Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors

Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors

ABSTRACT
This test method establishes the apparatuses required, the standard procedures, and associated calculations involved in the determination of relatively polar nonvolatile ultraviolet (UV) absorbing extractable components that may migrate from microwave susceptor packaging into food simulants, such as corn oil and Miglyol 812. This test method has been collaboratively studied using bilaminate susceptors constructed of paperboard, adhesive, and a layer of polyethylene terephthalate polymer (PETE) susceptor.
SCOPE
1.1 This test method covers the determination of nonpolar and relatively polar ultraviolet (UV) absorbing components that may migrate from microwave susceptor packaging into food simulants, such as corn oil and Miglyol 812.  
1.2 This test method has been collaboratively studied using bilaminate susceptors constructed of paperboard, adhesive, and a layer of polyethylene terephthalate polymer (PETE) susceptor. Adhesive and PETE related compounds were quantitated using this test method.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific warning statements are given in 4.3.2.3.

General Information

Status
Historical
Publication Date
31-Mar-2014
ICS
19.100 - Non-destructive testing
Technical Committee
F02 - Primary Barrier Packaging
Drafting Committee
F02.15 - Chemical/Safety Properties
Current Stage
Ref Project

Relations

Replaces
ASTM F1349-08 - Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors
Effective Date
01-Apr-2014
Replaced By
ASTM F1349-08(2019) - Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors
Effective Date
01-Mar-2019
Referred By
ASTM F1500-98(2019) - Standard Test Method for Quantitating Non-UV-Absorbing Nonvolatile Extractables from Microwave Susceptors Utilizing Solvents as Food Simulants
Effective Date
01-Apr-2014
Referred By
ASTM F874-98(2019) - Standard Test Method for Temperature Measurement and Profiling for Microwave Susceptors
Effective Date
01-Apr-2014
Referred By
ASTM F17-20 - Standard Terminology Relating to Primary Barrier Packaging
Effective Date
01-Apr-2014
Referred By
ASTM F1317-98(2019) - Standard Test Method for Calibration of Microwave Ovens
Effective Date
01-Apr-2014

Buy Standard

ASTM F1349-08(2014) - Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave SusceptorsASTM F1349-08(2014) - Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors
PreviousNext
Standard
ASTM F1349-08(2014) - Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors
English language
5 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:F1349 −08 (Reapproved 2014)
Standard Test Method for
Nonvolatile Ultraviolet (UV) Absorbing Extractables from
1
Microwave Susceptors
This standard is issued under the fixed designation F1349; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3.2 High-Pressure Liquid Chromatograph (HPLC), consist-
ing of:
1.1 This test method covers the determination of nonpolar
3.2.1 Pump, capable of 1.5 mL/min with flow precision
and relatively polar ultraviolet (UV) absorbing components
62%.
that may migrate from microwave susceptor packaging into
3.2.2 Injector, loop-type, equipped with 20-µL loop.
food simulants, such as corn oil and Miglyol 812.
3.2.3 Guard Column, C , 5 µm.
8
1.2 This test method has been collaboratively studied using
3.2.4 Analytical Column, C , 5 µm, 250 by 4.6 mm.
8
bilaminatesusceptorsconstructedofpaperboard,adhesive,and
3.2.5 Detector-UV Absorbance, set for 254 nm. Adjust
a layer of polyethylene terephthalate polymer (PETE) suscep-
sensitivity to give a 70 to 100 % of full scale peak for the 5-
tor. Adhesive and PETE related compounds were quantitated
ppm dimethylterephthalate DMT standard.
using this test method.
3.2.6 Gradient Program, 4 to 60 % Mobile Phase B in 8
min; 60 to 70 % B in 9 min; 70 to 100 % B in 7 min; 100 % B
1.3 The values stated in SI units are to be regarded as
standard. No other units of measurement are included in this for 11 min; 100 to 4 % B in 5 min; 4 % B for minimum of 5
min. Where Mobile Phase A (v/v) is 85 + 15 + 0.25 %
standard.
water:acetonitrile:acetic acid, and Mobile Phase B (v/v)is
1.4 This standard does not purport to address all of the
15 + 85 % water:acetonitrile.
safety concerns, if any, associated with its use. It is the
3.2.7 Peak Area Integration System—Initialize data acqui-
responsibility of the user of this standard to establish appro-
sition or integration system, or both, from 5 to 35 min during
priate safety and health practices and determine the applica-
the separation.
bility of regulatory limitations prior to use. Specific warning
statements are given in 4.3.2.3.
3.3 Hexane, LC/UV grade.
3.4 Acetonitrile, LC/UV grade.
2. Referenced Documents
2
3.5 Corn Oil—Obtain corn oil that is as pure and fresh as
2.1 ASTM Standards:
possible to minimize peaks in nonvolatiles extractables chro-
F874 Test Method for Temperature Measurement and Pro-
matogram. Alternatively, Miglyol 812 (a fractionated coconut
filing for Microwave Susceptors
oil)orsyntheticfatsimulantHB307canbeusedasasubstitute
F1317 Test Method for Calibration of Microwave Ovens
for corn oil.
3. Apparatus and Reagents
3.6 Dimethylacetamide (DMAC), LC/UV grade.
3.1 Microwave Oven, 700 6 35 W, calibrated. Refer to Test
3.7 Conical Bottom Test Tubes, 50 mL, graduated.
Method F1317.
3.8 Bishydroxyethyleneterephthalate (BHET).
3.9 Diethylterephthalate (DET).
1
This test method is under the jurisdiction ofASTM Committee F02 on Flexible
Barrier Packaging and is the direct responsibility of Subcommittee F02.15 on
3.10 Dimethylterephthalate (DMT).
Chemical/Safety Properties.
Current edition approved April 1, 2014. Published April 2014. Originally 3.11 Fluoroptic Thermometry System.
approved in 1991. Last previous edition approved in 2008 as F1349 – 08. DOI:
3.12 Temperature Probes, four, high temperature.
10.1520/F1349-08R14.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
3.13 Glass Beads, 3 to 4 mm, clean thoroughly by rinsing
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
with methylene chloride followed by soaking for 30 min in
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. acetonitrile. Dry thoroughly before using.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
F1349−08 (2014)
1
NOTE 1—The ⁄16-in. (1.6-mm) diameter hole is for a Luxtron MIW
temperature sensing probe. Number of holes and location may vary by
application.
FIG. 1Collar Section of Waldorf Polytetrafluoroethylene Micro-
wave Nonvolatile Extraction Cell
NOTE 1—Relieve thread at bottom. Collar must seal to bottom of cap.
FIG. 2Cap Section of Waldorf Polytetrafluorethylene Nonvolatile
Extraction Cell
2

---------------------- Page: 2 ----------------------
F1349−08 (2014)
FIG. 3 Suggested Modifications to Waldorf Cell
3.14 Recommended Microwave Nonvolatile Extraction activesusceptormaterial.Thesusceptorshouldbecuttofitinto
3
Cell—Waldorf Polytetrafluoroethylene cell. (See Figs. 1-3). a Wal
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM F2227-13(2021)(Test Method)
Standard Test Method for Non-Destructive Detection of Leaks in Non-sealed and Empty Packaging Trays by CO2 Tracer Gas Method

SIGNIFICANCE AND USE
5.1 Harmful biological or particulate contaminants may enter the package through imperfections such as pinholes or cracks in trays.  
5.2 After initial instrument set-up and calibration, the operations of individual tests and test results do not need operator interpretation.  
5.3 Leak test results that exceed the permissible threshold setting are indicated by audible or visual signal responses, or both, or by other means.  
5.4 This non-destructive test method may be performed in either laboratory or production environments and may be undertaken on either a 100 % or a statistical sampling basis. This test method, in single instrument use and current implementation, may not be fast enough to work on a production packaging line, but is well suited for statistical testing as well as package developmental design work.
SCOPE
1.1 This non-destructive test method detects pinhole leaks in trays, as small as 50 μm (0.002 in.) in diameter, or equivalently sized cracks, subject to trace gas concentration in the tray, tray design and manufacturing tolerances.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM F2228-13(2021)(Test Method)
Standard Test Method for Non-Destructive Detection of Leaks in Packaging Which Incorporates Porous Barrier Material by CO2 Tracer Gas Method

SIGNIFICANCE AND USE
5.1 Harmful biological or particulate contaminants may enter the package through incomplete seals or imperfections such as pinholes or cracks in the trays.  
5.2 After initial instrument set-up and calibration, the operations of individual tests and test results do not need operator interpretation. The non-destructive nature of the test may be important when testing high value added products.  
5.3 Leak test results that exceed the permissible threshold setting are indicated by audible or visual signal responses, or both, or by other means.  
5.4 This non-destructive test method may be performed in either laboratory or production environments. This testing may be undertaken on either a 100 % or a statistical sampling basis. This test method, in single instrument use and current implementation, may not be fast enough to work on a production packaging line, but is well suited for statistical testing as well as package developmental design work.
SCOPE
1.1 This non-destructive test method detects leaks in non-porous rigid thermoformed trays, as well as the seal between the porous lid and the tray. The test method detects channel leaks in packages as small as 100 μm (0.004 in.) diameter in the seal as well as 50 μm (0.002 in.) diameter pinholes, or equivalently sized cracks in the tray, subject to trace gas concentration in the package, package design and manufacturing tolerances.
Note 1: This test method does not claim to challenge the porous (breathable) lidding material. Any defects that may exist in the porous portion of the package will not be detected by this test method.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM F1349-08(2019)(Test Method)
Standard Test Method for Nonvolatile Ultraviolet (UV) Absorbing Extractables from Microwave Susceptors

ABSTRACT
This test method establishes the apparatuses required, the standard procedures, and associated calculations involved in the determination of relatively polar nonvolatile ultraviolet (UV) absorbing extractable components that may migrate from microwave susceptor packaging into food simulants, such as corn oil and Miglyol 812. This test method has been collaboratively studied using bilaminate susceptors constructed of paperboard, adhesive, and a layer of polyethylene terephthalate polymer (PETE) susceptor.
SCOPE
1.1 This test method covers the determination of nonpolar and relatively polar ultraviolet (UV) absorbing components that may migrate from microwave susceptor packaging into food simulants, such as corn oil and Miglyol 812.  
1.2 This test method has been collaboratively studied using bilaminate susceptors constructed of paperboard, adhesive, and a layer of polyethylene terephthalate polymer (PETE) susceptor. Adhesive and PETE related compounds were quantitated using this test method.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific warning statements are given in 4.3.2.3.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D6855-17(2023)(Test Method)
Standard Test Method for Determination of Turbidity Below 5 NTU in Static Mode

SIGNIFICANCE AND USE
5.1 Turbidity is undesirable in drinking water, plant effluent waters, water for food and beverage processing, and for a large number of other water-dependent manufacturing processes. Removal is often accomplished by coagulation, settling, and filtration. Measurement of turbidity provides a rapid means of process control for when, how, and to what extent the water must be treated to meet specifications.  
5.2 This test method is suitable to turbidity such as that found in drinking water, process water, and high purity industrial water.  
5.3 When reporting the measured result, appropriate units should also be reported. The units are reflective of the technology used to generate the result, and if necessary, provide more adequate comparison to historical data sets.  
5.3.1 Table 1 describes technologies and reporting results (see also Refs (1-3)).6 Those technologies listed are appropriate for the range of measurement prescribed in this test method. Others may come available in the future. Fig. X5.1 provides a flow chart to aid in selection of the appropriate technology for low-level static turbidity applications.  
5.3.2 If a design that falls outside of the criteria listed in Table 1 is used, the turbidity should be reported in turbidity units (TU) with a subscripted wavelength value to characterize the light source that was used.
SCOPE
1.1 This test method covers the static determination of turbidity in water (see 4.1).  
1.2 This test method is applicable to the measurement of turbidities under 5.0 nephelometric turbidity units (NTU).  
1.3 This test method was tested on municipal drinking water, ultra-pure water, and low turbidity samples. It is the users responsibility to ensure the validity of this test method for waters of untested matrices.  
1.4 This test method uses calibration standards are defined in NTU values, but other assigned turbidity units are assumed to be equivalent.  
1.5 This test method assigns traceable reporting units to the type of respective technology that was used to perform the measurement. Units are numerically equivalent with respect to the calibration standard. For example, a 1.0 NTU formazin standard is also equal to a 1.0 FNU standard, a 1.0 FNRU standard, and so forth.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Refer to the MSDSs for all chemicals used in this test method.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    15 pages
    English language
    sale 15% off
ASTM
ASTM E1316-23b(Terminology)
Standard Terminology for Nondestructive Examinations

SIGNIFICANCE AND USE
3.1 The terms found in this standard are intended to be used uniformly and consistently in all nondestructive testing standards. The purpose of this standard is to promote a clear understanding and interpretation of the NDT standards in which they are used.
SCOPE
1.1 This standard covers the terminology used in the standards prepared by the E07 Committee on Nondestructive Testing. These nondestructive testing (NDT) methods include: acoustic emission, electromagnetic testing, gamma- and X-radiology, leak testing, liquid penetrant testing, magnetic particle testing, neutron radiology and gauging, ultrasonic testing, and other technical methods.  
1.2 Committee E07 recognizes that the terms examination, testing, and inspection are commonly used as synonyms in nondestructive testing. For uniformity and consistency in E07 nondestructive testing standards, Committee E07 encourages the use of the terms examination or inspection and their derivatives when describing the application of nondestructive test methods. In a specific standard, either examination or inspection shall be used consistently throughout the document. Similarly, E07 encourages the use of the term test and its derivatives when referring to the body of knowledge of a nondestructive testing method. There are, however, appropriate exceptions when the term test and its derivatives may be used to describe the application of a nondestructive test, such as measurements which produce a numeric result (for example, when using the leak testing method to perform a leak test on a component, or an ultrasonic measurement of velocity). Additionally, the term test should be used when referring to the NDT method, that is, Radiologic Testing (RT), Ultrasonic Testing (UT), and so forth. (Example: Radiologic Testing (RT) is often used to examine material to detect internal discontinuities.)
Note 1: The following sentences clarify this policy and illustrate its use:
(a) Nondestructive testing methods are used extensively for the examination or inspection of materials and components.
(b) The E07 Committee on Nondestructive Testing has prepared many documents to promote uniform usage of the nondestructive testing methods that are applied to examine or inspect materials and components.  
(c) Radiologic Testing (RT) is often used to inspect material to detect internal discontinuities.
(d) Magnetic Particle Testing (MT), Liquid Penetrant Testing (PT), and Visual Testing (VT) are often used to examine the surface of a component.
(e) The Bubble Leak Testing (BLT) method is sometimes used to leak test a pressure containing component to detect leaks.
(f) A guide for Nondestructive Testing of additively manufactured materials will describe several methods but a practice will focus on a single inspection method.  
1.3 Section A defines terms that are common to multiple NDT methods, whereas the subsequent sections define terms pertaining to specific NDT methods.  
1.4 As shown on the chart below, when a nondestructive examination or inspection produces an indication, the indication is subject to interpretation as false, nonrelevant, or relevant. If it has been interpreted as relevant, the necessary subsequent evaluation will result in the decision to accept or reject the material. With the exception of accept and reject, which retain the meaning found in most dictionaries, all the words used in the chart are defined in Section A.    
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    41 pages
    English language
    sale 15% off
  • Standard
    41 pages
    English language
    sale 15% off
ASTM
ASTM E2546-15(2023)(Practice)
Standard Practice for Instrumented Indentation Testing

SIGNIFICANCE AND USE
5.1 IIT Instruments are used to quantitatively measure various mechanical properties of thin coatings and other volumes of material when other traditional methods of determining material properties cannot be used due to the size or condition of the sample. This practice will establish the basic requirements for those instruments. It is intended that IIT based test methods will be able to refer to this practice for the basic requirements for force and displacement accuracy, reproducibility, verification, reporting, etc., that are necessary for obtaining meaningful test results.  
5.2 IIT is not restricted to specific test forces, displacement ranges, or indenter types. This practice covers the requirements for a wide range of nano, micro, and macro (see ISO 14577-1) indentation testing applications. The various IIT instruments are required to adhere to the requirements of the practice within their specific design ranges.
SCOPE
1.1 This practice defines the basic steps of Instrumented Indentation Testing (IIT) and establishes the requirements, accuracies, and capabilities needed by an instrument to successfully perform the test and produce the data that can be used for the determination of indentation hardness and other material characteristics. IIT is a mechanical test that measures the response of a material to the imposed stress and strain of a shaped indenter by forcing the indenter into a material and monitoring the force on, and displacement of, the indenter as a function of time during the full loading-unloading test cycle.  
1.2 The operational features of an IIT instrument, as well as requirements for Instrument Verification (Annex A1), Standardized Reference Blocks (Annex A2) and Indenter Requirements (Annex A3) are defined. This practice is not intended to be a complete purchase specification for an IIT instrument.  
1.3 With the exception of the non-mandatory Appendix X4, this practice does not define the analysis necessary to determine material properties. That analysis is left for other test methods. Appendix X4 includes some basic analysis techniques to allow for the indirect performance verification of an IIT instrument by using test blocks.  
1.4 Zero point determination, instrument compliance determination and the indirect determination of an indenter’s area function are important parts of the IIT process. The practice defines the requirements for these items and includes non-mandatory appendixes to help the user define them.  
1.5 The use of deliberate lateral displacements is not included in this practice (that is, scratch testing).  
1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    24 pages
    English language
    sale 15% off
ASTM
ASTM E2862-23(Practice)
Standard Practice for Probability of Detection Analysis for Hit/Miss Data

SIGNIFICANCE AND USE
5.1 The POD analysis method described herein is based on a well-known and well established statistical regression method. It shall be used to quantify the demonstrated POD for a specific set of examination parameters and known range of discontinuity sizes under the following conditions.  
5.1.1 The initial response from a nondestructive evaluation inspection system is ultimately binary in nature (that is, hit or miss).  
5.1.2 Discontinuity size is the predictor variable and can be accurately quantified.  
5.1.3 A relationship between discontinuity size and POD exists and is best described by a generalized linear model with the appropriate link function for binary outcomes.  
5.2 This practice does not limit the use of a generalized linear model with more than one predictor variable or other types of statistical models if justified as more appropriate for the hit/miss data.  
5.3 If the initial response from a nondestructive evaluation inspection system is measurable and can be classified as a continuous variable (for example, data collected from an Eddy Current inspection system), then Practice E3023 may be more appropriate.  
5.4 Prior to performing the analysis it is assumed that the discontinuity of interest is clearly defined; the number and distribution of induced discontinuity sizes in the POD specimen set is known and well-documented; discontinuities in the POD specimen set are unobstructed; and the POD examination administration procedure (including data collection method) is well-designed, well-defined, under control, and unbiased. The analysis results are only valid if convergence is achieved and the model adequately represents the data.  
5.5 The POD analysis method described herein is consistent with the analysis method for binary data described in MIL-HDBK-1823A, and is included in several widely utilized POD software packages to perform a POD analysis on hit/miss data. It is also found in statistical software packages that have generalized line...
SCOPE
1.1 This practice covers the procedure for performing a statistical analysis on nondestructive testing hit/miss data to determine the demonstrated probability of detection (POD) for a specific set of examination parameters. Topics covered include the standard hit/miss POD curve formulation, validation techniques, and correct interpretation of results.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    14 pages
    English language
    sale 15% off
  • Standard
    14 pages
    English language
    sale 15% off
ASTM
ASTM E165/E165M-23(Practice)
Standard Practice for Liquid Penetrant Testing for General Industry

SIGNIFICANCE AND USE
5.1 Liquid penetrant testing methods indicate the presence, location, and to a limited extent, the nature and magnitude of the detected discontinuities. Each of the various penetrant methods has been designed for specific uses such as critical service items, volume of parts, portability, or localized areas of examination. The method selected will depend accordingly on the design and service requirements of the parts or materials being tested.
SCOPE
1.1 This practice2 covers procedures for penetrant examination of materials. Penetrant testing is a nondestructive testing method for detecting discontinuities that are open to the surface such as cracks, seams, laps, cold shuts, shrinkage, laminations, through leaks, or lack of fusion and is applicable to in-process, final, and maintenance examinations. It can be effectively used in the examination of nonporous, metallic materials, ferrous and nonferrous metals, and of nonmetallic materials such as nonporous glazed or fully densified ceramics, as well as certain nonporous plastics, and glass.  
1.2 This practice also provides a reference:  
1.2.1 By which a liquid penetrant examination process recommended or required by individual organizations can be reviewed to ascertain its applicability and completeness.  
1.2.2 For use in the preparation of process specifications and procedures dealing with the liquid penetrant testing of parts and materials. Agreement by the customer requesting penetrant testing is strongly recommended. All areas of this practice may be open to agreement between the cognizant engineering organization and the supplier, or specific direction from the cognizant engineering organization.  
1.2.3 For use in the organization of facilities and personnel concerned with liquid penetrant testing.  
1.3 This practice does not indicate or suggest criteria for evaluation of the indications obtained by penetrant testing. It should be pointed out, however, that after indications have been found, they must be interpreted or classified and then evaluated. For this purpose there must be a separate code, standard, or a specific agreement to define the type, size, location, and direction of indications considered acceptable, and those considered unacceptable.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    19 pages
    English language
    sale 15% off
  • Standard
    19 pages
    English language
    sale 15% off
ASTM
ASTM E3370-23(Practice)
Standard Practice for Matrix Array Ultrasonic Testing of Composites, Sandwich Core Constructions, and Metals

SIGNIFICANCE AND USE
5.1 The procedures described in this practice have proven utility in the inspecting (1) monolithic polymer matrix composites (laminates) for bulk defects, (2) metals for corrosion during the service life of the part of interest, (3) thickness checks, (4) adhesive bonding of metals, composites, and sandwich core constructions, (5) coatings, and (6) composite filament windings. Both unpressurized, and with suitable precautions, pressurized materials and components are inspected.  
5.2 This practice provides guidelines for the application of longitudinal wave examination to the detection and quantitative evaluation of damage, discontinuities, and thickness variations in materials.  
5.3 This practice is intended primarily for the testing of parts to acceptance criteria most typically specified in a purchase order or other contractual document, and for testing of parts in-service to detect and evaluate damage.  
5.4 MAUT search units provide near-surface resolution and detection of small discontinuities comparable to phased array transducers. They may or may not be capable of beam steering. The advantage of MAUT for straight-beam longitudinal wave inspections is the ability to provide real-time C-scan data, which facilitates data interpretation and shortens inspection time. Depending on inspection needs, data can be displayed as A-, B- or C-scans, or three-dimensional renderings. Toggling between pulse-echo and through transmission ultrasonic (TTU) modes without having to use another system or changing transducers is also possible.  
5.5 The MAUT technique has proven utility in the inspection of multi-ply carbon-fiber reinforced laminates used in primary aircraft structures.11  
5.6 For ultrasonic testing of laminate composites and sandwich core materials using conventional UT equipment consult Practice E2580. Consult Practice E114 for ultrasonic testing of materials by the pulse-echo method using straightbeam longitudinal waves introduced by a piezoelectric elemen...
SCOPE
1.1 This practice covers procedures for matrix array ultrasonic testing (MAUT) of monolithic composites, composite sandwich constructions, and metallic test articles. These procedures can be used throughout the life cycle of a part during product and process design optimization, on line process control, post-manufacturing inspection, and in-service inspection.  
1.2 In general, ultrasonic testing is a common volumetric method for detection of embedded or subsurface discontinuities. This practice includes general requirements and procedures which may be used for detecting flaws and for making a relative or approximate evaluation of the size of discontinuities and part anomalies. The types of flaws or discontinuities detected include interply delaminations, foreign object debris (FOD), inclusions, disbond/un-bond, fiber debonding, fiber fracture, porosity, voids, impact damage, thickness variation, and corrosion.  
1.3 Typical test articles include monolithic composite layups such as uniaxial, cross ply and angle ply laminates, sandwich constructions, bonded structures, and filament windings, as well as forged, wrought and cast metallic parts. Two techniques can be considered based on accessibility of the inspection surface: namely, pulse echo inspection for one-sided access and through-transmission for two-sided access. As used in this practice, both require the use of a pulsed straight-beam ultrasonic longitudinal wave followed by observing indications of either the reflected (pulse-echo) or received (through transmission) wave.  
1.4 This practice provides two ultrasonic test procedures. Each has its own merits and requirements for inspection and shall be selected as agreed upon in a contractual document.  
1.4.1 Test Procedure A, Pulse Echo (non-contacting and contacting) is at a minimum a single matrix array transducer transmitting and receiving longitudinal waves in the range of 0.5 MHz to 20 MHz (see Fig. 1). Th...

  • Standard
    14 pages
    English language
    sale 15% off
  • Standard
    14 pages
    English language
    sale 15% off
ASTM
ASTM E1901-23(Guide)
Standard Guide for Detection and Evaluation of Discontinuities by Contact Pulse-Echo Straight-Beam Ultrasonic Methods

SIGNIFICANCE AND USE
6.1 This guide provides procedures for the application of contact straight-beam examination for the detection and quantitative evaluation of discontinuities in materials.  
6.2 Although not all requirements of this guide can be applied universally to all examinations, situations, and materials, it does provide basis for establishing contractual criteria between the users, and may be used as a general guide for preparing detailed specifications for a particular application.  
6.3 This guide is directed towards the evaluation of discontinuities detectable with the beam normal to the entry surface. If discontinuities or other orientations are of concern, alternate scanning techniques are required.
SCOPE
1.1 This guide covers procedures for the contact ultrasonic examination of bulk materials or parts by transmitting pulsed ultrasonic waves into the material and observing the indications of reflected waves. This guide covers only examinations in which one search unit is used as both transmitter and receiver (pulse-echo). This guide includes general requirements and procedures that may be used for detecting discontinuities, locating depth and distance from a point of reference and for making a relative or approximate evaluation of the size of discontinuities as compared to a reference standard.  
1.2 This guide complements Practice E114 by providing more detailed procedures for the selection and standardization of the examination system and for evaluation of the indications obtained.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This guide does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this guide to establish the appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    7 pages
    English language
    sale 15% off
  • Guide
    7 pages
    English language
    sale 15% off