SIST EN 13108-6:2006
(Main)Bituminous mixtures - Material specifications - Part 6: Mastic Asphalt
Bituminous mixtures - Material specifications - Part 6: Mastic Asphalt
The document specifies requirements for mixtures of the mix group mastic asphalt. It deals also with the selection of the constituent materials. Mastic asphalt is a voidless asphalt consisting of mineral aggregate, filler and bitumen. The mineral aggregates is the mixture is grades to be of low void content. The binder content is so adjusted to the void content in the mineral aggregate that the voids are completely filled. A slight excess of binder may be acceptable. Mastic asphalt is pourable when hot and requires no compaction. Mastic asphalt can be used in all kinds of traffic and climates on roads, bridges, airfields and other trafficked areas. It is mainly to be used for surface cource and may also be used for binder courses.
Asphaltmischgut - Mischgutanforderungen - Teil 6: Gussasphalt
Diese Europäische Norm legt Anforderungen an Mischgüter der Mischgutgruppe Gussasphalt fest, die für die Verwendung beim Bau von Straßen, Flugplätzen und sonstigen Verkehrsflächen bestimmt sind.
ANMERKUNG Die Spezifikation des Mischgutes nach dieser Europäischen Norm kann entweder zur Konformitätserklärung dieses Mischgutes mit bekannten Anforderungen verwendet werden oder zur Bekanntmachung welche diese Anforderungen sind.
Diese Europäische Norm enthält Anforderungen an die Auswahl der Bestandteile. Sie ist in Verbindung mit EN 13108 20 und EN 13108 21 anzuwenden.
Gussasphalt mit chemisch modifizierten Bindemitteln, die nicht durch EN 14023 abgedeckt sind, sind nicht Gegenstand dieser Europäischen Norm.
Mélanges bitumineux - Spécifications des matériaux - Partie 6: Asphalte coulé routier
Cette norme européenne spécifie les exigences relatives a la famille des asphaltes coulés routiers destinés a etre utilisés pour les routes, les aéroports et autres zones de circulation.
Note : Une spécification sur un mélange issue de cette norme peut etre utilisée soit pour déclarer la conformité d’un mélange a des exigences connues soit pour faire savoir ce que sont ces exigences.
Cette norme européenne comporte des exigences relatives a la sélection des divers constituants. Elle est destinée a etre utilisée conjointement avec les normes EN 13108-20 et EN 13108-21.
Les asphaltes coulés routiers contenant des liants chimiquement modifiés qui ne sont pas couverts par la norme EN 14023, ne sont pas couverts par la présente Norme européenne.
Bitumenske zmesi - Specifikacije materialov - 6. del: Liti asfalt
Ta evropski standard določa zahteve za skupino zmesi litih asfaltov za uporabo na cestah, letališčih in drugih prometnih površinah. OPOMBA: Določila za zmesi, ki izhajajo iz tega evropskega standarda, se lahko upoštevajo pri oblikovanju izjave o skladnosti zmesi s poznanimi zahtevami ali pa samo za obveščanje o teh zahtevah. Ta evropski standard vključuje zahteve za izbiro sestavnih materialov. Zasnovan je tako, da se uporablja skupaj s standardoma EN 13108-20 in EN 13108-21. Zmesi litega asfalta s kemično modificiranimi vezivi, ki niso predmet standarda EN 14023, niso predmet tega evropskega standarda.
General Information
Relations
Standards Content (Sample)
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Bituminous mixtures - Material specifications - Part 6: Mastic AsphaltBitumenske zmesi - Specifikacije materialov - 6. del: Liti asfaltMélanges bitumineux - Spécifications des matériaux - Partie 6: Asphalte coulé routierAsphaltmischgut - Mischgutanforderungen - Teil 6: GussasphaltTa slovenski standard je istoveten z:EN 13108-6:2006SIST EN 13108-6:2006en93.080.20ICS:SLOVENSKI
STANDARDSIST EN 13108-6:200601-julij-2006
EUROPEAN STANDARDNORME EUROPÉENNEEUROPÄISCHE NORMEN 13108-6May 2006ICS 93.080.20 English VersionBituminous mixtures - Material specifications - Part 6: MasticAsphaltMélanges bitumineux - Spécifications des matériaux -Partie 6: Asphalt coulé routierAsphaltmischgut - Mischgutanforderungen - Teil 6:GussasphaltThis European Standard was approved by CEN on 12 October 2005.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the Central Secretariat or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the officialversions.CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMITÉ EUROPÉEN DE NORMALISATIONEUROPÄISCHES KOMITEE FÜR NORMUNGManagement Centre: rue de Stassart, 36
B-1050 Brussels© 2006 CENAll rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 13108-6:2006: E
EN 13108-6:2006 (E) 2 Contents Page Foreword.3 Introduction.4 1 Scope.5 2 Normative references.5 3 Terms and definitions, symbols and abbreviations.6 3.1 Terms and definitions.6 3.2 Symbols and abbreviations.7 4 Requirements for constituent materials.7 4.1 General.7 4.2 Binder.7 4.2.1 General.7 4.2.2 Selection of binder.7 4.2.3 Surface courses with reclaimed asphalt.8 4.3 Aggregates.8 4.3.1 Coarse aggregate.8 4.3.2 Fine aggregate.8 4.3.3 All-in aggregates.8 4.3.4 Added filler.8 4.4 Reclaimed asphalt.9 4.5 Additives.9 5 Requirements for the mixture.9 5.1 General.9 5.2 Composition, grading, binder content and additives.9 5.2.1 Composition.9 5.2.2 Grading.9 5.2.3 Binder content.11 5.2.4 Additives.12 5.3 Coating and homogeneity.12 5.4 Resistance to abrasion by studded tyres.12 5.5 Reaction to fire.13 5.6 Resistance to fuel for application on airfields.13 5.7 Resistance to de-icing fluid for application on airfields.13 5.8 Temperature of the mixture.14 5.9 Indentation (Resistance to permanent deformation).14 5.10 Durability.16 6 Evaluation of conformity.17 7 Identification.17 Annex A (normative)
Calculations of the penetration or the softening point of the binder of a mixture when reclaimed asphalt is used.18 A.1 General.18 A.2 Calculation of the penetration of the binder of a mixture.18 A.3 Calculation of the softening point of the binder of a mixture.18 Annex ZA (informative)
Clauses of this European Standard addressing the provisions of the EU Construction Product directive.20 ZA.1 Scope and relevant characteristics.20 ZA.2 Procedure(s) for attestation of conformity of Mastic Asphalt.22 ZA.3 CE marking and labelling.25
EN 13108-6:2006 (E) 3 Foreword This European Standard (EN 13108-6:2006) has been prepared by Technical Committee CEN/TC 227 “Road materials”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by November 2006, and conflicting national standards shall be withdrawn at the latest by January 2008. This European Standard has been prepared under a mandate given to CEN by the European Commission and the European Free Trade Association, and supports essential requirements of EU Directive(s). For relationship with EU Directive(s), see informative Annex ZA, which is an integral part of this European Standard. This European Standard is one of a series of standards as listed below: EN 13108-1, Bituminous mixtures Material specifications Part 1: Asphalt Concrete. EN 13108-2, Bituminous mixtures Material specifications Part 2: Asphalt Concrete for very thin layers. EN 13108-3, Bituminous mixtures Material specifications Part 3: Soft Asphalt. EN 13108-4, Bituminous mixtures Material specifications Part 4: Hot Rolled Asphalt. EN 13108-5, Bituminous mixtures Material specifications Part 5: Stone Mastic Asphalt. EN 13108-6, Bituminous mixtures Material specifications Part 6: Mastic Asphalt. EN 13108-7, Bituminous mixtures Material specifications Part 7: Porous Asphalt. EN 13108-8, Bituminous mixtures Material specifications Part 8: Reclaimed asphalt. EN 13108-20, Bituminous mixtures Material specifications Part 20: Type Testing. EN 13108-21, Bituminous mixtures Material specifications Part 21: Factory Production Control. No existing European Standard is superseded. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EN 13108-6:2006 (E) 4 Introduction The ultimate aim is to specify the required fundamental properties of the bituminous mixtures. However, as specifications for Mastic Asphalt have traditionally been based empirically on compositional recipes combined with specifications for the constituent materials with additional requirements based on performance related tests and as insufficient experience is available with fundamental testing of Mastic Asphalt, this European Standard, for the moment, specifies empirical requirements only. Mastic Asphalt is to be used for surface courses and may also be used for binder courses. Mastic Asphalt is also used for protection layers and inter-layers for bridges, tunnels and roughs. NOTE Mastic Asphalt for waterproofing purposes in the construction and civil engineering fields is specified in CEN/TC 314 – Mastic Asphalt for waterproofing.
EN 13108-6:2006 (E) 5 1 Scope This European Standard specifies requirements for mixtures of the mix group Mastic Asphalt for use on roads, airfields and other trafficked areas. NOTE A mixture specification derived from this European Standard can be used either to declare the conformity of a mixture with known requirements or to make known what those requirements are. This European Standard includes requirements for the selection of the constituent materials. It is designed to be read in conjunction with EN 13108-20 and EN 13108-21. Mastic Asphalt mixes with chemical modified binders not covered by EN 14023 are not covered by this European Standard. 2 Normative references The following referenced documents are indispensable for the application of this European Standard. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 1097-6, Tests for mechanical and physical properties of aggregates — Part 6: Determination of particle density and water absorption EN 1426, Bitumen and bituminous binders — Determination of needle penetration EN 1427, Bitumen and bituminous binders — Determination of softening point — Ring and ball method EN 12591, Bitumen and bituminous binders — Specifications for paving grade bitumens EN 12697-3, Bituminous mixtures — Test methods for hot mix asphalt — Part 3: Bitumen recovery: Rotary evaporator EN 12697-4, Bituminous mixtures — Test methods for hot mix asphalt — Part 4: Bitumen recovery: Fractionating column EN 12697-13, Bituminous mixtures — Test methods for hot mix asphalt — Part 13: Temperature measurement EN 13043, Aggregates for bituminous mixtures and surface treatments for roads, airfields and other trafficked areas EN 13108-4:2005, Bituminous mixtures — Material specifications — Part 4: Hot Rolled Asphalt EN 13108-8, Bituminous mixtures — Material specifications — Part 8: Reclaimed asphalt EN 13108-20:2005, Bituminous mixtures — Material specifications — Part 20: Type Testing EN 13108-21:2005, Bituminous mixtures — Material specifications — Part 21: Factory Production Control EN 13501-1, Fire classification of construction products and building elements — Part 1: Classification using test data from reaction to fire tests prEN 13924, Bitumen and bituminous binders — Specifications for hard paving grade bitumens EN 14023, Bitumen and bituminous binders - Framework specification for polymer modified bitumens
EN 13108-6:2006 (E) 6 ISO 565, Test sieves — Metal wire cloth, perforated metal plate and electroformed sheet — Nominal sizes of openings. 3 Terms and definitions, symbols and abbreviations 3.1 Terms and definitions For the purposes of this European Standard, the following terms and definitions apply. 3.1.1 pavement structure, composed of one or more courses, to assist the passage of traffic over terrain 3.1.2 layer element of a pavement laid in a single operation 3.1.3 course structural element of a pavement constructed with a single material. A course may be laid in one or more layers 3.1.4 surface course upper course of a pavement, which is in contact with the traffic 3.1.5 binder course part of a pavement between the surface course and the base 3.1.6 regulating course course of variable thickness applied to an existing course to provide the necessary profile for a further course of consistent thickness 3.1.7 base main structural element of a pavement. The base may be laid in one or more courses, described as “upper“ base, “lower“ base etc. 3.1.8 Mastic Asphalt voidless asphalt mixtures with bitumen as a binder in which the volume of filler and binder exceeds the volume of the remaining voids in the mix 3.1.9 mix formulation composition of a single mixture expressed as a target composition NOTE A target composition may be expressed in two ways (see 3.1.10 and 3.1.11). 3.1.10 input target composition expression of a mix formulation in terms of the constituent materials, the grading curve and the percentage of bitumen added to the mixture NOTE This will usually be the result of a laboratory mix design and validation.
EN 13108-6:2006 (E) 7 3.1.11 output target composition expression of a mix formulation in terms of the constituent materials and the mid point grading and soluble binder content to be found on analysis NOTE This will usually be the result of a production validation. 3.1.12 additive constituent material which can be added in small quantities to the mixture, e.g. polymers for improvement of the mechanical properties, the workability or the colour of the mixture 3.2 Symbols and abbreviations MA Mastic Asphalt D the upper sieve size of the aggregate in the mixture, in millimetres (mm) 4 Requirements for constituent materials 4.1 General Only constituent materials with established suitability shall be used. The establishment of suitability shall result from one or more of the following: European Standard; European Technical Approval; specifications for materials based on a demonstrable history of satisfactory use in asphalt. Evidence shall be provided on their suitability. This evidence may be based on research combined with evidence from practice. NOTE In the European asphalt industry it is common practice to use additives like inorganic or organic fibres, pigments, waxes etc., which are not covered by a European Standard or ETA. This European Standard allows the use of those materials.
4.2 Binder 4.2.1 General The binder shall be a paving grade bitumen, modified bitumen or hard grade bitumen. The paving grade bitumen shall conform to EN 12591, the modified bitumen to EN 14023 and the hard grade bitumen to EN 13924. Natural asphalt conforming to EN 13108-4:2005, Annex B, may be added. 4.2.2 Selection of binder The grade of the bitumen, the type and grade of modified bitumen, the grade of the hard grade bitumen and the amount and category of natural asphalt shall be as specified. In case of a paving grade bitumen the grade shall be selected from the grades between 20/30 and 70/100 inclusively and in case of a hard grade bitumen the grade shall be selected from the grades 10/20 and 15/25.
EN 13108-6:2006 (E) 8 NOTE 1 Given the wide variety of climates, traffic loads, used materials etc. it can be necessary to select on a regional level specific binders. When modified bitumen is used to improve properties that are not covered by the empirical specification additional proof shall be provided. This proof shall be delivered through investigation using European Standards in the EN 12697 series, that the modified bitumen is suitable for improving the desired functional characteristics. The proof may be based on earlier research. NOTE 2 EN 14023 is a grading system and is only meant to characterise the modified bitumen. The modified bitumen specifications are not functionally based, and it is not possible to combine these specifications with empirical asphalt specifications to demonstrate functional behaviour. The proof required would normally be a Type Testing on a similar mixture incorporating the modified binder showing fulfilment of the relevant property. The grade of the bitumen, the type and grade of the modified bitumen and the amount and category of natural asphalt may be selected. 4.2.3 Surface courses with reclaimed asphalt When using more than 10 % by mass of the total mixture of reclaimed asphalt from mixtures in which only paving grade bitumen has been used and when the binder added to the mixture is a paving grade bitumen and the grade of the bitumen is selected, the binder shall conform to the following requirement: Penetration or the softening point of the binder in the resulting mixture, calculated from the penetrations or the softening points of the added binder and the recovered binder from the reclaimed asphalt, shall meet the penetration or softening point requirements of the selected grade. The calculation shall be executed according to Annex A. Either the penetration or the softening point requirement shall be selected. 4.3 Aggregates 4.3.1 Coarse aggregate Coarse aggregate shall conform to EN 13043 as appropriate for the intended use. 4.3.2 Fine aggregate Fine aggregate shall conform to EN 13043 as appropriate for the intended use. 4.3.3 All-in aggregates All-in aggregate shall conform to EN 13043 as appropriate for the intended use. 4.3.4 Added filler Filler aggregate shall conform to EN 13043 as appropriate for the intended use. The amount of added filler shall be as specified. NOTE 1 Filler includes materials as cement and hydrated lime. NOTE 2 The expression “as appropriate for the intended use” in 4.3.1 to 4.3.4 means that the selection of the requirements and the particular category depends on a number of conditions. These conditions will include traffic density, climatic conditions, the construction of the course in which the mixture will be used, and economic considerations.
EN 13108-6:2006 (E) 9 4.4 Reclaimed asphalt The use and the amount of reclaimed asphalt and the mix group from which the reclaimed asphalt has been or will be derived shall be as specified. The properties of reclaimed asphalt declared in accordance with EN 13108-8 shall conform to the specified requirements appropriate to the intended use. NOTE The expression “appropriate to the intended use” means that the selection of the requirements and the particular category depends on a number of conditions. These conditions will include traffic density, climatic conditions, the construction of the course in which the mixture will be used, and economic considerations. The upper sieve size D of the aggregate in the reclaimed asphalt shall not exceed the upper sieve size D of the mixture. The aggregate properties of the reclaimed asphalt shall fulfil the requirements specified for the aggregate for the mixture. 4.5 Additives The nature and properties of all additives shall be declared and they shall conform to the specifications required in 4.1. 5 Requirements for the mixture 5.1 General The mix formulation shall be declared and documented. At the target composition the mixture shall conform to the selected requirements. When using reclaimed asphalt from mixtures in which a modified bitumen and/or a modifier additive has been used, and /or the mixture itself contains a modified bitumen or a modifier, the amount of reclaimed asphalt added to a surface course shall not, unless otherwise agreed between client and manufacturer, exceed 10 % by mass of the total mixture. Any agreement made between client and manufacturer shall not be in conflict with national regulatory requirements. 5.2 Composition, grading, binder content and additives 5.2.1 Composition At the target composition the grading shall conform to 5.2.2. At the target composition the binder content shall conform to 5.2.3. At the target composition the additive content shall conform to 5.2.4. The grading shall be expressed in percentages by mass of total aggregate, using the sieves belonging either to the basic sieve set plus set 1 or the basic set plus set 2 according to EN 13043. The binder and additive content shall be expressed in percentages by mass of total mixture. The percentages passing the sieves, with exception of the sieve 0,063 mm shall be expressed to 1 %, the binder content, the percentage passing sieve 0,063 and any additive content shall be expressed to 0,1 %. 5.2.2 Grading The requirements for the grading shall be expressed in terms of maximum and minimum values by selection for the percentages passing the sieves 1,4 D, D, 2 mm, a characteristic coarse sieve and 0,063 mm. A combination of sieve sizes from set 1 and set 2 is not permissible.
EN 13108-6:2006 (E) 10 The requirements for the grading of the target composition shall be expressed in terms of a grading envelope of maximum and minimum values for the percentages passing the sieves 1,4 D; D; 2 mm and 0,063 mm. In addition the requirements for the grading envelope may include the percentages passing one optional sieve between D and 2 mm and one optional fine sieve between 2 mm and 0,063 mm. The target composition of the mixture shall be within this grading envelope. D and the sieves between D and 2 mm shall be selected from the following sieves: basic sieve set plus set 1: 4 mm; 5,6 mm; 8 mm; 11,2 mm; 16 mm; basic sieve set plus set 2: 4 mm; 6,3 mm; 8 mm; 10 mm; 12,5 mm; 14 mm; 16 mm. The optional fine sieve shall be selected from the following sieves: 1 mm; 0,5 mm; 0,25 mm and 0,125 mm. Tables 1 and 2 specify the overall grading limits for Stone Mastic Asphalt. Table 1 — Overall limits of target composition - basic sieve set plus set 1 D 4 5 (5,6) 8 11 (11,2) 16 Sieve mm Passing sieve % by mass 1,4 D a 100 100 100 100 100 D 90 to 100 90 to 100 90 to 100 90 to 100 90 to 100 2 50 to 80 45 to 70 45 to 70 40 to 70 35 to 60 0,063 20,0 to 45,0 20,0 to 40,0 20,0 to 40,0 18,0 to 35,0 18,0 to 28,0 a Where the sieve calculated as 1,4 D is not an exact number in the ISO 565/R 20 series then the next nearest sieve in the set shall be adopted.
EN 13108-6:2006 (E) 11 Table 2 — Overall limits of target composition - basic sieve set plus set 2 D 4 6 (6,3) 8 10 12(12,5) 14 16 Sieve mm Passing sieve % by mass 1,4 Da 100 100 100 100 100 100 100 D 90 to 100 90 to 100 90 to 100 90 to 100 90 to 100 90 to 100 90 to 100 2 50 to 80 45 to 70 45 to 70 40 to 70 40 to 70 35 to 55 35 to 55 0,063 20,0 to 45,020,0 to 40,0 20,0 to 40,018,0 to 35,018,0 to 35,0 18,0 to 28,0 18,0 to 28,0a Where the sieve calculated as 1,4 D is not an exact number in the basic set plus set 2 series then the next nearest sieve in the set shall be adopted.
Table 3 specifies the width of the required grading envelope. The ranges between the maximum and minimum values for the grading envelope shall be selected as a single value within the given limits (both included) from Table 3. Table 3 — Grading of target composition - ranges between maximum and minimum values
for the selected grading envelope Ranges % by mass Sieve mm Smallest range Widest range Characteristic coarse sieve 10 25 Optional sieve between D and 2 10 25 2 5 15 Characteristic fine sieve 4 15 0,063 2,0 8,0
5.2.3 Binder content The minimum binder content of the target composition shall be selected from the categories in Table 4. The binder content requirements shall be corrected by multiplying by the factor d2,650ρα= (1) where ρd is the particle density of the aggregate, in megagrams per cubic metre (Mg/m3), determined according to EN 1097-6. NOTE The binder content includes binder in reclaimed asphalt and natural asphalt when used.
EN 13108-6:2006 (E) 12 Table 4 — Minimum binder content, Bmin Minimum binder content % Category Bmin 6,0 Bmin6,0 6,2 Bmin6,2 6,5 Bmin6,5 6,8 Bmin6,8 7,0 Bmin7,0 7,5 Bmin7,5 8,0 Bmin8,0 8,5 Bmin8,5 9,0 Bmin9,0 9,5 Bmin9,5
5.2.4 Additives The requirements for additives shall be expressed in terms of the type and amount of each additive constituent. 5.3 Coating and homogeneity The material when discharged from the mixer shall be homogenous in appearance with the aggregate completely coated with binder, and there shall be no evidence of balling of fine aggregate. 5.4 Resistance to abrasion by studded tyres The resistance abrasion by studded tyres of specimens shall be selected from the categories in Table 5. The resistance to abrasion by studded tyres shall be determined in accordance with EN 13108-20:2005, D.4.
EN 13108-6:2006 (E) 13 Table 5 — Maximum Abrasion value, AbrA
Maximum abrasion value ml Category AbrA
20 AbrA20
24 AbrA24
28 AbrA28
32 AbrA32
36 AbrA36
40 AbrA40
45 AbrA45
50 AbrA50
55 AbrA55
60 AbrA60
No requirement AbrNR
5.5 Reaction to fire If the manufacturer declares a Euroclass for reaction to fire, (i.e. it is subject to regulatory requirements) the Mastic Asphalt shall be tested and classified in accordance with EN 13501-1. 5.6 Resistance to fuel for application on airfields The resistance to fuel of specimens shall be selected from the categories good, moderate, poor or no requirement. The resistance to fuel shall be determined according with EN 13108-20:2005, D.11. 5.7 Resistance to de-icing fluid for application on airfields The resistance to de-icing fluid of specimens shall be selected from the categories in Table 6. The resistance to de-icing fluids shall be determined in accordance with EN 13108-20:2005, D.12.
EN 13108-6:2006 (E) 14 Table 6 — Retained strength, β
Minimum retained strength % Category ββββ
100 β100 85 β85 70 β70 55 β55 No requirement βNR
5.8 Temperature of the mixture When using paving grade bitumen, the temperatures of the mixture, measured according to EN 12697-13 shall be within the limits of Table 7. The maximum temperature applies at any place in the plant, the minimum temperature applies at the delivery. Table 7 — Temperature limits of the mixture Paving grade bitumen Temperature °C
20/30 210 to 250 30/45, 35/50, 40/60 200 to 240 50/70 and 70/100 190 to 230
When using modified bitumen or hard grade bitumen or additives different temperatures may be applicable. These shall then be documented and declared as part of the regulatory marking. 5.9 Indentation (Resistance to permanent deformation) The indentation of specimens prepared in accordance with EN 13108-20:2005, 6.5, shall be specified by selection from the categories in Table 8 to Table 11. The indentation shall be determined in accordance with EN 13108-20:2005, D.14.
EN 13108-6:2006 (E) 15 Table 8 — Minimum indentation, Imin Minimum indentation mm Category Imin 1,0 Imin1,0 1,5 Imin1,5 2,0 Imin2,0 2,5 Imin2,5 3,0 Imin3,0 No requirement Imin NR
Table 9 — Maximum indentation, Imax Maximum indentation mm Category Imax 3,0 Imax3,0 3,5 Imax3,5 4,0 Imax4,0 5,0 Imax5,0 6,0 Imax6,0 7,0 Imax7,0 8,0 Imax8,0 9,0 Imax9,0 10,0 Imax10,0 11,0 Imax11,0 13,0 Imax13,0 15,0 Imax15,0 No requirement Imax NR
N
...
SLOVENSKI SIST EN 13108-6
STANDARD
julij 2006
Bitumenske zmesi – Specifikacije materialov – 6. del: Liti asfalt
Bituminous mixtures – Material specifications – Part 6: Mastic Asphalt
Mélanges bitumineux – Spécifications des matériaux – Partie 6: Asphalte coulé
routier
Asphaltmischgut – Mischgutanforderungen – Teil 6: Gussasphalt
Referenčna oznaka
ICS 93.080.20 SIST EN 13108-6:2006 (sl)
Nadaljevanje na straneh II in od 1 do 24
© 2010-11. Standard je založil in izdal Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST EN 13108-6 : 2006
NACIONALNI UVOD
Standard SIST EN 13108-6 (sl), Bitumenske zmesi – Specifikacije materialov – 6. del: Liti asfalt, 2006,
ima status slovenskega standarda in je enakovreden evropskemu standardu EN 13108-6 (en, de, fr),
Bituminous mixtures – Material specifications – Part 6: Mastic Asphalt, 2006.
NACIONALNI PREDGOVOR
Evropski standard EN 13108-6:2006 je pripravil tehnični odbor Evropskega komiteja za
standardizacijo CEN/TC 227 Materiali za ceste. Slovenski standard SIST EN 13108-6:2006 je prevod
evropskega standarda EN 13108-6:2006. V primeru spora glede besedila slovenskega prevoda v tem
standardu je odločilen izvirni evropski standard v enem izmed treh uradnih jezikov CEN. Slovensko
izdajo standarda je pripravil tehnični odbor SIST/TC CES Ceste.
Odločitev za izdajo tega standarda je dne 7. junija 2006 sprejel SIST/TC CES Ceste.
OSNOVA ZA IZDAJO STANDARDA
– privzem standarda EN 13108-6:2006
OPOMBE
– Povsod, kjer se v besedilu standarda uporablja izraz “evropski standard”, v SIST EN 13108-
6:2006 to pomeni “slovenski standard”.
– Uvod in nacionalni predgovor nista sestavni del standarda.
– Ta nacionalni dokument je istoveten EN 13108-6:2006 in je objavljen z dovoljenjem
CEN
Management Centre
Avenue Marnix 17
B-1000 Bruselj
This national document is identical with EN 13108-6:2006 and is published with the permission of
CEN
Management Centre
Avenue Marnix 17
B-1000 Brussels
II
---------------------- Page: 2 ----------------------
EVROPSKI STANDARD EN 13108-6
EUROPEAN STANDARD
NORME EUROPÉENNE
EUROPÄISCHE NORM maj 2006
ICS 93.080.20
Slovenska izdaja
Bitumenske zmesi – Specifikacije materialov – 6. del: Liti asfalt
Bituminous mixtures – Material Mélanges bitumineux – Spécification Asphaltmischgut –
specifications – Part 6: Mastic des matériaux – Partie 6: Asphalte Mischgutanforderungen –
Asphalt coulé routier Teil 6: Gussasphalt
Ta evropski standard je CEN sprejel 12. oktobra 2005.
Člani CEN morajo izpolnjevati notranje predpise CEN/CENELEC, ki določajo pogoje, pod katerimi
dobi ta standard status nacionalnega standarda brez kakršnihkoli sprememb. Seznami najnovejših
izdaj teh nacionalnih standardov in njihovi bibliografski podatki so na voljo pri Centralnem sekretariatu
ali članih CEN.
Ta evropski standard obstaja v treh uradnih izdajah (angleški, francoski in nemški). Izdaje v drugih
jezikih, ki jih člani CEN na lastno odgovornost prevedejo in izdajo ter prijavijo pri Centralnem
sekretariatu CEN, veljajo kot uradne izdaje.
Člani CEN so nacionalni organi za standarde Avstrije, Belgije, Cipra, Češke republike, Danske, Estonije,
Finske, Francije, Grčije, Islandije, Irske, Italije, Latvije, Litve, Luksemburga, Madžarske, Malte, Nemčije,
Nizozemske, Norveške, Poljske, Portugalske, Romunije, Slovaške, Slovenije, Španije, Švedske, Švice in
Združenega kraljestva.
CEN
Evropski komite za standardizacijo
European Committee for Standardisation
Comité Européen de Normalisation
Europäisches Komitee für Normung
Centralni sekretariat: rue de Stassart, B-1050 Bruselj
© 2006 Lastnice avtorskih pravic so vse države članice CEN Ref. oznaka EN 13108-6:2006 E
---------------------- Page: 3 ----------------------
SIST EN 13108-6 : 2006
VSEBINA Stran
Predgovor .4
Uvod .5
1 Področje uporabe .6
2 Zveze s standardi .6
3 Izrazi in definicije, simboli in kratice .7
3.1 Izrazi in definicije .7
3.2 Simboli in kratice .8
4 Zahteve za sestavne materiale .8
4.1 Splošno.8
4.2 Vezivo.8
4.2.1 Splošno.8
4.2.2 Izbor veziva .8
4.2.3 Obrabne plasti s ponovno uporabljenim asfaltom.9
4.3 Zmesi kamnitih zrn .9
4.3.1 Grobe zmesi kamnitih zrn.9
4.3.2 Fine zmesi kamnitih zrn.9
4.3.3 Združene zrnavosti zmesi kamnitih zrn.9
4.3.4 Dodano polnilo.9
4.4 Ponovno uporabljeni asfalt .9
4.5 Dodatki .10
5 Zahteve za zmes .10
5.1 Splošno.10
5.2 Sestava, zrnavost, delež veziva in dodatki .10
5.2.1 Sestava.10
5.2.2 Zrnavost.10
5.2.3 Delež veziva .11
5.2.4 Dodatki .12
5.3 Obvitost in homogenost.12
5.4 Odpornost proti obrabi z ježevkami.12
5.5 Odziv na ogenj.12
5.6 Odpornost proti gorivu pri uporabi na letališčih.13
5.7 Odpornost proti sredstvu za odmrzovanje za uporabo na letališčih .13
5.8 Temperatura zmesi.13
5.9 Globina vtisa (odpornost proti trajnemu preoblikovanju).13
5.10 Trajnost.15
6 Vrednotenje skladnosti .15
7 Identifikacija.15
Dodatek A (normativni): Izračun penetracije ali točke zmehčišča veziva v zmesi ob ponovni
uporabi asfalta .17
2
---------------------- Page: 4 ----------------------
SIST EN 13108-6 : 2006
A.1 Splošno .17
A.2 Izračun penetracije veziva v zmesi .17
A.3 Izračun točke zmehčišča veziva v zmesi .17
Dodatek ZA (informativni): Točke tega evropskega standarda v zvezi z določili Direktive EU
o gradbenih proizvodih.18
ZA.1 Področje uporabe in ustrezne lastnosti.18
ZA.2 Postopek(-i) za potrjevanje skladnosti litega asfalta.20
ZA.3 CE-označevanje in etiketiranje .22
3
---------------------- Page: 5 ----------------------
SIST EN 13108-6 : 2006
Predgovor
Ta evropski standard (EN 13108-6: 2006) je pripravil tehnični odbor CEN/TC 227 Materiali za ceste,
katerega tajništvo vodi DIN.
Ta evropski standard mora dobiti status nacionalnega standarda bodisi z objavo istovetnega besedila
ali z razglasitvijo najpozneje do novembra 2006, nacionalni standardi, ki so z njim v nasprotju, pa
morajo biti razveljavljeni najpozneje do januarja 2008.
Ta evropski standard je bil pripravljen v okviru mandata, ki sta ga CEN dala Evropska komisija in
Evropsko združenje za prosto trgovino (EFTA), in podpira bistvene zahteve direktive (direktiv)
Evropske unije.
Za zveze z direktivo(-ami) EU glej informativni dodatek ZA, ki je sestavni del tega evropskega standarda.
Ta evropski standard je eden iz skupine standardov, ki so našteti spodaj:
EN 13108-1 Bitumenske zmesi – Specifikacije materialov – 1. del: Bitumenski beton
EN 13108-2 Bitumenske zmesi – Specifikacije materialov – 2. del: Bitumenski beton za zelo tanke
plasti
EN 13108-3 Bitumenske zmesi – Specifikacije materialov – 3. del: Zelo mehak asfalt
EN 13108-4 Bitumenske zmesi – Specifikacije materialov – 4. del: Vroče valjani asfalt
EN 13108-5 Bitumenske zmesi – Specifikacije materialov – 5. del: Drobir z bitumenskim
mastiksom
EN 13108-6 Bitumenske zmesi – Specifikacije materialov – 6. del: Liti asfalt
EN 13108-7 Bitumenske zmesi – Specifikacije materialov – 7. del: Drenažni asfalt
EN 13108-8 Bitumenske zmesi – Specifikacije materialov – 8. del: Ponovno uporabljeni asfalt
EN 13108-20 Bitumenske zmesi – Specifikacije materialov – 20. del: Tipski preskus
EN 13108-21 Bitumenske zmesi – Specifikacije materialov – 21. del: Kontrola proizvodnje v obratu
Ta standard ne nadomešča nobenega obstoječega evropskega standarda.
Po notranjih predpisih CEN/CENELEC so dolžne ta evropski standard privzeti nacionalne organizacije za
standarde naslednjih držav Avstrije, Belgije, Cipra, Češke republike, Danske, Estonije, Finske, Francije,
Grčije, Islandije, Irske, Italije, Latvije, Litve, Luksemburga, Madžarske, Malte, Nemčije, Nizozemske,
Norveške, Poljske, Portugalske, Romunije, Slovaške, Slovenije, Španije, Švedske, Švice in Združenega
kraljestva.
4
---------------------- Page: 6 ----------------------
SIST EN 13108-6 : 2006
Uvod
Končni cilj je določiti zahtevane temeljne lastnosti bitumenskih zmesi. Vendar, ker so bile specifikacije
za liti asfalt tradicionalno zasnovane izkustveno na obstoječih recepturah ter kombinirane z zahtevami
za sestavne materiale z dodatnimi zahtevami, ki temeljijo na izvajanju preskusov, povezanih z
obnašanjem, in ker ni na voljo dovolj izkušenj, pridobljenih s temeljnim preskušanjem litega asfalta, ta
evropski standard trenutno določa le izkustvene zahteve.
Liti asfalt se uporablja za obrabne plasti, lahko pa tudi za vezne plasti. Liti asfalt se uporablja tudi za
zaščitne plasti in vmesne plasti na mostovih, v predorih in na neravninah.
OPOMBA: Liti asfalt, namenjen za tesnitev konstrukcij in na področju gradbeništva, je opredeljen v CEN/TC 314 Liti asfalt
za tesnitev.
5
---------------------- Page: 7 ----------------------
SIST EN 13108-6 : 2006
1 Področje uporabe
Ta evropski standard določa zahteve za skupino zmesi litih asfaltov za uporabo na cestah, letališčih in
drugih prometnih površinah.
OPOMBA: Določila za zmesi, ki izhajajo iz tega evropskega standarda, se lahko upoštevajo pri oblikovanju izjave o
skladnosti zmesi s poznanimi zahtevami ali pa samo za obveščanje o teh zahtevah.
Ta evropski standard vključuje zahteve za izbiro sestavnih materialov. Zasnovan je tako, da se
uporablja skupaj s standardoma EN 13108-20 in EN 13108-21.
Zmesi litega asfalta s kemično modificiranimi vezivi, ki niso predmet standarda EN 14023, niso
predmet tega evropskega standarda.
2 Zveze s standardi
Pri uporabi tega evropskega standarda so nujno potrebni naslednji referenčni dokumenti. Pri datiranih
sklicevanjih velja le navedena izdaja. Pri nedatiranih sklicevanjih velja zadnja izdaja referenčnega
dokumenta (skupaj z dopolnili).
EN 1097-6 Preskusi mehanskih in fizikalnih lastnosti agregatov – 6. del: Določevanje
prostorninske mase zrn in vpijanja vode
EN 1426 Bitumen in bitumenska veziva – Določanje penetracije z iglo
EN 1427 Bitumen in bitumenska veziva – Določanje zmehčišča – Metoda prstana in kroglice
EN 12591 Bitumen in bitumenska veziva – Specifikacije za cestogradbene bitumne
EN 12697-3 Bitumenske zmesi – Preskusne metode za vroče asfaltne zmesi – 3. del:
Ugotavljanje vsebnosti veziva: rotacijski uparjalnik
EN 12697-4 Bitumenske zmesi – Preskusne metode za vroče asfaltne zmesi – 4. del:
Ugotavljanje vsebnosti veziva: kolonska frakcionirana destilacija
EN 12697-13 Bitumenske zmesi – Preskusne metode za vroče asfaltne zmesi – 13. del: Merjenje
temperature
EN 13043 Agregati za bitumenske zmesi in površinske prevleke za ceste, letališča in druge
prometne površine
EN 13108-4 Bitumenske zmesi – Specifikacije materialov – 4. poglavje: Vroče valjani asfalt
EN 13108-8 Bitumenske zmesi – Specifikacije materialov – 8. del: Ponovno uporabljen asfalt
EN 13108-20 Bitumenske zmesi – Specifikacije materialov – 20. poglavje: Tipski preskus
EN 13108-21 Bitumenske zmesi – Specifikacije materialov – 21. poglavje: Kontrola proizvodnje v
obratu
EN 13501-1 Požarna klasifikacija gradbenih proizvodov in elementov stavb – 1. del: Klasifikacija
po podatkih iz preskusov odziva na ogenj
prEN 13924 Bitumen in bitumenska veziva – Specifikacije za trše cestogradbene bitumne
EN 14023 Bitumen in bitumenska veziva – Okvirna specifikacija za bitumne, modificirane s
polimeri
6
---------------------- Page: 8 ----------------------
SIST EN 13108-6 : 2006
3 Izrazi in definicije, simboli in kratice
3.1 Izrazi in definicije
V tem evropskem standardu imajo uporabljeni izrazi in definicije naslednji pomen:
3.1.1
voziščna konstrukcija (ang. pavement)
gradnja, sestavljena iz ene ali več plasti, namenjena odvijanju prometa prek terena
3.1.2
sloj (ang. layer)
element voziščne konstrukcije, vgrajen v posameznem postopku
3.1.3
plast (ang. course)
konstrukcijski element voziščne konstrukcije iz enega materiala. Plast je lahko izdelana iz enega ali
več slojev
3.1.4
obrabna plast (ang. surface course)
vrhnja plast voziščne konstrukcije, ki je v neposrednem stiku s prometom
3.1.5
vezna plast (ang. binder course)
del voziščne konstrukcije med nosilno in obrabno plastjo
3.1.6
izravnalna plast (ang. regulating course)
plast različne debeline, vgrajena na obstoječo plast za zagotavljanje potrebnega profila za naslednjo
plast enakomerne debeline
3.1.7
nosilna plast (ang. base)
glavni konstrukcijski element voziščne konstrukcije. Nosilna plast je lahko vgrajena v eni ali več
plasteh, kot zgornja ali spodnja nosilna plast itd.
3.1.8
liti asfalt (ang. Mastic Asphalt)
asfaltna zmes brez votlin z bitumnom kot vezivom, v kateri prostornina polnila in veziva presega
prostornino preostalih votlin v zmesi
3.1.9
sestava asfaltne zmesi (ang. mix formulation)
sestava asfaltne zmesi, izražena kot ciljna sestava
OPOMBA: Ciljna sestava je lahko izražena na dva načina (glej 3.1.10 in 3.1.11).
3.1.10
vhodna ciljna sestava (ang. input target composition)
izraz za sestavo asfaltne zmesi s podatki o sestavnih materialih, sejalni krivulji zmesi kamnitih zrn in
deležu bitumna, dodanega zmesi
OPOMBA To je običajno rezultat laboratorijskega načrtovanja in ovrednotenja asfaltne zmesi.
7
---------------------- Page: 9 ----------------------
SIST EN 13108-6 : 2006
3.1.11
izhodna ciljna sestava (ang. output target composition)
izraz za sestavo asfaltne zmesi s podatki o sestavnih materialih, povprečni sejalni krivulji zmesi
kamnitih zrn in deležu topnega bitumna, dobljenimi z analizo v laboratoriju
OPOMBA: To je ponavadi rezultat ovrednotenja proizvodnje.
3.1.12
dodatek (ang. additive)
sestavni material, ki je lahko dodan zmesi v manjši količini, npr. anorganska ali organska vlakna ali
polimeri za izboljšanje mehanskih lastnosti, obdelavnosti ali barve asfaltne zmesi
3.2 Simboli in kratice
MA (LA) liti asfalt (Mastic Asphalt)
D nazivna velikost zrn v kamniti zmesi, v milimetrih (mm)
4 Zahteve za sestavne materiale
4.1 Splošno
Uporabljati je treba samo sestavne materiale z ugotovljeno ustreznostjo.
Ustreznost je treba ugotoviti na podlagi enega ali več naslednjih dokumentov:
– evropskega standarda,
– evropskega tehničnega soglasja,
– določil za materiale, ki temeljijo na dokazljivi zgodovini zadovoljive uporabe v proizvodnji asfaltnih
zmesi v preteklosti. Ustreznost materialov mora biti dokazana. Dokazi so lahko osnovani na
raziskavah, združenih z dokazi iz prakse.
OPOMBA: V evropski asfaltni proizvodnji je običajna praksa uporaba dodatkov, kot so anorganska ali organska vlakna,
barvila, voski itd., ki jih evropski standardi ali evropska tehnična soglasja ne obravnavajo. Ta evropski standard
dopušča uporabo teh materialov.
4.2 Vezivo
4.2.1 Splošno
Kot vezivo je treba uporabljati cestogradbeni bitumen, modificirani bitumen ali trdi bitumen.
Cestogradbeni bitumen mora biti skladen s standardom EN 12591, modificirani bitumen s standardom
EN 14023 in trdi bitumen s standardom EN 13924.
Dodaja se lahko naravni asfalt, ki je skladen s standardom EN 13108-4:2005, dodatek B.
4.2.2 Izbor veziva
Vrsta cestogradbenega bitumna, tip in vrsta modificiranega bitumna, vrsta trdega bitumna ter količina
in kategorija naravnega asfalta morajo biti, kot so določeni.
V primeru uporabe cestogradbenega bitumna je treba izbrati med vrstami 20/30 do vključno 70/100 in
v primeru trdega bitumna med vrstama 10/20 in 15/25.
OPOMBA 1: Pri izbiri veziv v posameznih regijah je treba upoštevati raznolikost podnebja, prometnih obremenitev,
uporabljenih materialov itd.
Če se za izboljšanje lastnosti, ki niso obravnavane z izkustvenimi določili, uporabi modificirani
bitumen, je treba zagotoviti dodatne dokaze. Takšen dokaz mora temeljiti na preskusih po standardih
8
---------------------- Page: 10 ----------------------
SIST EN 13108-6 : 2006
skupine EN 12697, ki potrdijo, da je modificirani bitumen primeren za izboljšavo želenih funkcionalnih
lastnosti. Dokaz lahko temelji na predhodnem raziskovanju.
OPOMBA 2: Sistem razvrščanja v standardu EN 14023 je namenjen samo za okarakterizacijo modificiranega bitumna.
Določila za modificirani bitumen niso funkcionalno osnovana in jih ni mogoče kombinirati z izkustvenimi določili
za asfaltne zmesi za predstavitev funkcionalnega obnašanja. Zahtevani dokaz bi bil ponavadi tipski preskus
podobne zmesi, ki vsebuje modificirani bitumen, s prikazom izpolnjevanja relevantne lastnosti. Vrsto bitumna,
tip in vrsto modificiranega bitumna ter količino in kategorijo naravnega asfalta je mogoče izbrati.
4.2.3 Obrabne plasti s ponovno uporabljenim asfaltom
Če je v masi celotne zmesi več kot 10 % mase ponovno uporabljenega asfalta vzetih iz zmesi, v katerih je
bil uporabljen samo cestogradbeni bitumen, in če je kot vezivo dodana zmesi določena vrsta
cestogradbenega bitumna, mora vezivo ustrezati naslednji zahtevi:
– penetracija ali točka zmehčišča veziva v dobljeni zmesi, izračunani iz penetracije ali točke
zmehčišča dodanega veziva in veziva iz ponovno uporabljenega asfalta, morata izpolnjevati
zahteve za penetracijo ali točko zmehčišča izbrane vrste. Izračun je treba izpeljati skladno z
dodatkom A. Zahtevo za penetracijo ali za točko zmehčišča je treba izbrati.
4.3 Zmesi kamnitih zrn
4.3.1 Grobe zmesi kamnitih zrn
Grobe zmesi kamnitih zrn morajo ustrezati standardu EN 13043, kot je primerno za namen uporabe.
4.3.2 Fine zmesi kamnitih zrn
Fine zmesi kamnitih zrn morajo ustrezati standardu EN 13043, kot je primerno za namen uporabe.
4.3.3 Združene zrnavosti zmesi kamnitih zrn
Združene zrnavosti zmesi kamnitih zrn morajo ustrezati standardu EN 13043, kot je primerno za
namen uporabe.
4.3.4 Dodano polnilo
Dodano polnilo mora ustrezati standardu EN 13043, kot je primerno za namen uporabe. Količina
dodanega polnila mora biti, kot je določeno.
OPOMBA 1: Polnilo vključuje materiale, kot sta cement in hidratizirano apno.
OPOMBA 2: Izraz "kot je primerno za namen uporabe" v točkah od 4.3.1 do 4.3.4 pomeni, da je izbor zahtev in posebnih
kategorij odvisen od številnih pogojev. Ti pogoji vključujejo gostoto prometa, podnebne pogoje, konstrukcijo
plasti, v kateri bo zmes uporabljena, in ekonomsko proučitev.
4.4 Ponovno uporabljeni asfalt
Uporaba in količina ponovno uporabljenega asfalta in vrsta izvorne asfaltne zmesi, iz katere je ali bo
le-ta vzet, morajo biti, kot so določene.
Lastnosti ponovno uporabljenega asfalta, navedene v skladu s standardom EN 13108-8, morajo
ustrezati zahtevam, primernim za namen uporabe.
OPOMBA: Izraz "kot je primerno za namen uporabe" pomeni, da je izbor zahtev in posebnih kategorij odvisen od številnih
pogojev. Ti pogoji vključujejo gostoto prometa, podnebne pogoje, konstrukcijo plasti, v kateri bo zmes
uporabljena, in ekonomsko proučitev.
Nazivna velikost zrna D zmesi kamnitih zrn v ponovno uporabljenem asfaltu ne sme presegati nazivne
velikosti zrna D asfaltne zmesi. Lastnosti zmesi kamnitih zrn ponovno uporabljenega asfalta morajo
izpolnjevati zahteve za lastnosti zmesi kamnitih zrn za asfaltno zmes.
9
---------------------- Page: 11 ----------------------
SIST EN 13108-6 : 2006
4.5 Dodatki
Vrsta in lastnosti vseh dodatkov morajo biti navedene in morajo ustrezati zahtevam iz točke 4.1.
5 Zahteve za zmes
5.1 Splošno
Sestava zmesi mora biti opredeljena in dokumentirana.
Ciljna sestava zmesi mora biti v skladu z izbranimi zahtevami.
Pri uporabi ponovno uporabljenega asfalta iz zmesi, v katerih je bil uporabljen modificirani bitumen
in/ali dodatek za modificiranje, in/ali iz zmesi, ki sama vsebuje modificirani bitumen ali modifikator,
količina ponovno uporabljenega asfalta za obrabne plasti ne sme presegati 10 % mase celotne zmesi,
razen če se proizvajalec in naročnik nista dogovorila drugače. Kakršenkoli dogovor med naročnikom in
proizvajalcem ne sme biti v nasprotju z nacionalno predpisanimi zahtevami.
5.2 Sestava, zrnavost, delež veziva in dodatki
5.2.1 Sestava
Zrnavost ciljne sestave mora biti v skladu s točko 5.2.2.
Delež veziva ciljne sestave mora biti v skladu s točko 5.2.3.
Delež dodatkov ciljne sestave mora biti v skladu s točko 5.2.4.
Zrnavost mora biti določena v odstotkih mase glede na celotno maso zmesi kamnitih zrn z uporabo sit,
ki pripadajo ali osnovnemu stavku sit plus stavku 1 ali osnovnemu stavku sit plus stavku 2, v skladu s
standardom EN 13043. Delež veziva in dodatkov mora biti naveden v odstotkih mase celotne zmesi.
Odstotki presejkov, ki gredo skozi sita, z izjemo sita 0,063 mm, morajo biti navedeni s točnostjo 1 %,
delež veziva, odstotek presejka, ki gre skozi sito 0,063 mm, in delež vsakega dodatka pa morajo biti
navedeni s točnostjo 0,1 %.
5.2.2 Zrnavost
Zahteve za zrnavost morajo biti izražene z največjimi in najmanjšimi vrednostmi odstotkov presejkov,
ki gredo skozi sita 1,4 D, D, 2 mm, karakteristično grobo sito in sito 0,063 mm. Kombiniranje sit iz
stavkov sit 1 in 2 ni dovoljeno.
Zahteve za zrnavost ciljne sestave morajo biti izražene v odstotkih mase med največjimi in
najmanjšimi vrednostmi odstotkov presejkov, ki gredo skozi sita 1,4 D, D, 2 mm in 0,063 mm.
Dodatno zahteve za območje zrnavosti lahko vključujejo odstotke presejkov, ki gredo skozi eno
neobvezno sito med D in 2 mm ter eno neobvezno fino sito med 2 mm in 0,063 mm.
Ciljna sestava zmesi mora biti v okviru navedenega območja zrnavosti.
Sita z velikostjo odprtin D in med D in 2 mm morajo biti izbrana izmed naslednjih sit:
– osnovni stavek sit plus stavek 1: 4 mm; 5,6 mm; 8 mm; 11,2 mm; 16 mm;
– osnovni stavek sit plus stavek 2: 4 mm; 6,3 mm; 8 mm; 10 mm; 12,5 mm; 14 mm; 16 mm.
Neobvezno fino sito mora biti izbrano izmed sit: 1 mm; 0,5 mm; 0,25 mm in 0,125 mm.
V preglednicah 1 in 2 so določene mejne vrednosti zrnavosti za liti asfalt.
10
---------------------- Page: 12 ----------------------
SIST EN 13108-6 : 2006
Preglednica 1: Mejne vrednosti ciljne sestave – osnovni stavek sit plus stavek 1
D 4 5(5,6) 8 11(11,2) 16
Sito Presejki skozi sita
mm % mase
a
1,4 D 100 100 100 100 100
D 90–100 90–100 90–100 90–100 90–100
2 50–80 45–70 45–70 40–70 35–60
18,0–35,0 18,0–28,0
0,063 20,0–45,0 20,0–40,0 20,0–40,0
a
Če izračunano sito 1,4 D ni točno število iz standardov skupine ISO 565/R20, mora biti privzeto naslednje najbližje sito v
stavku.
Preglednica 2: Mejne vrednosti ciljne sestave – osnovni stavek sit plus stavek 2
D 4 6(6,3) 8 10 12(12,5) 14 16
Sito
Presejki skozi sita
mm
% mase
a
1,4 D 100 100 100 100 100 100 100
D 90–100 90–100 90–100 90–100 90–100 90–100 90–100
2 50–80 45–70 45–70 40–70 40–70 35–55 35–55
0,063 20,0–45,0 20,0–40,0 20,0–40,0 18,0–35,0 18,0–35,0 18,0–28,0 18,0–28,0
a
Če izračunano sito 1,4 D ni točno število v osnovnem stavku plus stavku 2, mora biti privzeto naslednje najbližje sito v
stavku.
V preglednici 3 je določena širina zahtevanega območja zrnavosti. Iz območij med najmanjšimi in
največjimi vrednostmi območja zrnavosti je treba izbrati posamezne vrednosti (vključno z obema
mejnima vrednostma) iz preglednice 3.
Preglednica 3: Zrnavost ciljne sestave – območja med največjimi in najmanjšimi vrednostmi za
izbrano območje zrnavosti
Območja
Sito
% mase
mm
Najožje območje Najširše območje
Karakteristično grobo sito 10 25
Neobvezno sito med D in 2 10 25
2 5 15
Karakteristično fino sito 4 15
0,063 2,0 8,0
5.2.3 Delež veziva
Najmanjši delež veziva v ciljni sestavi mora biti izbran iz kategorij, navedenih v preglednici 4. Zahteve
za delež veziva je treba korigirati z množenjem s faktorjem
2,650
α =
ρ
d
kjer je
3
ρ = gostota zmesi kamnitih zrn v megagramih na kubični meter (Mg/m ), določena v skladu s
d
standardom EN 1097-6
OPOMBA: Delež veziva vključuje vezivo v ponovno uporabljenem asfaltu in naravnem asfaltu, če je bil uporabljen.
11
---------------------- Page: 13 ----------------------
SIST EN 13108-6 : 2006
Preglednica 4: Najmanjši delež veziva, B
min
Najmanjši delež veziva Kategorija
% B
min
6,0 B
min6,0
6,2 B
min6,2
6,5 B
min6,5
6,8 B
min6,8
B
7,0
min7,0
7,5 B
min7,5
8,0 B
min8,0
8,5 B
min8,5
9,0 B
min9,0
9,5 B
min9,5
5.2.4 Dodatki
Zahteve za dodatke je treba izraziti z navedbo vrste in količine vsake dodatne sestavine.
5.3 Obvitost in homogenost
Po praznjenju iz mešalnika mora biti material po videzu homogen, kamnita zrna morajo biti popolnoma
ob
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.