ASTM D5213-12
(Specification)Standard Specification for Polymeric Resin Film for Electrical Insulation and Dielectric Applications
Standard Specification for Polymeric Resin Film for Electrical Insulation and Dielectric Applications
ABSTRACT
This specification establishes the requirements for the material, dimensions and tolerances, and property values of polymeric resin films, in sheet or strip form, for use in electrical insulation and dielectric applications. Type I are flexible unsupported films for general purpose, while Type II are heat-sealable coated on one (Grade 1) or both (Grade 2) sides. Materials covered here are (A) poly(N,N'-p,p'-oxydiphenylene pyromellitimide), (B) poly(N,N'-p,p'-oxydiphenylene biphenyltetracarboxylimide, (C) poly(N,N'-p-phenylene biphenyltetracarboxylimide), (D) FEP-fluorocarbon, (E) polyethylene terephthalate, (F) polyethylene naphthalate, and (G) polyetherimide. Individual materials class of films shall be tested and conform accordingly the following property values: tensile strength; elongation; shrinkage; moisture absorption; dielectric strength; volume resistivity; permittivity; and dissipation factor.
SCOPE
1.1 This specification covers requirements for the material, dimensions and tolerances, and property values of film, in sheet or strip form, with or without heat-sealable coatings.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. Note 1—This document is similar to IEC 60674, Part 3, Sheets 2, 4, 5, 6, and 7.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D5213 −12
Standard Specification for
Polymeric Resin Film for Electrical Insulation and Dielectric
1
Applications
This standard is issued under the fixed designation D5213; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope* 3. Terminology
3.1 Definitions—Definitions are in accordance with Termi-
1.1 This specification covers requirements for the material,
nologies D1711 and D883 unless otherwise specified.
dimensionsandtolerances,andpropertyvaluesoffilm,insheet
or strip form, with or without heat-sealable coatings.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 sheet, n—material greater than 75 mm in width.
1.2 The values stated in SI units are to be regarded as the
3.2.2 strip, n—material 75 mm or less in width.
standard. The values given in parentheses are for information
only.
4. Classification
NOTE 1—This document is similar to IEC 60674, Part 3, Sheets 2, 4, 5,
6, and 7. 4.1 This specification covers the following:
4.1.1 Type I—General purpose,
4.1.2 Type II—Heat sealable,
2. Referenced Documents
4.1.2.1 Grade 1—One side coated, and
2
2.1 ASTM Standards:
4.1.2.2 Grade 2—Two sides coated.
D149 Test Method for Dielectric Breakdown Voltage and
4.2 Materials:
DielectricStrengthofSolidElectricalInsulatingMaterials
4.2.1 Item A—Poly(N,N'-p,p'-oxydiphenylene
at Commercial Power Frequencies
pyromellitimide),
D883 Terminology Relating to Plastics
4.2.2 Item B—Poly(N,N'-p,p'-oxydiphenylene
D1711 Terminology Relating to Electrical Insulation
biphenyltetracarboxylimide,
D2305 Test Methods for Polymeric Films Used for Electri-
4.2.3 Item C—Poly(N,N'-p-phenylene
cal Insulation
biphenyltetracarboxylimide),
D3636 Practice for Sampling and Judging Quality of Solid
4.2.4 Item D—FEP-fluorocarbon, and
Electrical Insulating Materials
4.2.5 Item E—Polyethylene terephthalate.
D4088 Practice for Preparation for Shipment of Solid Elec-
3
4.2.6 Item F—Polyethylene naphthalate.
trical Insulating Materials (Withdrawn 2003)
4.2.7 Item G—Polyetherimide.
2.2 IEC Standards:
Publication 60674-3 Specification for Electrical Films for
5. Ordering Information
4
Electrical Purposes
5.1 Order the film covered by this specification stating the
type, grade, class, thickness, width, and roll dimensions.
1
This specification is under the jurisdiction of ASTM Committee D09 on
6. Materials
Electrical and Electronic Insulating Materials and is the direct responsibility of
Subcommittee D09.07 on Flexible and Rigid Insulating Materials.
6.1 Type I material is flexible, unsupported film.
Current edition approved Nov. 1, 2012. Published November 2012. Orginally
6.2 Type II material is film meeting all of the requirements
approved in 1991. Last previous edition approved in 2007 as D5213 – 07. DOI:
10.1520/D5213-12. of Type I, and having a heat-sealable coating on one or both
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
sides.
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
7. Requirements
the ASTM website.
3
The last approved version of this historical standard is referenced on
7.1 The film covered by this specification shall meet the
www.astm.org.
4
property requirements given in Tables 1-7 and Table 8 when
Available from American National Standards Institute (ANSI), 25 W. 43rd St.,
4th Floor, New York, NY 10036, http://www.ansi.org. tested by the methods given in Test Methods D2305.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D5213−12
TABLE 1 Property Values for Type I, Class A Film poly(N,N'-p-p'-oxydiphenylene pyromellitimide)
Average Property Value
Nominal Thickness, µm (mils)
7.5 (0.3) 13 (0.5) 20 (0.8) 25 (1.0) 50 (2.0) 75 (3.0) 100 (4.0) 130 (5.0)
Tensile strength, min MPa (psi), 69 97 138 138 138 138 138 138
machine direction and transverse (10 000) (14 000) (20 000) (20 000) (20 000) (20 000) (20 000) (20 000)
direction
Elongation, min percent, machine 10 20 35 35 40 45 45 45
and transverse direction
Shrinkage, max percent, after . . 0.30 0.30 0.35 0.35 0.35 0.35
exposure to 200 °C (392 F),
machine and transverse direction
Moisture absorption, max percent, 100 % RH 4.0 4.0 4.0 4.0 4.0 4.0 4.0 4.0
Dielectric strength, min kV/mm 120 120 180 180 150 140 100 100
A,B
(V/mil), 60 Hz (3000) (3000) (4500) (4500) (3
...
Designation: D5213 − 07 D5213 − 12 An American National Standard
Standard Specification for
Polymeric Resin Film for Electrical Insulation and Dielectric
1
Applications
This standard is issued under the fixed designation D5213; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon («) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope*
1.1 This specification covers requirements for the material, dimensions and tolerances, and property values of film, in sheet or
strip form, with or without heat-sealable coatings.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
NOTE 1—This document is similar to IEC 60674, Part 3, Sheets 2, 4, 5, 6, and 7.
2. Referenced Documents
2
2.1 ASTM Standards:
D149 Test Method for Dielectric Breakdown Voltage and Dielectric Strength of Solid Electrical Insulating Materials at
Commercial Power Frequencies
D883 Terminology Relating to Plastics
D1711 Terminology Relating to Electrical Insulation
D2305 Test Methods for Polymeric Films Used for Electrical Insulation
D3636 Practice for Sampling and Judging Quality of Solid Electrical Insulating Materials
3
D4088 Practice for Preparation for Shipment of Solid Electrical Insulating Materials (Withdrawn 2003)
2.2 IEC Standards:
4
Publication 60674-3 Specification for Electrical Films for Electrical Purposes
3. Terminology
3.1 Definitions—Definitions are in accordance with Terminologies D1711 and D883 unless otherwise specified.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 sheet, n—material greater than 75 mm in width.
3.2.2 strip, n—material 75 mm or less in width.
4. Classification
4.1 This specification covers the following:
4.1.1 Type I—General purpose,
4.1.2 Type II—Heat sealable,
4.1.2.1 Grade 1—One side coated, and
4.1.2.2 Grade 2—Two sides coated.
4.2 Materials:
4.2.1 Item A—Poly(N,N`-p,p`-oxydiphenylene pyromellitimide),
4.2.2 Item B—Poly(N,N`-p,p`-oxydiphenylene biphenyltetracarboxylimide,
4.2.3 Item C—Poly(N,N`-p-phenylene biphenyltetracarboxylimide),
4.2.4 Item D—FEP-fluorocarbon, and
4.2.5 Item E—Polyethylene terephthalate.
4.2.6 Item F—Polyethylene naphthalate.
4.2.7 Item G—Polyetherimide.
5. Ordering Information
5.1 Order the film covered by this specification stating the type, grade, class, thickness, width, and roll dimensions.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D5213 − 12
6. Materials
6.1 Type I material is flexible, unsupported film.
6.2 Type II material is film meeting all of the requirements of Type I, and having a heat-sealable coating on one or both sides.
7. Requirements
7.1 The film covered by this specification shall meet the property requirements given in Tables 1-7 and Table 8 when tested by
the methods given in Test Methods D2305.
7.1.1 Type II films, prior to coating, shall meet all of the requirements given in Table 1 for films of the thicknesses given in Table
9.
7.1.2 Type II films, after coating, shall meet all of the requirements given in Table 1 for elongation, before and after heating,
and for shrinkage as given in Table 1 for films of the thicknesses given in Table 9.
7.2 Roll Diameters:
7.2.1 The outside diameters of rolls of film shall not vary from the value specified on the purchase order by more than6 6 mm
(0.25 in.).
7.2.2 The inside diameters of cores of standard rolls of film shall not vary from the value specified on the purchase order by
more than 6 1.5 mm (0.060 in.).
7.3 The widths of film in rolls shall be within the following tolerances:
7.3.1 Twenty-five mm (1 in.) wide or less, 6 0.4 mm (0.015 in.).
7.3.2 Over 25 to 100 mm (over 1 to 4 in.), 6 0.8 mm (0.030 in.).
7.3.3 Over 100 mm (4 in.), 6 1.6 mm (0.062 in.).
7.4 The number of splices in standard rolls shall not exceed the values given in Table 10 for Type I film or Table 11 and Table
12 for Type II films.
7.5 The thicknesses shall be within the tolerances specified in Table 13 for Type I film or Table 3 for Type II film.
7.6 The color of the sheet or strip shall be uniform within a given lot, as determined by visual examination.
7.7 The film shall be uniform in appearance, as determined by visual examination. The film shall be clean and free from
contamination, wrinkles, holes, scratches, and other defects that might affect either appearance or serviceability. The heat-sealable
coating for Type II material shall be uniform in appearance.
1
This specification is under the jurisdiction of ASTM Committee D09 on Electrical and Electronic Insulating Materials and is the direct responsibility of Subcommitt
...
Questions, Comments and Discussion