ISO 3211:2018

Anodizing of aluminium and its alloys — Assessment of resistance of anodic oxidation coatings to cracking by deformation

This document specifies an empirical method for assessing the resistance of anodic oxidation coatings to cracking by deformation. The method is applicable particularly to sheet material with anodic oxidation coatings of thickness less than 5 µm, and is useful for development purposes. NOTE If the test specimen is thick, more than 5 µm of coating can be measured (see Clause 9).

Anodisation de l'aluminium et de ses alliages — Évaluation de la résistance des couches anodiques à la formation de criques par déformation

Le présent document spécifie une méthode empirique permettant d'évaluer la résistance des couches anodiques à la formation de criques par déformation. La méthode est applicable particulièrement aux matériaux en feuille avec une couche anodique d'une épaisseur inférieure à 5 μm, et est utilisée pour le développement. NOTE Si l'éprouvette est épaisse, une couche de plus de 5 μm peut être évaluée (voir Article 9).

General Information

• Status: Published
• Publication Date: 27-Nov-2018
• ICS: 25.220.20 - Surface treatment
• Technical Committee: ISO/TC 79/SC 2 - Organic and anodic oxidation coatings on aluminium
• Drafting Committee: ISO/TC 79/SC 2/WG 15 - Anodic oxidation coatings on aluminium
• Current Stage: 9093 - International Standard confirmed
• Completion Date: 13-May-2024

Relations

• Consolidates: ISO 14707:2015 - Surface chemical analysis — Glow discharge optical emission spectrometry (GD-OES) — Introduction to use
• Effective Date: 06-Jun-2022
• Revises: ISO 3211:2010 - Anodizing of aluminium and its alloys — Assessment of resistance of anodic oxidation coatings to cracking by deformation
• Effective Date: 20-Aug-2016

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 3211
Fourth edition
2018-11
Anodizing of aluminium and its
alloys — Assessment of resistance of
anodic oxidation coatings to cracking
by deformation
Anodisation de l'aluminium et de ses alliages — Évaluation de la
résistance des couches anodiques à la formation de criques par
déformation
Reference number
ISO 3211:2018(E)
©
ISO 2018

---------------------- Page: 1 ----------------------
ISO 3211:2018(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2018
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Fax: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii © ISO 2018 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 3211:2018(E)

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 1
6 Test specimen . 2
6.1 Sampling . 2
6.2 Size . 2
6.3 Treatment before testing . 2
7 Procedure. 4
8 Expression of results . 5
9 Test report . 5
Bibliography . 6
© ISO 2018 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 3211:2018(E)

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collabor
...

NORME ISO
INTERNATIONALE 3211
Quatrième édition
2018-11
Anodisation de l'aluminium et de ses
alliages — Évaluation de la résistance
des couches anodiques à la formation
de criques par déformation
Anodizing of aluminium and its alloys — Assessment of resistance of
anodic oxidation coatings to cracking by deformation
Numéro de référence
ISO 3211:2018(F)
©
ISO 2018

---------------------- Page: 1 ----------------------
ISO 3211:2018(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2018
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
Fax: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii © ISO 2018 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 3211:2018(F)

Sommaire Page
Avant-propos .iv
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 1
5 Appareillage . 1
5.1 Dispositifs de mesurage. . 1
6 Éprouvette . 2
6.1 Échantillonnage . 2
6.2 Dimension . 2
6.3 Traitement avant essai . 2
7 Mode opératoire. 3
8 Expression des résultats. 4
9 Rapport d'essai . 5
Bibliographie . 6
© ISO 2018 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 3211:2018(F)

Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé
...