ASTM D5139-90(1996)
(Specification)Standard Specification for Sample Preparation for Qualification Testing of Coatings to be Used in Nuclear Power Plants
Standard Specification for Sample Preparation for Qualification Testing of Coatings to be Used in Nuclear Power Plants
SCOPE
1.1 This specification defines the size composition and surface preparation requirements for test samples used to evaluate coatings according to the following ASTM test procedures.
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Designation: D 5139 – 90 (Reapproved 1996)
AMERICAN SOCIETY FOR TESTING AND MATERIALS
100 Barr Harbor Dr., West Conshohocken, PA 19428
Reprinted from the Annual Book of ASTM Standards. Copyright ASTM
Standard Specification for
Sample Preparation for Qualification Testing of Coatings to
be Used in Nuclear Power Plants
This standard is issued under the fixed designation D 5139; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope D 4259 Practice for Abrading Concrete
D 4260 Practice for Acid Etching Concrete
1.1 This specification defines the size composition and
D 4541 Test Method for Pull-Off Strength of Coatings
surface preparation requirements for test samples used to
Using Portable Adhesion Testers
evaluate coatings according to the following ASTM test
2.2 Other Standards:
procedures.
American Concrete Institute, ACI 301 Specifications for
1.2 The values stated in inch-pound units are to be regarded
Structural Concrete for Buildings
as the standard. The values given in parentheses are for
SSPC-SP-1, 2, 3, 5, 6, 7, 10, or 11
information only.
3. Significance and Use
2. Referenced Documents
3.1 This specification provide uniform requirements for the
2.1 ASTM Standards:
preparation of test samples used for qualification testing of
A 36 Specification for Carbon Structural Steel
3 coatings used in nuclear power plant construction and mainte-
C 33 Specification for Concrete Aggregates
nance.
C 150 Specification for Portland Cement
C 192 Practice for Making and Curing Concrete Test Speci-
4. Steel Samples
mens in the Laboratory
4.1 Sample size shall be a minimum of 2-in. wide by 4-in.
C 260 Specification for Air-Entraining Admixtures for Con-
3 long by ⁄8-in. thick (50.8-mm wide by 101.6-mm long by
crete
3 3.175-mm thick). Edges and corners may be rounded. A ⁄4 in.
C 494 Specification for Chemical Admixtures for Concrete
diameter hole suitably located may be in the test panel as
C 618 Specification for Coal Fly Ash and Raw or Calcined
appropriate for the test samples in Test Methods D 3911,
Natural Pozzolan for Use as a Mineral Admixture in
3 D 3912, D 4082 and D 4256.
Portland Cement Concrete
4.1.1 For Test Method D 4541 the minimum size shall be
D 3911 Test Method for Evaluating Coatings Used in Light-
3-in. wide by 5 in.-long by ⁄4 in.-thick (76.2-mm wide by
Water Nuclear Power Plants at Simulated Design Basis
127-mm long by 6.35-mm thick).
Accident (DBA) Conditions
4.2 All panels should be carbon steel, meeting the require-
D 3912 Test Method for Chemical Resistance of Coatings
ments of Specification A 36.
Used in Light-Water Nuclear Power Plants
4.3 Surface preparation shall be in accordance with
D 4060 Test Method for Abrasion Resistance of Organic
6 SSPC-SP 10 for qualification testing. Other surface preparation
Coatings by the Taber Abraser
as required by the project or specific conditions may be used
D 4082 Test Method for Effects of Radiation on Coatings
5 when testing for evaluation over surfaces other than SSPC-SP
Used in Light-Water Nuclear Power Plants
10, such as SSPC-SP 1, 2, 3, 5, 6, 7, or 11.
D 4256 Test Method for Determination of the Decontamin-
ability of Coatings Used in Light-Water Nuclear Power
5. Concrete Blocks
Plants
5 5.1 Applicable to Test Methods D 3911, D 3912, D 4082,
D 4258 Practice for Surface Cleaning Concrete for Coating
D 4256 and D 4541. The minimum size shall be 2-in. by 2-in.
deep by 4-in. long (50.8-mm by 50.8-mm deep by 101.6-mm
long). The edges may be chamfered up to ⁄4 in. (6.35 mm)
This specification is under the jurisdiction of ASTM Committee D-33 on
maximum.
Protective Coating and Lining Work for Power Generation Facilities and is the direct
responsibility of Subcommittee D33.02 on Service and Material Parameters. 5.2 Composition shall be as follows:
Current edition approved Dec. 12, 1990. Published January 1991.
Annual Book of ASTM Standards, Vol 01.04.
3 7
Annual Book of ASTM Standards, Vol 04.02. Available from American Concrete Institute, P.O. Box 19150, Detroit, MI
Annual Book of ASTM Standards, Vol 04.01. 48219.
5 8
Annual Book of ASTM Standards, Vol 06.02. Surface Preparation Standards are available from Steel Structures Painting
Annual Book of ASTM Standards, Vol 06.01. Council, 4400 5th Ave., Pittsburg, PA 15213-2683.
D 5139
6. Miscellaneous Materials
Cement Specification C 150, Type II 7 sacks/yd
Gravel Specification C 33, size ⁄8 in. 45 % by volume
6.1 Follow 4.1 and 4.3 for metallic materials such as
Sand Specification C 33 55 % by volume
Air-entraining Specification C 260 As recommended
aluminum, galvanized steel, and other metals.
admixture 4to7%
6.2 Follow 5.1 and 5.3 for castable materials such as grout,
Water-red
...