative) Precision . 7
Annex B (informative) Suitable blotting paper . 9
Bibliography .10
iii
© ISO 2022 – All rights reserved

---------------------- Page: 3 ----------------------
ISO/FDIS 535:2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non­governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 6, Paper, board and pulps, Subcommittee
SC 2, Test methods and quality specifications for paper and board, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 172, Pulp, paper and board, in
accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This fourth edition cancels and replaces the third edition (ISO 535:2014), which has been technically
revised.
The main changes are as follows:
— requirements in 5.1 and 5.2 added;
— Clause 6 and 6.2 revised;
— preparation of test pieces added in Clause 9;
— Subclauses 10.3 and 10.4 revised and requirements added;
— several additional explanations added in 10.5;
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
  © ISO 2022 – All rights reserved

---------------------- Page: 4 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 535:2022(E)
Paper and board — Determination of water absorptiveness
— Cobb method
1 Scope
This document specifies a method for determining the water absorptiveness of paper and board,
including corrugated fibreboard, under standard conditions.
2
This document is not applicable for paper of grammage less than 50 g/m or embossed paper. It is not
applicable for porous papers such as newsprint or papers such as blotting paper or other papers having
a relatively high-water absorptiveness for which ISO 8787 is more suitable.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 186, Paper and board — Sampling to determine average quality
ISO 187, Paper, board and pulps — Standard atmosphere for conditioning and testing and procedure for
monitoring the atmosphere and conditioning of samples
ISO 14487, Pulps — Standard water for physical testing
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
water absorptiveness
Cobb value
2
calculated mass of water absorbed in a specified time by 1 m of paper or board under specified
conditions
2
Note 1 to entry: The test area is normally 100 cm .
4 Principle
A test piece is weighed immediately before and after exposure for a specified time of one surface to
water, followed by blotting. The result of the increase in mass is expressed in grams per square
2
metre (g/m ).
The test piece shall not show any sign of penetration through or leakage outside the test ring (see 10.5).
1
© ISO 2022 – All rights reserved

---------------------- Page: 5 ----------------------
ISO/FDIS 535:2022(E)
5 Reagents and materials
5.1 Water, distilled or deionized, at the laboratory conditioning temperature, i.e. 23 °C ± 1 °C or
27 °C ± 1 °C in tropical countries. The water shall fulfil the requirements of ISO 14487.
2 2
5.2 Blotting paper, having a grammage of 250 g/m ± 25 g/m .
The blotting paper shall have dimensions of at least 140 mm × 140 mm either circular or rectangular.
Blotting papers in accordance with ISO 5269-1 are suitable, see Annex B.
6 Apparatus
6.1 Absorptiveness tester for the determination of water absorptiveness.
Any type of apparatus may be used which permits
— an immediate and uniform contact of the water with the part of the test piece submitted to the test,
— controlled rapid removal of the unabsorbed water from the test piece at the end of the contact
period, and
— the rapid removal of the test piece without the risk of water contacting the test piece outside the test
area.
In its simplest form, the apparatus consists of a rigid base with a smooth, planar surface, and a rigid
2
metal cylinder of 112,8 mm ± 0,2 mm internal diameter (corresponding to a test area of 100 cm ) and
with a means of clamping it firmly to the base plate. The edge of the cylinder in contact with the test
piece shall be flat and machined smooth with a thickness sufficient to prevent the cylinder cutting into
the test piece. The height of the cylinder is not important, provided it is sufficient to contain a water
depth of 10 mm.
For materials where leakage between the cylinder and the upper surface of the test piece can occur
during the test, a soft, elastic, non-absorbent gasket may be interposed to prevent this. This gasket shall
have the same internal diameter as the cylinder after clamping.
If a gasket is used, it shall be used for all test pieces.
The diameter of the compressed gasket can be tested as follows: mount a piece of carbonless paper
which has roughly the same dimensions as the test piece, into the absorptiveness tester, and close
the cylinder as for the test. If the pressure is not high enough for an adequate impression, use a usual
test piece and the carbonless paper to increase the thickness of the arrangement. In some cases, a
compressible, blotter­like paper or other papers can be more suitable to test the diameter of the gasket.
To prevent damage to the machined edge of the cylinder caused by clamping it upside down it is
recommended to mark the top in some way so that it can be identified readily. If a cylinder of a small
2
area is used it should not be less than 50 cm . The water depth shall still be 10 mm.
When testing corrugated fibreboard, it is recommended to use an apparatus with adjustable pressure
to adjust the cylinder according to the structural conditions of the test piece.
6.2 Metal roller, with a smooth face, 200 mm ± 10 mm wide, a diameter of 90 mm ± 10 mm and a
mass of 10 kg ± 0,5 kg.
6.3 Balance, which can be read to the nearest 1 mg.
6.4 Timer, readi
...

PROJET
NORME ISO/FDIS
FINAL
INTERNATIONALE 535
ISO/TC 6/SC 2
Papier et carton — Détermination
Secrétariat: SIS
de la capacité d'absorption d'eau —
Début de vote:
2022-11-17 Méthode de Cobb
Vote clos le:
Paper and board — Determination of water absorptiveness — Cobb
2023-01-12
method
TRAITEMENT PARALLÈLE ISO/CEN
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/FDIS 535:2022(F)
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
TION NATIONALE. © ISO 2022

---------------------- Page: 1 ----------------------
ISO/FDIS 535:2022(F)
FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 535
ISO/TC 6/SC 2
Paper and board — Determination of
Secretariat: SIS
water absorptiveness — Cobb method
Voting begins on:
2022-11-17
Papier et carton — Détermination de la capacité d'absorption d'eau
— Méthode de Cobb
Voting terminates on:
2023-01-12
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2022
ISO/CEN PARALLEL PROCESSING
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
RECIPIENTS OF THIS DRAFT ARE INVITED TO
ISO copyright office
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
Case postale 401 • Ch. de Blandonnet 8
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
CH-1214 Vernier, Genève
DOCUMENTATION.
Tél.: [phone]
IN ADDITION TO THEIR EVALUATION AS
Reference number
E-mail: [e-mail]
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 535:2022(E)
Web: www.iso.org
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
Publié en Suisse
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
ii
  © ISO 2022 – Tous droits réservés
NATIONAL REGULATIONS. © ISO 2022

---------------------- Page: 2 ----------------------
ISO/FDIS 535:2022(E)
Contents Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives .1
3 Termes et définitions . 1
4 Principe. 1
5 Réactifs et matériaux . 2
6 Appareillage . 2
7 Échantillonnage .3
8 Conditionnement .3
9 Préparation des éprouvettes . 3
10 Mode opératoire . 3
10.1 Généralités . 3
10.2 Mise en place des éprouvettes . 3
10.3 Exposition à l’eau et essuyage . 3
10.4 Durées d’essai . 5
10.5 Rejet des éprouvettes . 5
11 Expression des résultats . 6
12 Fidélité . 6
13 Rapport d’essai . 6
Annexe A (informative) Fidélité .8
Annexe B (informative) Papier buvard adapté .10
Bibliographie .11
iii
© ISO 2022 – All rights reserved

---------------------- Page: 3 ----------------------
ISO/FDIS 535:2022(E)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l'intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l'Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant : www.iso.org/iso/fr/avant-propos.html.
Le présent document a été élaboré par le comité technique ISO/TC 6, Papiers, cartons et pâtes,
sous-comité SC 2, Méthodes d’essais et spécifications de qualité des papiers et cartons, en collaboration avec
le comité technique CEN/TC 172, Pâtes, papier et carton, du Comité européen de normalisation (CEN),
conformément à l'Accord de coopération technique entre l'ISO et le CEN (Accord de Vienne).
Cette quatrième édition annule et remplace la troisième édition (ISO 535:2014), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes :
— ajout d’exigences aux paragraphes 5.1 et 5.2 ;
révision de l’Article 6 et du paragraphe 6.2 ;
— ajout d’informations sur la préparation des éprouvettes à l’Article 9 ;
— révision des paragraphes 10.3 et 10.4 et ajout d’exigences dans ceux-ci ;
— ajout de nombreuses explications supplémentaires dans le paragraphe 10.5.
Il convient que l'utilisateur adresse tout retour d'information ou toute question concernant le présent
document à l'organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/members.html.
iv
  © ISO 2022 – All rights reserved

---------------------- Page: 4 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 535:2022(E)
Paper and board — Determination of water absorptiveness
— Cobb method
1 Domaine d’application
Le présent document spécifie une méthode de détermination de la capacité d’absorption d’eau du papier
et du carton, y compris du carton ondulé, dans des conditions normalisées.
Le présent document ne s’applique pas aux types de papiers suivants : papier de grammage inférieur
2
à 50 g/m , papier gaufré, papiers poreux tels que le papier journal, papiers tels que le papier buvard
ou d’autres papiers ayant une capacité d’absorption d’eau relativement élevée, l’ISO 8787 étant mieux
adaptée dans ces cas.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l'édition citée s'applique.
Pour les références non datées, la dernière édition du document de référence s'applique (y compris les
éventuels amendements).
ISO 186, Paper and board — Sampling to determine average quality
ISO 187, Paper, board and pulps — Standard atmosphere for conditioning and testing and procedure for
monitoring the atmosphere and conditioning of samples
ISO 14487, Pulps — Standard water for physical testing
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L'ISO et l'IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes :
— ISO Online browsing platform : disponible à l'adresse https:// www .iso .org/ obp
— IEC Electropedia : disponible à l'adresse https:// www .electropedia .org/
3.1
capacité d’absorption de l’eau
indice de Cobb
résultat du calcul de la masse d’eau absorbée par mètre carré de papier ou de carton, pendant un temps
défini et dans des conditions spécifiées
2
Note 1 to entry: D’ordinaire, la zone d’essai mesure 100 cm .
4 Principe
Une éprouvette est pesée immédiatement avant et immédiatement après exposition à l’eau d’une de
ses faces pendant un temps défini, suivi d’un essuyage. Le résultat de l’accroissement de la masse est
2
exprimé en grammes par mètre carré (g/m ).
L’éprouvette ne doit présenter aucun signe de transpercement ou de fuite à l’extérieur du cylindre
(voir 10.5).
1
© ISO 2022 – All rights reserved

---------------------- Page: 5 ----------------------
ISO/FDIS 535:2022(E)
5 Réactifs et matériaux
5.1 Eau distillée ou déionisée, à la température de conditionnement du laboratoire, c’est-à-dire
(23 ± 1) °C, ou (27 ± 1) °C dans les pays tropicaux. L’eau doit respecter les exigences de l’ISO 14487.
2
5.2 Papier buvard, de grammage égal à (250 ± 25) g/m .
Le papier buvard doit être de forme circulaire ou rectangulaire et mesurer au moins 140 mm × 140 mm.
Les papiers buvards conformes à l’ISO 5269-1 sont adaptés (voir l’Annexe B).
6 Appareillage
6.1 Appareil d’essai de capacité d’absorption pour déterminer la capacité d’absorption de l’eau.
Tout type d’appareil permettant d’effectuer les actions suivantes peut être utilisé :
— la mise en contact immédiate et uniforme de l’eau avec la partie de l’éprouvette soumise à essai ;
— le retrait rapide et contrôlé de l’eau non absorbée par l’éprouvette à la fin de la période de mise en
contact ;
— le retrait rapide de l’éprouvette sans qu’il existe un risque de contact de l’eau avec une surface
extérieure à la surface d’essai.
Sous sa forme la plus simple, l’appareil se compose d’une embase rigide à surface lisse et plane et d’un
cylindre métallique rigide de diamètre intérieur égal à (112,8 ± 0,2) mm (correspondant à une surface
2
d’essai d’environ 100 cm ), muni d’un dispositif permettant de le fixer solidement à l’embase. Le bord du
cylindre qui vient au contact de l’éprouvette doit être plat et poli par usinage, et posséder une épaisseur
suffisante pour ne pas entailler l’éprouvette. La hauteur du cylindre importe peu pourvu qu’il puisse
contenir une hauteur d’eau de 10 mm.
Si des fuites sont susceptibles de se produire en cours d’essai entre le cylindre et la face supérieure de
l’éprouvette en raison du matériau utilisé, celles-ci peuvent être évitées par l’interposition d’un joint
mou, élastique et non absorbant. Ce joint doit avoir le même diamètre intérieur que celui du cylindre
après fixation.
Si un joint est utilisé, il doit l’être pour toutes les éprouvettes.
Le diamètre du joint comprimé peut être soumis à essai comme suit : mettre en place, sur l’appareil
d’essai de capacité d’absorption, un morceau de papier autocopiant de dimensions approximativement
identiques à celles de l’éprouvette et fermer le cylindre comme pour l’essai. Si la pression n’est pas
assez élevée pour que l’impression soit suffisante, utiliser une éprouvette habituelle en plus du papier
autocopiant afin d’augmenter l’épaisseur de l’ensemble. Dans certains cas, un papier de type buvard
compressible ou d’autres papiers peuvent se révéler plus adaptés pour soumettre à essai le diamètre du
joint.
Pour éviter d’endommager le bord usiné du cylindre si ce dernier est fixé à l’envers, il est conseillé
de marquer la face supérieure du cylindre de façon à pouvoir l’identifier facilement. Si un cylindre de
2
section réduite est utilisé, il convient que celle-ci ne soit pas inférieure à 50 cm . La hauteur d’eau doit
toujours être de 10 mm.
Si du carton ondulé est utilisé, il est recommandé d’utiliser un appareil dont la pression est réglable afin
d’adapter le cylindre aux conditions structurelles de l’éprouvette.
6.2 Rouleau métallique, présentant une face polie, d’une largeur de (200 ± 10) mm, d’un diamètre de
(90 ± 10) mm et d’une masse de (10 ± 0,5) kg.
2
  © ISO 2022 – All rights reserved

---------------------- Page: 6 ----------------------
ISO/FDIS 535:2022(E)
6.3 Balance, pouvant indiquer une masse à 1 mg près.
6.4 Chronomètre, permettant la lecture en secondes d’une durée d’au moins 30 min.
6.5 Éprouvette graduée, ou autre moyen permettant de mesurer des aliquote
...