ASTM D7376-10
(Practice)Standard Practice for Outdoor Evaluation of Wet Stack Storage Conditions on Coil-Coated Metals
Standard Practice for Outdoor Evaluation of Wet Stack Storage Conditions on Coil-Coated Metals
SIGNIFICANCE AND USE
This practice provides for periodic testing to compare the relative performance of specific coatings, substrates, and/or pretreatments used on coil-coated metal for resistance to wet conditions during storage.
When performed in south Florida, this practice gives accelerated corrosion and blistering results relative to other locations within the continental United States.
This practice allows comparison of different coatings, substrates, and pretreatments when they are tested at the same time. The results must be considered relative and do not indicate absolute performance.
Because the outdoor environment shows year-to-year climatological, seasonal, and geographic variation, the absolute amount of degradation based on corrosion and blistering may vary (see Practice G 7).
Temperature, rain, and humidity are important factors in wet stack corrosion. Corrosion and blistering will accelerate with increased temperature. The preferred test location is south of 27°N latitude in Florida. Other locations may be used, but differences in temperature and moisture must be considered, and the amount of corrosion and blistering are expected to vary considerably with climate. Test sites must have the instrumentation to measure and record ambient temperature and rainfall as in Practice G 7.
This practice is not meant to support the field storage of coil-coated metal in any way other than what is recommended by the manufacturer.
SCOPE
1.1 This procedure describes the practice for determining relative performance of coil-coated metal in an outdoor wet stack testing environment.
1.2 The purpose of this test is to evaluate relative wet stack corrosion resistance and blistering. Substrates, pretreatments, primers, topcoats, and backers may be evaluated.
1.3 This test simulates coil or stacked building panel bundle storage at a job site in wet outdoor conditions. The results from panels tested during the same time period may be used to compare products as an indicator of actual field performance. Environments with higher temperature and moisture levels accelerate degradation.
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information.
Designation:D7376–10
Standard Practice for
Outdoor Evaluation of Wet Stack Storage Conditions on
1
Coil-Coated Metals
This standard is issued under the fixed designation D7376; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope D714 Test Method for Evaluating Degree of Blistering of
Paints
1.1 This procedure describes the practice for determining
D1654 Test Method for Evaluation of Painted or Coated
relative performance of coil-coated metal in an outdoor wet
Specimens Subjected to Corrosive Environments
stack testing environment.
G7 Practice forAtmospheric Environmental Exposure Test-
1.2 The purpose of this test is to evaluate relative wet stack
ing of Nonmetallic Materials
corrosion resistance and blistering. Substrates, pretreatments,
primers, topcoats, and backers may be evaluated.
3. Summary of Practice
1.3 This test simulates coil or stacked building panel bundle
3.1 This practice is for the evaluation of relative wet stack
storage at a job site in wet outdoor conditions.The results from
corrosion resistance and blistering of coil-coated metal. The
panels tested during the same time period may be used to
test is to be conducted in an outdoor environment with
compare products as an indicator of actual field performance.
coil-coated panels placed on a flat surface while allowing
Environments with higher temperature and moisture levels
exposure to environmental conditions such as rain, dew,
accelerate degradation.
humidity, and high temperatures.
1.4 The values stated in SI units are to be regarded as the
3.2 Panels are evaluated periodically for corrosion and
standard. The values given in parentheses are for information
blistering as specified in 6.7.
only.
1.5 This standard does not purport to address all of the
4. Significance and Use
safety concerns, if any, associated with its use. It is the
4.1 This practice provides for periodic testing to compare
responsibility of the user of this standard to establish appro-
the relative performance of specific coatings, substrates, and/or
priate safety and health practices and determine the applica-
pretreatments used on coil-coated metal for resistance to wet
bility of regulatory limitations prior to use.
conditions during storage.
4.2 When performed in south Florida, this practice gives
2. Referenced Documents
2 accelerated corrosion and blistering results relative to other
2.1 ASTM Standards:
locations within the continental United States.
D610 Practice for Evaluating Degree of Rusting on Painted
4.3 This practice allows comparison of different coatings,
Steel Surfaces
substrates, and pretreatments when they are tested at the same
time. The results must be considered relative and do not
1
This practice is under the jurisdiction of ASTM Committee D01 on Paint and indicate absolute performance.
Related Coatings, Materials, and Applications and is the direct responsibility of
4.4 Because the outdoor environment shows year-to-year
Subcommittee D01.53 on Coil Coated Metal.
climatological,seasonal,andgeographicvariation,theabsolute
Current edition approved Feb. 1, 2010. Published February 2010. Originally
amount of degradation based on corrosion and blistering may
approved in 2007. Last previous edition approved in 2007 as D7376 - 07. DOI:
10.1520/D7376-10.
vary (see Practice G7).
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
4.5 Temperature, rain, and humidity are important factors in
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
wet stack corrosion. Corrosion and blistering will accelerate
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. with increased temperature. The preferred test location is south
Copyright ©ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA19428-2959, United States.
1
---------------------- Page: 1 ----------------------
D7376–10
of 27°N latitude in Florida. Other locations may be used, but 6.3 It is recommended that a minimum of two extra panels
differences in temperature and moisture must be considered, be placed at the top and bottom of the stack to act as a barrier
and the amount of corrosion and blistering are expected to vary to any influences from the wood or water accumulation.
considerably with climate. Test sites must have the instrumen- 6.4 The test panel numbers shall be recorded along with
tation to measure and record ambient temperature and rainfall information such as coater, paint code, substrate, primer,
as in Practice G7. pretreatment, and date of test initiation.
4.6 This practi
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:D7376–07 Designation: D7376 – 10
Standard Practice for
Outdoor Evaluation of Wet Stack Storage Conditions on
1
Coil-Coated Metals
This standard is issued under the fixed designation D7376; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope
1.1 This procedure describes the practice for determining relative performance of coil-coated metal in an outdoor wet stack
testing environment.
1.2 The purpose of this test is to evaluate relative wet stack corrosion resistance and blistering. Substrates, pretreatments,
primers, topcoats, and backers may be evaluated.
1.3 This test simulates coil or stacked building panel bundle storage at a job site in wet outdoor conditions. The results from
panels tested during the same time period may be used to compare products as an indicator of actual field performance.
Environments with higher temperature and moisture levels accelerate degradation.
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2
2.1 ASTM Standards:
D610 Practice for Evaluating Degree of Rusting on Painted Steel Surfaces
D714 Test Method for Evaluating Degree of Blistering of Paints
D1654 Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
G7 Practice for Atmospheric Environmental Exposure Testing of Nonmetallic Materials
3. Summary of Practice
3.1 This practice is for the evaluation of relative wet stack corrosion resistance and blistering of coil-coated metal. The test is
to be conducted in an outdoor environment with coil-coated panels placed on a flat surface while allowing exposure to
environmental conditions such as rain, dew, humidity, and high temperatures.
3.2 Panels are evaluated periodically for corrosion and blistering as specified in 6.7.
4. Significance and Use
4.1 This practice provides for periodic testing to compare the relative performance of specific coatings, substrates, and/or
pretreatments used on coil-coated metal for resistance to wet conditions during storage.
4.2 When performed in south Florida, this practice gives accelerated corrosion and blistering results relative to other locations
within the continental United States.
4.3 This practice allows comparison of different coatings, substrates, and pretreatments when they are tested at the same time.
The results must be considered relative and do not indicate absolute performance.
4.4 Because the outdoor environment shows year-to-year climatological, seasonal, and geographic variation, the absolute
amount of degradation based on corrosion and blistering may vary (see Practice G7).
4.5 Temperature, rain, and humidity are important factors in wet stack corrosion. Corrosion and blistering will accelerate with
increased temperature.The preferred test location is south of 27°N latitude in Florida. Other locations may be used, but differences
in temperature and moisture must be considered, and the amount of corrosion and blistering are expected to vary considerably with
1
This practice is under the jurisdiction of ASTM Committee D01 on Paint and Related Coatings, Materials, and Applications and is the direct responsibility of
Subcommittee D01.53 on Coil Coated Metal.
Current edition approved July 1, 2007. Published July 2007. DOI: 10.1520/D7376-07.
Current edition approved Feb. 1, 2010. Published February 2010. Originally approved in 2007. Last previous edition approved in 2007 as D7376 - 07. DOI:
10.1520/D7376-10.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book ofASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright ©ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA19428-2959, United States.
1
---------------------- Page: 1 ----------------------
D7376 – 10
climate. Test sites must have the instrumentation to measure and record ambient temperature
...
Questions, Comments and Discussion