ISO/TR 17671-5:2004

Welding — Recommendations for welding of metallic materials — Part 5: Welding of clad steels

ISO/TR 17671-5:2004 gives general recommendations for the welding of clad steels by means of appropriate arc welding processes and electroslag strip cladding. It is generally applicable to all clad steels and is appropriate regardless of the type of fabrication involved, although the application standard may have additional requirements. Non-ferrous claddings, such as titanium, tantalum, zirconium and their alloys are not covered by ISO/TR 17671-5:2004. ISO/TR 17671-5:2004 covers welding of cladding deposits as well as welding of the transition zone(s), when existant, between parent metal and cladding. These transition zones are metal combinations of non-alloyed ferrous parent metal with high alloyed stainless steels, nickel alloys or other non-ferrous metals. The mechanical and physical design of the joints is not covered by ISO/TR 17671-5:2004. Methods of testing and acceptance levels are not included because they depend on the service conditions of the fabrication. The corrosion resistance of the cladding depends on many factors and is not part of ISO/TR 17671:2004.

Soudage — Recommandations pour le soudage des matériaux métalliques — Partie 5: Soudage des aciers plaqués

L'ISO/TR 17671-5:2004 donne des recommandations générales pour le soudage d'aciers plaqués à l'aide de procédés appropriés de soudage à l'arc et de rechargement sous laitier avec électrode en feuillard. L'ISO/TR 17671-5:2004 est applicable en général à tous les aciers plaqués, et il est approprié quel que soit le type de fabrication concerné, bien que la norme d'application puisse comporter des exigences supplémentaires. Les placages en métaux non ferreux tels que le titane, le tantale, le zirconium et leurs alliages ne sont pas couverts par l'ISO/TR 17671-5:2004. L'ISO/TR 17671-5:2004 couvre l'exécution des rechargements par soudage ainsi que le soudage de la (ou des) zone(s) de transition, lorsqu'elles existent, entre le métal support et le placage. Ces zones de transition sont des combinaisons métalliques constituées du métal support ferreux non allié et d'aciers inoxydables fortement alliés, d'alliages de nickel ou d'autres métaux non ferreux. La conception mécanique et physique des assemblages n'est pas couverte par l'ISO/TR 17671-5:2004. Les méthodes de contrôle et d'essai, ainsi que les niveaux d'acceptation ne sont pas décrits, car ils dépendent des conditions de service de la structure. Il convient de rechercher ces détails dans les spécifications de conception. La résistance à la corrosion des placages dépend de plusieurs facteurs et elle ne fait pas partie intégrante de l'ISO/TR 17671-5:2004.

General Information

• Status: Published
• Publication Date: 17-May-2004
• ICS: 25.160.10 - Welding processes
• Technical Committee: ISO/TC 44/SC 10 - Quality management in the field of welding
• Drafting Committee: ISO/TC 44/SC 10 - Quality management in the field of welding
• Current Stage: 9093 - International Standard confirmed
• Completion Date: 25-May-2022

Standards Content (Sample)

TECHNICAL ISO/TR
REPORT 17671-5
First edition
2004-05-15

Welding — Recommendations for
welding of metallic materials —
Part 5:
Welding of clad steels
Soudage — Recommandations pour le soudage des matériaux
métalliques —
Partie 5: Soudage des aciers plaqués




Reference number
ISO/TR 17671-5:2004(E)
©
ISO 2004

---------------------- Page: 1 ----------------------
ISO/TR 17671-5:2004(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
should not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.


©  ISO 2004
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland

ii © ISO 2004 – All rights reserved

---------------------- Page: 2 ----------------------
ISO/TR 17671-5:2004(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
In exceptional circumstances, when a technical committee has collected data of a different kind from that
which is normally published as an International Standard (“state of the art”, for example), it may decide by a
simple majority vote of its participating members to publish a Technical Report. A Technical Report is entirely
informative in nature and does not have to be reviewed until the data it provides are considered to be no
longer valid or useful.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO should not be held responsible for identifying any or all such patent rights.
ISO/TR 17671-5 was prepared by Technical Committee ISO/TC 44, Welding and allied processes,
Subcommittee SC 10, Unification of requirements in the field of metal welding.
ISO/TR 17671 consists of the following parts, under the general title Welding — Recommendations for
welding of metallic materials:
 Part 1: General guidance for arc welding
 Part 2: Arc welding of ferritic steels
 Part 3: Arc welding of stainless steels
 Part 4: Arc welding of aluminium and aluminium alloys
 Part 5: Welding of clad steels
 Part 6: Laser beam welding
 Part 7: Electron beam welding
© ISO 2004 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO/TR 17671-5:2004(E)
Introduction
This Technical Report is based on the European Standard EN 1011-5:2003, Welding — Recommendations
for welding of metallic materials — Part 5: Welding of clad steel.
Requests for official interpretations of any aspect of this Technical Report should be directed to the Secretariat
of ISO/TC 44/SC 10 via your national standards body, a complete listing which can be found at www.iso.org.

iv © ISO 2004 – All rights reserved

---------------------- Page: 4 ----------------------
TECHNICAL REPORT ISO/TR 17671-5:2004(E)

Welding — Recommendations for welding of metallic
materials —
Part 5:
Welding of clad steels
1 Scope
This part of ISO/TR 17671 gives general recommendations for welding of clad steels by means of appropriate
arc welding processes and electroslag strip cladding.
It is generally applicable to all clad steels and is appropriate regardless of the type of fabrication involved,
although the application standard may have additional requirements. Non-ferrous claddings, such as titanium,
tantalum, zirconium and their alloys are not covered by this part of ISO/TR 17671.
Examples for joint preparation are given in ISO 9692-4.
This part of ISO/TR 17671 covers welding of cladding deposits as well as welding of the transition zone(s),
when existing, between parent metal and cladding. These transition zones are metal combinations of non-
alloyed ferrous parent metal with high alloyed stainless steels, nickel alloys or other non-ferrous metals.
The mechanical and physical design of the joints is not covered by this part of ISO/TR 17671. Methods of
testing and acceptance levels are not included because they depend on the service conditions of the
fabrication. These details should be obtained from the design specification. The corrosion resistance of the
cladding depends on many factors and is not part of this part of ISO/TR 17671.
For general guidelines see ISO/TR 17671-1.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 2553, Welded, brazed and soldered joints — Symbolic representation on drawings
ISO 5817, Welding — Fusion-welded joints in steel, nickel, titanium and their alloys (beam welding
excluded) — Quality levels for imperfections
ISO 8249, Welding — Determination of Ferrite Number (FN) in austenitic and duplex ferritic-austenitic Cr-Ni
stainless steel weld metals
ISO 9692-4:2003, Welding and allied processes — Recommendations for joint preparation — Part 4: Clad
steels
ISO 13916, Welding — Guidance on the measurement of preheating temperature, interpass temperature and
preheat maintenance temperature
ISO 14175, Welding consumables — Shielding gases for arc welding and cutting
© ISO 2004 – All rights reserved 1

---------------------- Page: 5 ----------------------
ISO/TR 17671-5:2004(E)
ISO 15607, Specification and qualification of welding procedures for metallic materials — General rules
ISO/TR 15608:2000, Welding — Guidelines for a metallic materials grouping system
ISO 15609-1, Specification and qualification of welding procedures for metallic materials — Welding
procedure specification — Part 1: Arc welding
ISO 15614-1, Specification and qualification of welding procedures for metallic materials — Welding
procedure test — Part 1: Arc and gas welding of steels and arc welding of nickel and nickel alloys
ISO/TR 17671-1, Welding — Recommendations for welding of metallic materials — Part 1: General guidance
for arc welding
ISO/TR 17671-3, Welding — Recommendations for welding of metallic materials — Part 3: Arc welding of
stainless steels
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1
clad steel
combination of two or more dissimilar metals bonded inseparably by different cladding processes
4 Materials
4.1 Clad steels
Clad steels can be produced by several cladding processes such as:
 hot roll cladding;
 explosive welding;
 surfacing by welding;
 combined weld/hot roll cladding.
The inseparable cladding (commonly t W 2 mm wall thickness), which will be in contact with the adjacent
2
medium, is designed to meet requirements such as corrosion resistance, abrasion and/or heat resistance at
different working temperatures.
4.2 Parent metal
The parent metal is a weldable steel, commonly in accordance with those referenced in groups 1 to 6 of
ISO/TR 15608:2000. The parent metal should provide the required strength and toughness to maintain
mechanical integrity.
 Stainless steels (e.g. see EN 10088-1).
 Nickel and nickel alloys.
 Copper and copper alloys.
 Cobalt alloys (stellites).
2 © ISO 2004 – All rights reserved

---------------------- Page: 6 ----------------------
ISO/TR 17671-5:2004(E)
Cladding should be capable of being joined by arc welding processes to the parent metals.
The finished surface conditions of cladding, particularly used in components for the chemical industry, should
guarantee adequate corrosion resistance and other specified characteristics. For information on corrosion
resistance of cladding, see relevant application standards.
5 Welding consumables for cladding deposits
The cladding deposit, including dilution with the cladding, should be compatible with the cladding. Therefore,
consumables should be selected with regard to the parent metal, to the cladding and the particular application.
The consumables should comply with the relevant standards and/or specifications.
Where consumable inserts are used, they should correspond with the relevant filler metal composition.
In some cases, the filler metals used for the buttering may also be used for filling and capping runs, if
appropriate for the application.
The service conditions of a clad steel component, such as working temperature or possible post-weld heat
treatment (PWHT) should be considered when selecting appropriate consumables.
It is necessary to pay attention to the effects of dilution when depositing one layer on another, especially the
first layer on the parent metal. The welding process, the welding conditions and the consumables have a
significant influence on the chemical compositions and the ferrite numbers (FN) of a stainless cladding deposit.
Gains or losses of alloying elements, e.g. the metallurgical reactions between wire/strip and fluxes or gases,
should be taken into account.
If the ferrite number is a requirement in the specification, the methods of measurement in accordance with
ISO 8249, e.g. the magnetic determination with calibrated instruments, should be in accordance wi
...

RAPPORT ISO/TR
TECHNIQUE 17671-5
Première édition
2004-05-15

Soudage — Recommandations pour le
soudage des matériaux métalliques —
Partie 5:
Soudage des aciers plaqués
Welding — Recommendations for welding of metallic materials —
Part 5: Welding of clad steels




Numéro de référence
ISO/TR 17671-5:2004(F)
©
ISO 2004

---------------------- Page: 1 ----------------------
ISO/TR 17671-5:2004(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.


©  ISO 2004
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Publié en Suisse

ii © ISO 2004 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO/TR 17671-5:2004(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
Exceptionnellement, lorsqu'un comité technique a réuni des données de nature différente de celles qui sont
normalement publiées comme Normes internationales (ceci pouvant comprendre des informations sur l'état
de la technique par exemple), il peut décider, à la majorité simple de ses membres, de publier un Rapport
technique. Les Rapports techniques sont de nature purement informative et ne doivent pas nécessairement
être révisés avant que les données fournies ne soient plus jugées valables ou utiles.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO/TR 17671-5 a été élaboré par le comité technique ISO/TC 44, Soudage et techniques connexes,
sous-comité SC 10, Unification des prescriptions dans la technique du soudage des métaux.
L'ISO/TR 17671 comprend les parties suivantes, présentées sous le titre général Soudage —
Recommandations pour le soudage des matériaux métalliques:
 Partie 1: Lignes directrices générales pour le soudage à l'arc
 Partie 2: Soudage à l'arc des aciers ferritiques
 Partie 3: Soudage à l'arc des aciers inoxydables
 Partie 4: Soudage à l'arc de l'aluminium et des alliages d'aluminium
 Partie 5: Soudage des aciers plaqués
 Partie 6: Soudage par faisceau laser
 Partie 7: Soudage par faisceau d'électrons
© ISO 2004 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO/TR 17671-5:2004(F)
Introduction
Le présent Rapport technique est basé sur la Norme européenne EN 1011-5:2003, Soudage —
Recommandations pour le soudage des matériaux métalliques — Partie 5 :Soudage des aciers plaqués.
Il convient de faire parvenir les demandes d'interprétations officielles de l'un quelconque des aspects du
présent Rapport technique au secrétariat de l'ISO/TC 44/SC 10 via le comité membre national, dont une liste
exhaustive peut être trouvée à l'adresse www.iso.org.
iv © ISO 2004 – Tous droits réservés

---------------------- Page: 4 ----------------------
RAPPORT TECHNIQUE ISO/TR 17671-5:2004(F)

Soudage — Recommandations pour le soudage des matériaux
métalliques —
Partie 5:
Soudage des aciers plaqués
1 Domaine d'application
La présente partie de l'ISO/TR 17671 donne des recommandations générales pour le soudage d'aciers
plaqués à l'aide de procédés appropriés de soudage à l'arc et de rechargement sous laitier avec électrode en
feuillard.
Elle est applicable en général à tous les aciers plaqués, et elle est appropriée quel que soit le type de
fabrication concerné, bien que la norme d'application puisse comporter des exigences supplémentaires. Les
placages en métaux non ferreux, tels que le titane, le tantale, le zirconium et leurs alliages, ne sont pas
couverts par la présente partie de l'ISO/TR 17671.
Des exemples de préparations de joints sont présentés dans l'ISO 9692-4.
La présente partie de l'ISO/TR 17671 couvre l'exécution des rechargements par soudage ainsi que le
soudage de la (ou des) zone(s) de transition, lorsqu'elles existent, entre le métal support et le placage. Ces
zones de transition sont des combinaisons métalliques constituées du métal support ferreux non allié et
d'aciers inoxydables fortement alliés, d'alliages de nickel, ou d'autres métaux non ferreux.
La conception mécanique et physique des assemblages n'est pas couverte par la présente partie de
l'ISO/TR 17671. Les méthodes de contrôle et d'essai, ainsi que les niveaux d'acceptation, ne sont pas décrits,
car ils dépendent des conditions de service de la structure. Il convient de rechercher ces détails dans les
spécifications de conception.
Pour des lignes directrices générales, voir l'ISO/TR 17671-1. La résistance à la corrosion des placages
dépend de plusieurs facteurs et elle ne fait pas partie intégrante de la présente partie de l’ISO/TR 17671.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 2553, Joints soudés et brasés — Représentations symboliques sur les dessins
ISO 5817, Soudage — Assemblages en acier, nickel, titane et leurs alliages soudés par fusion (soudage par
faisceau exclu) — Niveaux de qualité par rapport aux défauts
ISO 8249, Soudage — Détermination de l'Indice de Ferrite (FN) dans le métal fondu en acier inoxydable
austénitique et duplex ferritique-austénitique au chrome-nickel
ISO 9692-4:2003, Soudage et techniques connexes — Recommandations pour la préparation de joints —
Partie 4: Aciers plaqués
© ISO 2004 – Tous droits réservés 1

---------------------- Page: 5 ----------------------
ISO/TR 17671-5:2004(F)
ISO 13916, Soudage — Lignes directrices pour le mesurage de la température de préchauffage, de la
température entre passes et de la température de maintien du préchauffage
ISO 14175, Produits consommables pour le soudage — Gaz de protection pour le soudage et le coupage à
l'arc
ISO 15607, Descriptif et qualification d'un mode opératoire de soudage pour les matériaux métalliques —
Règles générales
ISO/TR 15608:2000, Soudage — Lignes directrices pour un système de groupement des matériaux
métalliques
ISO 15609-1, Descriptif et qualification d'un mode opératoire de soudage pour les matériaux métalliques —
Descriptif d'un mode opératoire de soudage — Partie 1: Soudage à l'arc
ISO 15614-1, Descriptif et qualification d'un mode opératoire de soudage pour les matériaux métalliques —
Épreuve de qualification d'un mode opératoire de soudage — Partie 1: Soudage à l'arc et aux gaz des aciers
et soudage à l'arc des nickels et alliages de nickel
ISO/TR 17671-1, Soudage — Recommandations pour le soudage des matériaux métalliques — Partie 1:
Lignes directrices générales pour le soudage à l'arc
ISO/TR 17671-3, Soudage — Recommandations pour le soudage des matériaux métalliques — Partie 3:
Soudage à l'arc des aciers inoxydables
3 Termes et définitions
Pour les besoins du présent document, le terme et la définition suivants s'appliquent.
3.1
acier plaqué
combinaison de deux ou de plusieurs métaux dissemblables, assemblés de façon permanente à l'aide de
différents procédés de placage
4 Matériaux
4.1 Aciers plaqués
Les aciers plaqués peuvent être produits à l'aide de plusieurs procédés de placage tels que:
 placage par laminage à chaud;
 placage par explosion;
 revêtement par soudage;
 procédé combiné soudage/laminage à chaud.
Le métal rapporté (en général t W 2 mm d'épaisseur), qui sera en contact avec le milieu actif, est choisi pour
2
satisfaire aux exigences telles que la résistance à la corrosion, à l'abrasion et/ou à la chaleur, à différentes
températures de service.
2 © ISO 2004 – Tous droits réservés

---------------------- Page: 6 ----------------------
ISO/TR 17671-5:2004(F)
4.2 Métal support
Le métal support est un acier soudable, en général selon l'ISO/TR 15608:2000 (groupes 1 à 6). Il convient
que le métal support assure la résistance mécanique et la ténacité exigées pour préserver l'intégrité
mécanique.
 Acier inoxydable (par exemple selon l'EN 10088-1).
 Nickel et alliages de nickel.
 Cuivre et alliages de cuivre.
 Alliages de cobalt (stellites).
Il convient que le placage puisse pouvoir être soudé au métal support à l'aide des procédés de soudage à
l'arc.
Il convient que la finition de surface des placages réalisés en particulier sur des composants destinés à
l'industrie chimique garantisse une résistance à la corrosion adéquate ou toutes autres propriétés spécifiées.
Pour obtenir des informations sur la résistance à la corrosion des placages, consulter les normes d'application
correspondantes.
5 Produits consommables pour le revêtement par soudage
Il convient que le métal de revêtement déposé, compte tenu de la dilution avec le revêtement (initial), soit
compatible avec celui-ci. Il convient donc de choisir les produits consommables en fonction du métal support,
du revêtement et de l'application concernée. Il est recommandé que les produits consommables soient
conformes aux normes et/ou aux spécifications applicables.
Si des inserts fusibles sont utilisés, il convient qu'ils soient compatibles avec la composition chimique du métal
d'apport.
Dans certains cas, les métaux d'apport utilisés pour la réalisation de beurrage peuvent également être utilisés
pour les passes de remplissage et terminales, dans la mesure où ils conviennent à l'application.
Il est recommandé que les conditions de service d'un composant en acier plaqué, comme la température de
service ou un éventuel traitement thermique après soudage (TTAS), soient considérées lors du choix des
produits consommables.
Il est nécessaire de faire attention aux effets de dilution lorsqu'une couche est déposée sur une autre,
spécialement la première couche sur le métal support. Le procédé de soudage, les conditions de soudage et
les produits consommables influent fortement sur la composition chimique et les indices de ferrite (FN) des
placages en acier inoxydable. Il convient de prendre en considération les gains ou pertes en éléments
d'alliage, par exemple les réactions métallurgiques entre le fil-électrode ou l'électrode en feuillard et les flux ou
les gaz.
Si l'indice de ferrite représente une exigence de la spécification, il convient que les méthodes de mesure
selon l'ISO 8249, par exemple la détermination magnétique à l'aide d'instruments étalonnés, soient conformes
à la spécification de conception. En cas de litige, il convient d'utiliser le diagramme de constitution WRC-92.
6 Modes opératoires de soudage
Différents procédés de soudage à l'arc peuvent être utilisés pour réaliser des revê
...