Plastics -- Polytetrafluoroethylene (PTFE) semi-finished products

Plastiques -- Semi-produits en polytétrafluoroéthylène (PTFE)

General Information

Status
Published
Current Stage
5020 - FDIS ballot initiated: 2 months. Proof sent to secretariat
Start Date
19-May-2021
Completion Date
19-May-2021
Ref Project

RELATIONS

Buy Standard

Draft
ISO/FDIS 13000-2 - Plastics -- Polytetrafluoroethylene (PTFE) semi-finished products
English language
10 pages
sale 15% off
Preview
sale 15% off
Preview
Draft
ISO/FDIS 13000-2:Version 15-maj-2021 - Plastics -- Polytetrafluoroethylene (PTFE) semi-finished products
English language
10 pages
sale 15% off
Preview
sale 15% off
Preview
Draft
ISO/FDIS 13000-2 - Plastiques -- Semi-produits en polytétrafluoroéthylène (PTFE)
French language
11 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (sample)

FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 13000-2
ISO/TC 61/SC 9
Plastics — Polytetrafluoroethylene
Secretariat: KATS
(PTFE) semi-finished products —
Voting begins on:
2021-05-19
Part 2:
Voting terminates on:
Preparation of test specimens and
2021-07-14
determination of properties
Plastiques — Semi-produits en polytétrafluoroéthylène (PTFE) —
Partie 2: Préparation des éprouvettes et détermination des propriétés
ISO/CEN PARALLEL PROCESSING
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 13000-2:2021(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
NATIONAL REGULATIONS. ISO 2021
---------------------- Page: 1 ----------------------
ISO/FDIS 13000-2:2021(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2021

All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may

be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting

on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address

below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2021 – All rights reserved
---------------------- Page: 2 ----------------------
ISO/FDIS 13000-2:2021(E)
Contents  Page

Foreword ........................................................................................................................................................................................................................................iv

1  Scope ................................................................................................................................................................................................................................. 1

2  Normative references ...................................................................................................................................................................................... 1

3  Terms and definitions ..................................................................................................................................................................................... 2

4  Sampling ........................................................................................................................................................................................................................ 2

5  Preparation of test specimens ................................................................................................................................................................ 2

6  Testing of semi-finished PTFE products ....................................................................................................................................... 2

6.1 General ........................................................................................................................................................................................................... 2

6.2 Linear dimensions ............................................................................................................................................................................... 2

6.3 Tensile properties ................................................................................................................................................................................. 3

6.3.1 Tensile specimens ........................................................................................................................................................... 3

6.3.2 Procedure ............................................................................................................................................................................... 7

6.4 Density ........................................................................................................................................................................................................... 7

6.5 Loss in mass at 300 °C ...................................................................................................................................................................... 7

6.6 Dimensional stability — General method ....................................................................................................................... 8

6.6.1 Apparatus ............................................................................................................................................................................... 8

6.6.2 Test specimen ..................................................................................................................................................................... 8

6.6.3 Procedure ............................................................................................................................................................................... 8

6.6.4 Expression of results .................................................................................................................................................... 8

6.7 Dimensional stability — Special method for the determination of the dimensional

and the geometrical stability of thick-walled tubes ................................................................................................ 8

6.7.1 Apparatus ............................................................................................................................................................................... 8

6.7.2 Test specimen ..................................................................................................................................................................... 8

6.7.3 Procedure ............................................................................................................................................................................... 9

6.7.4 Expression of results .................................................................................................................................................... 9

6.8 Dielectric strength................................................................................................................................................................................ 9

6.9 Hardness ....................................................................................................................................................................................................... 9

6.10 Colour .............................................................................................................................................................................................................. 9

6.11 Resistance to environmental stress cracking (ESC) ................................................................................................ 9

Bibliography .............................................................................................................................................................................................................................10

© ISO 2021 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO/FDIS 13000-2:2021(E)
Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards

bodies (ISO member bodies). The work of preparing International Standards is normally carried out

through ISO technical committees. Each member body interested in a subject for which a technical

committee has been established has the right to be represented on that committee. International

organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.

ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of

electrotechnical standardization.

The procedures used to develop this document and those intended for its further maintenance are

described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the

different types of ISO documents should be noted. This document was drafted in accordance with the

editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).

Attention is drawn to the possibility that some of the elements of this document may be the subject of

patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of

any patent rights identified during the development of the document will be in the Introduction and/or

on the ISO list of patent declarations received (see www .iso .org/ patents).

Any trade name used in this document is information given for the convenience of users and does not

constitute an endorsement.

For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and

expressions related to conformity assessment, as well as information about ISO's adherence to the

World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www .iso .org/

iso/ foreword .html.

This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 9,

Thermoplastic materials, in collaboration with the European Committee for Standardization (CEN)

Technical Committee CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation

between ISO and CEN (Vienna Agreement).

This third edition cancels and replaces the second edition (ISO 13000-2:2005), which has been

technically revised.
The main changes compared to the previous edition are as follows:
— in Clause 2, normative references have been updated;

— the former Figure 2 has been split into two figures (Figures 2 and 3) and subsequent figures have

been renumbered;

— in Figures 2 and 3, new dimensions (thickness 1,5 ± 0,25 and 1,0 ± 0,20) have been added;

— in Clause 6:
— Table 1 has been edited to compliment Figures 2 and 3;
— a new Table 2 has been added to compliment Figure 4;

— former Annex A has been changed to Bibliography, and titles for standards have been corrected.

A list of all parts in the ISO 13000 series can be found on the ISO website.

Any feedback or questions on this document should be directed to the user’s national standards body. A

complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2021 – All rights reserved
---------------------- Page: 4 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 13000-2:2021(E)
Plastics — Polytetrafluoroethylene (PTFE) semi-finished
products —
Part 2:
Preparation of test specimens and determination of
properties

WARNING — Persons using this document should be familiar with normal laboratory practice,

if applicable. This document does not purport to address all of the safety concerns, if any,

associated with its use. It is the responsibility of the user to establish appropriate safety and

health practices and to determine the applicability of regulatory requirements prior to use.

1  Scope

This document specifies the preparation of test specimens and gives the test methods applicable to

semi-finished products of polytetrafluoroethylene (PTFE).
2  Normative references

The following documents are referred to in the text in such a way that some or all of their content

constitutes requirements of this document. For dated references, only the edition cited applies. For

undated references, the latest edition of the referenced document (including any amendments) applies.

ISO 472, Plastics — Vocabulary

ISO 527-2, Plastics — Determination of tensile properties — Part 2: Test conditions for moulding and

extrusion plastics

ISO 527-3, Plastics — Determination of tensile properties — Part 3: Test conditions for films and sheets

ISO 868, Plastics and ebonite — Determination of indentation hardness by means of a durometer (Shore

hardness)

ISO 1183 (all parts), Plastics — Methods for determining the density of non-cellular plastics

ISO 1923, Cellular plastics and rubbers — Determination of linear dimensions

ISO 2039-1, Plastics — Determination of hardness — Part 1: Ball indentation method

ISO 3611, Geometrical product specifications (GPS) — Dimensional measuring equipment: Micrometers for

external measurements — Design and metrological characteristics

ISO 22088-3, Plastics — Determination of resistance to environmental stress cracking (ESC) — Part 3:

Bent strip method

ISO 22088-4, Plastics — Determination of resistance to environmental stress cracking (ESC) — Part 4: Ball

or pin impression method

ISO 13000-1, Plastics — Polytetrafluoroethylene (PTFE) semi-finished products — Part 1: Requirements

and designation

IEC 60243-1:2013, Electrical strength of insulating materials — Test methods — Part 1: Tests at power

frequencies
© ISO 2021 – All rights reserved 1
---------------------- Page: 5 ----------------------
ISO/FDIS 13000-2:2021(E)

IEC 60243-2, Electric strength of insulating materials — Test methods — Part 2: Additional requirements

for tests using direct voltage
CIE 1931standard colorimetric system
CIE 1964standard colorimetric system
CIE Publication No 15, Colorimetry
3  Terms and definitions

For the purposes of this document, the terms and definitions given in ISO 472 and ISO 13000-1 apply.

ISO and IEC maintain terminological databases for use in standardization at the following addresses:

— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at http:// www .electropedia .org/
4  Sampling

Details of procedures for sampling semi-finished products depend to a large extent on the physical

shape of the particular material. Whenever feasible, the materials shall be sampled. Sampling shall be

statistically adequate to satisfy the requirements of the test method concerned.
5  Preparation of test specimens

The specimens used for testing shall be taken directly from or shall be machined from the semi-finished

product without other treatment. Thus, conversion of a semi-finished product into a test specimen by

any moulding procedure is not permitted. In some instances, special procedures are required that are

described either in the general discussion or in the method.
6  Testing of semi-finished PTFE products
6.1  General

Properties required for specification purposes shall be determined in accordance with the procedures

given in this document. For the determination of density, tensile properties, hardness and electrical

properties, condition the test specimens at 23 °C ± 2 °C for a period of at least 4 h prior to test. The other

tests require no conditioning.
6.2  Linear dimensions

These shall be determined by the procedures provided in ISO 1923 for cellular plastics.

2 © ISO 2021 – All rights reserved
---------------------- Page: 6 ----------------------
ISO/FDIS 13000-2:2021(E)
6.3  Tensile properties
6.3.1  Tensile specimens
6.3.1.1  General

The appropriate type of test specimen shall be chosen from those given in 6.3.1.2 to 6.3.1.5. At least

three test specimens shall be prepared from the sample and three specimens shall be tested.

NOTE Test specimens prepared from moulded basic shapes, rods or tubes conforming to 6.3.1.2 are likely

to give results similar to those obtained with test specimens prepared from the same product but conforming to

6.3.1.3.

When testing extruded products, the test specimens shall be cut parallel to the axis of extrusion so that,

as far as possible, each test specimen represents a different section along the axis and a different area of

the cross-section. When testing skived tape, skived sheet or skived film, the test specimens shall be cut

perpendicular to the direction in which the pressure was applied when moulding the billet from which

the product was skived. If this direction is not known, two sets of test specimens shall be prepared and

tested, the test specimens in one set being cut at 90° to those in the other set and the mean result shall

be calculated from the higher set of values (indicating, typically, the direction perpendicular

...

FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 13000-2
ISO/TC 61/SC 9
Plastics — Polytetrafluoroethylene
Secretariat: KATS
(PTFE) semi-finished products —
Voting begins on:
2021-05-19
Part 2:
Voting terminates on:
Preparation of test specimens and
2021-06-14
determination of properties
Plastiques — Semi-produits en polytétrafluoroéthylène (PTFE) —
Partie 2: Préparation des éprouvettes et détermination des propriétés
ISO/CEN PARALLEL PROCESSING
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 13000-2:2021(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
NATIONAL REGULATIONS. ISO 2021
---------------------- Page: 1 ----------------------
ISO/FDIS 13000-2:2021(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2021

All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may

be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting

on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address

below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2021 – All rights reserved
---------------------- Page: 2 ----------------------
ISO/FDIS 13000-2:2021(E)
Contents  Page

Foreword ........................................................................................................................................................................................................................................iv

1  Scope ................................................................................................................................................................................................................................. 1

2  Normative references ...................................................................................................................................................................................... 1

3  Terms and definitions ..................................................................................................................................................................................... 2

4  Sampling ........................................................................................................................................................................................................................ 2

5  Preparation of test specimens ................................................................................................................................................................ 2

6  Testing of semi-finished PTFE products ....................................................................................................................................... 2

6.1 General ........................................................................................................................................................................................................... 2

6.2 Linear dimensions ............................................................................................................................................................................... 2

6.3 Tensile properties ................................................................................................................................................................................. 3

6.3.1 Tensile specimens ........................................................................................................................................................... 3

6.3.2 Procedure ............................................................................................................................................................................... 7

6.4 Density ........................................................................................................................................................................................................... 7

6.5 Loss in mass at 300 °C ...................................................................................................................................................................... 7

6.6 Dimensional stability — General method ....................................................................................................................... 8

6.6.1 Apparatus ............................................................................................................................................................................... 8

6.6.2 Test specimen ..................................................................................................................................................................... 8

6.6.3 Procedure ............................................................................................................................................................................... 8

6.6.4 Expression of results .................................................................................................................................................... 8

6.7 Dimensional stability — Special method for the determination of the dimensional

and the geometrical stability of thick-walled tubes ................................................................................................ 8

6.7.1 Apparatus ............................................................................................................................................................................... 8

6.7.2 Test specimen ..................................................................................................................................................................... 8

6.7.3 Procedure ............................................................................................................................................................................... 9

6.7.4 Expression of results .................................................................................................................................................... 9

6.8 Dielectric strength................................................................................................................................................................................ 9

6.9 Hardness ....................................................................................................................................................................................................... 9

6.10 Colour .............................................................................................................................................................................................................. 9

6.11 Resistance to environmental stress cracking (ESC) ................................................................................................ 9

Bibliography .............................................................................................................................................................................................................................10

© ISO 2021 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO/FDIS 13000-2:2021(E)
Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards

bodies (ISO member bodies). The work of preparing International Standards is normally carried out

through ISO technical committees. Each member body interested in a subject for which a technical

committee has been established has the right to be represented on that committee. International

organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.

ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of

electrotechnical standardization.

The procedures used to develop this document and those intended for its further maintenance are

described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the

different types of ISO documents should be noted. This document was drafted in accordance with the

editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).

Attention is drawn to the possibility that some of the elements of this document may be the subject of

patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of

any patent rights identified during the development of the document will be in the Introduction and/or

on the ISO list of patent declarations received (see www .iso .org/ patents).

Any trade name used in this document is information given for the convenience of users and does not

constitute an endorsement.

For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and

expressions related to conformity assessment, as well as information about ISO's adherence to the

World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www .iso .org/

iso/ foreword .html.

This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 9,

Thermoplastic materials, in collaboration with the European Committee for Standardization (CEN)

Technical Committee CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation

between ISO and CEN (Vienna Agreement).

This third edition cancels and replaces the second edition (ISO 13000-2:2005), which has been

technically revised.
The main changes compared to the previous edition are as follows:
— in Clause 2, normative references have been updated;

— the former Figure 2 has been split into two figures (Figures 2 and 3) and subsequent figures have

been renumbered;

— in Figures 2 and 3, new dimensions (thickness 1,5 ± 0,25 and 1,0 ± 0,20) have been added;

— in Clause 6:
— Table 1 has been edited to compliment Figures 2 and 3;
— a new Table 2 has been added to compliment Figure 4;

— former Annex A has been changed to Bibliography, and titles for standards have been corrected.

A list of all parts in the ISO 13000 series can be found on the ISO website.

Any feedback or questions on this document should be directed to the user’s national standards body. A

complete listing of these bodies can be found at www .iso .org/ members .html.
iv © ISO 2021 – All rights reserved
---------------------- Page: 4 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 13000-2:2021(E)
Plastics — Polytetrafluoroethylene (PTFE) semi-finished
products —
Part 2:
Preparation of test specimens and determination of
properties

WARNING — Persons using this document should be familiar with normal laboratory practice,

if applicable. This document does not purport to address all of the safety concerns, if any,

associated with its use. It is the responsibility of the user to establish appropriate safety and

health practices and to determine the applicability of regulatory requirements prior to use.

1  Scope

This document specifies the preparation of test specimens and gives the test methods applicable to

semi-finished products of polytetrafluoroethylene (PTFE).
2  Normative references

The following documents are referred to in the text in such a way that some or all of their content

constitutes requirements of this document. For dated references, only the edition cited applies. For

undated references, the latest edition of the referenced document (including any amendments) applies.

ISO 472, Plastics — Vocabulary

ISO 527-2, Plastics — Determination of tensile properties — Part 2: Test conditions for moulding and

extrusion plastics

ISO 527-3, Plastics — Determination of tensile properties — Part 3: Test conditions for films and sheets

ISO 868, Plastics and ebonite — Determination of indentation hardness by means of a durometer (Shore

hardness)

ISO 1183 (all parts), Plastics — Methods for determining the density of non-cellular plastics

ISO 1923, Cellular plastics and rubbers — Determination of linear dimensions

ISO 2039-1, Plastics — Determination of hardness — Part 1: Ball indentation method

ISO 3611, Geometrical product specifications (GPS) — Dimensional measuring equipment: Micrometers for

external measurements — Design and metrological characteristics

ISO 22088-3, Plastics — Determination of resistance to environmental stress cracking (ESC) — Part 3:

Bent strip method

ISO 22088-4, Plastics — Determination of resistance to environmental stress cracking (ESC) — Part 4: Ball

or pin impression method

ISO 13000-1, Plastics — Polytetrafluoroethylene (PTFE) semi-finished products — Part 1: Requirements

and designation

IEC 60243-1:2013, Electrical strength of insulating materials — Test methods — Part 1: Tests at power

frequencies
© ISO 2021 – All rights reserved 1
---------------------- Page: 5 ----------------------
ISO/FDIS 13000-2:2021(E)

IEC 60243-2, Electric strength of insulating materials — Test methods — Part 2: Additional requirements

for tests using direct voltage
CIE 1931standard colorimetric system
CIE 1964standard colorimetric system
CIE Publication No 15, Colorimetry
3  Terms and definitions

For the purposes of this document, the terms and definitions given in ISO 472 and ISO 13000-1 apply.

ISO and IEC maintain terminological databases for use in standardization at the following addresses:

— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at http:// www .electropedia .org/
4  Sampling

Details of procedures for sampling semi-finished products depend to a large extent on the physical

shape of the particular material. Whenever feasible, the materials shall be sampled. Sampling shall be

statistically adequate to satisfy the requirements of the test method concerned.
5  Preparation of test specimens

The specimens used for testing shall be taken directly from or shall be machined from the semi-finished

product without other treatment. Thus, conversion of a semi-finished product into a test specimen by

any moulding procedure is not permitted. In some instances, special procedures are required that are

described either in the general discussion or in the method.
6  Testing of semi-finished PTFE products
6.1  General

Properties required for specification purposes shall be determined in accordance with the procedures

given in this document. For the determination of density, tensile properties, hardness and electrical

properties, condition the test specimens at 23 °C ± 2 °C for a period of at least 4 h prior to test. The other

tests require no conditioning.
6.2  Linear dimensions

These shall be determined by the procedures provided in ISO 1923 for cellular plastics.

2 © ISO 2021 – All rights reserved
---------------------- Page: 6 ----------------------
ISO/FDIS 13000-2:2021(E)
6.3  Tensile properties
6.3.1  Tensile specimens
6.3.1.1  General

The appropriate type of test specimen shall be chosen from those given in 6.3.1.2 to 6.3.1.5. At least

three test specimens shall be prepared from the sample and three specimens shall be tested.

NOTE Test specimens prepared from moulded basic shapes, rods or tubes conforming to 6.3.1.2 are likely

to give results similar to those obtained with test specimens prepared from the same product but conforming to

6.3.1.3.

When testing extruded products, the test specimens shall be cut parallel to the axis of extrusion so that,

as far as possible, each test specimen represents a different section along the axis and a different area of

the cross-section. When testing skived tape, skived sheet or skived film, the test specimens shall be cut

perpendicular to the direction in which the pressure was applied when moulding the billet from which

the product was skived. If this direction is not known, two sets of test specimens shall be prepared and

tested, the test specimens in one set being cut at 90° to those in the other set and the mean result shall

be calculated from the higher set of values (indicating, typically, the direction perpendicular

...

PROJET
NORME ISO/FDIS
FINAL
INTERNATIONALE 13000-2
ISO/TC 61/SC 9
Plastiques — Semi-produits en
Secrétariat: KATS
polytétrafluoroéthylène (PTFE) —
Début de vote:
2021-05-19
Partie 2:
Vote clos le:
Préparation des éprouvettes et
2021-07-14
détermination des propriétés
Plastics — Polytetrafluoroethylene (PTFE) semi-finished products —
Part 2: Preparation of test specimens and determination of properties
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
TRAITEMENT PARALLÈLE ISO/CEN
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/FDIS 13000-2:2021(F)
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
TION NATIONALE. ISO 2021
---------------------- Page: 1 ----------------------
ISO/FDIS 13000-2:2021(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2021

Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette

publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,

y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut

être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.

ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii © ISO 2021 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO/FDIS 13000-2:2021(F)
Sommaire Page

Avant-propos ..............................................................................................................................................................................................................................iv

1 Domaine d’application ................................................................................................................................................................................... 1

2 Références normatives ................................................................................................................................................................................... 1

3 Termes et définitions ....................................................................................................................................................................................... 2

4 Échantillonnage ..................................................................................................................................................................................................... 2

5 Préparation des éprouvettes ................................................................................................................................................................... 2

6 Essais auxquels sont soumis les semi-produits en PTFE ............................................................................................ 2

6.1 Généralités .................................................................................................................................................................................................. 2

6.2 Dimensions linéaires ......................................................................................................................................................................... 2

6.3 Propriétés en traction ....................................................................................................................................................................... 3

6.3.1 Éprouvettes de traction ........................................................................................................................................... ... 3

6.3.2 Mode opératoire ............................................................................................................................................................... 7

6.4 Masse volumique................................................................................................................................................................................... 7

6.5 Perte de masse à 300 °C .................................................................................................................................................................. 7

6.6 Stabilité dimensionnelle — Méthode générale ........................................................................................................... 8

6.6.1 Appareillage ......................................................................................................................................................................... 8

6.6.2 Éprouvette ............................................................................................................................................................................. 8

6.6.3 Mode opératoire ............................................................................................................................................................... 8

6.6.4 Expression des résultats ........................................................................................................................................... 8

6.7 Stabilité dimensionnelle — Méthode spécifique de détermination des stabilités

dimensionnelle et géométrique des tubes à paroi épaisse ............................................................................... 8

6.7.1 Appareillage ......................................................................................................................................................................... 8

6.7.2 Éprouvette ............................................................................................................................................................................. 8

6.7.3 Mode opératoire ............................................................................................................................................................... 9

6.7.4 Expression des résultats ........................................................................................................................................... 9

6.8 Rigidité diélectrique ........................................................................................................................................................................... 9

6.9 Dureté ............................................................................................................................................................................................................. 9

6.10 Couleur ........................................................................................................................................................................................................... 9

6.11 Fissuration sous contrainte dans un environnement donné (ESC) ........................................................10

Bibliographie ...........................................................................................................................................................................................................................11

© ISO 2021 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
ISO/FDIS 13000-2:2021(F)
Avant-propos

L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes

nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est

en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude

a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,

gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.

L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui

concerne la normalisation électrotechnique.

Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont

décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents

critères d'approbation requis pour les différents types de documents ISO. Le présent document a été

rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www

.iso .org/ directives).

L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de

droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable

de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant

les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de

l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de

brevets reçues par l'ISO (voir www .iso .org/ brevets).

Les appellations commerciales éventuellement mentionnées dans le présent document sont données

pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un

engagement.

Pour une explication de la nature volontaire des normes, la signification des termes et expressions

spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion

de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles

techniques au commerce (OTC), voir: www .iso .org/ iso/ fr/ avant -propos.

Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 9,

Matériaux thermoplastiques, en collaboration avec le Comité Européen de Normalisation (CEN), comité

technique CEN/TC 249, Plastiques, conformément à l'Accord de coopération technique entre l'ISO et le

CEN (Accord de Vienne).

Cette troisième édition annule et remplace la deuxième édition (ISO 13000-2:2005), qui a fait l’objet

d’une révision technique. Les principales modifications par rapport à l'édition précédente sont les

suivantes:
— dans l’Article 2, les références normatives ont été mises à jour;

— l’ancienne Figure 2 a été divisée en deux figures (Figures 2 and 3) et les figures suivantes ont été

renumérotées;

— dans les Figures 2 et 3, de nouvelles dimensions (épaisseurs 1,5 ± 0,25 et 1,0 ± 0,20) ont été ajoutées;

— à l’Article 6:
— le Tableau 1 a été modifié afin de compléter les Figures 2 et 3 ;
— un nouveau Tableau 2 a été ajouté afin de compléter la Figure 4 ;

— l'ancienne Annexe A a été remplacée par une Bibliographie et les titres des normes ont été corrigés.

Une liste de toutes les parties de la série ISO 13000 est disponible sur le site web de l’ISO.

Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent

document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes

se trouve à l’adresse www .iso .org/ fr/ members .html.
iv © ISO 2021 – Tous droits réservés
---------------------- Page: 4 ----------------------
PROJET FINAL DE NORME INTERNATIONALE ISO/FDIS 13000-2:2021(F)
Plastiques — Semi-produits en polytétrafluoroéthylène
(PTFE) —
Partie 2:
Préparation des éprouvettes et détermination des
propriétés

AVERTISSEMENT — Il convient que les personnes utilisant le présent document soient familières

avec les pratiques courantes de laboratoire, le cas échéant. Le présent document n’a pas pour

but de traiter tous les problèmes de sécurité éventuels qui sont liés à son utilisation. Il incombe

à l’utilisateur d’établir des pratiques d’hygiène et de sécurité appropriées et de déterminer

l'applicabilité des exigences réglementaires avant utilisation.
1 Domaine d’application

Le présent document spécifie le mode de préparation des éprouvettes et les méthodes d’essai applicables

aux semi-produits en polytétrafluoroéthylène (PTFE).
2 Références normatives

Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des

exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les

références non datées, la dernière édition du document de référence s’applique (y compris les éventuels

amendements).
ISO 472, Plastiques — Vocabulaire

ISO 527-2, Plastiques — Détermination des propriétés en traction — Partie 2: Conditions d'essai des

plastiques pour moulage et extrusion

ISO 527-3, Plastiques — Détermination des propriétés en traction — Partie 3: Conditions d'essai pour films

et feuilles

ISO 868, Plastiques et ébonite — Détermination de la dureté par pénétration au moyen d'un duromètre

(dureté Shore)

ISO 1183 (toutes les parties), Plastiques — Méthodes pour déterminer la masse volumique et la densité

relative des plastiques non alvéolaires

ISO 1923, Plastiques et caoutchoucs alvéolaires — Détermination des dimensions linéaires

ISO 2039-1, Plastiques — Détermination de la dureté — Partie 1: Méthode de pénétration à la bille

ISO 3611, Spécification géométrique des produits (GPS) — Équipement de mesurage dimensionnel:

Micromètres d'extérieur — Caractéristiques de conception et caractéristiques métrologiques

ISO 22088-3, Plastiques — Détermination de la fissuration sous contrainte dans un environnement donné

(ESC) — Partie 3: Méthode de l'éprouvette courbée

ISO 22088-4, Plastiques — Détermination de la fissuration sous contrainte dans un environnement donné

(ESC) — Partie 4: Méthode par enfoncement de billes ou de goupilles

ISO 13000-1, Plastiques — Produits semi-finis en polytétrafluoroéthylène (PTFE) — Partie 1: Spécifications

et désignation
© ISO 2021 – Tous droits réservés 1
---------------------- Page: 5 ----------------------
ISO/FDIS 13000-2:2021(F)

IEC 60243-1:2013, Rigidité diélectrique des matériaux isolants — Méthodes d’essai — Partie 1: Essais aux

fréquences industrielles

IEC 60243-2, Rigidité diélectrique des matériaux isolants — Méthodes d’essai — Partie 2: Exigences

complémentaires pour les essais à tension continue
CIE 1931, Système colorimétrique normalisé CIE 1931
CIE 1964, Système colorimétrique normalisé CIE 1964
Publication CIE 15, Colorimétrie
3 Termes et définitions

Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 472 et l’ISO 13000-1

s’appliquent.

L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en

normalisation, consultables aux adresses suivantes:

— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp

— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
4 Échantillonnage

Certains détails propres aux méthodes d’échantillonnage des semi-produits dépendent, dans une large

mesure, de la forme physique sous laquelle se présente le matériau considéré. Lorsque c’est réalisable,

les matériaux doivent être échantillonnés. L’échantillonnage doit être statistiquement adéquat pour

satisfaire aux exigences de la méthode d’essai concernée.
5 Préparation des éprouvettes

Les éprouvettes utilisées pour les essais doivent être prélevées directement dans des semi-produits

n’ayant subi aucun traitement ou être usinées à partir de ces produits. Ainsi, il est exclu de transformer

un semi-produit en éprouvette par le biais d’une quelconque méthode de moulage. Dans certains cas,

des modes opératoires particuliers sont requis, qui sont décrits soit dans les dispositions générales, soit

dans la méthode.
6 Essais auxquels sont soumis les semi-produits en PTFE
6.1 Généralités

Les propriétés requises à des fins de spécification doivent être déterminées conformément aux

modes opératoires donnés dans le présent document. Pour la détermination de la masse volumique,

des propriétés en traction, de la dureté et des propriétés électriques, conditionner les éprouvettes à

23 °C ± 2 °C pendant au moins 4 h avant l’essai. Les autres essais ne nécessitent aucun conditionnement.

6.2 Dimensions linéaires

Elles doivent être déterminées conformément aux modes opératoires indiqués dans l’ISO 1923 pour les

plastiques alvéolaires.
2 © ISO 2021 – Tous droits réservés
---------------------- Page: 6 ----------------------
ISO/FDIS 13000-2:2021(F)
6.3 Propriétés en traction
6.3.1 Éprouvettes de traction
6.3.1.1 Généralités

Le type approprié d’éprouvette doit être choisi parmi ceux indiqués de 6.3.1.2 à 6.3.1.5. Au moins trois

éprouvettes doivent être préparées à partir de l’échantillon, et en tout état de cause, trois éprouvettes

doivent être soumises à l’essai.

NOTE Il y a de fortes chances pour que des éprouvettes préparées à partir des ébauches moulées, de

barreaux ou de tubes, et conformes à 6.3.1.2 donnent des résultats similaires à ceux obtenus avec des éprouvettes

préparées à partir du même produit, mais conformes à 6.3.1.3.

Lorsque l’essai porte sur des produits extrudés, les éprouvettes doivent être découpées parallèlement

à l’axe d’extrusion de sorte que, dans la mesure du possible, chaque éprouvette représente une section

différente le long de l’axe, avec une aire de section transversale différente. Lorsque l’essai porte sur une

bande, une feuille ou un film déroulé(e), les éprouvettes doivent être découpées perpendiculairement à

la direction dans laquelle la pression a été appliquée lors du moulage du bloc à partir duquel le produit a

été déroulé. Si cette direction n’est pas connue, deux jeux d’éprouvettes doivent être préparés et soumis

à l’essai après avoir découpé les éprouvettes d’un jeu à 90° par rapport à celles de l’autre jeu, le résultat

moyen devant être calculé à partir des valeurs les plus élevées (indiquant généralement la direction

perpendiculaire à l’axe selon lequel la pression est exercée). Le présent mode opératoire garantit un

mode uniforme de notation des résultats d’essai. La micro-éprouvette de traction (voir 6.3.1.3) est la

plus utilisée pour les produits en PTFE.
6.3.1.2 Éprouvettes en forme d’haltères, usinées au tour

Les éprouvettes doivent être usinées au tour de façon que leurs dimensions soient comprises dans les

limites indiquées à la Figure 1, et selon la forme représentée à la Figure 1
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.