ISO 1875:1982

Plastics - Plasticized cellulose acetate - Determination of matter extractable by diethyl ether

The determination method applies to plasticized cellulose acetate in any form, such as moulding material, sheet, manufactured articles. Conversion of the plastizised sample to a film, prepared by dissolving and casting, and subsequent extraction by ethylether in a Soxhlet apparatus. Removal of the ether by heating under vacuum and weighing the residual matter.

Plastiques — Acétate de cellulose plastifié — Détermination des matières extractibles par l'oxyde diéthylique

Polimerni materiali - Mehčani acetat celuloze - Določanje izlužljivega z dietiletrom

General Information

• Status: Published
• Publication Date: 31-Jan-1982
• ICS: 83.080.20 - Thermoplastic materials
• Technical Committee: ISO/TC 61/SC 9 - Thermoplastic materials
• Drafting Committee: ISO/TC 61/SC 9 - Thermoplastic materials
• Current Stage: 9093 - International Standard confirmed
• Start Date: 07-Oct-2024
• Completion Date: 13-Dec-2025
• Ref Project: SIST ISO 1875:1996 - Plastics -- Plasticized cellulose acetate -- Determination of matter extractable by diethyl ether

Overview

ISO 1875:1982 specifies a laboratory method for the determination of the percentage of matter extractable by diethyl ether from plasticized cellulose acetate. The method applies to samples in any form (moulding material, sheet, manufactured articles). The procedure converts the plasticized sample to a cast film, extracts soluble matter in a Soxhlet apparatus using diethyl ether, removes the solvent by heating under vacuum and determines the mass of the residual extract. Note: the extract consists principally of the plasticizer.

Key Topics

• Scope and applicability: method applicable to plasticized cellulose acetate in any physical form.
• Reagents and solvents: use analytical-grade solvents. For film preparation a 90:10 (v/v) mixture of dichloromethane and methanol is specified for dissolution. Diethyl ether used for extraction must be free of peroxides.
• Sample preparation: typically 10 ±0.2 g of sample is dissolved in 100 ±2 ml of the dichloromethane/methanol mixture and cast to produce a film of about 0.1 mm thickness on a glass plate (~200 mm × 400 mm, 4 mm thick). After solvent evaporation the film is cut into strips for extraction.
• Extraction apparatus and conditions: a Soxhlet extractor with a 250 ml flask and suitable cartridge is used. Around 2 g of prepared film is placed in the cartridge and extracted with approximately 200 ml diethyl ether. Extraction is carried out for 3 hours on a water bath.
• Drying and weighing: remove most ether by aspiration, then dry the extract-containing flask in a vacuum oven at 50 ±2 °C for 2 hours, cool in a desiccator and weigh to 0.001 g. The cartridge is dried 30 minutes at 50 ±2 °C under vacuum, then 3 hours at 105 ±2 °C, cooled and weighed.
• Modes A and B: the standard defines alternative preparatory modes (freshly prepared sample versus pre-dried sample); results are reported accordingly.
• Reporting and calculation: extractable matter is reported as mass percent. The final reported value is the arithmetic mean of two determinations. The test record should include standard reference, full product identification, percentage extractables, and mode used.

Applications

• Quality control: routine assessment of plasticizer content and extractables in raw materials and finished articles.
• Material safety and compliance: verification of leachable components relevant to product safety, regulatory compliance and formulation stability.
• Development and acceptance testing: comparative testing during formulation trials or batch acceptance where extractable content is a critical parameter.

Related Standards

• Complementary ISO methods on plastics testing, laboratory glassware and solvent purity should be consulted for equipment and reagent specifications.
• Cross-reference other ISO tests for comprehensive characterization of plasticized cellulose acetate when broader mechanical or chemical property data are required.

Keywords: ISO 1875:1982, plasticized cellulose acetate, diethyl ether extractables, Soxhlet extraction, quality control, material testing.

Standards Content (Sample)

SLOVENSKI STANDARD
01-junij-1996
3ROLPHUQLPDWHULDOL0HKþDQLDFHWDWFHOXOR]H'RORþDQMHL]OXåOMLYHJD]GLHWLOHWURP
Plastics -- Plasticized cellulose acetate -- Determination of matter extractable by diethyl
ether
Plastiques -- Acétate de cellulose plastifié -- Détermination des matières extractibles par
l'oxyde diéthylique
Ta slovenski standard je istoveten z: ISO 1875:1982
ICS:
83.080.20 Plastomeri Thermoplastic materials
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

International Standard
INTERNATIONAL ORGANIZATION FOR STANDARDlZATION.MEIK,QYHAPO~HAR OPrAHM3ALWlR fl0 CTAH~APTbl3AlJMbWORGANISATION INTERNATIONALE DE NORMALISATION
Plastics - Plasticized cellulose acetate - Determination
of matter extractable by diethyl ether
Determination des ma tieres extrac tibles par /‘Oxyde die th ylique
Plas tiques - Acetate de celhlose plastifi6 -
First edition - 1982-02-15
UDC 678.544 Ref. No. ISO 18754982 (E)
w
-
Descriptors : plastics, plastified cellulose acetate, tests, determination, soluble matter, ethyl ether.
i#
Price based on 3 pages
M.l (Pl-Ie hternational organization for Standardization) OS a wddwide federatisn of
national standards institutes WO member bedies). The work of developing Qnter-
national Standards is carried out through ISO technical committees. Every member
bsdy ireterested in a subject for which a technical committee has been set up has the
right to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with BSO, also take part in the werk.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approvai bedore their acceptance as International Standards by
the ISO Council.
International Standard ISO 1875 was develsped by Technical Csmmittee %SO/TC 61,
Plas tics .
It was submitted directiy to the SS0 Councii, in accordance witk clause 5.10.1 of part 1
sf the Directives for the technical werk of $SO. lt cancels and replaces ISO Recommen-
dation R 1875EU1 I which had been approved by the member bedies sf the follswing
countries :
Austria Greece Spain
Belgium Hungary Swede8-n
Canada Italy Switzerland
Chile Netherlands 7% rkey
Czechsslovakia New Zealand United Klingdorn
Qohnd
Egypt, As-ab Rep. od USA
France Womania ussw
South Africa, Rep. sf
Ns member body had expressed disapproval of the document.
Printed in Seitzerland
INTERNATIONALSTANDARD ISO 1875-1982 (E)
Plastics - Plasticized cellulose acetate - Determination
of matter extractable by diethyl ether
4.2 Flat rectangular glass sheet, 4 mm in thickness and
1 Scope and field of application
about 200 mm x 400 mm.
This International Standard specifies a method for the deter-
mination of the percentage of matter which tan be extracted by
4.3 Film casting device to lay a cast film of about 0,l mm
diethyl ether from plasticized cellulose acetate.
thickness. A suitable type of device is shown in the figure.
The method applies to plasticized cellulose acetate in any form,
4.4 Soxhlet extraction apparatus, comprising the follow-
such as moulding material, sheet, manufactured articles, etc.
ing items :
NOTE - The extractable matter comprises principally the plasticizer.
4.4.1 Extraction flask, of capacity 250 ml.
2 Principle
4.4.2 Condenser.
Conversion of plasticized cellulose acetate to film by dissolving
4.5 Thimble for Soxhlet extractor.
and casting, then extraction by diethyl ether in a Soxhlet ap-
paratus. Removal of the ether by heating under vacuum, then
weighing of the residual matter.
4.6 Thermostatic oven, capable of being maintained at
50 - + 2 OC and at 105 + 2 OC.
3 Reagents
4.7 Vacuum thermostatic oven, capable of being main-
tained at 50 -+ 2 OC.
During the analysis use only reagents of recognized analytical
grade.
4.8 Desiccator, containing dry silica gel.
3.1 Dichloromethane, with relative densi
...

International Standard
INTERNATIONAL ORGANIZATION FOR STANDARDlZATION.MEIK,QYHAPO~HAR OPrAHM3ALWlR fl0 CTAH~APTbl3AlJMbWORGANISATION INTERNATIONALE DE NORMALISATION
Plastics - Plasticized cellulose acetate - Determination
of matter extractable by diethyl ether
Determination des ma tieres extrac tibles par /‘Oxyde die th ylique
Plas tiques - Acetate de celhlose plastifi6 -
First edition - 1982-02-15
UDC 678.544 Ref. No. ISO 18754982 (E)
w
-
Descriptors : plastics, plastified cellulose acetate, tests, determination, soluble matter, ethyl ether.
i#
Price based on 3 pages
M.l (Pl-Ie hternational organization for Standardization) OS a wddwide federatisn of
national standards institutes WO member bedies). The work of developing Qnter-
national Standards is carried out through ISO technical committees. Every member
bsdy ireterested in a subject for which a technical committee has been set up has the
right to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with BSO, also take part in the werk.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approvai bedore their acceptance as International Standards by
the ISO Council.
International Standard ISO 1875 was develsped by Technical Csmmittee %SO/TC 61,
Plas tics .
It was submitted directiy to the SS0 Councii, in accordance witk clause 5.10.1 of part 1
sf the Directives for the technical werk of $SO. lt cancels and replaces ISO Recommen-
dation R 1875EU1 I which had been approved by the member bedies sf the follswing
countries :
Austria Greece Spain
Belgium Hungary Swede8-n
Canada Italy Switzerland
Chile Netherlands 7% rkey
Czechsslovakia New Zealand United Klingdorn
Qohnd
Egypt, As-ab Rep. od USA
France Womania ussw
South Africa, Rep. sf
Ns member body had expressed disapproval of the document.
Printed in Seitzerland
INTERNATIONALSTANDARD ISO 1875-1982 (E)
Plastics - Plasticized cellulose acetate - Determination
of matter extractable by diethyl ether
4.2 Flat rectangular glass sheet, 4 mm in thickness and
1 Scope and field of application
about 200 mm x 400 mm.
This International Standard specifies a method for the deter-
mination of the percentage of matter which tan be extracted by
4.3 Film casting device to lay a cast film of about 0,l mm
diethyl ether from plasticized cellulose acetate.
thickness. A suitable type of device is shown in the figure.
The method applies to plasticized cellulose acetate in any form,
4.4 Soxhlet extraction apparatus, comprising the follow-
such as moulding material, sheet, manufactured articles, etc.
ing items :
NOTE - The extractable matter comprises principally the plasticizer.
4.4.1 Extraction flask, of capacity 250 ml.
2 Principle
4.4.2 Condenser.
Conversion of plasticized cellulose acetate to film by dissolving
4.5 Thimble for Soxhlet extractor.
and casting, then extraction by diethyl ether in a Soxhlet ap-
paratus. Removal of the ether by heating under vacuum, then
weighing of the residual matter.
4.6 Thermostatic oven, capable of being maintained at
50 - + 2 OC and at 105 + 2 OC.
3 Reagents
4.7 Vacuum thermostatic oven, capable of being main-
tained at 50 -+ 2 OC.
During the analysis use only reagents of recognized analytical
grade.
4.8 Desiccator, containing dry silica gel.
3.1 Dichloromethane, with relative density (20 OC/20 “C)
from 1,321 to 1,331, and not less than 95 % ( V/ v) distilling
4.9 Balance, accurate to 0,001 g.
between 39 and 40,5 OC under a pressure of 101,3 kPa*.
4.10 Shaking device to hold the glass bottle (4.1).
3.2 Methanol, with relative density (20 OC/20 OC) from
0,792 to 0,795 and distillation range from 64,5 to 65,5 OC under
a pressure of 101,3 kPa*.
5 Preparation of test Sample
3.3 Diethly ether, free from Peroxides, with relative density
5.1 Prepare
...

Norme internationale
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION.ME~YHAPO~HAR OPl-AHM3AlJ4R Il0 CTAH~APTl43AW’WORGANISATlON INTERNATIONALE DE NORMALISATION
Acétate de cellulose plastifié -
Plastiques -
Détermination des matières extractibles par l’oxyde
diéthylique
Plastics - P/as ticlied cellulose ace ta te - Determination of matter extractable by diethyl ether
Première édition - 1982-02-15
CDU 678.544 Réf. no : ISO 18754982 (BD)
Descripteurs : matière plastique, acétate de cellulose plastifié, essai, détermination, produit en solution, éther éthylique.
Prix basé sur 3 pages
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est confiée aux comités techniques de I’ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I’ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO.
La Norme internationale ISO 1875 a été élaborée par le comité technique ISO/TC 61,
Plastiques.
Elle fut soumise directement au Conseil de I’ISO, conformément au paragraphe 510.1
de la partie 1 des Directives pour les travaux techniques de I’ISO. Elle annule et rem-
place la Recommandation ISO/R 18751971, qui avait été approuvée par les comités
membres des pays suivants :
Afrique du Sud, Rép. d’ France Royaume-Uni
Allemagne, R. F. Grece Suède
Autriche
Hongrie Suisse
Belgique Italie Tchécoslovaquie
Canada Nouvelle-Zelande
Turquie
Chili Pays-Bas URSS
Egypte, Rép. arabe d’ Pologne
USA
Espagne Roumanie
Aucun comite membre ne l’avait désapprouvée.
@ Organisation internationale de normalisation, 1982 0
Imprimé en Suisse
NORME INTERNATIONALE ISO 1875-1982 (F)
Plastiques - Acétate de cellulose plastifié -
Détermination des matières extractibles par l’oxyde
diéthylique
4.2 Plaque de verre, rectangulaire, de 4 mm d’épaisseur et
1 Objet et domaine d’application
d’environ 200 mm x 400 mm.
La présente Norme internationale spécifie une méthode de
détermination du pourcentage de matières extractibles par
4.3 Dispositif pour couler une feuille d’environ 0,l mm
l’oxyde diéthylique dans l’acétate de cellulose plastifié.
d’épaisseur. Un type convenable de dispositif est représenté à
la figure.
La methode est applicable aux acétates de cellulose plastifiés se
présentant sous n’importe quelle forme, telle que matières
4.4 Extracteur de Soxhlet, comprenant, entre autres, les
moulées, plaques, produits manufacturés, etc.
éléments suivants :
NOTE - L’extrait est constitué principalement par le plastifiant.
4.4.1 Ballon, de 250 ml de capacité.
2 Principe
4.4.2 Réfrigérant.
Transformation de l’acétate de cellulose en une feuille coulée
par dissolution, suivie d’une extraction par l’oxyde diéthylique
Cartouche pour extracteur de Soxhlet.
dans un extracteur de Soxhlet. Élimination de l’oxyde diéthyli-
que par chauffage sous vide, et pesée du résidu.
4.6 Étuve, réglable à 50 & 2 OC et à 105 & 2 OC.
3 Réactifs
4.7 Étuve à vide, réglable à 50 + 2 OC.
Au cours de l’analyse, utiliser uniquement des réactifs de qua-
Iite analytique reconnue.
4.8 Dessiccateur, garni de gel de silice.
3.1 Dichlorométhane, ayant une densite relative
4.9 Balance, précise à 0,001 g.
(20 OC/20 OC) comprise entre 1,321 et 1,331, et dont au moins
95 % ( V/ v) distillent entre 39 et 4O,5 OC sous une pression de
101,3 kPa*.
4.10 Dispositif d’agitation, sur lequel peut être fixé le fla-
con (4.1).
3.2 MethanoI, ayant une densité relative (20 OC/20 OC)
comprise entre 0,792 et 0,795, et un intervalle de distillation
compris entre 64,5 et 65,5 OC sous une pression de 101,3 kPa*.
5 Préparation de l’échantillon pour essai
3.3 Oxyde diéthylique, exempt de peroxydes, ayant une
5.1 Préparer un mélange à 90 parties de dichlorométhane
densite relative (20 OC/20 OC) comprise entre 0,714 et 0,716, et
(3.1) et 10 parties de méthanol (3.21, en volume, à la tem
...

Norme internationale
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION.ME~YHAPO~HAR OPl-AHM3AlJ4R Il0 CTAH~APTl43AW’WORGANISATlON INTERNATIONALE DE NORMALISATION
Acétate de cellulose plastifié -
Plastiques -
Détermination des matières extractibles par l’oxyde
diéthylique
Plastics - P/as ticlied cellulose ace ta te - Determination of matter extractable by diethyl ether
Première édition - 1982-02-15
CDU 678.544 Réf. no : ISO 18754982 (BD)
Descripteurs : matière plastique, acétate de cellulose plastifié, essai, détermination, produit en solution, éther éthylique.
Prix basé sur 3 pages
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est confiée aux comités techniques de I’ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I’ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO.
La Norme internationale ISO 1875 a été élaborée par le comité technique ISO/TC 61,
Plastiques.
Elle fut soumise directement au Conseil de I’ISO, conformément au paragraphe 510.1
de la partie 1 des Directives pour les travaux techniques de I’ISO. Elle annule et rem-
place la Recommandation ISO/R 18751971, qui avait été approuvée par les comités
membres des pays suivants :
Afrique du Sud, Rép. d’ France Royaume-Uni
Allemagne, R. F. Grece Suède
Autriche
Hongrie Suisse
Belgique Italie Tchécoslovaquie
Canada Nouvelle-Zelande
Turquie
Chili Pays-Bas URSS
Egypte, Rép. arabe d’ Pologne
USA
Espagne Roumanie
Aucun comite membre ne l’avait désapprouvée.
@ Organisation internationale de normalisation, 1982 0
Imprimé en Suisse
NORME INTERNATIONALE ISO 1875-1982 (F)
Plastiques - Acétate de cellulose plastifié -
Détermination des matières extractibles par l’oxyde
diéthylique
4.2 Plaque de verre, rectangulaire, de 4 mm d’épaisseur et
1 Objet et domaine d’application
d’environ 200 mm x 400 mm.
La présente Norme internationale spécifie une méthode de
détermination du pourcentage de matières extractibles par
4.3 Dispositif pour couler une feuille d’environ 0,l mm
l’oxyde diéthylique dans l’acétate de cellulose plastifié.
d’épaisseur. Un type convenable de dispositif est représenté à
la figure.
La methode est applicable aux acétates de cellulose plastifiés se
présentant sous n’importe quelle forme, telle que matières
4.4 Extracteur de Soxhlet, comprenant, entre autres, les
moulées, plaques, produits manufacturés, etc.
éléments suivants :
NOTE - L’extrait est constitué principalement par le plastifiant.
4.4.1 Ballon, de 250 ml de capacité.
2 Principe
4.4.2 Réfrigérant.
Transformation de l’acétate de cellulose en une feuille coulée
par dissolution, suivie d’une extraction par l’oxyde diéthylique
Cartouche pour extracteur de Soxhlet.
dans un extracteur de Soxhlet. Élimination de l’oxyde diéthyli-
que par chauffage sous vide, et pesée du résidu.
4.6 Étuve, réglable à 50 & 2 OC et à 105 & 2 OC.
3 Réactifs
4.7 Étuve à vide, réglable à 50 + 2 OC.
Au cours de l’analyse, utiliser uniquement des réactifs de qua-
Iite analytique reconnue.
4.8 Dessiccateur, garni de gel de silice.
3.1 Dichlorométhane, ayant une densite relative
4.9 Balance, précise à 0,001 g.
(20 OC/20 OC) comprise entre 1,321 et 1,331, et dont au moins
95 % ( V/ v) distillent entre 39 et 4O,5 OC sous une pression de
101,3 kPa*.
4.10 Dispositif d’agitation, sur lequel peut être fixé le fla-
con (4.1).
3.2 MethanoI, ayant une densité relative (20 OC/20 OC)
comprise entre 0,792 et 0,795, et un intervalle de distillation
compris entre 64,5 et 65,5 OC sous une pression de 101,3 kPa*.
5 Préparation de l’échantillon pour essai
3.3 Oxyde diéthylique, exempt de peroxydes, ayant une
5.1 Préparer un mélange à 90 parties de dichlorométhane
densite relative (20 OC/20 OC) comprise entre 0,714 et 0,716, et
(3.1) et 10 parties de méthanol (3.21, en volume, à la tem
...